CN108467553A - 用于wpc地板加工的环保钙锌复合稳定剂 - Google Patents

用于wpc地板加工的环保钙锌复合稳定剂 Download PDF

Info

Publication number
CN108467553A
CN108467553A CN201810227291.6A CN201810227291A CN108467553A CN 108467553 A CN108467553 A CN 108467553A CN 201810227291 A CN201810227291 A CN 201810227291A CN 108467553 A CN108467553 A CN 108467553A
Authority
CN
China
Prior art keywords
parts
zinc
calcium
wpc
floors
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810227291.6A
Other languages
English (en)
Inventor
谭学政
潘学良
孟庆举
蒋建林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shandong Sanyi Industry Ltd By Share Ltd
Original Assignee
Shandong Sanyi Industry Ltd By Share Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shandong Sanyi Industry Ltd By Share Ltd filed Critical Shandong Sanyi Industry Ltd By Share Ltd
Priority to CN201810227291.6A priority Critical patent/CN108467553A/zh
Publication of CN108467553A publication Critical patent/CN108467553A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种用于WPC地板加工的环保钙锌复合稳定剂，涉及化工技术领域，由以下重量份数的物质组成：主稳定剂30‑50份，辅助稳定剂20‑50份，自制络合物10‑30份，润滑剂20‑50份，所述自制络合物生产工艺如下：称取以下质量份的物质，偶联剂19‑21份，螯合剂19‑21份，亚磷酸酯14‑16份，季戊四醇19‑21份，填充物24‑26份，把称好的螯合物和季戊四醇加入高速搅拌机搅拌，搅拌到温度为60℃时加入亚磷酸酯，继续搅拌到温度80℃，加入填充物、偶联剂搅拌均匀；本发明通过加入一种自制络合物，清模周期延长7天，发泡均匀，生产使用方便。

