CN108301239A - A kind of method that Multifunctional aramid fiber is yarn beam printed - Google Patents
A kind of method that Multifunctional aramid fiber is yarn beam printed Download PDFInfo
- Publication number
- CN108301239A CN108301239A CN201810118544.6A CN201810118544A CN108301239A CN 108301239 A CN108301239 A CN 108301239A CN 201810118544 A CN201810118544 A CN 201810118544A CN 108301239 A CN108301239 A CN 108301239A
- Authority
- CN
- China
- Prior art keywords
- aramid fiber
- yarn
- function
- multifunctional
- type self
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of methods that Multifunctional aramid fiber is yarn beam printed, include the following steps:The micronizing of photic light storage type self luminous material, anionic additive;Function micro mist is the same as bath warp prints color paste deployment;Function warp prints technical process.The present invention utilizes the fire-retardant aramid fiber piece yarn after warping that difference is added during coating rotary scream printing with functional materials such as fluorescence and anions, it is multi-functional to assign aramid fiber warp thread, warp thread and untreated weft yarn are weaved, have the function of persistently effective warning, antibacterial and anti-electromagnetic-radiation etc. while assigning fire-retardant aramid fiber PRINTED FABRIC dim effect.The weaving of various aramid fibers is applied to by addition several functions material using the alternative conventional yarn dyeing of the present invention and the technique for arranging two-step method, finishing technique is simple, realizes printing paste joint, anhydrous printing, energy conservation and environmental protection.
Description
Technical field
The invention belongs to function textile function dyeing and finishing manufacture fields, and in particular to a kind of Multifunctional aramid fiber warp beam print
Colored method.
Background technology
In general functional mainly arranged by cheese of yarn assigns its functionality, and cheese arrangement is by yarn
Line or the process of the dyed final finishing of long filament, the method complex process, high energy consumption high pollution.The present invention, which utilizes, has superelevation
Intensity, high-modulus and high temperature resistant, acid-fast alkali-proof and fire-retardant aramid fiber carry out network by yarn beam printed technique, using aramid yarn
Warping after silk twisting carries out coating rotary scream printing to organizine;Sizing after stamp, then carry out wearing brown reed, weaving, finally to fabric into
Row desizing, preshrunk (backtwisting), washing, stabilised finish and at product examine packet.Aramid fiber piece yarn after warping is in coating rotary scream printing
Different functionalities material is added in technical process, assigns aramid fiber warp thread functionality, aramid fiber warp thread and untreated weft yarn is knitted
It makes, has the function of that antibacterial anti-electromagnetic-radiation warns etc. other while assigning aramid fiber high-tenacity, high flame retardant.
Invention content
Goal of the invention:In order to solve the deficiencies in the prior art, the present invention provides a kind of Multifunctional aramid fiber warp beam prints
Colored method, the present invention utilize the aramid fiber piece yarn after warping to be added in rotary scream printing technique with warning, anionic additive
Equal functional materials realize anhydrous printing with the aramid fiber piece yarn after warping in the circle rotary scream printing one-bath finishing of printing paste combination plant,
Have the function of that antibacterial anti-electromagnetic-radiation warns etc. other while assigning aramid fiber high-tenacity, high flame retardant.
Technical solution:A kind of method that Multifunctional aramid fiber is yarn beam printed, includes the following steps:
(1) micronizing of photic light storage type self luminous material, anionic additive:
Grain size is ground to grain by photic light storage type self luminous material, anionic additive by ball mill or colloid mill
Diameter is less than 5 μm of functional material micro mist, spare;
(2) method of the function micro mist with bath warp prints color paste deployment:
Photic light storage type self luminous material and anionic additive powder content are respectively 1-5%, low-temperature adhesive dosage 20-
70%, coating 10-50%, acrylic crosslinking agent 0-3%, water and appropriate emulsion thickening, total amount 100% are configured to function stamp
Mill base;
(3) function warp prints technical process:
By the aramid fiber piece yarn after warping, by printing paste combination plant in rotary scream printing technical process concentrator stamp,
Starching after thermosetting color, the aramid fiber warp thread after stamp are weaved to obtain the multi-functional fabric in one, specific steps with weft yarn
It is as follows:Raw yarn → beam warping → printing paste joint → weaving → fabric is examined;
The printing paste process integration includes the following steps:And axis → function micro mist bathes stamp → fixation → starching together,
In, technological parameter is:Speed 20-60m/min, 100-160 DEG C of temperature bake time 1-4min.
