CN100560854C - A kind of multi-functional coatings fabric and production method of polymer coating - Google Patents

A kind of multi-functional coatings fabric and production method of polymer coating Download PDF

Info

Publication number
CN100560854C
CN100560854C CNB2006101544376A CN200610154437A CN100560854C CN 100560854 C CN100560854 C CN 100560854C CN B2006101544376 A CNB2006101544376 A CN B2006101544376A CN 200610154437 A CN200610154437 A CN 200610154437A CN 100560854 C CN100560854 C CN 100560854C
Authority
CN
China
Prior art keywords
parts
coating
toluene
dimethyl formamide
pellet
Prior art date
Application number
CNB2006101544376A
Other languages
Chinese (zh)
Other versions
CN1948607A (en
Inventor
吴新初
楚伟峰
王悦群
左金华
Original Assignee
浙江锦达新材料股份有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 浙江锦达新材料股份有限公司 filed Critical 浙江锦达新材料股份有限公司
Priority to CNB2006101544376A priority Critical patent/CN100560854C/en
Publication of CN1948607A publication Critical patent/CN1948607A/en
Application granted granted Critical
Publication of CN100560854C publication Critical patent/CN100560854C/en

Abstract

The present invention relates to a kind of multi-functional coatings manufacturing method of fabrics of polymer coating, its the coating surface layer be by the following weight proportioning raw material make, dissolve pellet: 100 parts, toluene: 10~30 parts, dimethyl formamide: 5~30 parts, hydroxy polyethers modified dimethyl polysiloxane: 0.05~0.5 part, toner: 1~10 part and function additive: 0.01~0.5 part, wherein dissolve pellet by the following weight proportioning raw material make the thermoplastic polyurethane pellet: 100 parts, solvent dimethyl formamide: 10~60 parts, diluent toluene: 20~50 parts; Its coating adhesion layer is to be made by the following weight proportion raw material, the two liquid type polyurethane resin: 100 parts, and toluene: 10~50 parts, solvent dimethyl formamide DMF:5~30 parts, butanone: 5~30 parts, toner: 1~10 part, function additive: 0.01~0.5 part.The effect that the present invention is useful is: product can reach multifunctionalities such as waterproof, rainproof, ventilative, saturating wet, perspire, dry and comfortable, antistatic, fire-retardant and uvioresistant; Especially water pressure resistance can reach 5000mmH 2More than the O, vapor transfer rate can reach 5000g/m 2.24h more than.

Description

A kind of multi-functional coatings manufacturing method of fabrics of polymer coating

Technical field

The invention belongs to the fabric coating field, especially a kind of multi-functional coatings manufacturing method of fabrics of polymer coating.

Background technology

Fabric coating is the new industry that China develops rapidly in recent ten years.Coated fabric then is to be base cloth with all kinds of textiless, the special material with function of shielding that forms coated with immersion coating materials processing.Development is very fast on this series products both at home and abroad, because its special function of shielding makes it be widely used in civilian (life is used), industrial or agricultural (especially transportation building), health care and military various aspects.

The top finish of fabric is an important branch of after-finishing of textile products technology, and the main application of coating product can be divided into three major types: clothes, shoes and hats class, industrial dry goods, decorating cloth class, wherein clothes, shoes and hats class consumption maximum.

Coating is given the function of fabric and is not only shielding, also has other, promptly when a certain function of shielding is provided, also will take into account other one or more functions.With the closely-related raincoat of the people's livelihood or other protective clothings, in shielding rainwater or other invaders, must take into account and wet in the market, make the wearer feel comfortable.Yet owing to technical elements or otherwise reason, when requiring water pressure resistance very high and when being strictly on guard against invader, this take into account just very difficult.The related coatings product mainly makes with direct coating macromolecular material or MULTILAYER COMPOSITE forms, and protection efficiency and water vapour permeability can not be taken into account; In addition, feel hard partially, wear the time slightly length will feel sultry.Thereby " Waterproof Breathable " fabric, " ventilative " fabric be still very important part in the coated fabric at present, and it also is the direction and goal of our enterprise technology development, Product Renewal.For remedying many deficiencies that this series products in use exists and better adapting to market demand, through sufficient market watch and investigation, I take charge of conscientious research and analysis, decision is with the existing advanced coating apparatus of company, in conjunction with advanced factory formula and technology, carry out a kind of exploitation and production application of high polymer multi-functional coatings fabric.

