CN113892732A - Method for manufacturing fireproof fastening tape - Google Patents
Method for manufacturing fireproof fastening tape Download PDFInfo
- Publication number
- CN113892732A CN113892732A CN202111121393.8A CN202111121393A CN113892732A CN 113892732 A CN113892732 A CN 113892732A CN 202111121393 A CN202111121393 A CN 202111121393A CN 113892732 A CN113892732 A CN 113892732A
- Authority
- CN
- China
- Prior art keywords
- fireproof
- embryonic band
- manufacturing
- fastening tape
- embryonic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a method for manufacturing a fireproof fastening tape, which is characterized by comprising the following steps of: a. selecting nylon filaments as a raw material and manufacturing a blank belt by a ribbon loom; c. putting the embryo belt into a dip dyeing machine, and cleaning the fireproof embryo belt for 15-20 minutes by using a cleaning agent at 50-60 ℃; d. whitening and finishing the cleaned embryonic band, and then dehydrating and drying; e. putting the dried fireproof embryonic band into high-temperature dyeing equipment for dyeing according to requirements to obtain a dyed embryonic band; b. weaving glass fiber warps, wefts and hot melt adhesive lines on the dyed embryonic band to form a fireproof embryonic band; f. carrying out gluing and sizing treatment on the hook surface of the fireproof embryonic band, and then carrying out hook breaking treatment on the hook surface by a hook breaking machine to form a hook surface embryonic band; g. and f, cutting the dyed fireproof embryonic band processed in the step f to obtain a finished product.
Description
Technical Field
The invention relates to the field of fastening tapes, in particular to a manufacturing method of a fireproof fastening tape.
Background
The flame-retardant fastening tape which is circulated in the market at present is widely applied to fasteners in vehicles such as airplanes and automobiles, when the fastening tape is processed, flame-retardant powder is generally added into coating glue, after the flame-retardant powder is added, the glue has a flame-retardant function, but smoke smell is heavy, toxicity is high, optical density is high during combustion, and the glue is harmful to personnel and environment safety, and meanwhile, powder is separated out from the glue surface of the fastening tape, and some powder is separated out
Oil spilling phenomenon, beautiful appearance, large tearing strength, poor solidification of colloid and fabric tissue, no tearing brittleness, unstable texture of the fastening tape and reduced fatigue resistance.
Disclosure of Invention
The technical problem to be solved by the present invention is to solve the above-mentioned deficiencies of the prior art,
provided is a method for manufacturing a fireproof fastening tape.
In order to achieve the purpose, the invention provides the following technical scheme: the manufacturing method of the fireproof fastening tape is characterized by comprising the following steps:
a. selecting nylon filaments as a raw material and manufacturing a blank belt by a ribbon loom;
c. putting the embryo belt into a dip dyeing machine, and cleaning the fireproof embryo belt for 15-20 minutes by using a cleaning agent at 50-60 ℃;
d. whitening and finishing the cleaned embryonic band, and then dehydrating and drying;
e. putting the dried fireproof embryonic band into high-temperature dyeing equipment for dyeing according to requirements to obtain a dyed embryonic band;
b. weaving glass fiber warps, wefts and hot melt adhesive lines on the dyed embryonic band to form a fireproof embryonic band;
f. carrying out gluing and sizing treatment on the hook surface of the fireproof embryonic band, and then carrying out hook breaking treatment on the hook surface by a hook breaking machine to form a hook surface embryonic band;
g. and f, cutting the dyed fireproof embryonic band processed in the step f to obtain a finished product.
The manufacturing method of the fireproof fastening tape can be further provided as follows: the glass fiber weft or warp and the hot melt adhesive thread are interwoven on the surface of the nylon filament.
The manufacturing method of the fireproof fastening tape can be further provided as follows: the cleaning in the step c comprises the steps of preparing a cleaning solution, wherein the formula of the cleaning solution is added to every 100kg of the embryonic band: emulsifier LF 1001 KG, flake base PJ 0.5-0.8KG, water 4000-4500 KG.
The manufacturing method of the fireproof fastening tape can be further provided as follows: the formula of the whitening finishing agent is that every 100kg of the embryo strip needs to be added with: emulsifier LF-1001-1.5 KG, flake base PJ 0.01-0.05KG, fluorescent essence SP 7000cc-7500cc, glacial acetic acid HAC 550-.