As an optimization:The photic light storage type self luminous material is:Zinc sulphide/copper, cobalt compound or rare earth metal salt,
Fluorescent paint.
As an optimization:The anionic additive is:Tourmaline or opal ore.
Advantageous effect:The yarn beam printed method of Multifunctional aramid fiber of the present invention, utilizes the fire-retardant virtue after warping
Difference, which is added, in synthetic fibre piece yarn during coating rotary scream printing has the functional materials such as fluorescence and anion, and it is more to assign aramid fiber warp thread
Functionality weaves warp thread and untreated weft yarn, has while assigning fire-retardant aramid fiber PRINTED FABRIC dim effect and holds
The functions such as effective warning, antibacterial and anti-electromagnetic-radiation long.Using the alternative conventional yarn dyeing of the present invention and arrange two-step method
Technique, by add several functions material, be applied to various aramid fibers weaving, finishing technique is simple, realize printing paste
Joint, anhydrous printing, energy conservation and environmental protection.
The present invention knits the kevlar fabric flame retardant property of technology formation by print:Limit oxygen index value 28-30;Anion is dense
Degree:800-1000/cm3;Persistence:15-20min, colorfastness to rubbing:Dry fastness is 4-5 grades, fastness to wet rubbing 3
~4 grades;4 grades of color fastness to washing, 4 grades of colour fastness to perspiration meet the requirement of features textile items fastness.
Specific implementation mode
The technical scheme in the embodiments of the invention will be clearly and completely described below, so that the technology of this field
Personnel can be better understood from advantages and features of the invention, to make apparent boundary to protection scope of the present invention
It is fixed.Embodiment described in the invention is only a part of the embodiment of the present invention, instead of all the embodiments, based on the present invention
In embodiment, the every other implementation that those of ordinary skill in the art are obtained without making creative work
Example, shall fall within the protection scope of the present invention.
Specific embodiment 1
A kind of method that Multifunctional aramid fiber is yarn beam printed, includes the following steps:
(1) micronizing of photic light storage type self luminous material, anionic additive:
The photic light storage type self luminous material is:Zinc sulphide/copper, cobalt compound or rare earth metal salt, fluorescent paint;
The anionic additive is:Tourmaline or opal ore.
Grain size is ground to grain by photic light storage type self luminous material, anionic additive by ball mill or colloid mill
Diameter is less than 5 μm of functional material micro mist, spare.
(2) method of the function micro mist with bath warp prints color paste deployment:
Photic light storage type self luminous material and anionic additive powder content are respectively 1%, low-temperature adhesive dosage 20%,
Coating 10%, water and appropriate emulsion thickening, total amount 100% are configured to function print paste.
(3) function warp prints technical process:
By the aramid fiber piece yarn after warping, by printing paste combination plant in rotary scream printing technical process concentrator stamp,
Starching after thermosetting color, the aramid fiber warp thread after stamp are weaved to obtain the multi-functional fabric in one, specific steps with weft yarn
It is as follows:Raw yarn → beam warping → printing paste joint → weaving → fabric is examined;
The printing paste process integration includes the following steps:And axis → function micro mist bathes stamp → fixation → starching together,
In, technological parameter is:Speed 20m/min, 100 DEG C of temperature, bakes time 1min.
Specific embodiment 2
A kind of method that Multifunctional aramid fiber is yarn beam printed, includes the following steps:
(1) micronizing of photic light storage type self luminous material, anionic additive:
The photic light storage type self luminous material is:Zinc sulphide/copper, cobalt compound or rare earth metal salt, fluorescent paint;
The anionic additive is:Tourmaline or opal ore.
Grain size is ground to grain by photic light storage type self luminous material, anionic additive by ball mill or colloid mill
Diameter is less than 5 μm of functional material micro mist, spare.
(2) method of the function micro mist with bath warp prints color paste deployment:
Photic light storage type self luminous material and anionic additive powder content are respectively 5%, low-temperature adhesive dosage 70%,
Coating 50%, acrylic crosslinking agent 3%, water and appropriate emulsion thickening, total amount 100% are configured to function print paste.
(3) function warp prints technical process:
By the aramid fiber piece yarn after warping, by printing paste combination plant in rotary scream printing technical process concentrator stamp,
Starching after thermosetting color, the aramid fiber warp thread after stamp are weaved to obtain the multi-functional fabric in one, specific steps with weft yarn
It is as follows:Raw yarn → beam warping → printing paste joint → weaving → fabric is examined;
The printing paste process integration includes the following steps:And axis → function micro mist bathes stamp → fixation → starching together,
In, technological parameter is:Speed 60m/min, 160 DEG C of temperature, bakes time 4min.