Description

用于WPC地板加工的环保钙锌复合稳定剂
技术领域
本发明涉及化工技术领域，具体涉及一种用于WPC地板加工的环保钙锌复合稳定剂。
背景技术
WPC板是一种新型绿色环保复合材料，它是将木屑、竹屑、糠壳等和PE、PP、PVC加入一些助剂合成，通过挤出机挤出而成。
PVC的WPC板的生产都需要加热稳定剂，以延缓或防止加热过程中的PVC分子降解，并延长制品的使用寿命，PVC热稳定剂种类很多，可分为铅类、镉类、金属皂类、有机锡类等，其中铅类用量广泛，由于WPC板是一种新型环保材料，并且在80℃高温下容易收缩翘曲，WPC的LVT层只有1.5mm厚，对发泡性能要求严格，这就对热稳定剂有较高的要求，热稳定剂必须环保。目前WPC板用的环保钙锌稳定剂大多以多元醇和重金属皂类为基础，以水滑石和辅助稳定剂和滑剂组成，国内钙锌稳定剂目前性能不够成熟，有的钙锌稳定剂在WPC板中应用四五天就要清模，有的发泡不均匀，给生产带来不便，国外钙锌稳定剂价格贵，厂家为了节省成本难以接受。
发明内容
本发明所要解决的技术问题是：提供一种用于WPC地板加工的环保钙锌复合稳定剂，通过加入自制的络合物，解决现有技术中清模周期和发泡均匀性的问题。
本发明的目的是通过以下技术措施来实现的：
用于WPC地板加工的环保钙锌复合稳定剂，由以下重量份数的物质组成：主稳定剂30-50份，辅助稳定剂20-50份，自制络合物10-30份，润滑剂20-50份，所述自制络合物生产工艺如下：
称取以下质量份的物质，偶联剂19-21份，螯合剂19-21份，亚磷酸酯14-16份，季戊四醇19-21份，填充物24-26份，把称好的螯合物和季戊四醇加入高速搅拌机搅拌，搅拌到温度为60℃时加入亚磷酸酯，继续搅拌到温度80℃，加入填充物、偶联剂搅拌均匀。
作为一种优选的方案，所述主稳定剂包括锌皂、钙皂和镁皂，所述锌皂包括硬脂酸锌、月桂酸锌、柠檬酸锌、氰脲酸锌，所述钙皂包括硬脂酸钙和乙酰丙酮钙，所述镁皂包括硬脂酸镁。
作为一种优选的方案，所述辅助稳定剂包括碱性无机物。
作为一种优选的方案，所述润滑剂包括饱和烃类、脂肪酸类和脂肪醇类。
采用了上述方案后，本发明的有益效果是：
本发明用于WPC地板加工的环保钙锌复合稳定剂使用时清模时间较以前使用的复合稳定剂延长7天，发泡效果好，生产使用方便，受到用户的好评。
具体实施方式
下面对本发明中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明的其中的几个实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1：用于WPC地板加工的环保钙锌复合稳定剂，包括主稳定剂，辅助稳定剂、自制络合物和润滑剂。
自制络合物生产工艺如下：称取以下质量份的物质，偶联剂19份，螯合剂19份，亚磷酸酯15份，季戊四醇21份，填充物26份，把称好的螯合物和季戊四醇加入高速搅拌机搅拌，搅拌到温度为60℃时加入亚磷酸酯，继续搅拌到温度80℃，加入填充物、偶联剂搅拌均匀。
上述偶联剂为硅烷偶联剂，螯合剂主要包括B-二酮-二氢吡啶和脱氢乙酸，亚磷酸酯主要包括亚磷酸二甲酯、亚磷酸三甲酯、亚磷酸三苯酯、亚磷酸三乙酯，上述季戊四醇主要包括单季戊四醇、双季戊四醇和三季戊四醇，上述填充物主要包括碳酸钙、滑石粉和硫酸钡。
上述主稳定剂包括锌皂、钙皂和镁皂，锌皂主要包括硬脂酸锌、月桂酸锌、柠檬酸锌、氰脲酸锌，钙皂主要包括硬脂酸钙和乙酰丙酮钙，镁皂主要包括硬脂酸镁。
上述辅助稳定剂主要包括碱性无机物，例如水滑石、沸石、抗氧剂等。
上述润滑剂主要包括饱和烃类、脂肪酸类和脂肪醇类，例如石蜡、聚乙烯蜡、硬脂酸、褐煤酯、硬脂醇等。
使用时按重量份称取主稳定剂30份，辅助稳定剂20份，自制络合物10份，润滑剂20份，将上述物质成分混合搅拌均匀，本发明用于WPC地板加工的环保钙锌复合稳定剂使用后清模时间较以往使用的复合稳定剂延长7天，发泡均匀，发泡效果好。
实施例2：用于WPC地板加工的环保钙锌复合稳定剂，包括主稳定剂，辅助稳定剂、自制络合物和润滑剂。
自制络合物生产工艺如下：称取以下质量份的物质，偶联剂20份，螯合剂20份，亚磷酸酯15份，季戊四醇20份，填充物25份，把称好的螯合物和季戊四醇加入高速搅拌机搅拌，搅拌到温度为60℃时加入亚磷酸酯，继续搅拌到温度80℃，加入填充物、偶联剂搅拌均匀。
上述偶联剂为硅烷偶联剂，螯合剂主要包括B-二酮-二氢吡啶和脱氢乙酸，亚磷酸酯主要包括亚磷酸二甲酯、亚磷酸三甲酯、亚磷酸三苯酯、亚磷酸三乙酯，上述季戊四醇主要包括单季戊四醇、双季戊四醇和三季戊四醇，上述填充物主要包括碳酸钙、滑石粉和硫酸钡。
上述主稳定剂主要包括锌皂、钙皂和镁皂，锌皂主要包括硬脂酸锌、月桂酸锌、柠檬酸锌、氰脲酸锌，钙皂主要包括硬脂酸钙和乙酰丙酮钙，镁皂主要包括硬脂酸镁。
上述辅助稳定剂主要包括碱性无机物，例如水滑石、沸石、抗氧剂等。
上述润滑剂包括饱和烃类、脂肪酸类和脂肪醇类，例如石蜡、聚乙烯蜡、硬脂酸、褐煤酯、硬脂醇等。
使用时按重量份称取主稳定剂40份，辅助稳定剂35份，自制络合物20份，润滑剂35份，将上述物质成分混合搅拌均匀，本发明用于WPC地板加工的环保钙锌复合稳定剂使用后清模时间较以往使用的复合稳定剂延长7天，发泡均匀，发泡效果好。
实施例3：用于WPC地板加工的环保钙锌复合稳定剂，包括主稳定剂，辅助稳定剂、自制络合物和润滑剂。
自制络合物生产工艺如下：称取以下质量份的物质，偶联剂21份，螯合剂21份，亚磷酸酯15份，季戊四醇19份，填充物24份，把称好的螯合物和季戊四醇加入高速搅拌机搅拌，搅拌到温度为60℃时加入亚磷酸酯，继续搅拌到温度80℃，加入填充物、偶联剂搅拌均匀。
上述偶联剂为硅烷偶联剂，螯合剂主要包括B-二酮-二氢吡啶和脱氢乙酸，亚磷酸酯主要包括亚磷酸二甲酯、亚磷酸三甲酯、亚磷酸三苯酯、亚磷酸三乙酯，上述季戊四醇主要包括单季戊四醇、双季戊四醇和三季戊四醇，上述填充物主要包括碳酸钙、滑石粉和硫酸钡。
上述主稳定剂主要包括锌皂、钙皂和镁皂，锌皂主要包括硬脂酸锌、月桂酸锌、柠檬酸锌、氰脲酸锌，钙皂主要包括硬脂酸钙和乙酰丙酮钙，镁皂主要包括硬脂酸镁。
上述辅助稳定剂主要包括碱性无机物，例如水滑石、沸石、抗氧剂等。
上述润滑剂包括饱和烃类、脂肪酸类和脂肪醇类，例如石蜡、聚乙烯蜡、硬脂酸、褐煤酯、硬脂醇等。
使用时按重量份称取主稳定剂50份，辅助稳定剂50份，自制络合物30份，润滑剂50份，将上述物质成分混合搅拌均匀，本发明用于WPC地板加工的环保钙锌复合稳定剂使用后清模时间较以往使用的复合稳定剂延长7天，发泡均匀，发泡效果好。
以上所述仅为本发明的较佳实施例而已，并不用以限制本发明，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (4)

