CN112897976A - 一种轻质抹灰柠檬酸石膏砂浆 - Google Patents
一种轻质抹灰柠檬酸石膏砂浆 Download PDFInfo
- Publication number
- CN112897976A CN112897976A CN202110253385.2A CN202110253385A CN112897976A CN 112897976 A CN112897976 A CN 112897976A CN 202110253385 A CN202110253385 A CN 202110253385A CN 112897976 A CN112897976 A CN 112897976A
- Authority
- CN
- China
- Prior art keywords
- citric acid
- gypsum
- acid gypsum
- mortar
- citric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于砂浆技术领域，具体涉及一种轻质抹灰柠檬酸石膏砂浆。一种轻质抹灰柠檬酸石膏砂浆，所述砂浆以柠檬酸石膏粉、重钙粉、河砂、玻化微珠混合为骨料；以可再分散乳胶粉、纤维素醚、触变剂、引气剂混合为母料，最后将骨料与母料搅拌混合得到轻质抹灰柠檬酸石膏砂浆，其中柠檬酸石膏粉是α‑半水柠檬酸石膏和β‑半水柠檬酸石膏的混合物，本发明将柠檬酸石膏进行废物利用，不仅变废为宝，而且有效发挥了抹灰石膏砂浆抗空鼓、抗开裂、绿色环保等优点，并提高了建筑品质。
Description
技术领域
本发明属于砂浆技术领域，具体涉及一种轻质抹灰柠檬酸石膏砂浆。
背景技术
抹灰石膏砂浆是一种高效节能的建筑物室内墙面及顶棚抹灰材料，是传统水泥砂浆、石灰砂浆的升级产品，是一种新型的室内装饰装修材料。然而天然石膏作为抹灰石膏砂浆的主要原料，其市场需求巨大；但多数天然石膏生产企业也都面临着环保和天然石膏资源限制的双重压力，这种情况直接影响到抹灰石膏砂浆的成本和市场推广应用。
在这样的国家大背景下，利用柠檬酸副产石膏生产轻质抹灰柠檬酸石膏砂浆为柠檬酸生产企业提供一条行之有效的固废处理的道路。
目前，较为常见的工业副产石膏有脱硫石膏、柠檬酸石膏、磷石膏等。根据石膏产品的质量要求，脱硫石膏和磷石膏仅是白度指标就无法满足石膏产品要求，而且由于这两种石膏都含有大量硫酸钙以外的杂质，在生产石膏粉的过程需要复杂的预处理过程，进一步生产石膏产品时又需要加入多种促进剂才能达到石膏产品的抗折、抗压的指标要求；利用脱硫石膏或磷石膏生产的石膏产品，不仅在成本上高于天然石膏产品，而且其建筑施工性也达不到要求。在这些方面，柠檬酸石膏具有得天独厚的优势：柠檬酸石膏中硫酸钙含量高，只含有少量柠檬酸杂质，简单预处理即可除去，用其生产的石膏粉无论是在白度还是抗折、抗压方面，都接近甚至超过了天然石膏。
发明内容
为克服现有技术的缺陷，本发明一方面为了实现柠檬酸副产石膏的固废综合利用，另一方面，为了解决石膏资源限制，扩大抹灰石膏砂浆市场应用，提供了一种轻质抹灰柠檬酸石膏砂浆，不仅变废为宝，而且有效发挥了抹灰石膏砂浆抗空鼓、抗开裂、绿色环保等优点，并提高了建筑品质。
本发明通过以下技术方案实现：
一种轻质抹灰柠檬酸石膏砂浆，以柠檬酸石膏、重钙粉、河砂、玻化微珠混合为骨料；以可再分散乳胶粉、纤维素醚、触变剂、引气剂混合为母料，最后将骨料与母料搅拌混合得到轻质抹灰柠檬酸石膏砂浆。
具体地，以生产1000kg轻质抹灰柠檬酸石膏砂浆计算，所述骨料中各原料的用量如下：柠檬酸石膏800.0kg、重钙粉30.0-80.0kg、河砂40.0-80.0kg、玻化微珠40.0-100.0kg。
具体地，以生产1000kg轻质抹灰柠檬酸石膏砂浆计算，所述母料中各原料的用量如下：可再分散乳胶粉2.0-6.0kg、纤维素醚1.0-5.0kg、触变剂0.5kg、引气剂0.2kg。
具体地，所述柠檬酸石膏是α-半水柠檬酸石膏和β-半水柠檬酸石膏的混合物。
进一步地，所述α-半水柠檬酸石膏为100-160目；所述β-半水柠檬酸石膏为300-500目；以生产1000kg轻质抹灰柠檬酸石膏砂浆计算，所述柠檬酸石膏中各原料的用量如下：α-半水柠檬酸石膏100.0-300.0kg、β-半水柠檬酸石膏500.0-700.0kg。
