CN108642338A - 压铸铝合金 - Google Patents
压铸铝合金 Download PDFInfo
- Publication number
- CN108642338A CN108642338A CN201810686751.1A CN201810686751A CN108642338A CN 108642338 A CN108642338 A CN 108642338A CN 201810686751 A CN201810686751 A CN 201810686751A CN 108642338 A CN108642338 A CN 108642338A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- present
- pack alloy
- pack
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种压铸铝合金,包括如下重量份原料:Si:7‑12重量份;P:1‑6重量份;W:8‑15重量份;Mg:2‑17重量份;Ti:3‑6重量份;B:9‑14重量份;La:7‑15重量份;Y:8‑20重量份;Ce:4‑13重量份;Al:1008‑1100重量份。本发明的有益效果为:其具有较好的导热导电性能。
Description
技术领域
本发明涉及合金技术领域,具体涉及一种压铸铝合金。
背景技术
现有的压铸合金导热导电性能还存在一定的不足。
发明内容
本发明的目的在于提供一种压铸铝合金,其具有较好的导热导电性能。
为实现上述目的,本发明的技术方案是
一种压铸铝合金,包括如下重量份原料:
Si:7-12重量份;
P:1-6重量份;
W:8-15重量份;
Mg:2-17重量份;
Ti:3-6重量份;
B:9-14重量份;
La:7-15重量份;
Y:8-20重量份;
Ce:4-13重量份;
Al:1008-1100重量份。
本发明的工作原理为:La和Ce的加入增加了合金的导热导电性能。
本发明的有益效果为:其具有较好的导热导电性能。
具体实施方式
下面结合实施例,对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案,而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是:
实施例1
一种压铸铝合金,包括如下重量份原料:
Si:7重量份;
P:1重量份;
W:8重量份;
Mg:2重量份;
Ti:3重量份;
B:9重量份;
La:7重量份;
Y:8重量份;
Ce:4重量份;
Al:1008重量份。
实施例2
一种压铸铝合金,包括如下重量份原料:
Si:12重量份;
P:6重量份;
W:15重量份;
Mg:17重量份;
Ti:6重量份;
B:14重量份;
La:15重量份;
Y:20重量份;
Ce:13重量份;
Al:1100重量份。
实施例3
一种压铸铝合金,包括如下重量份原料:
Si:10重量份;
P:5重量份;
W:9重量份;
Mg:16重量份;
Ti:4重量份;
B:11重量份;
La:12重量份;
Y:10重量份;
Ce:7重量份;
Al:1050重量份。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明技术原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (1)
1.一种压铸铝合金,其特征在于,包括如下重量份原料:
Si:7-12重量份;
P:1-6重量份;
W:8-15重量份;
Mg:2-17重量份;
Ti:3-6重量份;
B:9-14重量份;
La:7-15重量份;
Y:8-20重量份;
Ce:4-13重量份;
Al:1008-1100重量份。