CN1085579A - 新型防水聚乙烯醇复合材料(烯酯复合材料)及其制法和用途 - Google Patents

新型防水聚乙烯醇复合材料(烯酯复合材料)及其制法和用途 Download PDF

Info

Publication number
CN1085579A
CN1085579A CN 93118533 CN93118533A CN1085579A CN 1085579 A CN1085579 A CN 1085579A CN 93118533 CN93118533 CN 93118533 CN 93118533 A CN93118533 A CN 93118533A CN 1085579 A CN1085579 A CN 1085579A
Authority
CN
China
Prior art keywords
polyvinyl alcohol
composite material
water
purposes
alcohol composite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 93118533
Other languages
English (en)
Inventor
刘永浩
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 93118533 priority Critical patent/CN1085579A/zh
Publication of CN1085579A publication Critical patent/CN1085579A/zh
Pending legal-status Critical Current

Abstract

一种聚乙烯醇复合材料，它是由聚乙烯醇与三聚 氰胺，甲醛与尿素进行缩聚，并加入氧化石蜡，三乙氧 基硅烷，丁二醇，邻苯二甲酸二乙酯改性而制得的聚 合物混合物，将此聚合物混合物再加入二氧化硅及钛 酸酯进行交联，注入模具制成各种制品，具有耐油、耐 水、耐磨等优点，用作建筑用的防水层或再配成胶粘 剂，用途十分广阔。

Description

本发明涉及一种以聚乙烯醇为主要原料的复合材料及其制法和用途，特别涉及一种防水型的聚乙烯醇复合材料及其制法和用途。
众所周知，聚乙烯醇的成型制品和涂料是不防水的，因此限制了其用途，例如目前作建筑材料的防水层大部分采用沥青油毡，虽然有各种各样的改性沥青出现但还不能根除漏水的缺点，最近出现的防水复合材料也由于价格昂贵，施工困难，故也难于大规模开发和采用。故寻求一种价兼易得的原料加以改性使其赋有优良的防水能力是当前研究的课题。
本发明的目的在于提供一种以聚乙烯醇为原料，进行改性使其具有防水能力的复合材料和胶粘剂，适合于建筑上的防水层或防水涂料，适合于屋面防漏雨、厕所防水、地下工程及仓库防潮的良好复合材料或胶粘剂。该复合材料的商品名称为烯酯复合材料。
本发明的实施方案是在聚乙烯醇水溶液下加入酸化剂使三聚氰胺进行聚合，并在氯化蜡、三乙氧基硅烷、丁二醇、邻苯二甲酸二乙酯等溶剂和增塑下进行改性制成白色乳液，然后再加入甲醛和尿素并缩合成尿醛的聚合物混合物，再用硅酸钠中和控制PH为6-7加入填料二氧化硅或轻质碳酸钙并以钛酸酯为偶联剂，注入各种模具中制成各种具有橡胶、塑料两种性能，具有优良的防水耐油、耐温、抗老化、耐摩擦的复合材料制品，或将上述的聚合物混合物与二氧化硅、水、硅烷偶联剂混合制成防水胶粘剂是建筑上价兼物美的防水胶粘剂。
本发明的具体实施方案如下：
（1）混合聚合物的配方及其制备工艺
（ⅱ）配方（重量份）
聚乙烯醇  100
盐酸35%  12-15
三聚氰胺  18-22
水  1000
氧化石蜡  6-8
三乙氧基硅烷  2-4
丁二醇  1-2
邻苯二甲酸二乙酯  4-6
甲醛  15-20
尿素  4-6
硅酸钠  约1（调PH＝6-7）
（ⅱ）制备工艺条件：
将聚乙烯醇与水在溶解槽内加热到95  C，待完全溶解后温度降低到75℃-80℃之间，加入35%盐酸作催化剂，然后加入三聚氰胺水溶液，再升温到85℃-95℃，再加入氧化石蜡、三乙氧基硅烷、丁二醇、邻苯二甲酸二乙酯进行改性和增塑，再加入甲醛与尿素进行缩聚，最后用硅酸钠中和至PH＝6-7即成混合聚合物。
（2）聚乙烯醇复合材料的配方及制备工艺
（ⅰ）配方（重量份）
上述制备的混合聚合物  100
气相二氧化硅  10-12
或轻质碳酸钙  5-8
钛酸酯（偶联剂）  2-4
（ⅱ）制备工艺条件
在通用反应器内加入上述制备的混合聚合物，然后按量加入气相二氧化硅或轻质碳酸钙及钛酸酯反应温度在室温下进行交联，然后配色，注入模具，在35℃-45℃的温度下固化就可制备各种制品，当然也可进行喷涂浇注等成型方法，制品性能柔软、能耐水、耐油、抗老化、耐摩擦等优点，可代替橡胶与塑料的复合材料。
下面的优选例对本发明作详细说明，但不限制本发明的范围。
例1  （1）在一个带有搅拌容积为1.5立方米的反应器内加入聚乙烯醇（聚合度为1700，醇解度为99%）100公斤和水1000公斤，开动搅拌，升温加热到95℃+2℃，使聚乙烯醇全部溶解，停止加热，待温度降低到78℃时，加入35%盐酸13公斤，然后加入三聚氰胺20公斤，温度控制在87+2℃之间，再加入氯化石蜡7公斤，三乙氧基硅烷3公斤，丁二醇1.5公斤，邻苯二甲酸二乙酯5公斤，继续搅拌，待料液温度下降到80℃后，加入甲醛15公斤，尿素5公斤，保持室温4小时后，用硅酸钠1公斤中和使其PH＝6.7，即成为混合聚合物，共得1151公斤。
（2）将上述混合聚合物100公斤，气相二氧化硅11公斤钛酸脂3公斤，加入通用反应器内在室温下进行交联，然后将此交联物配色及注入模具在40+2℃下固化成本发明的聚乙烯醇复合材料片（厚3m/m）。其性能是：抗张强度380kg/cm2，冲击张度10kg/cm2，伸长率50%，吸水率0.2%（24小时），脆点-25℃，耐热95℃（24小时）。
例2 除甲醛改为20公斤外，其余条件不变，所得复合材料片（厚3m/m），其性能是抗张强度420kg/cm2，冲击强度12kg/cm2，伸长率60%，吸水率0.2%（24小时），脆点-25℃，耐热95℃（24小时）。
例3  将例1制成的混合聚合物100公斤，二氧化硅80公斤，水15公斤和硅烷偶联剂2公斤于混合器内配制成防水胶粘剂共197公斤，经分析其耐热95℃，耐冻-20℃，耐汽油60天无变化，粘结性大于0.5泊。
本发明的优点如下：
（1）本复合材料耐水、耐油、耐磨性能优越，其有橡胶与塑料的性能，可代替橡胶和塑料。
（2）本复合材料非常适合于屋面防水层，地下室防湿层。
（3）本复合材料制法简便。

