CN106811971A - A kind of natural plants antibacterial Cashmere composite shell fabric with fatigue resistance and preparation method thereof - Google Patents
A kind of natural plants antibacterial Cashmere composite shell fabric with fatigue resistance and preparation method thereof Download PDFInfo
- Publication number
- CN106811971A CN106811971A CN201611202001.XA CN201611202001A CN106811971A CN 106811971 A CN106811971 A CN 106811971A CN 201611202001 A CN201611202001 A CN 201611202001A CN 106811971 A CN106811971 A CN 106811971A
- Authority
- CN
- China
- Prior art keywords
- cashmere
- shell fabric
- composite shell
- fatigue resistance
- minutes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of natural plants antibacterial Cashmere composite shell fabric with fatigue resistance, it is made from the following raw materials in parts by weight:Cashmere 25 28, expanded goose feather powder 20 22, apocynum fibre 8 10, cotton rose stem follicarpium glue 10 12,40%(owf)Natural sericin solution 30 35, amido silicon oil 35, nano active powdered carbon 24, ten difluoro heptyl propyl trimethoxy silicanes 13, butyl acrylate 57, soybean residue 68, the N-Methylimidazoleacetic salt 170 190 of 1 butyl 3, suitable quantity of water, optimization of C/C composites of the present invention improves production technology, cashmere composite fibre is obtained through wet spinning technology, blended dressing liquid impregnation process improves cashmere antibacterial again, antiultraviolet and anti-felting property, obtained Cashmere composite shell fabric is soft abundant, gloss is naturally soft, with antibacterial, ultraviolet radiation preventing and antifatigue healthcare function.
Description
Technical field
The present invention relates to textile material technical field, more particularly to a kind of natural plants antibacterial cashmere with fatigue resistance
Composite material and preparation method thereof.
Background technology
Cotton rose also known as Flos Hibisci Mutabilis, cotton rose, are Malvaceae machaka or dungarunga, and its flower, leaf can be used as medicine, with cool
The effects such as blood hemostasis, clearing heat and detoxicating, alleviating pain and detumescence, and no side effectses.Recent studies indicate that, Huang is contained in cotton rose
Ketone compounds, have inhibitory action to typhoid bacillus, staphylococcus aureus etc..At present, the application for cotton rose is main
Its flower, Ye Zhong is concentrated on, the research for its stem skin and accompaniment is less.Research shows that certain plants stem skin is produced through degumming
Pectin have more significant antibacterial and radiation proof the effects such as.For knitting fleece fabrics uv resistance energy and anti-microbial property compared with
Poor characteristic, is further to lift knitting cashmere product added value,《The extraction of cotton rose stem follicarpium glue and its to knitting cashmere face
The application of material》One literary grace acid-extraction, with sour dilution as extract solution, the technique such as research pH value, extraction time, solid-liquid ratio
Cotton rose stem skin pectous extracting method is optimized, and it is whole for the function of knitting fleece fabrics to prepare good pectin
Reason, as a result shows:Cotton rose stem skin using tartaric acid dilution as extract solution, in pH value 2, extraction time 90min, solid-liquid ratio 1
: under 30 process conditions, pectin yield up to 13.24%, after knitting fleece fabrics is arranged through cotton rose pectin, anti-microbial property and anti-
Ultraviolet performance is significantly improved.
Because cashmere is compared with common fine wool, its surface has regular thin thin scale layer, when cashmere fiber is machine-washed
Easily felting, the easy shrinking deformation influence taking of manufactured goods.And the antibiotic radiation proof performance in text only to cashmere changes
Enter, in order to further improve the wearability of cashmere fiber, overcome its shortcoming, cashmere fiber needs to carry out feld proofing.Will
Cotton rose stem follicarpium glue is very few to the report that the felt proofing of cashmere fiber is studied with natural sericin Combined Treatment.Except this it
Outward, cashmere is compared to wool one is that yield is few but price is high is difficult volume production, so that develop substituting having for cashmere
The NEW TYPE OF COMPOSITE cashmere fiber of the functions such as warmth retention property is high, low cost, felt proofing, antibiotic radiation proof.
The content of the invention
The object of the invention is exactly to make up the defect of prior art, there is provided a kind of natural plants with fatigue resistance resist
Bacterium Cashmere composite shell fabric and preparation method thereof.