Summary of the invention

The objective of the invention is to overcome the deficiency of said structure, and a kind of multi-functional coatings manufacturing method of fabrics of polymer coating is provided.

The technical solution adopted for the present invention to solve the technical problems.The multi-functional coatings fabric of this polymer coating, its the coating surface layer be by the following weight proportioning raw material make, dissolve pellet: 100 parts, toluene: 10~30 parts, dimethyl formamide (DMF): 5~30 parts, hydroxy polyethers modified dimethyl polysiloxane: 0.05~0.5 part, toner: 1~10 part and function additive: 0.01~0.5 part, wherein dissolve pellet by the following weight proportioning raw material make the thermoplastic polyurethane pellet: 100 parts, solvent dimethyl formamide (DMF): 10~60 parts, diluent toluene: 20~50 parts; Its coating adhesion layer be by the following weight proportioning raw material make the two liquid type polyurethane resin: 100 parts, toluene: 10~50 parts, solvent dimethyl formamide DMF:5~30 parts, butanone (MEK): 5~30 parts, toner: 1~10 part, function additive: 0.01~0.5 part.

The multi-functional coatings manufacturing method of fabrics of this polymer coating mainly comprises the steps:

1), pellet is dissolved: dissolve pellet and made by the following weight proportion raw material, the thermoplastic polyurethane pellet: 100 parts, solvent dimethyl formamide (DMF): 10~60 parts, diluent toluene: 20~50 parts, viscosity is controlled: 8000~50000cps;

2), slurry preparation: its coating surface layer be by the following weight proportioning raw material make, dissolve pellet: 100 parts, toluene: 10~30 parts, dimethyl formamide (DMF): 5~30 parts, hydroxy polyethers modified dimethyl polysiloxane: 0.05~0.5 part, toner: 1~10 part and function additive: 0.01~0.5 part, viscosity control: 2000~5000cps; Its coating adhesion layer be by the following weight proportioning raw material make the two liquid type polyurethane resin: 100 parts, toluene: 10~50 parts, solvent dimethyl formamide DMF:5~30 parts, butanone (MEK): 5~30 parts, toner: 1~10 part, function additive: 0.01~0.5 part; Viscosity control: 5000~10000cps;

3), the used base cloth of product is Woven Fabrics, woven cloth or knitted cloth, thickness is 0.2~0.6mm; Release liners at first goes up coating machine through the check back, carries out the surface layer coating then, coating weight 50~250g/m 2, weight in wet base, cutter then enters oven drying, 90~150 ℃ of temperature, time 2~5min apart from 0.05~0.2mm;

4), the surface layer after the oven dry is proceeded adhesion layer coating, coating weight 50~250g/m 2, weight in wet base, cutter carries out base cloth then and fits 30~80 ℃ of binding temperatures, pressure 0.1~2kgf/cm apart from 0.05~0.2mm 2Product after posting enters the baking oven preliminarily dried, 90~120 ℃ of temperature, time 0.5~3min and cure crosslinking curing, 130~160 ℃ of temperature, time 2~5min; Cool off at last to peel off and obtain the finished product coated fabric.

