CN108468210A - A kind of air-ventilating garments fabric and its preparation process - Google Patents
A kind of air-ventilating garments fabric and its preparation process Download PDFInfo
- Publication number
- CN108468210A CN108468210A CN201810108497.7A CN201810108497A CN108468210A CN 108468210 A CN108468210 A CN 108468210A CN 201810108497 A CN201810108497 A CN 201810108497A CN 108468210 A CN108468210 A CN 108468210A
- Authority
- CN
- China
- Prior art keywords
- air
- titanium alloy
- ventilating garments
- fabric
- acrylate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of air-ventilating garments fabrics, including polyurethanes, acrylate and titanium alloy, weight percent to be respectively:Polyurethanes 70 77%;Acrylate 22 25%;Titanium alloy 1 5%.Also disclose a kind of preparation process of air-ventilating garments fabric.The beneficial effects of the invention are as follows:Raw material proportioning is scientific and reasonable, using titanium alloy coating, and can reduce rapidly temperature with extraneous thermal insulation, to make wearer reach comfortable state, and can work contentedly.
Description
Technical field
The present invention relates to a kind of air-ventilating garments fabrics, further relate to a kind of preparation process of air-ventilating garments fabric.
Background technology
It is well known that textile is as a kind of closely bound up product of living with people, with social progress and science
The development of technology, requirement of the people to textile are also improved constantly, from pervious wearing property, durability, aesthetic appearance to mesh
Preceding functionality, comfort, popular sex reversal.But it needs to wear clothes made of special fabric in the environment of particular job,
Domestic and international protective clothes type is relatively more, and the worker in high temperature open air needs special fabric that can just overcome, air-conditioning fiber product
Difference lies in heat preservation mechanism is different from traditional textile.Traditional clothing mainly avoids skin temperature by insulation method
Degree reduces excessively, depends primarily on the still air amount for being trapped in fabric, so thickness is bigger, density is smaller, thermal insulation effect
Fruit is better.And the heat preservation mechanism of air-conditioning fiber is then that the completely new heat preservation mechanism of comfortable " moist heat " can be provided for human body, energy
Enough thermal conditionings are rather than just thermal isolation.
Therefore, to solve the above problems, providing a kind of new technical solution.
Invention content
A kind of air-ventilating garments fabric of present invention offer and its preparation process.
The technical solution adopted by the present invention is:
A kind of air-ventilating garments fabric, including polyurethanes, acrylate and titanium alloy, weight percent be respectively:
Polyurethanes 70-77%;
Acrylate 22-25%;
Titanium alloy 1-5%.
Further, weight percent is respectively:
Polyurethanes 72-76%;
Acrylate 23-25%;
Titanium alloy 1-3%.
A kind of preparation process of air-ventilating garments fabric, using polyurethanes, acrylate and titanium alloy as raw material, including with
Lower processing step:Using polyurethanes as substrate shell fabric, acrylate and titanium alloy are mixed to form titanium alloy coating, profit
Titanium alloy coating is coated by the way of gluing on the base layer with glue spreader, air-ventilating garments fabric, the sizing temperature of glue spreader is made
Degree is 150-160 DEG C, and sizing speed is 50-60M/min.
Further, the fiber dimensious that air-ventilating garments fabric is made is 75D.
Further, the density that air-ventilating garments fabric is made is 240T.
The beneficial effects of the invention are as follows:Raw material proportioning is scientific and reasonable, using titanium alloy coating, can with extraneous thermal insulation, and
And temperature can be reduced rapidly, to make wearer reach comfortable state, and can work contentedly.
Specific implementation mode
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, the embodiment
It is only used for explaining the present invention, not restrict the protection scope of the present invention.
Embodiment 1
A kind of air-ventilating garments fabric, including polyurethanes, acrylate and titanium alloy, weight percent be respectively:
Polyurethanes 70%;
Acrylate 25%;
Titanium alloy 5%.
