CN104988716A - Non-ironing processing method of cotton shirt with physiotherapy function - Google Patents
Non-ironing processing method of cotton shirt with physiotherapy function Download PDFInfo
- Publication number
- CN104988716A CN104988716A CN201510318412.4A CN201510318412A CN104988716A CN 104988716 A CN104988716 A CN 104988716A CN 201510318412 A CN201510318412 A CN 201510318412A CN 104988716 A CN104988716 A CN 104988716A
- Authority
- CN
- China
- Prior art keywords
- physiotherapy
- parts
- ironing
- ready
- physical therapy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a non-ironing processing method of a cotton shirt with a physiotherapy function. The method includes the steps of coating the skirt with first physiotherapy non-ironing processing liquid, conducting primary preliminary drying, spraying second physiotherapy non-ironing processing liquid in an atomized mode and conducting secondary preliminary drying, pressing, baking, cooling, washing and drying, wherein the temperature of a freezing chamber in the cooling process ranges from -10 DEG C to 0 DEG C, and the cooling time ranges from 0.5 h to 5 h. The ready-to-wear shirt is processed through the first physiotherapy non-ironing processing liquid and the second physiotherapy non-ironing processing liquid; through the steps of pressing, baking and the like, compared with non-ironing processing in the prior art, the flatness of processed seams of the ready-to-wear shirt can be remarkably improved. The shirt can be endowed with a multi-layer physiotherapy effect; through the combination of physiotherapy solid powder and physiotherapy microcapsules at the processed seams, in-vivo free radicals can be eliminated, and blood circulation is promoted.
Description
Technical field
The present invention relates to the post-processing approach of shirt, be specifically related to a kind of no-iron treatment method of physical therapy function cotton shirt.
Background technology
Along with the progress and development of society and improving constantly of people's living standard, contemporary clothes have been not only for hiding body, the warming and general decoration of work, but to high-qualityization, stylishization, comfortableization future development.Be mainly or all cotton fiber in the face liber composition of cotton shirt.Cotton fiber has good hygroscopicity, and under normal conditions, fiber can absorb moisture in peripherad air, and its moisture content is 8-10%, so the skin of its contact people, makes people feel soft and not stiff.If cotton humidity increases, environment temperature is higher, and the amount of moisture contained in fiber can all leave in evaporation, makes fabric keep water equilibrated state, makes people feel comfortable.Therefore, compared with chemical fiber plus material, cotton fabric shirt has excellent moisture absorbability and moisture retentivity.But cotton fiber is without natural physical therapy function, and the chemical therapy piece such as heating plate, vibrating reed is installed in the many employings of technical scheme of improvement additional, or adopt the fiber containing physiotherapy performance as the raw material of fabric.
Disclose a kind of Magnetic physical therapy fabric in CN 102806732A, this fabric comprises skin and nexine, and skin is the fabric side bed of material, and nexine is Magnetic physical therapy fabric layer, and nexine adopts knitting to take shape in outer inner side.Its nexine face liber adopts melt spinning technology permanent magnetism particulate and fabric fibre to be combined, nexine fabric is made to have magnetic physiotherapeutic function, its average magnetic flux is greater than 0.4mvb, and the magnetic line of force of generation can penetrate the human body skin 1.2cm degree of depth, and magnetic therapy effect is obvious; Clothing prepared by this fabric of everyday general purpose can play promotion cellular metabolism to human body, strengthens and improves immunologic function, and dispelling fatigue, promotion antisecosis, eliminate effects such as having a sleepless night and delay senility.CN 104248057A discloses a kind of multi-functional warm fabric physical therapy costume, comprise garment body, air bag is provided with at the clothes nexine of garment body back side neck and waist, at the garment interior of garment body back side neck and waist, electromagnetic shock sheet is installed, on the downside of the predecessor of garment body, controller is installed; Garment body is made up of fabric, and fabric comprises intermediate layer, ultra-fine suede heat-preservation cotton layer and surface layer and nexine, and intermediate layer is the composite non woven layer of cloth being positioned at described thermal fabric centre position.The former physical therapy function fiber mostly is chemical fibre, and degree comfortable and easy to wear is poor, and the latter's gained to ready-made clothes can not apply to everyday general purpose.Therefore the advantage of physiotherapy and cotton fiber shirt organically combined, having become those skilled in the art has technical problem to be solved.
