CN108530001B - 一种电石渣制备的白色墙体饰面砂浆 - Google Patents

一种电石渣制备的白色墙体饰面砂浆 Download PDF

Info

Publication number
CN108530001B
CN108530001B CN201810701026.7A CN201810701026A CN108530001B CN 108530001 B CN108530001 B CN 108530001B CN 201810701026 A CN201810701026 A CN 201810701026A CN 108530001 B CN108530001 B CN 108530001B
Authority
CN
China
Prior art keywords
carbide slag
facing mortar
parts
wall facing
white
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201810701026.7A
Other languages
English (en)
Other versions
CN108530001A (zh
Inventor
兰明章
聂松
王剑锋
张巧伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Beijing University of Technology
Original Assignee
Beijing University of Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Beijing University of Technology filed Critical Beijing University of Technology
Priority to CN201810701026.7A priority Critical patent/CN108530001B/zh
Publication of CN108530001A publication Critical patent/CN108530001A/zh
Application granted granted Critical
Publication of CN108530001B publication Critical patent/CN108530001B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供了一种电石渣制备的白色墙体饰面砂浆，该砂浆由电石渣、白水泥、重钙、石英砂、可再分散乳胶粉以及其它外加剂组成。本发明的饰面砂浆采用了电石渣作为胶凝材料，对于减少工业废渣对环境的污染和降低了生产成本具有重要的意义。另外，高贝利硫铝酸盐水泥水化生成膨胀钙矾石，有利于提高饰面砂浆的抗裂性能。本发明的饰面砂浆具有优异的柔韧性、抗折强度、抗压强度、透气性等，适用于建筑墙体的装饰。