The present invention is achieved by the following technical solutions:
A kind of natural plants antibacterial Cashmere composite shell fabric with fatigue resistance, is made from the following raw materials in parts by weight:Cashmere
25-28, expanded goose feather powder 20-22, apocynum fibre 8-10, cotton rose stem follicarpium glue 10-12,40%(owf)Natural sericin
Solution 30-35, amido silicon oil 3-5, nano active powdered carbon 2-4, ten difluoro heptyl propyl trimethoxy silicane 1-3, acrylic acid fourth
Ester 5-7, soybean residue 6-8,1- butyl -3- N-Methylimidazoleacetic salt 170-190, suitable quantity of water.
A kind of preparation method of described natural plants antibacterial Cashmere composite shell fabric with fatigue resistance, including following step
Suddenly:
(1)By nano active powdered carbon in drying box 100-120 DEG C preheating and drying 1-2 hours, keeping temperature added for ten difluoro heptan
Base propyl trimethoxy silicane is stirred 10-15 minutes, is vacuum dried to obtain modified Nano activated carbon powder;
(2)Soybean residue is dried into ground 100 eye mesh screen, sprinkling mass concentration is stirred and evenly mixed for the hydrochloric acid solution of 4-8%, in 60-
Magnetic agitation 2-3 hours in 80 DEG C of waters bath with thermostatic control, washing to neutrality is vacuum dried, and adds butyl acrylate ultrasonic grinding 1-3 small
When, dry the soybean residue superfines that must be modified;
(3)To extrude powdered after the cotton rose stem follicarpium glue air drying of extraction, add suitable quantity of water to be made into 7.5% pectin
Solution, is stirred continuously to whole dissolvings in 85-95 DEG C of water bath with thermostatic control, adds 40%(owf)Natural sericin solution, step
(1)Material ultrasonic disperse must mix dressing liquid in 30-40 minutes;
(4)Cashmere, expanded goose feather powder, apocynum fibre are added during 1- butyl -3- N-Methylimidazoleacetics salt is put into reactor
Grinding 20-40 minutes, is heated to 100-120 DEG C, adds step(2)Material stirring reacts 50-70 minutes, and spinning obtains cashmere and is combined
Fiber;
(5)By step(4)Obtained cashmere composite fibre puts into step(3)In mixing dressing liquid, bath raio 1: 50 impregnates 30-40
Minute, take out, clean with distilled water flushing, room temperature is dried, discharging.
It is an advantage of the invention that:Optimization of C/C composites of the present invention improves production technology, and cashmere is obtained through wet spinning technology is combined
Fiber, then blended dressing liquid impregnation process improves cashmere antibacterial, antiultraviolet and anti-felting property;Be modified for soybean residue by the present invention
After be added in raw material, play the cementation between fiber, add expanded goose feather powder, apocynum fibre, reduce making for cashmere
Consumption reduces cost, cashmere composite fibre obtained in spinning has the advantages that insulation, high adsorption capacity, is conducive to strengthening silk gum egg
White adsorbance, improves the hydrophily of cashmere fiber, further reduces the direction friction effect of fiber surface, thus shrinkproof
Obtain bigger improvement;It is naturally soft using the soft abundant, gloss of Cashmere composite shell fabric obtained in the present invention, with antibacterial,
Ultraviolet radiation preventing and antifatigue healthcare function.
Specific embodiment
A kind of natural plants antibacterial Cashmere composite shell fabric with fatigue resistance, is made from the following raw materials in parts by weight:Mountain
Cashmere 25, expanded goose feather powder 20, apocynum fibre 8, cotton rose stem follicarpium glue 10,40%(owf)Natural sericin solution 30,
Amido silicon oil 3, nano active powdered carbon 2, ten difluoro heptyl propyl trimethoxy silicanes 1, butyl acrylate 5, soybean residue 6,1- fourths
Base -3- N-Methylimidazoleacetics salt 170, suitable quantity of water.
