CN108477765A - A kind of processing method of fire-retardant magic tape - Google Patents
A kind of processing method of fire-retardant magic tape Download PDFInfo
- Publication number
- CN108477765A CN108477765A CN201810117028.1A CN201810117028A CN108477765A CN 108477765 A CN108477765 A CN 108477765A CN 201810117028 A CN201810117028 A CN 201810117028A CN 108477765 A CN108477765 A CN 108477765A
- Authority
- CN
- China
- Prior art keywords
- magic tape
- hook
- hair
- fire
- hook side
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention is a kind of processing method of fire-retardant magic tape, it is impregnated in the mixed liquor that fire retardant and common dyes are mixed in semi-finished product germ band, flame retarding function is imparted while dyeing, shaping glue to improving the strength of coating of magic tape in normal state, further improve fire retardancy, magic tape is when the pipelines such as high-temperature flue, water channel and air flue for 120 150 DEG C of temperature are as magic tape is fastened, magic tape is indeformable, intensity does not decline, it does not fail, meanwhile present invention process is easy to implement.
Description
Technical field
The present invention relates to textile technology field more particularly to a kind of processing methods of fire-retardant magic tape.
Background technology
Magic tape is a kind of connection auxiliary material, is used extensively, and clothes, footwear, watchband and binding harness are can be used as.It is domestic
The outer existing magic tape to circulate in the market is mainly chinlon gluing buckle, and small part is polyester fiber adhesive fastening strip etc., chinlon gluing buckle hook
Material is polyamide fibre 66, and 93 DEG C of glass transition temperature, 253 DEG C of heat fusion joint temperature, remaining warp thread and weft material are polyamide fibre 6, heat fusion joint
It it is 215 DEG C, polyester fiber adhesive fastening strip material is terylene, and heat fusion joint is 256 DEG C.These magic tapes are being higher than 100 DEG C of height for temperature
When the pipelines such as warm flue, water channel and air flue fasten magic tape, high temperature makes magic tape soften, deformation and intensity drastically decline and lose
Effect, while this kind of magic tape does not have flame retarding function, just to have flame retarding function through special flame-proof treatment.
Invention content
Present invention seek to address that the deficiencies in the prior art, and a kind of processing method of fire-retardant magic tape is provided.
The present invention to achieve the above object, using following technical scheme：
A kind of processing method of fire-retardant magic tape, step include：
(1) coiled hair and germ band are made, raw material are fabricated to coiled hair through high-speed warping machine, then the coiled hair made is passed through
Inkle loom makes semi-finished product germ band；
(2) it impregnates：Semi-finished product germ band is impregnated in the mixed liquor that fire retardant and dyestuff are mixed, impregnates 70-
90 minutes, solution PH 3.8, treatment temperature was 55-65 DEG C；So that semi-finished product germ band becomes required color, and assign fire-retardant
Function；
(3) it dries：Semi-finished product germ band after immersion enters drying box and carries out moisture drying, and temperature is controlled at 120-130 DEG C,
The speed run in pre-baking box is 8m/min；
(4) hair side is made, the Polyamide Yarns on the hair side germ band surface after drying is carried out again after raising machine brush plays frizzle
Glue sizing treatment；
(5) hook side is made, the hook side germ band after drying is first subjected to gluing sizing treatment, then by the Buddhist nun on hook side germ band surface
Imperial monofilament carries out the broken hook processing of hook side by breaking hook machine；
(6) glue in shaping, by hair side and hook side carry out it is whole scald and Shape correction, by after shaping hair side and hook side go to glue
In sink, polyurethane colloidal sol is coated with to hair side and hook side surface；
(7) it dries：Magic tape after glue is cured by the steam roller that vapor (steam) temperature is 170-180 DEG C, steam rolling
Cylinder speed is 8-12 minutes/circle；The steam roller maturation that magic tape after solidification is again 140-155 DEG C by vapor (steam) temperature, steams
Vapour drum speed is 15-20 minutes/circle, can be obtained finished product after maturation；
(8) cooling, the product after drying enters cooling cylinder and carries out cooling treatment；
(9) divide, adjust the cut size of hair side and hook side, and slot segmentation is set in corresponding position, then setting
Hair side and hook side with slot segmentation, which are placed on banding machine, carries out dividing processing；
(10) it packs, the hair side divided and hook side is subjected to plastics package.
Preferably, fire retardant uses polyolefin halogen-free flame retardants in the step (2).
Preferably, dyestuff is reactive dye in the step (2), and the addition volume ratio of dyestuff and fire retardant is 1: 3.
Preferably, hair side germ band base surface is dacron thread and Polyamide Yarns mixing material in the step (4), and hair side is polyamide fibre
Wire material.