A kind of preparation process of air-ventilating garments fabric, using polyurethanes, acrylate and titanium alloy as raw material, including with
Lower processing step:Using polyurethanes as substrate shell fabric, acrylate and titanium alloy are mixed to form titanium alloy coating, profit
Titanium alloy coating is coated by the way of gluing on the base layer with glue spreader, air-ventilating garments fabric, the sizing temperature of glue spreader is made
Degree is 150 DEG C, and sizing speed is 50M/min, and the fiber dimensious that air-ventilating garments fabric is made is 75D, and the close of air-ventilating garments fabric is made
Degree is 240T.
The beneficial effects of the invention are as follows:Raw material proportioning is scientific and reasonable, using titanium alloy coating, can with extraneous thermal insulation, and
And temperature can be reduced rapidly, to make wearer reach comfortable state, and can work contentedly.
Embodiment 2
A kind of air-ventilating garments fabric, including polyurethanes, acrylate and titanium alloy, weight percent be respectively:
Polyurethanes 75%;
Acrylate 22%;
Titanium alloy 3%.
A kind of preparation process of air-ventilating garments fabric, using polyurethanes, acrylate and titanium alloy as raw material, including with
Lower processing step:Using polyurethanes as substrate shell fabric, acrylate and titanium alloy are mixed to form titanium alloy coating, profit
Titanium alloy coating is coated by the way of gluing on the base layer with glue spreader, air-ventilating garments fabric, the sizing temperature of glue spreader is made
Degree is 155 DEG C, and sizing speed is 55M/min, and the fiber dimensious that air-ventilating garments fabric is made is 75D, and the close of air-ventilating garments fabric is made
Degree is 240T.
The beneficial effects of the invention are as follows:Raw material proportioning is scientific and reasonable, using titanium alloy coating, can with extraneous thermal insulation, and
And temperature can be reduced rapidly, to make wearer reach comfortable state, and can work contentedly.
Embodiment 3
A kind of air-ventilating garments fabric, including polyurethanes, acrylate and titanium alloy, weight percent be respectively:
Polyurethanes 77%;
Acrylate 22%;
Titanium alloy 1%.
A kind of preparation process of air-ventilating garments fabric, using polyurethanes, acrylate and titanium alloy as raw material, including with
Lower processing step:Using polyurethanes as substrate shell fabric, acrylate and titanium alloy are mixed to form titanium alloy coating, profit
Titanium alloy coating is coated by the way of gluing on the base layer with glue spreader, air-ventilating garments fabric, the sizing temperature of glue spreader is made
Degree is 150-160 DEG C, and sizing speed is 50-60M/min, and the fiber dimensious that air-ventilating garments fabric is made is 75D, and air-ventilating garments are made
The density of fabric is 240T.
The beneficial effects of the invention are as follows:Raw material proportioning is scientific and reasonable, using titanium alloy coating, can with extraneous thermal insulation, and
And temperature can be reduced rapidly, to make wearer reach comfortable state, and can work contentedly.
The above described is only a preferred embodiment of the present invention, being not the limit for making any other form to the present invention
System, and according to the technical essence of the invention made by any modification or equivalent variations, still fall within present invention model claimed
It encloses.
Claims (5)
1. a kind of air-ventilating garments fabric, it is characterised in that:Including polyurethanes, acrylate and titanium alloy, weight percent
Than being respectively:
Polyurethanes 70-77%;
Acrylate 22-25%;
Titanium alloy 1-5%.
2. a kind of air-ventilating garments fabric according to claim 1, it is characterised in that:Its weight percent is respectively:
Polyurethanes 72-76%;
Acrylate 23-25%;
Titanium alloy 1-3%.
3. a kind of preparation process of air-ventilating garments fabric, it is characterised in that:It is original with polyurethanes, acrylate and titanium alloy
Material, comprises the following steps that:Using polyurethanes as substrate shell fabric, acrylate and titanium alloy are mixed to form titanium and closed
Gold plating is coated titanium alloy coating by glue spreader in the way of gluing, air-ventilating garments fabric, glue spreader is made on the base layer
Setting temperature be 150-160 DEG C, sizing speed be 50-60M/min.
4. a kind of preparation process of air-ventilating garments fabric according to claim 3, it is characterised in that:Air-ventilating garments fabric is made
Fiber dimensious is 75D.
5. a kind of preparation process of air-ventilating garments fabric according to claim 3, it is characterised in that:Air-ventilating garments fabric is made
Density is 240T.