Summary of the invention
The object of the invention is to overcome the defect existed in prior art, a kind of no-iron treatment method of physical therapy function cotton shirt is provided, it is characterized in that, comprise the steps:
S1: coating, is coated with the non-ironing treatment fluid of the first physiotherapy at the processing sealing of ready-made clothes, repeats aforesaid operations 1 ~ 2 time;
S2: preliminary drying, carries out a preliminary drying process to the ready-made clothes of the non-ironing treatment fluid of coating first physiotherapy;
S3: upper liquid, the non-ironing treatment fluid of atomized spray second physiotherapy, evenly applying the non-ironing treatment fluid of the second physiotherapy to ready-made clothes liquid carrying rate to ready-made clothes is 60 ~ 95%;
S4: secondary preliminary drying, carries out secondary preliminary drying to upper liquid gained ready-made clothes, and pre-baked ready-made clothes is 6 ~ 9 one-tenth to be done;
S5: pressing, carries out pressing respectively to each position of secondary preliminary drying gained ready-made clothes;
S6: bake, bakes process to the ready-made clothes after pressing;
S7: cooling, proceeds in refrigerating chamber carry out cooling processing by baking the ready-made clothes after process;
S8: washing is dried, and must have the non-ironing cotton shirt of physical therapy function;
Wherein, in described refrigerating work procedure, the temperature of refrigerating chamber is-10 ~ 0 DEG C, and the cooling processing time is 0.5 ~ 5h.
The non-ironing weak effect of processing sealing place after single treatment of ready-made clothes, poor flatness, in order to improve non-ironing effect, in addition, the general multidigit of processing sealing is in positions of easily straining such as joint shoulders, in order to give processing sealing further physiotheraping effect, preferred technical scheme is, the component of the non-ironing treatment fluid of described first physiotherapy comprises physiotherapy microcapsules 5 ~ 30 parts, physiotherapy pressed powder 20 ~ 40 parts, fibroin albumen 0.5 ~ 7 part, deoxycholic acid 0.1 ~ 1 part, vinylpyrrolidone/dimethylaminoethyl methacrylate copolymer 10 ~ 25 part, sepiolite 2 ~ 8 parts, 60 ~ 100 parts, water,
Described physiotherapy pressed powder is made up of following components in mass portion: nanoscale infrared magnetic stone flour 5 ~ 15 parts, 5 ~ 15 parts, nanoscale ochre powder, 10 ~ 20 parts, Nanometer Maifan Stone powder, 10 ~ 20 parts, nanoscale agate powder, 5 ~ 40 parts, nanometer level pearl powder.
The wall material of described physiotherapy microcapsules is collagen or phycobniliprotein, the core of described physiotherapy microcapsules is mixed by component A and B component, described component A is selected from least one in Tea Polyphenols, grape seed polyphenols, vine polyphenol, pycnogenol, described B component is made up of following components in mass portion: vitamin E2 0 ~ 30 part, stem of noble dendrobium active polysaccharide 2 ~ 10 parts, gingkgo flavonoids 2 ~ 15 parts, lipoic acid 1 ~ 7 part, shitosan 5 ~ 20 parts, in the core of physiotherapy microcapsules, the percentage by weight of B component is 40 ~ 80%.
In order to ensure the non-ironing effect of ready-made clothes, preferred technical scheme is, in the non-ironing treatment fluid of second physiotherapy, key component is no-ironing resin, fiber protection agent, softener, catalyst, PH conditioning agent and water, the parts by weight of key component are: no-ironing resin 35 ~ 130 parts, fiber protection agent 5 ~ 45 parts, softener 15 ~ 65 parts, catalyst 5 ~ 20 parts, 400 ~ 800 parts, water, and the pH value of the non-ironing treatment fluid of described second physiotherapy is 3 ~ 5.5; Described fiber protection agent is be selected from least one in the silicone emulsion of elastic polyurethane and the common emulsion of oxidized polyethylene homopolymers and amido silicon oil; Described pH adjusting agent is be selected from the one in citric acid-sodium citrate buffer solution, acetic acid-sodium acetate buffer solution and sodium dihydrogen phosphate-citrate buffer solution, and described softener is be selected from least one in quaternised modified amino-silicone oil and polyether block/chain alkyl amino-modified silicone oil.