A kind of preparation method of described natural plants antibacterial Cashmere composite shell fabric with fatigue resistance, including following step
Suddenly:
(1)By nano active powdered carbon in drying box 100-120 DEG C preheating and drying 1-2 hours, keeping temperature added for ten difluoro heptan
Base propyl trimethoxy silicane is stirred 10-15 minutes, is vacuum dried to obtain modified Nano activated carbon powder;
(2)Soybean residue is dried into ground 100 eye mesh screen, sprinkling mass concentration is stirred and evenly mixed for the hydrochloric acid solution of 4-8%, in 60-
Magnetic agitation 2-3 hours in 80 DEG C of waters bath with thermostatic control, washing to neutrality is vacuum dried, and adds butyl acrylate ultrasonic grinding 1-3 small
When, dry the soybean residue superfines that must be modified;
(3)To extrude powdered after the cotton rose stem follicarpium glue air drying of extraction, add suitable quantity of water to be made into 7.5% pectin
Solution, is stirred continuously to whole dissolvings in 85-95 DEG C of water bath with thermostatic control, adds 40%(owf)Natural sericin solution, step
(1)Material ultrasonic disperse must mix dressing liquid in 30-40 minutes;
(4)Cashmere, expanded goose feather powder, apocynum fibre are added during 1- butyl -3- N-Methylimidazoleacetics salt is put into reactor
Grinding 20-40 minutes, is heated to 100-120 DEG C, adds step(2)Material stirring reacts 50-70 minutes, and spinning obtains cashmere and is combined
Fiber;
(5)By step(4)Obtained cashmere composite fibre puts into step(3)In mixing dressing liquid, bath raio 1: 50 impregnates 30-40
Minute, take out, clean with distilled water flushing, room temperature is dried, discharging.
Uv transmittance using Cashmere composite shell fabric obtained in the present invention for wavelength less than 290nm goes to zero, UPF
Value reaches 53, and the bacteriostasis rate to staphylococcus aureus can reach 95.571%.
Claims (2)
1. a kind of natural plants antibacterial Cashmere composite shell fabric with fatigue resistance, it is characterised in that by the original of following weight portion
Material is made:Cashmere 25-28, expanded goose feather powder 20-22, apocynum fibre 8-10, cotton rose stem follicarpium glue 10-12,40%
(owf)Natural sericin solution 30-35, amido silicon oil 3-5, nano active powdered carbon 2-4, ten difluoro heptyl propyl trimethoxies
Silane 1-3, butyl acrylate 5-7, soybean residue 6-8,1- butyl -3- N-Methylimidazoleacetic salt 170-190, suitable quantity of water.
2. the making side of a kind of natural plants antibacterial Cashmere composite shell fabric with fatigue resistance according to claim 1
Method, it is characterised in that comprise the following steps:
(1)By nano active powdered carbon in drying box 100-120 DEG C preheating and drying 1-2 hours, keeping temperature added for ten difluoro heptan
Base propyl trimethoxy silicane is stirred 10-15 minutes, is vacuum dried to obtain modified Nano activated carbon powder;
(2)Soybean residue is dried into ground 100 eye mesh screen, sprinkling mass concentration is stirred and evenly mixed for the hydrochloric acid solution of 4-8%, in 60-
Magnetic agitation 2-3 hours in 80 DEG C of waters bath with thermostatic control, washing to neutrality is vacuum dried, and adds butyl acrylate ultrasonic grinding 1-3 small
When, dry the soybean residue superfines that must be modified;
(3)To extrude powdered after the cotton rose stem follicarpium glue air drying of extraction, add suitable quantity of water to be made into 7.5% pectin
Solution, is stirred continuously to whole dissolvings in 85-95 DEG C of water bath with thermostatic control, adds 40%(owf)Natural sericin solution, step
(1)Material ultrasonic disperse must mix dressing liquid in 30-40 minutes;
(4)Cashmere, expanded goose feather powder, apocynum fibre are added during 1- butyl -3- N-Methylimidazoleacetics salt is put into reactor
Grinding 20-40 minutes, is heated to 100-120 DEG C, adds step(2)Material stirring reacts 50-70 minutes, and spinning obtains cashmere and is combined
Fiber;
(5)By step(4)Obtained cashmere composite fibre puts into step(3)In mixing dressing liquid, bath raio 1: 50 impregnates 30-40
Minute, take out, clean with distilled water flushing, room temperature is dried, discharging.