进一步地，所述α-半水柠檬酸石膏是通过对柠檬酸生产产生的副产石膏进行预处理除去杂质，烘干除去游离水，蒸压，陈化，获得α-半水柠檬酸石膏。
进一步地，所述β-半水柠檬酸石膏是通过对柠檬酸生产产生的副产石膏进行预处理除去杂质，烘干除去游离水，球磨，煅烧，陈化，获得β-半水柠檬酸石膏。
进一步地，所述重钙粉为150-200目；所述河砂为70-90目；所述玻化微珠为70-90目。
进一步地，所述可再分散乳胶粉为醋酸乙烯酯、乙烯共聚粉等市售可再分散乳胶粉中的任意一种或多种组合。
进一步地，所述纤维素醚粘度为4-15MPa•s。
进一步地，所述触变剂为硅酸镁铝、膨润土等市售触变剂中的任意一种或多种组合。
进一步地，所述引气剂为松香树脂类引气剂、烷基苯磺酸盐类引气剂或脂肪醇磺酸盐类引气剂中的一种或多种组合。
现在砂浆市场95%的都是使用脱硫石膏。脱硫石膏存在产品颜色发黄、粒径大（约100目）、基配差、施工性能差；而本发明使用的β半水柠檬酸石膏的粒径小（约500目）、白度高，α-半水柠檬酸石膏的强度高（比β还要高）、粒径约100目，二者混合基配好、施工性能好。
本发明将柠檬酸石膏进行废物利用，制成抹灰柠檬酸石膏砂浆，不仅变废为宝，而且有效发挥了抹灰石膏砂浆抗空鼓、抗开裂、绿色环保等优点，并提高了建筑品质。
本发明所制备的抹灰柠檬酸石膏砂浆具有保水性好、黏结力大、保温、隔热、耐火等特点，其最大优点是凝固后微膨胀性，不仅有效解决了因水泥砂浆保水性差、干后收缩大，造成墙体空鼓、裂缝等建筑质量通病，同时本发明所采用的主要原料是由生产柠檬酸所产生的副产石膏加工生产的，实现了资源的综合利用，保护环境的同时也节约了资源。
本发明的有益效果：
第一，有效解决了柠檬酸石膏作为固体废弃物难处理、污染大的问题，不仅变废为宝，而且柠檬酸石膏的生产工艺简单、成本投入低、零排放；
第二，柠檬酸石膏相对于天然石膏或其它化学石膏具有品位高、白度高、容重低的突出特点，具体表现在轻质抹灰柠檬酸石膏砂浆中的优势就是单位重量的轻质抹灰柠檬酸石膏砂浆涂布率高可轻易达到P160的标准，白度高可减少后续涂刮腻子的次数、有效的省工省料，粘结强度及抗压强度高、抗空鼓、抗开裂、绿色环保。
具体实施方式
下面通过多份实施例和对比例对本发明的技术方案进行清楚、完整地描述，显然，下面所描述的实施例仅仅是本发明的一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
本发明提供了一种轻质抹灰柠檬酸石膏砂浆，以柠檬酸石膏、重钙粉、河砂、玻化微珠混合为骨料；以可再分散乳胶粉、纤维素醚、触变剂、引气剂混合为母料，最后将骨料与母料搅拌混合得到轻质抹灰柠檬酸石膏砂浆。
其中所述柠檬酸石膏是α-半水柠檬酸石膏和β-半水柠檬酸石膏的混合物。
具体地，所述α-半水柠檬酸石膏是通过对柠檬酸生产产生的副产石膏进行预处理除去杂质，烘干除去游离水，蒸压，陈化，获得α-半水柠檬酸石膏。
具体地，所述β-半水柠檬酸石膏是通过对柠檬酸生产产生的副产石膏进行预处理除去杂质，烘干除去游离水，球磨，煅烧，陈化，获得β-半水柠檬酸石膏。
应该说明的是：本发明中所述α-半水柠檬酸石膏和β-半水柠檬酸石膏的生产工艺仅是经过优选的较成熟的工艺方法，并不用于限制本发明，对于本领域的技术人员来说，依然可以对上述实施例所述的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所做的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
实施例1
以生产1000kg轻质抹灰柠檬酸石膏砂浆计算，其组成和原料用量如下：以α-半水柠檬酸石膏121.8kg、β-半水柠檬酸石膏678.2kg、60.0kg重钙粉、53.0kg河砂、80.0kg玻化微珠混合为骨料；以3.3kg可再分散乳胶粉、3.0kg纤维素醚、0.5kg硅酸镁铝、0.2kg烷基苯磺酸盐类混合为母料，最后将骨料与母料搅拌混合得到轻质抹灰柠檬酸石膏砂浆；其中所用的α-半水柠檬酸石膏为140目；所用的β-半水柠檬酸石膏为400目；所用的重钙粉为200目；所用的河砂为70-90目；所用的玻化微珠为70-90目；所用的纤维素醚的粘度为10MPa•s。
实施例2