In order to ensure that no-ironing resin adapts to the characteristic of cotton fiber, and ensure the hydrophily of resin, preferred technical scheme is, described no-ironing resin is be selected from least one in modification bishydroxymethyl dihydroxy ethylene urea, nano-dispersed self-crosslinking polyether-polyurethane, modified alkyl dihydroxy ethylene urea.
In order to ensure that no-ironing resin is thoroughly crosslinked, microcapsules well can be coated on wherein, preferred technical scheme is, described catalyst is magnesium chloride, or is composite catalyst; Described composite catalyst is composited by metal salt catalyst and hydroxycarboxylic acid, described metal salt catalyst is be selected from least one in magnesium chloride, magnesium nitrate, zinc chloride, zinc nitrate, described hydroxycarboxylic acid is citric acid, dihydromethyl propionic acid, 2, at least one in 3-dyhydrobutanedioic acid, in described composite catalyst, the percentage by weight of metal salt catalyst is 30 ~ 40%.
Heating using microwave can catalysis no-ironing resin further crosslinked, and preferred technical scheme is, described in bake employing heating using microwave, the baking temperature baked in operation is 100 ~ 130 DEG C, described in bake the time be 5 ~ 25min.
In order to give the physiotherapy performance of shirt fabric entirety, preferred technical scheme is, also containing 3 ~ 13 parts of wooden fish stone powder and 2 ~ 15 parts of coral powders in the non-ironing treatment fluid of described second physiotherapy.
Microcapsule diameter is excessive easily destroyed, cause the too fast release of core wherein, microcapsule diameter is too small, is covered by no-ironing resin completely, and preferred technical scheme is, the core of described physiotherapy microcapsules and the weight ratio of wall material are (1 ~ 2): 1, and the diameter of described physiotherapy microcapsules is 5 ~ 8 μm.
Preferred technical scheme is, the process conditions of described pressing are pressure 1.2 ~ 3.4Kg, and temperature is 90 ~ 170 DEG C.
Preferred technical scheme is, the temperature of described secondary preliminary drying is 60 ~ 85 DEG C.
Advantage of the present invention and beneficial effect are:
The present invention, processing with the non-ironing treatment fluid of the first physiotherapy and the non-ironing treatment fluid of the second physiotherapy respectively shirt ready-made clothes, by steps such as pressing bake, compared with non-ironing process of the prior art, can significantly improve the flatness of the processing sealing of ready-made clothes;
The physiotherapy function that shirt is multi-level can be given: physiotherapy pressed powder and the physiotherapy microcapsules at processing sealing place combine, can free radical in purged body, promote blood hemal ring, and the persistence of physiotheraping effect can be ensured, and wooden fish stone powder in the non-ironing treatment fluid of the second physiotherapy and coral powder contain abundant mineral matter and trace element, be coated under the effect of infrared magnetite mineral matter in no-ironing resin and the sustainable precipitation of trace element absorb by human body, thus safeguard health.
Detailed description of the invention
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
Embodiment 1
The no-iron treatment method of the physical therapy function cotton shirt of embodiment 1, comprises the steps:
S1: coating, is coated with the non-ironing treatment fluid of the first physiotherapy at the processing sealing of ready-made clothes, repeats aforesaid operations 1 time;
S2: preliminary drying, carries out a preliminary drying process to the ready-made clothes of the non-ironing treatment fluid of coating first physiotherapy;
S3: upper liquid, the non-ironing treatment fluid of atomized spray second physiotherapy, evenly applying the non-ironing treatment fluid of the second physiotherapy to ready-made clothes liquid carrying rate to ready-made clothes is 60%;
S4: secondary preliminary drying, carries out secondary preliminary drying to upper liquid gained ready-made clothes, and pre-baked ready-made clothes is 6 ~ 9 one-tenth to be done;
S5: pressing, carries out pressing respectively to each position of secondary preliminary drying gained ready-made clothes;
S6: bake, bakes process to the ready-made clothes after pressing;
S7: cooling, proceeds in refrigerating chamber carry out cooling processing by baking the ready-made clothes after process;
S8: washing is dried, and must have the non-ironing cotton shirt of physical therapy function;
Wherein, in refrigerating work procedure, the temperature of refrigerating chamber is-10 DEG C, and the cooling processing time is 0.5h.