Preferably, hook side germ band base surface is dacron thread and Polyamide Yarns mixing material in the step (5), and hook side is nylon
Monofilament material.
The beneficial effects of the invention are as follows：It is soaked in the mixed liquor that fire retardant and dyestuff are mixed in semi-finished product germ band
Bubble imparts flame retarding function while dyeing, and shaping glue to improving the strength of coating of magic tape in normal state, into
One step improves fire retardancy, and magic tape is in pipelines such as high-temperature flue, water channel and air flues for 120-150 DEG C of temperature as solid
When tight magic tape, magic tape is indeformable, and intensity does not decline, and does not fail, meanwhile, present invention process is easy to implement.
Specific implementation mode
The present invention is further explained in the light of specific embodiments：
A kind of processing method of fire-retardant magic tape, step include：
(1) coiled hair and germ band are made, raw material are fabricated to coiled hair through high-speed warping machine, then the coiled hair made is passed through
Inkle loom makes semi-finished product germ band；
(2) it impregnates：Semi-finished product germ band is impregnated in the mixed liquor that fire retardant and dyestuff are mixed, impregnates 70-
90 minutes, solution PH 3.8, treatment temperature was 55-65 DEG C；So that semi-finished product germ band becomes required color, and assign fire-retardant
Function；
(3) it dries：Semi-finished product germ band after immersion enters drying box and carries out moisture drying, and temperature is controlled at 120-130 DEG C,
The speed run in pre-baking box is 8m/min；
(4) hair side is made, the Polyamide Yarns on the hair side germ band surface after drying is carried out again after raising machine brush plays frizzle
Glue sizing treatment；
(5) hook side is made, the hook side germ band after drying is first subjected to gluing sizing treatment, then by the Buddhist nun on hook side germ band surface
Imperial monofilament carries out the broken hook processing of hook side by breaking hook machine；
(6) glue in shaping, by hair side and hook side carry out it is whole scald and Shape correction, by after shaping hair side and hook side go to glue
In sink, polyurethane colloidal sol is coated with to hair side and hook side surface；
(7) it dries：Magic tape after glue is cured by the steam roller that vapor (steam) temperature is 170-180 DEG C, steam rolling
Cylinder speed is 8-12 minutes/circle；The steam roller maturation that magic tape after solidification is again 140-155 DEG C by vapor (steam) temperature, steams
Vapour drum speed is 15-20 minutes/circle, can be obtained finished product after maturation；
(8) cooling, the product after drying enters cooling cylinder and carries out cooling treatment；
(9) divide, adjust the cut size of hair side and hook side, and slot segmentation is set in corresponding position, then setting
Hair side and hook side with slot segmentation, which are placed on banding machine, carries out dividing processing；
(10) it packs, the hair side divided and hook side is subjected to plastics package.
Preferably, fire retardant uses polyolefin halogen-free flame retardants in the step (2).
Preferably, dyestuff is reactive dye in the step (2), and the addition volume ratio of dyestuff and fire retardant is 1: 3.
Preferably, hair side germ band base surface is dacron thread and Polyamide Yarns mixing material in the step (4), and hair side is polyamide fibre
Wire material.
Preferably, hook side germ band base surface is dacron thread and Polyamide Yarns mixing material in the step (5), and hook side is nylon
Monofilament material.
Embodiment 1：
A kind of processing method of fire-retardant magic tape, step include：
(1) coiled hair and germ band are made, raw material are fabricated to coiled hair through high-speed warping machine, then the coiled hair made is passed through
Inkle loom makes semi-finished product germ band；
(2) it impregnates：Semi-finished product germ band is impregnated in the mixed liquor that fire retardant and dyestuff are mixed, impregnates 80 points
Clock, solution PH 3.8, treatment temperature are 60 DEG C；So that semi-finished product germ band becomes required color, and assign flame retarding function；
(3) it dries：Semi-finished product germ band after immersion enters drying box and carries out moisture drying, and temperature is controlled at 125 DEG C, pre-
The speed run in baking oven is 8m/min；
(4) hair side is made, the Polyamide Yarns on the hair side germ band surface after drying is carried out again after raising machine brush plays frizzle
Glue sizing treatment；
(5) hook side is made, the hook side germ band after drying is first subjected to gluing sizing treatment, then by the Buddhist nun on hook side germ band surface
Imperial monofilament carries out the broken hook processing of hook side by breaking hook machine；
(6) glue in shaping, by hair side and hook side carry out it is whole scald and Shape correction, by after shaping hair side and hook side go to glue
In sink, polyurethane colloidal sol is coated with to hair side and hook side surface；
(7) it dries：Magic tape after glue is cured by the steam roller that vapor (steam) temperature is 175 DEG C, steam roller speed
Degree is 12 minutes/circle；The steam roller maturation that magic tape after solidification is again 145 DEG C by vapor (steam) temperature, steam roller speed
For 15 minutes/circle, finished product can be obtained after maturation；
(8) cooling, the product after drying enters cooling cylinder and carries out cooling treatment；
(9) divide, adjust the cut size of hair side and hook side, and slot segmentation is set in corresponding position, then setting
Hair side and hook side with slot segmentation, which are placed on banding machine, carries out dividing processing；
(10) it packs, the hair side divided and hook side is subjected to plastics package.
