CN108486414A - 压铸钛合金 - Google Patents
压铸钛合金 Download PDFInfo
- Publication number
- CN108486414A CN108486414A CN201810686661.2A CN201810686661A CN108486414A CN 108486414 A CN108486414 A CN 108486414A CN 201810686661 A CN201810686661 A CN 201810686661A CN 108486414 A CN108486414 A CN 108486414A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- die casting
- titanium alloy
- casting titanium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种压铸钛合金,包括如下重量份原料:Si:3‑7.8重量份;P:9‑20重量份;Ni:6‑20重量份;W:5‑15重量份;B:8‑22重量份;La:7‑16重量份;Y:8‑32重量份;Ti:1680‑1800重量份。本发明的有益效果为:其具有较好的导热导电性能。
Description
技术领域
本发明涉及合金技术领域,具体涉及一种压铸钛合金。
背景技术
现有的压铸钛合金导热导电性能还存在一定的不足。
发明内容
本发明的目的在于提供一种压铸钛合金,其具有较好的导热导电性能。
为实现上述目的,本发明的技术方案是
一种压铸钛合金,包括如下重量份原料:
Si:3-7.8重量份;
P:9-20重量份;
Ni:6-20重量份;
W:5-15重量份;
B:8-22重量份;
La:7-16重量份;
Y:8-32重量份;
Ti:1680-1800重量份。
本发明的工作原理为:La的加入增加了合金的导热导电性能。
本发明的有益效果为:其具有较好的导热导电性能。
具体实施方式
下面结合实施例,对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案,而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是:
实施例1
一种压铸钛合金,包括如下重量份原料:
Si:3重量份;
P:9重量份;
Ni:6重量份;
W:5重量份;
B:8重量份;
La:7重量份;
Y:8重量份;
Ti:1680重量份。
实施例2
一种压铸钛合金,包括如下重量份原料:
Si:7.8重量份;
P:20重量份;
Ni:20重量份;
W:15重量份;
B:22重量份;
La:16重量份;
Y:32重量份;
Ti:1800重量份。
实施例3
一种压铸钛合金,包括如下重量份原料:
Si:8重量份;
P:15重量份;
Ni:12重量份;
W:10重量份;
B:11重量份;
La:10重量份;
Y:22重量份;
Ti:1750重量份。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明技术原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (1)
1.一种压铸钛合金,其特征在于,包括如下重量份原料:
Si:3-7.8重量份;
P:9-20重量份;
Ni:6-20重量份;
W:5-15重量份;
B:8-22重量份;
La:7-16重量份;
Y:8-32重量份;
Ti:1680-1800重量份。