The component of the non-ironing treatment fluid of the first physiotherapy comprises physiotherapy microcapsules 5 parts, physiotherapy pressed powder 20 parts, fibroin albumen 0.5 part, deoxycholic acid 0.1 part, vinylpyrrolidone/dimethylaminoethyl methacrylate copolymer 10 part, sepiolite 2 parts, 60 parts, water;
Physiotherapy pressed powder is made up of following components in mass portion: nanoscale infrared magnetic stone flour 5 parts, 5 parts, nanoscale ochre powder, 10 parts, Nanometer Maifan Stone powder, 10 parts, nanoscale agate powder, 5 parts, nanometer level pearl powder.
The wall material of physiotherapy microcapsules is collagen or phycobniliprotein, the core of physiotherapy microcapsules is mixed by component A and B component, component A is the mixture of Tea Polyphenols and pycnogenol, weight ratio 1:1, B component is made up of following components in mass portion: vitamin E2 0 part, stem of noble dendrobium active polysaccharide 2 parts, gingkgo flavonoids 2 parts, lipoic acid 1 part, shitosan 5 parts, in the core of physiotherapy microcapsules, the percentage by weight of B component is 40%.
In the non-ironing treatment fluid of second physiotherapy, key component is no-ironing resin, fiber protection agent, softener, catalyst, PH conditioning agent and water, the parts by weight of key component are: no-ironing resin 35 parts, fiber protection agent 5 parts, softener 15 parts, catalyst 5 parts, 400 parts, water, and the pH value of the non-ironing treatment fluid of the second physiotherapy is 3; Fiber protection agent is the silicone emulsion of elastic polyurethane; PH adjusting agent is citric acid-sodium citrate buffer solution, and softener is quaternised modified amino-silicone oil.
No-ironing resin is modification bishydroxymethyl dihydroxy ethylene urea.
Catalyst is magnesium chloride.
Bake employing heating using microwave, the baking temperature baked in operation is 100 DEG C, and the time of baking is 5min.
Also containing 3 parts of wooden fish stone powder and 2 parts of coral powders in the non-ironing treatment fluid of second physiotherapy.
The core of physiotherapy microcapsules and the weight ratio of wall material are 1:1, and the diameter of physiotherapy microcapsules is 5 ~ 8 μm.
The process conditions of pressing are pressure 1.2Kg, and temperature is 90 DEG C.
The temperature of secondary preliminary drying is 60 DEG C.
Embodiment 2
The no-iron treatment method of embodiment 2 physical therapy function cotton shirt, comprises the steps:
S1: coating, is coated with the non-ironing treatment fluid of the first physiotherapy at the processing sealing of ready-made clothes, repeats aforesaid operations 2 times;
S2: preliminary drying, carries out a preliminary drying process to the ready-made clothes of the non-ironing treatment fluid of coating first physiotherapy;
S3: upper liquid, the non-ironing treatment fluid of atomized spray second physiotherapy, evenly applying the non-ironing treatment fluid of the second physiotherapy to ready-made clothes liquid carrying rate to ready-made clothes is 95%;
S4: secondary preliminary drying, carries out secondary preliminary drying to upper liquid gained ready-made clothes, and pre-baked ready-made clothes is 6 ~ 9 one-tenth to be done;
S5: pressing, carries out pressing respectively to each position of secondary preliminary drying gained ready-made clothes;
S6: bake, bakes process to the ready-made clothes after pressing;
S7: cooling, proceeds in refrigerating chamber carry out cooling processing by baking the ready-made clothes after process;
S8: washing is dried, and must have the non-ironing cotton shirt of physical therapy function;
Wherein, in refrigerating work procedure, the temperature of refrigerating chamber is 0 DEG C, and the cooling processing time is 5h.
The component of the non-ironing treatment fluid of the first physiotherapy comprises physiotherapy microcapsules 30 parts, physiotherapy pressed powder 40 parts, fibroin albumen 7 parts, deoxycholic acid 1 part, vinylpyrrolidone/dimethylaminoethyl methacrylate copolymer 25 parts, sepiolite 8 parts, 100 parts, water;
Physiotherapy pressed powder is made up of following components in mass portion: nanoscale infrared magnetic stone flour 15 parts, 15 parts, nanoscale ochre powder, 20 parts, Nanometer Maifan Stone powder, 20 parts, nanoscale agate powder, 40 parts, nanometer level pearl powder.