Preferably, fire retardant uses polyolefin halogen-free flame retardants in the step (2).
Preferably, dyestuff is reactive dye in the step (2), and the addition volume ratio of dyestuff and fire retardant is 1: 3.
Preferably, hair side germ band base surface is dacron thread and Polyamide Yarns mixing material in the step (4), and hair side is polyamide fibre
Wire material.
Preferably, hook side germ band base surface is dacron thread and Polyamide Yarns mixing material in the step (5), and hook side is nylon
Monofilament material.
Embodiment 2：
A kind of processing method of fire-retardant magic tape, step include：
(1) coiled hair and germ band are made, raw material are fabricated to coiled hair through high-speed warping machine, then the coiled hair made is passed through
Inkle loom makes semi-finished product germ band；
(2) it impregnates：Semi-finished product germ band is impregnated in the mixed liquor that fire retardant and dyestuff are mixed, impregnates 70 points
Clock, solution PH 3.8, treatment temperature are 55 DEG C；So that semi-finished product germ band becomes required color, and assign flame retarding function；
(3) it dries：Semi-finished product germ band after immersion enters drying box and carries out moisture drying, and temperature is controlled at 120 DEG C, pre-
The speed run in baking oven is 8m/min；
(4) hair side is made, the Polyamide Yarns on the hair side germ band surface after drying is carried out again after raising machine brush plays frizzle
Glue sizing treatment；
(5) hook side is made, the hook side germ band after drying is first subjected to gluing sizing treatment, then by the Buddhist nun on hook side germ band surface
Imperial monofilament carries out the broken hook processing of hook side by breaking hook machine；
(6) glue in shaping, by hair side and hook side carry out it is whole scald and Shape correction, by after shaping hair side and hook side go to glue
In sink, polyurethane colloidal sol is coated with to hair side and hook side surface；
(7) it dries：Magic tape after glue is cured by the steam roller that vapor (steam) temperature is 170 DEG C, steam roller speed
Degree is 10 minutes/circle；The steam roller maturation that magic tape after solidification is again 140 DEG C by vapor (steam) temperature, steam roller speed
For 18 minutes/circle, finished product can be obtained after maturation；
(8) cooling, the product after drying enters cooling cylinder and carries out cooling treatment；
(9) divide, adjust the cut size of hair side and hook side, and slot segmentation is set in corresponding position, then setting
Hair side and hook side with slot segmentation, which are placed on banding machine, carries out dividing processing；
(10) it packs, the hair side divided and hook side is subjected to plastics package.
Preferably, fire retardant uses polyolefin halogen-free flame retardants in the step (2).
Preferably, dyestuff is reactive dye in the step (2), and the addition volume ratio of dyestuff and fire retardant is 1: 3.
Preferably, hair side germ band base surface is dacron thread and Polyamide Yarns mixing material in the step (4), and hair side is polyamide fibre
Wire material.
Preferably, hook side germ band base surface is dacron thread and Polyamide Yarns mixing material in the step (5), and hook side is nylon
Monofilament material.