Claims (3)

1、一种新型防水聚乙烯醇复合材料，其特征在于：
(1)混合聚合物的配方(重量份)
聚乙烯醇          100
盐酸35%           12-15
三聚氰胺          18-22
水                1000
氧化石蜡          6-8
三乙氧基硅烷      2-4
丁二醇            1-2
邻苯二甲酸二乙酯  4-6
甲醛              15-20
尿素              4-6
硅酸钠            约1(调PH=6.7)
(2)复合材料的配方(重量份)
混合聚合物    100
气相二氧化硅  10-12
(或轻质碳酸钙5-8)
钛酸酯        2-4
2、一种新型防水聚乙烯醇复合材料的制备方法，其特征在于
（1）聚乙烯醇在水温95℃下进行溶解
（2）在（1）溶液中加入三聚氰胺水溶液的温度为85-95℃
（3）在（2）溶液中加入甲醛和尿素的缩合温度为室温
（4）最后混合聚合物用硅酸钠中和至PH＝6-7
3、一种新型防水聚乙烯醇复合材料的用途，其特征在于：按权利要求1的配方所得的复合材料，可应用于建筑上的防水层，如屋面防漏，墙壁防水，地下室防湿层，以及再配成胶粘剂。
CN 93118533 1993-10-12 1993-10-12 新型防水聚乙烯醇复合材料(烯酯复合材料)及其制法和用途 Pending CN1085579A (zh)