The wall material of physiotherapy microcapsules is collagen or phycobniliprotein, the core of physiotherapy microcapsules is mixed by component A and B component, component A is the mixture being selected from Tea Polyphenols, grape seed polyphenols, vine polyphenol and pycnogenol, B component is made up of following components in mass portion: vitamin E 30 parts, stem of noble dendrobium active polysaccharide 210 parts, gingkgo flavonoids 15 parts, lipoic acid 7 parts, shitosan 20 parts, in the core of physiotherapy microcapsules, the percentage by weight of B component is 80%.
In the non-ironing treatment fluid of second physiotherapy, key component is no-ironing resin, fiber protection agent, softener, catalyst, PH conditioning agent and water, the parts by weight of key component are: no-ironing resin 130 parts, fiber protection agent 45 parts, softener 65 parts, catalyst 20 parts, 800 parts, water, and the pH value of the non-ironing treatment fluid of the second physiotherapy is 5.5; Fiber protection agent is the common emulsion of oxidized polyethylene homopolymers and amido silicon oil; PH adjusting agent is acetic acid-sodium acetate buffer solution, and softener is polyether block/chain alkyl amino-modified silicone oil.
No-ironing resin is nano-dispersed self-crosslinking polyether-polyurethane.
Catalyst is composite catalyst; Composite catalyst is composited by metal salt catalyst and hydroxycarboxylic acid, and metal salt catalyst is magnesium nitrate, and hydroxycarboxylic acid is dihydromethyl propionic acid, and in composite catalyst, the percentage by weight of metal salt catalyst is 30%.
Bake employing heating using microwave, the baking temperature baked in operation is 130 DEG C, and the time of baking is 25min.
Also containing 13 parts of wooden fish stone powder and 15 parts of coral powders in the non-ironing treatment fluid of second physiotherapy.
The core of physiotherapy microcapsules and the weight ratio of wall material are 2:1, and the diameter of physiotherapy microcapsules is 5 ~ 8 μm.
The process conditions of pressing are pressure 3.4Kg, and temperature is 170 DEG C.
The temperature of secondary preliminary drying is 85 DEG C.
Embodiment 3
The no-iron treatment method of embodiment 3 physical therapy function cotton shirt, comprises the steps:
S1: coating, is coated with the non-ironing treatment fluid of the first physiotherapy at the processing sealing of ready-made clothes, repeats aforesaid operations 1 ~ 2 time;
S2: preliminary drying, carries out a preliminary drying process to the ready-made clothes of the non-ironing treatment fluid of coating first physiotherapy;
S3: upper liquid, the non-ironing treatment fluid of atomized spray second physiotherapy, evenly applying the non-ironing treatment fluid of the second physiotherapy to ready-made clothes liquid carrying rate to ready-made clothes is 80%;
S4: secondary preliminary drying, carries out secondary preliminary drying to upper liquid gained ready-made clothes, and pre-baked ready-made clothes is 6 ~ 9 one-tenth to be done;
S5: pressing, carries out pressing respectively to each position of secondary preliminary drying gained ready-made clothes;
S6: bake, bakes process to the ready-made clothes after pressing;
S7: cooling, proceeds in refrigerating chamber carry out cooling processing by baking the ready-made clothes after process;
S8: washing is dried, and must have the non-ironing cotton shirt of physical therapy function;
Wherein, in refrigerating work procedure, the temperature of refrigerating chamber is-5 DEG C, and the cooling processing time is 3h.
The component of the non-ironing treatment fluid of the first physiotherapy comprises physiotherapy microcapsules 17 parts, physiotherapy pressed powder 30 parts, fibroin albumen 3 parts, deoxycholic acid 0.5 part, vinylpyrrolidone/dimethylaminoethyl methacrylate copolymer 17 parts, sepiolite 5 parts, 80 parts, water;
Physiotherapy pressed powder is made up of following components in mass portion: nanoscale infrared magnetic stone flour 10 parts, 10 parts, nanoscale ochre powder, 15 parts, Nanometer Maifan Stone powder, 15 parts, nanoscale agate powder, 25 parts, nanometer level pearl powder.
The wall material of physiotherapy microcapsules is collagen or phycobniliprotein, the core of physiotherapy microcapsules is mixed by component A and B component, component A is pycnogenol, B component is made up of following components in mass portion: vitamin E2 5 parts, stem of noble dendrobium active polysaccharide 6 parts, gingkgo flavonoids 9 parts, lipoic acid 4 parts, shitosan 12 parts, in the core of physiotherapy microcapsules, the percentage by weight of B component is 60%.