Embodiment 3：
A kind of processing method of fire-retardant magic tape, step include：
(1) coiled hair and germ band are made, raw material are fabricated to coiled hair through high-speed warping machine, then the coiled hair made is passed through
Inkle loom makes semi-finished product germ band；
(2) it impregnates：Semi-finished product germ band is impregnated in the mixed liquor that fire retardant and dyestuff are mixed, impregnates 90 points
Clock, solution PH 3.8, treatment temperature are 65 DEG C；So that semi-finished product germ band becomes required color, and assign flame retarding function；
(3) it dries：Semi-finished product germ band after immersion enters drying box and carries out moisture drying, and temperature is controlled at 130 DEG C, pre-
The speed run in baking oven is 8m/min；
(4) hair side is made, the Polyamide Yarns on the hair side germ band surface after drying is carried out again after raising machine brush plays frizzle
Glue sizing treatment；
(5) hook side is made, the hook side germ band after drying is first subjected to gluing sizing treatment, then by the Buddhist nun on hook side germ band surface
Imperial monofilament carries out the broken hook processing of hook side by breaking hook machine；
(6) glue in shaping, by hair side and hook side carry out it is whole scald and Shape correction, by after shaping hair side and hook side go to glue
In sink, polyurethane colloidal sol is coated with to hair side and hook side surface；
(7) it dries：Magic tape after glue is cured by the steam roller that vapor (steam) temperature is 180 DEG C, steam roller speed
Degree is 8 minutes/circle；The steam roller maturation that magic tape after solidification is again 140 DEG C by vapor (steam) temperature, steam roller speed are
20 minutes/circle, it can be obtained finished product after maturation；
(8) cooling, the product after drying enters cooling cylinder and carries out cooling treatment；
(9) divide, adjust the cut size of hair side and hook side, and slot segmentation is set in corresponding position, then setting
Hair side and hook side with slot segmentation, which are placed on banding machine, carries out dividing processing；
(10) it packs, the hair side divided and hook side is subjected to plastics package.
Preferably, fire retardant uses polyolefin halogen-free flame retardants in the step (2).
Preferably, dyestuff is reactive dye in the step (2), and the addition volume ratio of dyestuff and fire retardant is 1: 3.
Preferably, hair side germ band base surface is dacron thread and Polyamide Yarns mixing material in the step (4), and hair side is polyamide fibre
Wire material.
Preferably, hook side germ band base surface is dacron thread and Polyamide Yarns mixing material in the step (5), and hook side is nylon
Monofilament material.
The present invention is exemplarily described above in conjunction with specific embodiment, it is clear that the present invention implements not by upper
The limitation of mode is stated, if the various improvement of inventive concept and technical scheme of the present invention progress are used, or it is not improved straight
It scoops out for other occasions, within protection scope of the present invention.
Claims (5)
1. a kind of processing method of fire-retardant magic tape, step include：
(1) coiled hair and germ band are made, raw material are fabricated to coiled hair through high-speed warping machine, then the coiled hair made is passed through into ribbon
Machine makes semi-finished product germ band；
(2) it impregnates：Semi-finished product germ band is impregnated in the mixed liquor that fire retardant and dyestuff are mixed, impregnates 70-90 points
Clock, solution PH 3.8, treatment temperature are 55-65 DEG C；So that semi-finished product germ band becomes required color, and assign flame retarding function；
(3) it dries：Semi-finished product germ band after immersion enters drying box and carries out moisture drying, and temperature is controlled at 120-130 DEG C, pre-
The speed run in baking oven is 8m/min；
(4) hair side is made, the Polyamide Yarns on the hair side germ band surface after drying is carried out gluing again after raising machine brush plays frizzle and is determined
Type processing；
(5) hook side is made, the hook side germ band after drying is first subjected to gluing sizing treatment, then by the nylon list on hook side germ band surface
Silk carries out the broken hook processing of hook side by breaking hook machine；
(6) glue in shaping, by hair side and hook side carry out it is whole scald and Shape correction, by after shaping hair side and hook side go to gum box
In, polyurethane colloidal sol is coated with to hair side and hook side surface；
(7) it dries：Magic tape after glue is cured by the steam roller that vapor (steam) temperature is 170-180 DEG C, steam roller speed
Degree is 8-12 minutes/circle；The steam roller maturation that magic tape after solidification is again 140-155 DEG C by vapor (steam) temperature, steam rolling
Cylinder speed is 15-20 minutes/circle, can be obtained finished product after maturation；
(8) cooling, the product after drying enters cooling cylinder and carries out cooling treatment；
(9) divide, adjust the cut size of hair side and hook side, and slot segmentation is set in corresponding position, then the band set point
It cuts the hair side of slot and hook side is placed on banding machine and carries out dividing processing；
(10) it packs, the hair side divided and hook side is subjected to plastics package.
2. the processing method of fire-retardant magic tape according to claim 1, which is characterized in that fire retardant in the step (2)
Using polyolefin halogen-free flame retardants.
3. the processing method of fire-retardant magic tape according to claim 1, which is characterized in that dyestuff is in the step (2)
The addition volume ratio of reactive dye, dyestuff and fire retardant is 1: 3.
4. the processing method of fire-retardant magic tape according to claim 1, which is characterized in that hair side embryo in the step (4)
Band base surface is dacron thread and Polyamide Yarns mixing material, and hair side is polyamide fibre wire material.
5. the processing method of fire-retardant magic tape according to claim 1, which is characterized in that hook side embryo in the step (5)
Band base surface is dacron thread and Polyamide Yarns mixing material, and hook side is nylon monofilament material.