Specific embodiment 3
A kind of method that Multifunctional aramid fiber is yarn beam printed, includes the following steps:
(1) micronizing of photic light storage type self luminous material, anionic additive:
The photic light storage type self luminous material is:Zinc sulphide/copper, cobalt compound or rare earth metal salt, fluorescent paint;
The anionic additive is:Tourmaline or opal ore.
Grain size is ground to grain by photic light storage type self luminous material, anionic additive by ball mill or colloid mill
Diameter is less than 5 μm of functional material micro mist, spare.
(2) method of the function micro mist with bath warp prints color paste deployment:
Photic light storage type self luminous material and anionic additive powder content are respectively 3%, low-temperature adhesive dosage 40%,
Coating 30%, acrylic crosslinking agent 2%, water and appropriate emulsion thickening, total amount 100% are configured to function print paste.
(3) function warp prints technical process:
By the aramid fiber piece yarn after warping, by printing paste combination plant in rotary scream printing technical process concentrator stamp,
Starching after thermosetting color, the aramid fiber warp thread after stamp are weaved to obtain the multi-functional fabric in one, specific steps with weft yarn
It is as follows:Raw yarn → beam warping → printing paste joint → weaving → fabric is examined;
The printing paste process integration includes the following steps:And axis → function micro mist bathes stamp → fixation → starching together,
In, technological parameter is:Speed 50m/min, 140 DEG C of temperature, bakes time 3min.
The present invention knits the kevlar fabric flame retardant property of technology formation by print:Limit oxygen index value 28-30;Anion is dense
Degree:800-1000/cm3;Persistence:15-20min, colorfastness to rubbing:Dry fastness is 4-5 grades, fastness to wet rubbing 3
~4 grades;4 grades of color fastness to washing, 4 grades of colour fastness to perspiration meet the requirement of features textile items fastness.
The yarn beam printed method of Multifunctional aramid fiber of the present invention is being applied using the fire-retardant aramid fiber piece yarn after warping
Expect that rotary scream printing is added difference and has the functional materials such as fluorescence and anion in the process, assigns aramid fiber warp thread multifunctionality, it will
Warp thread is weaved with untreated weft yarn, is had while assigning fire-retardant aramid fiber PRINTED FABRIC dim effect persistently effective alert
Show, the functions such as antibacterial and anti-electromagnetic-radiation.Using the technique of the present invention alternative conventional yarn dyeing and arrangement two-step method, pass through
Several functions material is added, the weaving of various aramid fibers is applied to, finishing technique is simple, realizes printing paste joint, no-watermark
Flower, energy conservation and environmental protection.
Claims (3)
1. a kind of method that Multifunctional aramid fiber is yarn beam printed, it is characterised in that:Include the following steps:
(1) micronizing of photic light storage type self luminous material, anionic additive:
By photic light storage type self luminous material, anionic additive that grain size is ground to grain size by ball mill or colloid mill is low
It is spare in 5 μm of functional material micro mist;
(2) method of the function micro mist with bath warp prints color paste deployment:
Photic light storage type self luminous material and anionic additive powder content are respectively 1-5%, low-temperature adhesive dosage 20-
70%, coating 10-50%, acrylic crosslinking agent 0-3%, water and appropriate emulsion thickening, total amount 100% are configured to function stamp
Mill base;
(3) function warp prints technical process is as follows:
By the aramid fiber piece yarn after warping, concentrator stamp, thermosetting in rotary scream printing technical process by printing paste combination plant
Starching after color, the aramid fiber warp thread after stamp are weaved to obtain the multi-functional fabric in one with weft yarn, be as follows:
Raw yarn → beam warping → printing paste joint → weaving → fabric is examined;The printing paste process integration includes the following steps:And axis
→ function micro mist is the same as bathing stamp → fixation → starching, wherein technological parameter is:Speed 20-60m/min, 100-160 DEG C of temperature,
Bake time 1-4min.
2. the yarn beam printed method of Multifunctional aramid fiber according to claim 1, it is characterised in that:The photic storage
Light type self-luminescent material is:Zinc sulphide/copper, cobalt compound or rare earth metal salt, fluorescent paint.
3. the yarn beam printed method of Multifunctional aramid fiber according to claim 1, it is characterised in that:The anion
Additive is:Tourmaline or opal ore.