The manufacturing method of the fireproof fastening tape can be further provided as follows: and e, putting an anti-fading agent into high-temperature dyeing equipment in the step e, wherein the temperature of the equipment is controlled to be 90-95 ℃ during dyeing.
The manufacturing method of the fireproof fastening tape can be further provided as follows: and d, drying by adopting hot air of an oven in a drying mode, controlling the drying temperature to be 60-65 ℃ and the drying rate to be 7-10 meters per minute.
The manufacturing method of the fireproof fastening tape can be further provided as follows: and g, the cut finished product does not need to be impregnated with a fire retardant.
The manufacturing method of the fireproof sticking buckle can be further provided as follows: and f, gluing auxiliary agents adopted in gluing and shaping treatment in the step f comprise 90-10% of oily glue and 15-18% of N, N-dimethyl formamide DMF.
The invention has the beneficial effects that: the formed fastening tape does not need to be impregnated with a fire retardant, the glass fiber warps, wefts and hot melt adhesive lines woven in the fastening tape improve the fire resistance of the fastening tape, simplify the production process of the fire-proof fastening tape, reduce the production cost, and greatly improve the fire resistance of the fastening tape by the glass fibers.
Detailed Description
The first embodiment is as follows: the manufacturing method of the fireproof fastening tape is characterized by comprising the following steps:
a. selecting nylon filaments as a raw material and manufacturing a blank belt by a ribbon loom;
c. putting the embryonic band into a dip dyeing machine, and cleaning the fireproof embryonic band for 20 minutes by using a cleaning agent at 60 ℃;
d. whitening and finishing the cleaned embryonic band, and then dehydrating and drying;
e. putting the dried fireproof embryonic band into high-temperature dyeing equipment for dyeing according to requirements to obtain a dyed embryonic band;
b. weaving glass fiber warps, wefts and hot melt adhesive lines on the dyed embryonic band to form a fireproof embryonic band;
f. carrying out gluing and sizing treatment on the hook surface of the fireproof embryonic band, and then carrying out hook breaking treatment on the hook surface by a hook breaking machine to form a hook surface embryonic band;
g. cutting the dyed fireproof embryonic band processed in the step f to obtain a finished product;
preferably, the glass fiber weft or warp and the hot melt adhesive thread are interwoven on the surface of the nylon filament.
Preferably, the cleaning in step c includes preparing a cleaning solution, and the formula of the cleaning solution is added to every 100kg of the embryonic strip: emulsifier LF 1001 KG, flake base PJ 0.8KG, and water 4500 KG.
Preferably, the formula of the whitening finishing agent is that every 100kg of the embryonic band needs to be added with: emulsifier LF-1001.5 KG, flake alkali PJ 0.05KG, fluorescein SP 7500cc, glacial acetic acid HAC 600cc, water softener EP-60550 cc and water 5000 KG.
Preferably, the anti-fading agent is added into the high-temperature dyeing equipment in the step e, and the temperature of the equipment is controlled to be 95 ℃ during dyeing.
Preferably, the drying mode in the step d is drying by hot air in an oven, the drying temperature is controlled at 65 ℃, and the drying rate is controlled at 10 meters per minute.
Preferably, the cut product of step g does not need to be impregnated with a fire retardant.