1), this product is to be base cloth with the Woven Fabrics effect that the present invention is useful is:, soft, snugness of fit is good, has overcome old product Boardy Feeling, the narrow defective of the scope of application.2), adopt good high-performance coating agent and special addition agent, through optimizing preparation, played the remarkable environmental effect, azo class material, content of beary metal meet European EN14362-2003 environmental protection standard.3), the best adjustment of adopting the transfer heat posted technology of novelty and carrying out technological parameter produces this product, changed old technology and directly be coated with and scrape the various drawbacks of bringing (even as became uneven, appearance style is poor, and functional parameter is low etc.).4), outstanding behaviours is multifunctionality and good surface appearance style because the innovation of above aspect improves, product can reach waterproof, rainproof, ventilative, wet thoroughly, multifunctionalities such as perspire, dry and comfortable, antistatic, fire-retardant and uvioresistant; Especially water pressure resistance can reach 5000mmH 2More than the O, vapor transfer rate can reach 5000g/m 2.24h more than.5), the multifunctionality of product has been widened its Application Areas, develop into feather dress fabric, sportswear lining, hunting dress lining, medical protective clothing and woollen sweater etc. from raincoat, clothes lining, this product has been filled up domestic blank, has good economic and social benefit.

Description of drawings

Fig. 1 is a process flow diagram of the present invention;

The specific embodiment:

Below in conjunction with drawings and Examples the present invention is further described.

Embodiment 1: the multi-functional coatings fabric of this polymer coating, its coating surface layer is to be made by the following weight proportion raw material, dissolve pellet: 100 parts, toluene: 10 parts, dimethyl formamide (DMF): 5 parts, hydroxy polyethers modified dimethyl polysiloxane: 0.05 part, toner: 1 part and function additive: 0.01 part, wherein dissolve pellet by the following weight proportioning raw material make the thermoplastic polyurethane pellet: 100 parts, solvent dimethyl formamide (DMF): 10 parts, diluent toluene: 20 parts; Its coating adhesion layer be by the following weight proportioning raw material make the two liquid type polyurethane resin: 100 parts, toluene: 10 parts, solvent dimethyl formamide DMF:5 part, butanone (MEK): 5 parts, toner: 1 part, function additive: 0.02 part.

Described function additive is antiseptic or antistatic additive or ultra-violet absorber, and described antiseptic adopts a kind of in the inorganic antiseptic: nano-TiO 2The titanium series antibacterial agent, salt of phosphoric acid class, zeolites, activated carbon fiber class or smectites silver-series antibacterial agent, perhaps shitosan, chitin or Hinokitiol natural antibacterial agent.Described antistatic additive adopts alkylsulfonate, acid amides, amine, ester, quaternary amine or fatty acid soaps.Described ultra-violet absorber adopts zinc oxide, titanium dioxide, phenyl salicytate, dihydroxy benaophenonel or benzotriazole.

The multi-functional coatings manufacturing method of fabrics of this polymer coating mainly comprises the steps:

1), pellet dissolves: dissolve pellet by the following weight proportioning raw material make the thermoplastic polyurethane pellet: 100 parts, solvent dimethyl formamide (DMF): 10 parts, diluent toluene: 20 parts, viscosity control: 8000~50000cps;

2), slurry preparation: its coating surface layer be by the following weight proportioning raw material make, dissolve pellet: 100 parts, toluene: 10 parts, dimethyl formamide (DMF): 5 parts, hydroxy polyethers modified dimethyl polysiloxane: 0.05 part, toner: 1 part and function additive: 0.02 part, viscosity control: 2000~5000cps; Its coating adhesion layer be by the following weight proportioning raw material make the two liquid type polyurethane resin: 100 parts, toluene: 10 parts, solvent dimethyl formamide DMF:5 part, butanone (MEK): 5 parts, toner: 1 part, function additive: 0.02 part; Viscosity control: 5000~10000cps;

3), the used base cloth of product is Woven Fabrics, woven cloth or knitted cloth, thickness is 0.2~0.6mm; Release liners at first goes up coating machine through the check back, carries out the surface layer coating then, coating weight 50~250g/m 2, weight in wet base, cutter then enters oven drying, 90~150 ℃ of temperature, time 2~5min apart from 0.05~0.2mm;

4), the surface layer after the oven dry is proceeded adhesion layer coating, coating weight 50~250g/m 2, weight in wet base, cutter carries out base cloth then and fits 30~80 ℃ of binding temperatures, pressure 0.1~2kgf/cm apart from 0.05~0.2mm 2Product after posting enters the baking oven preliminarily dried, 90~120 ℃ of temperature, time 0.5~3min and cure crosslinking curing, 130~160 ℃ of temperature, time 2~5min; Cool off at last to peel off and obtain the finished product coated fabric.