In the non-ironing treatment fluid of second physiotherapy, key component is no-ironing resin, fiber protection agent, softener, catalyst, PH conditioning agent and water, the parts by weight of key component are: no-ironing resin 75 parts, fiber protection agent 25 parts, softener 40 parts, catalyst 14 parts, 600 parts, water, and the pH value of the non-ironing treatment fluid of the second physiotherapy is 4.2; Fiber protection agent is the mixture of the silicone emulsion of elastic polyurethane and the common emulsion of oxidized polyethylene homopolymers and amido silicon oil; PH adjusting agent is sodium dihydrogen phosphate-citrate buffer solution, and softener is the mixture of quaternised modified amino-silicone oil and polyether block/chain alkyl amino-modified silicone oil.
No-ironing resin is modified alkyl dihydroxy ethylene urea.
Catalyst is composite catalyst; Composite catalyst is composited by metal salt catalyst and hydroxycarboxylic acid, and metal salt catalyst is zinc nitrate, and hydroxycarboxylic acid is 2,3-dyhydrobutanedioic acid, and in composite catalyst, the percentage by weight of metal salt catalyst is 40%.
Bake employing heating using microwave, the baking temperature baked in operation is 100 ~ 130 DEG C, and the time of baking is 5 ~ 25min.
Also containing 3 ~ 13 parts of wooden fish stone powder and 2 ~ 15 parts of coral powders in the non-ironing treatment fluid of second physiotherapy.
The core of physiotherapy microcapsules and the weight ratio of wall material are (1 ~ 2): 1, and the diameter of physiotherapy microcapsules is 5 ~ 8 μm.
The process conditions of pressing are pressure 2.3Kg, and temperature is 130 DEG C.
The temperature of secondary preliminary drying is 72 DEG C.
The pressure of one square centimeter that pressing pressure: 1kg refers to.1kg/cm
2=9.8N/cm
2
Liquid carrying rate, also known as pick-up, pick-up rate is the number of webbing liquid measure after mangle.
Liquid carrying rate computing formula is: fabric heavy * 100% before pick-up rate=(after mangle before fabric weight-mangle fabric weight)/mangle
The representation of a few Cheng Gan refers to that the amount of moisture that band liquid ready-made clothes has dried accounts for the one-tenth number that should dry the component that anhydrates when being dried to dry ready-made clothes.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (10)
1. a no-iron treatment method for physical therapy function cotton shirt, is characterized in that, comprises the steps:
S1: coating, is coated with the non-ironing treatment fluid of the first physiotherapy at the processing sealing of ready-made clothes, repeats aforesaid operations 1 ~ 2 time;
S2: preliminary drying, carries out a preliminary drying process to the ready-made clothes of the non-ironing treatment fluid of coating first physiotherapy;
S3: upper liquid, the non-ironing treatment fluid of atomized spray second physiotherapy, evenly applying the non-ironing treatment fluid of the second physiotherapy to ready-made clothes liquid carrying rate to ready-made clothes is 60 ~ 95%;
S4: secondary preliminary drying, carries out secondary preliminary drying to upper liquid gained ready-made clothes, and pre-baked ready-made clothes is 6 ~ 9 one-tenth to be done;
S5: pressing, carries out pressing respectively to each position of secondary preliminary drying gained ready-made clothes;
S6: bake, bakes process to the ready-made clothes after pressing;
S7: cooling, proceeds in refrigerating chamber carry out cooling processing by baking the ready-made clothes after process;
S8: washing is dried, and must have the non-ironing cotton shirt of physical therapy function;
Wherein, in described refrigerating work procedure, the temperature of refrigerating chamber is-10 ~ 0 DEG C, and the cooling processing time is 0.5 ~ 5h.