Description

一种电石渣制备的白色墙体饰面砂浆
技术领域
本发明涉及一种对墙体起装饰作用的饰面砂浆，尤其涉及一种以电石渣和白水泥为胶凝材料的白色饰面砂浆，属于建筑材料领域。
背景技术
电石渣的主要成分是Ca(OH)2，是电石水解制备乙炔时的副产物，属于工业废渣。由于电石渣的产量大、含水量高、碱性强，若不对其进行回收处理，而将其长期堆放和晾晒，这将占用大量土地资源。同时，还能使土壤和水体碱性化，造成严重的环境污染。
目前，我国综合回收利用电石渣主要的方式是生产水泥。然而，电石渣在使用之前需对其进行烘干处理，能耗高。
另一方面，饰面砂浆一种可广泛应用于建筑墙体或顶棚的新型装饰材料，主要由无机胶凝材料、填料、石英砂、颜料及各种添加剂组成，颜色变化范围广，施工与造型方便。饰面砂浆的吸水率低，透气性好，使用厚度一般小于6mm，并且对水泥砂浆等基面材料具有良好的粘结性，不易开裂和脱落。饰面砂浆在欧洲等发达国家已经广泛替代涂料、瓷砖和板材，用作于建筑物墙体装饰材料。
国内传统的墙体饰面砂浆多以水泥为主要无机胶凝材料，在应用过程中容易出现开裂等问题。为解决这些问题，研究人员通常在饰面砂浆中引入大量可再分散乳胶粉来提升柔韧性，而可再分散乳胶粉的价格较高，造成饰面砂浆的造价昂贵；还有研究人员通过掺入适量纤维来改善饰面砂浆的柔韧性，但纤维会使砂浆流动度降低，加大施工难度，这些都阻碍了墙体饰面砂浆的推广与使用。
发明内容
本发明的目的是提供一种白色的墙体饰面砂浆，使其不仅价格低廉而且具有良好的柔韧性、力学性能和抗老化性能。
为了达到上述目的，本发明的技术方案提供了一种白色饰面砂浆，该饰面砂浆包括以下重量份的组份组成：电石渣50-70份(以干重计，全文中没有特殊说明电石渣的份数都为干重)，白水泥15-30份，重钙粉5-15份，可再分散乳胶粉6-20份，石英砂200-300份，憎水剂0.1-0.8份，缓凝剂0.1-0.4份，减水剂0-0.3份；其中电石渣、白水泥、重钙和可再分散乳胶粉之和为100份。
所述白水泥为高贝利特硫铝酸盐水泥，强度等级为42.5。
所述重钙为200-400目的重钙粉。
所述可再分散乳胶粉为醋酸乙烯酯-乙烯共聚乳胶粉或醋酸乙烯-乙烯共聚乳胶粉。
所述憎水剂为有机硅憎水剂。
所述缓凝剂为硼酸。
所述减水剂为聚羧酸减水剂。
本发明的白色墙体饰面砂浆，以电石渣、白水泥为无机胶凝材料，并加入重钙、石英砂、可再分散乳胶粉和其它外加剂配制而成。电石渣是一种气硬性胶凝材料，具有良好的柔韧性，并且高贝利特硫铝酸盐水泥水化生成一种膨胀晶体钙矾石，可以提高饰面砂浆的抗裂性能。本发明的白色饰面砂浆采用电石渣作为主要无机胶凝材料，减少了可再分散乳胶粉的用量，降低了砂浆的生产成本，并且具有优异的抗折、抗压强度等物理性能。
具体实施方式
下面结合实例来进一步说明本发明。
实施例1
一种白色墙体饰面砂浆由以下重量份的原料组成：电石渣58份，高贝利特硫铝酸盐水泥24份，重钙粉10份，醋酸乙烯酯-乙烯共聚乳胶粉8份，石英砂200份，道康宁有机硅粉末憎水剂SHP50型0.4份，硼酸0.1份，高效聚羧酸减水剂C900型0.1份，湿电石渣含水量和外加水共50份。
按照原料配比，先将干粉原料混合均匀，制备成干组分。然后，将含水的电石渣和适量的水加入搅拌锅中，再加入干组分，搅拌均匀。该饰面砂浆的性能指标如下表所示：
Figure BDA0001714396110000031
注：表中性能测试方法参照JC/T 1024-2007《墙体饰面砂浆》。
实施例2
一种白色墙体饰面砂浆由以下重量份的原料组成：电石渣67份，高贝利特硫铝酸盐水泥18份，重钙粉5份，醋酸乙烯酯-乙烯共聚乳胶粉10份，石英砂250份，道康宁有机硅粉末憎水剂SHP50型0.3份，硼酸0.1份，高效聚羧酸减水剂C900型0.1份，湿电石渣含水量和外加水共53份。
本实施例所述的饰面砂浆制备方法与实施例1相同，其性能指标如下表所示：
Figure BDA0001714396110000032
注：表中性能测试方法参照JC/T 1024-2007《墙体饰面砂浆》。

Claims (6)

1.一种电石渣制备的白色墙体饰面砂浆，其特征在于，该饰面砂浆包括以下重量份的组份组成：以干重计算的电石渣50-70份，白水泥15-30份，重钙粉5-15份，可再分散乳胶粉6-20份，石英砂200-300份，憎水剂0.1-0.8份，缓凝剂0.1-0.4份，减水剂0-0.3份；其中电石渣、白水泥、重钙和可再分散乳胶粉之和为100份；
所述白水泥为高贝利特硫铝酸盐水泥，强度等级为42.5。
2.根据权利要求1所述的一种电石渣制备的白色墙体饰面砂浆，其特征在于，所述重钙为200-400目的重钙粉。
3.根据权利要求1所述的一种电石渣制备的白色墙体饰面砂浆，其特征在于，所述可再分散乳胶粉为醋酸乙烯酯-乙烯共聚乳胶粉或醋酸乙烯-乙烯共聚乳胶粉。
4.根据权利要求1所述的一种电石渣制备的白色墙体饰面砂浆，其特征在于，所述憎水剂为有机硅憎水剂。
5.根据权利要求1所述的一种电石渣制备的白色墙体饰面砂浆，其特征在于，所述缓凝剂为硼酸。
6.根据权利要求1所述的一种电石渣制备的白色墙体饰面砂浆，其特征在于，所述减水剂为聚羧酸减水剂。
CN201810701026.7A 2018-06-29 2018-06-29 一种电石渣制备的白色墙体饰面砂浆 Active CN108530001B (zh)