Preferably, the formula of the gluing auxiliary agent adopted in the gluing and sizing treatment in the step f is 10% of oily glue and 18% of N, N-dimethyl formamide DMF;
example two: the manufacturing method of the fireproof fastening tape is characterized by comprising the following steps:
a. selecting nylon filaments as a raw material and manufacturing a blank belt by a ribbon loom;
c. putting the embryonic band into a dip dyeing machine, and cleaning the fireproof embryonic band for 15 minutes by using a 50-DEG C cleaning agent;
d. whitening and finishing the cleaned embryonic band, and then dehydrating and drying;
e. putting the dried fireproof embryonic band into high-temperature dyeing equipment for dyeing according to requirements to obtain a dyed embryonic band;
b. weaving glass fiber warps, wefts and hot melt adhesive lines on the dyed embryonic band to form a fireproof embryonic band;
f. carrying out gluing and sizing treatment on the hook surface of the fireproof embryonic band, and then carrying out hook breaking treatment on the hook surface by a hook breaking machine to form a hook surface embryonic band;
g. cutting the dyed fireproof embryonic band processed in the step f to obtain a finished product;
the glass fiber weft yarns or warp yarns and the hot melt adhesive threads are interwoven on the surface of the nylon filament yarns;
the cleaning in the step c comprises the steps of preparing a cleaning solution, wherein the formula of the cleaning solution is added to every 100kg of the embryonic band: emulsifier LF 1001 KG, flake base PJ 0.5KG, water 4000 KG;
the formula of the whitening finishing agent is that every 100kg of the embryo strip needs to be added with: emulsifier LF-1001-KG, flake base PJ 0.01KG, fluorescein SP 7000cccc, glacial acetic acid HAC 550cc, water softener EP-60450 cc, water 4000 KG;
e, putting an anti-fading agent into high-temperature dyeing equipment, wherein the temperature of the equipment is controlled to be 90 ℃ during dyeing;
d, drying by adopting a drying oven through hot air in a drying mode, wherein the drying temperature is controlled at 60 ℃, and the drying rate is controlled at 7 meters per minute;
g, the cut finished product does not need to be impregnated with a fire retardant;
and f, gluing auxiliary agents adopted in gluing and shaping treatment in the step f comprise 9% of oily glue and 15% of N, N-dimethyl formamide DMF.
Claims (8)
1. The manufacturing method of the fireproof fastening tape is characterized by comprising the following steps:
a. selecting nylon filaments as a raw material and manufacturing a blank belt by a ribbon loom;
c. putting the embryo belt into a dip dyeing machine, and cleaning the fireproof embryo belt for 15-20 minutes by using a cleaning agent at 50-60 ℃;
d. whitening and finishing the cleaned embryonic band, and then dehydrating and drying;
e. putting the dried fireproof embryonic band into high-temperature dyeing equipment for dyeing according to requirements to obtain a dyed embryonic band;
b. weaving glass fiber warps, wefts and hot melt adhesive lines on the dyed embryonic band to form a fireproof embryonic band;
f. carrying out gluing and sizing treatment on the hook surface of the fireproof embryonic band, and then carrying out hook breaking treatment on the hook surface by a hook breaking machine to form a hook surface embryonic band;
g. and f, cutting the dyed fireproof embryonic band processed in the step f to obtain a finished product.
2. The manufacturing method of the fireproof fastening tape according to claim 1, wherein: the glass fiber weft yarns or warp yarns and the hot melt adhesive threads are interwoven on the surfaces of the nylon filaments.
3. The manufacturing method of the fireproof fastening tape according to claim 1, wherein: the step c of cleaning comprises the step of preparing a cleaning solution, wherein the formula of the cleaning solution is added to every 100kg of the embryonic band: emulsifier LF 1001 KG, flake base PJ 0.5-0.8KG, water 4000-4500 KG.
4. The manufacturing method of the fireproof fastening tape according to claim 1, wherein: the formula of the whitening finishing agent is that every 100kg of the embryo tape needs to be added with: emulsifier LF-1001-1.5 KG, flake base PJ 0.01-0.05KG, fluorescent essence SP 7000cc-7500cc, glacial acetic acid HAC 550-.
5. The manufacturing method of the fireproof fastening tape according to claim 1, wherein: and e, putting an anti-fading agent into high-temperature dyeing equipment in the step e, wherein the temperature of the equipment is controlled to be 90-95 ℃ during dyeing.
6. The manufacturing method of the fireproof fastening tape according to claim 1, wherein: and d, drying by adopting a drying oven through hot air in the drying mode in the step d, controlling the drying temperature to be 60-65 ℃ and the drying rate to be 7-10 meters per minute.
7. The manufacturing method of the fireproof fastening tape according to claim 1, wherein: and g, the cut finished product does not need to be impregnated with a fire retardant.
8. The manufacturing method of the fireproof fastening tape according to claim 1, wherein: and f, the gluing auxiliary agent adopted in the gluing and sizing treatment in the step f comprises 90-10% of oily glue and 15-18% of N, N-dimethyl formamide DMF.