Technical indicator:

1) hydraulic pressure 5000~10000mmH 2O (ISO811-1981)

2) wet thoroughly 5000~6000g/m 2.24h (ASTM E96-2000BW)

3) dry-cleaning 4~5 grades of COLOR FASTNESS (ISO105D01-1993)

4) LIGHT COLOR FASTNESS is more than 4 grades (ISO105D02-1994)

5) TENSILE STRENGTH: through 600N, latitude 680N (ISO13934-1-1999)

6) azo, content of beary metal are by the test of EN14362-2003 European standard

Embodiment 2: the multi-functional coatings fabric of this polymer coating, its coating surface layer is to be made by the following weight proportion raw material, dissolve pellet: 100 parts, toluene: 30 parts, dimethyl formamide (DMF): 30 parts, hydroxy polyethers modified dimethyl polysiloxane: 0.5 part, toner: 10 parts and function additive: 0.5 part, wherein dissolve pellet by the following weight proportioning raw material make the thermoplastic polyurethane pellet: 100 parts, solvent dimethyl formamide (DMF): 60 parts, diluent toluene: 50 parts; Its coating adhesion layer be by the following weight proportioning raw material make the two liquid type polyurethane resin: 100 parts, toluene: 50 parts, solvent dimethyl formamide DMF:30 part, butanone (MEK): 30 parts, toner: 10 parts, function additive: 0.5 part.Function additive is an antiseptic, and described antiseptic adopts a kind of in the inorganic antiseptic: nano-TiO 2The titanium series antibacterial agent, salt of phosphoric acid class, zeolites, activated carbon fiber class or smectites silver-series antibacterial agent, perhaps shitosan, chitin or Hinokitiol natural antibacterial agent.

Embodiment 3: the multi-functional coatings fabric of this polymer coating, its coating surface layer is to be made by the following weight proportion raw material, dissolve pellet: 100 parts, toluene: 20 parts, dimethyl formamide (DMF): 20 parts, hydroxy polyethers modified dimethyl polysiloxane: 0.2 part, toner: 5 parts and function additive: 0.2 part, wherein dissolve pellet by the following weight proportioning raw material make the thermoplastic polyurethane pellet: 100 parts, solvent dimethyl formamide (DMF): 30 parts, diluent toluene: 35 parts; Its coating adhesion layer be by the following weight proportioning raw material make the two liquid type polyurethane resin: 100 parts, toluene: 30 parts, solvent dimethyl formamide DMF:15 part, butanone (MEK): 15 parts, toner: 5 parts, function additive: 0.2 part.Described function additive is an antistatic additive, adopts alkylsulfonate, acid amides, amine, ester, quaternary amine or fatty acid soaps.

Embodiment 4: the multi-functional coatings fabric of this polymer coating, its coating surface layer is to be made by the following weight proportion raw material, dissolve pellet: 100 parts, toluene: 15 parts, dimethyl formamide (DMF): 10 parts, hydroxy polyethers modified dimethyl polysiloxane: 0.1 part, toner: 3 parts and function additive: 0.2 part, wherein dissolve pellet by the following weight proportioning raw material make the thermoplastic polyurethane pellet: 100 parts, solvent dimethyl formamide (DMF): 20 parts, diluent toluene: 30 parts; Its coating adhesion layer be by the following weight proportioning raw material make the two liquid type polyurethane resin: 100 parts, toluene: 20 parts, solvent dimethyl formamide DMF:10 part, butanone (MEK): 10 parts, toner: 3 parts, function additive: 0.1 part.Described function additive is a ultra-violet absorber, adopts zinc oxide, titanium dioxide, phenyl salicytate, dihydroxy benaophenonel or benzotriazole.