以生产1000kg轻质抹灰柠檬酸石膏砂浆计算，其组成和原料用量如下：以α-半水柠檬酸石膏171.8kg、β-半水柠檬酸石膏628.2kg、50.0kg重钙粉、63.0kg河砂、80.0kg玻化微珠混合为骨料；以3.8kg可再分散乳胶粉、2.5kg纤维素醚、0.5kg膨润土、0.2kg松香树脂类引气剂混合为母料，最后将骨料与母料搅拌混合得到轻质抹灰柠檬酸石膏砂浆；其中所用的α-半水柠檬酸石膏为140目；所用的β-半水柠檬酸石膏为400目；所用的重钙粉为200目；所用的河砂为70-90目；所用的玻化微珠为70-90目；所用的纤维素醚的粘度为10MPa•s。
实施例3
以生产1000kg轻质抹灰柠檬酸石膏砂浆计算，其组成和原料用量如下：以α-半水柠檬酸石膏221.8kg、β-半水柠檬酸石膏578.2kg、40.0kg重钙粉、73.0kg河砂、80.0kg玻化微珠混合为骨料；以4.3kg可再分散乳胶粉、2.0kg纤维素醚、0.5kg触变剂、0.2kg脂肪醇磺酸盐类混合为母料，最后将骨料与母料搅拌混合得到轻质抹灰柠檬酸石膏砂浆；其中所用的α-半水柠檬酸石膏为140目；所用的β-半水柠檬酸石膏为400目；所用的重钙粉为200目；所用的河砂为70-90目；所用的玻化微珠为70-90目；所用的纤维素醚的粘度为10MPa•s。
对比例1
本对比例与实施例1相比，用市售天然石膏代替柠檬酸石膏，除此之外的原料种类、用量均相同。
对比例2
本对比例与实施例1相比，用市售脱硫石膏代替柠檬酸石膏，除此之外的原料种类、用量均相同。
对比例3
本对比例与实施例1相比，用市售磷石膏代替柠檬酸石膏，除此之外的原料种类、用量均相同。
各实施例、对比例的力学性能如下表所示：
数据显示，实施例1、实施例2、实施例3在各方面的力学性能均接近使用天然石膏的对比例1，甚至是优于对比例1；在保水性方面，实施例1优于对比例1，说明本发明提供的轻质抹灰柠檬酸石膏砂浆的抗开裂性能更好；在涂布率方面，实施例1优于对比例1，说明本发明提供的轻质抹灰柠檬酸石膏砂浆的施工成本要低于使用天然石膏的对比例1；而且，实施例1、实施例2、实施例3的各力学性能均比对比例2、对比例3要好，这说明本发明提供的轻质抹灰柠檬酸石膏砂浆的性能指标和施工性能比使用脱硫石膏的对比例2、使用磷石膏对比例3要好，进一步地证明本发明提供的轻质抹灰柠檬酸石膏砂浆可以作为传统的轻质抹灰石膏砂浆的升级产品。
本发明有效解决了柠檬酸石膏作为固体废弃物难处理、污染大的问题，不仅变废为宝，而且柠檬酸石膏的生产工艺简单、成本投入低、零排放；施工过程能有效的省工省料，粘结强度及抗压强度高、抗空鼓、抗开裂、绿色环保。
最后应说明的是：以上所述实施例仅是本发明的优选的较佳的实施例，并不用于限制本发明，尽管参照上述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，依然可以对上述实施例所述的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所做的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (6)
1.一种轻质抹灰柠檬酸石膏砂浆，其特征在于，以生产1000kg轻质抹灰柠檬酸石膏砂浆计算，其组成和原料用量如下：以800.0kg柠檬酸石膏、30.0-80.0kg重钙粉、40.0-80.0kg河砂、40.0-100.0kg玻化微珠混合为骨料；以2.0-6.0kg可再分散乳胶粉、1.0-5.0kg纤维素醚、0.5kg触变剂、0.2kg引气剂混合为母料。
2.根据权利要求1所述的柠檬酸石膏砂浆，其特征在于，所述柠檬酸石膏是α-半水柠檬酸石膏和β-半水柠檬酸石膏的混合物。
3.根据权利要求2所述的柠檬酸石膏砂浆，其特征在于，所述α-半水柠檬酸石膏为100-160目；所述β-半水柠檬酸石膏为300-500目；以生产1000kg轻质抹灰柠檬酸石膏砂浆计算，所述柠檬酸石膏中各原料的用量如下：α-半水柠檬酸石膏100.0-300.0kg、β-半水柠檬酸石膏500.0-700.0kg。
4.根据权利要求1所述的柠檬酸石膏砂浆，其特征在于，所述重钙粉为150-200目；所述河砂为70-90目；所述玻化微珠为70-90目。
5.根据权利要求1所述的柠檬酸石膏砂浆，其特征在于，所述纤维素醚粘度为4-15MPa•s。
6.根据权利要求1所述的柠檬酸石膏砂浆，其特征在于，所述引气剂为松香树脂类引气剂、烷基苯磺酸盐类引气剂和脂肪醇磺酸盐类引气剂中的一种或多种组合。