2. the no-iron treatment method of physical therapy function cotton shirt according to claim 1, it is characterized in that, the component of the non-ironing treatment fluid of described first physiotherapy comprises physiotherapy microcapsules 5 ~ 30 parts, physiotherapy pressed powder 20 ~ 40 parts, fibroin albumen 0.5 ~ 7 part, deoxycholic acid 0.1 ~ 1 part, vinylpyrrolidone/dimethylaminoethyl methacrylate copolymer 10 ~ 25 part, sepiolite 2 ~ 8 parts, 60 ~ 100 parts, water;
Described physiotherapy pressed powder is made up of following components in mass portion: nanoscale infrared magnetic stone flour 5 ~ 15 parts, 5 ~ 15 parts, nanoscale ochre powder, 10 ~ 20 parts, Nanometer Maifan Stone powder, 10 ~ 20 parts, nanoscale agate powder, 5 ~ 40 parts, nanometer level pearl powder;
The wall material of described physiotherapy microcapsules is collagen or phycobniliprotein, the core of described physiotherapy microcapsules is mixed by component A and B component, described component A is selected from least one in Tea Polyphenols, grape seed polyphenols, vine polyphenol, pycnogenol, described B component is made up of following components in mass portion: vitamin E2 0 ~ 30 part, stem of noble dendrobium active polysaccharide 2 ~ 10 parts, gingkgo flavonoids 2 ~ 15 parts, lipoic acid 1 ~ 7 part, shitosan 5 ~ 20 parts, in the core of physiotherapy microcapsules, the percentage by weight of B component is 40 ~ 80%.
3. the no-iron treatment method of physical therapy function cotton shirt according to claim 2, it is characterized in that, in the non-ironing treatment fluid of second physiotherapy, key component is no-ironing resin, fiber protection agent, softener, catalyst, PH conditioning agent and water, the parts by weight of key component are: no-ironing resin 35 ~ 130 parts, fiber protection agent 5 ~ 45 parts, softener 15 ~ 65 parts, catalyst 5 ~ 20 parts, 400 ~ 800 parts, water, and the pH value of the non-ironing treatment fluid of described second physiotherapy is 3 ~ 5.5; Described fiber protection agent is be selected from least one in the silicone emulsion of elastic polyurethane and the common emulsion of oxidized polyethylene homopolymers and amido silicon oil; Described pH adjusting agent is be selected from the one in citric acid-sodium citrate buffer solution, acetic acid-sodium acetate buffer solution and sodium dihydrogen phosphate-citrate buffer solution, and described softener is be selected from least one in quaternised modified amino-silicone oil and polyether block/chain alkyl amino-modified silicone oil.
4. the no-iron treatment method of the physical therapy function cotton shirt according to Claims 2 or 3, it is characterized in that, described no-ironing resin is be selected from least one in modification bishydroxymethyl dihydroxy ethylene urea, nano-dispersed self-crosslinking polyether-polyurethane, modified alkyl dihydroxy ethylene urea.
5. the no-iron treatment method of the physical therapy function cotton shirt according to Claims 2 or 3, is characterized in that, described catalyst is magnesium chloride, or is composite catalyst; Described composite catalyst is composited by metal salt catalyst and hydroxycarboxylic acid, described metal salt catalyst is be selected from least one in magnesium chloride, magnesium nitrate, zinc chloride, zinc nitrate, described hydroxycarboxylic acid is citric acid, dihydromethyl propionic acid, 2, at least one in 3-dyhydrobutanedioic acid, in described composite catalyst, the percentage by weight of metal salt catalyst is 30 ~ 40%.
6. the no-iron treatment method of physical therapy function cotton shirt according to claim 1, is characterized in that, described in bake employing heating using microwave, the baking temperature baked in operation is 100 ~ 130 DEG C, described in bake the time be 5 ~ 25min.
7. the no-iron treatment method of physical therapy function cotton shirt according to claim 3, is characterized in that, also containing 3 ~ 13 parts of wooden fish stone powder and 2 ~ 15 parts of coral powders in the non-ironing treatment fluid of described second physiotherapy.
8. the no-iron treatment method of physical therapy function cotton shirt according to claim 5, is characterized in that, the core of described physiotherapy microcapsules and the weight ratio of wall material are (1 ~ 2): 1, and the diameter of described physiotherapy microcapsules is 5 ~ 8 μm.
9. the no-iron treatment method of physical therapy function cotton shirt according to claim 1, is characterized in that, the process conditions of described pressing are pressure 1.2 ~ 3.4Kg, and temperature is 90 ~ 170 DEG C.
10. the no-iron treatment method of physical therapy function cotton shirt according to claim 1, is characterized in that, the temperature of described secondary preliminary drying is 60 ~ 85 DEG C.