Embodiment 5: the multi-functional coatings fabric of this polymer coating, its coating surface layer is to be made by the following weight proportion raw material, dissolve pellet: 100 parts, toluene: 25 parts, dimethyl formamide (DMF): 20 parts, hydroxy polyethers modified dimethyl polysiloxane: 0.3 part, toner: 7 parts and function additive: 0.3 part, wherein dissolve pellet by the following weight proportioning raw material make the thermoplastic polyurethane pellet: 100 parts, solvent dimethyl formamide (DMF): 40 parts, diluent toluene: 40 parts; Its coating adhesion layer be by the following weight proportioning raw material make the two liquid type polyurethane resin: 100 parts, toluene: 30 parts, solvent dimethyl formamide DMF:20 part, butanone (MEK): 20 parts, toner: 7 parts, function additive: 0.4 part.

Claims (4)

1, a kind of multi-functional coatings manufacturing method of fabrics of polymer coating is characterized in that: comprise the steps:
1.1), pellet dissolves: dissolve pellet and make, the thermoplastic polyurethane pellet: 100 parts, solvent dimethyl formamide (DMF): 10~60 parts, diluent toluene by the following weight proportion raw material: 20~50 parts, viscosity control: 8000~50000cps;
1.2), slurry preparation: its coating surface layer is to be made by the following weight proportion raw material, dissolve pellet: 100 parts, toluene: 10~30 parts, dimethyl formamide (DMF): 5~30 parts, hydroxy polyethers modified dimethyl polysiloxane: 0.05~0.5 part, toner: 1~10 part and function additive: 0.01~0.5 part, viscosity control: 2000~5000cps; Its coating adhesion layer is to be made by the following weight proportion raw material, the two liquid type polyurethane resin: 100 parts, and toluene: 10~50 parts, solvent dimethyl formamide DMF:5~30 parts, butanone (MEK): 5~30 parts, toner: 1~10 part, function additive: 0.01~0.5 part; Viscosity control: 5000~10000cps; Wherein function additive is antiseptic or antistatic additive or ultra-violet absorber;
1.3), the used base cloth of product is woven cloth or knitted cloth, thickness is 0.2~0.6mm; Release liners at first goes up coating machine through the check back, carries out the surface layer coating then, coating weight 50~250g/m 2, weight in wet base, cutter then enters oven drying, 90~150 ℃ of temperature, time 2~5min apart from 0.05~0.2mm;
1.4), the surface layer after the oven dry proceeds adhesion layer coating, coating weight 50~250g/m 2, weight in wet base, cutter carries out base cloth then and fits 30~80 ℃ of binding temperatures, pressure 0.1~2kgf/cm apart from 0.05~0.2mm 2Product after posting enters the baking oven preliminarily dried, 90~120 ℃ of temperature, time 0.5~3min and cure crosslinking curing, 130~160 ℃ of temperature, time 2~5min; Cool off at last to peel off and obtain the finished product coated fabric.
2, the multi-functional coatings manufacturing method of fabrics of polymer coating according to claim 1 is characterized in that: described antiseptic adopts shitosan, chitin or Hinokitiol.
3, the multi-functional coatings manufacturing method of fabrics of polymer coating according to claim 1 is characterized in that: described antistatic additive adopts alkylsulfonate, quaternary amine or fatty acid soaps.
4, the multi-functional coatings manufacturing method of fabrics of polymer coating according to claim 1 is characterized in that: described ultra-violet absorber adopts zinc oxide, titanium dioxide, phenyl salicytate, dihydroxy benaophenonel or benzotriazole.
CNB2006101544376A 2006-10-27 2006-10-27 A kind of multi-functional coatings fabric and production method of polymer coating CN100560854C (en)