1.用于WPC地板加工的环保钙锌复合稳定剂，其特征在于，由以下重量份数的物质组成：主稳定剂30-50份，辅助稳定剂20-50份，自制络合物10-30份，润滑剂20-50份，所述自制络合物生产工艺如下：
称取以下质量份的物质，偶联剂19-21份，螯合剂19-21份，亚磷酸酯14-16份，季戊四醇19-21份，填充物24-26份，把称好的螯合物和季戊四醇加入高速搅拌机搅拌，搅拌到温度为60℃时加入亚磷酸酯，继续搅拌到温度80℃，加入填充物、偶联剂搅拌均匀。
2.如权利要求1所述的用于WPC地板加工的环保钙锌复合稳定剂，其特征在于,所述主稳定剂包括锌皂、钙皂和镁皂，所述锌皂包括硬脂酸锌、月桂酸锌、柠檬酸锌、氰脲酸锌，所述钙皂包括硬脂酸钙和乙酰丙酮钙，所述镁皂包括硬脂酸镁。
3.如权利要求1所述的用于WPC地板加工的环保钙锌复合稳定剂，其特征在于,所述辅助稳定剂包括碱性无机物。
4.如权利要求1所述的用于WPC地板加工的环保钙锌复合稳定剂，其特征在于,所述润滑剂包括饱和烃类、脂肪酸类和脂肪醇类。
CN201810227291.6A 2018-03-20 2018-03-20 用于wpc地板加工的环保钙锌复合稳定剂 Pending CN108467553A (zh)