CN108456481A - A kind of automobile air brushing spray and preparation method thereof - Google Patents
A kind of automobile air brushing spray and preparation method thereof Download PDFInfo
- Publication number
- CN108456481A CN108456481A CN201810131986.4A CN201810131986A CN108456481A CN 108456481 A CN108456481 A CN 108456481A CN 201810131986 A CN201810131986 A CN 201810131986A CN 108456481 A CN108456481 A CN 108456481A
- Authority
- CN
- China
- Prior art keywords
- resin solution
- modified rosin
- ethyl cellulose
- ethyl alcohol
- mill base
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of automobile air brushing sprays and preparation method thereof, belong to lacquering technologies field, and spray of the present invention includes the component of following mass percentage：Ethyl cellulose resin solution 2%~5%, waterborne polyurethane resin 5%~8%, modified rosin resin solution 1%~3%, mill base 3%~5%, absolute ethyl alcohol 18%~25%, dispersant 0.5%~1% and propellant 60%~70%.Spray of the present invention is environmentally friendly, and will not corrode vehicle body.
Description
Technical field
The invention belongs to lacquering technologies fields more particularly to a kind of automobile air brushing spray and preparation method thereof.
Background technology
The vehicle body or rear window of automobile need to be pasted with paster, be publicized and noticeable effect with this to reach；However, patch
There are some defects for the use of paper：1) using process there is damage in paster, mass production, can lead to the wasting of resources；2) paster
It is difficult to tear and vehicle body, vehicle paint can be damaged.Currently, automobile air brushing spray has been released in the market, it is convenient and efficient, and
Any influence is not generated to vehicle body.
However, there is also some shortcomings for existing automobile air brushing spray：1) in spray after harmful organic solvent volatilization
Human body is damaged；2) spray meeting vehicle body damages.Therefore, it is necessary to develop a kind of novel automobile air brushing spraying
Agent, it is environmentally friendly, and vehicle body will not be corroded.
Invention content
Present invention aims to overcome that the shortcomings of the prior art, and provide a kind of automobile air brushing spray and its preparation
Method, the automobile air brushing spray prepared using the preparation method is environmentally friendly, and will not corrode vehicle body.
To achieve the above object, the technical solution that the present invention takes is：A kind of automobile air brushing spray, it includes following matter
Measure the component of percentage composition：Ethyl cellulose resin solution 2%~5%, waterborne polyurethane resin 5%~8%, modified rosin tree
Lipoprotein solution 1%~3%, mill base 3%~5%, absolute ethyl alcohol 18%~25%, dispersant 0.5%~1% and propellant 60%~
70%；The solvent of the ethyl cellulose resin solution and modified rosin resin solution is organic solvent.
Preferably, the dispersant is the mixing of low molecular weight unsaturation polycarboxylic acid polymers and polysiloxane copolymer
Object solution；Mill base is resin type mill base；Ethyl cellulose resin is the good resin of thermal stability, has excellent flexibility, energy
Anti-aging, and resistance to good hygroscopicity；Waterborne polyurethane resin has low VOC values or non-environmental-pollution using water as main medium, and
With excellent flexibility；Modified rosin resin has water-tolerant, feature with high hardness.The present invention is creatively by ethyl fibre
The plain resin solution of dimension, waterborne polyurethane resin and modified rosin resin solution are combined, and the spray prepared is environment friend
Good type, will not damage vehicle body, and stable storing, drying time are short.
As an improvement of the above technical solution, automobile air brushing spray includes that the component ethyl of following mass percentage is fine
The plain resin solution 3% of dimension, waterborne polyurethane resin 7%, modified rosin resin solution 2%, mill base 4%, absolute ethyl alcohol 18.5%,
Dispersant 0.5% and propellant 65%.
As a further improvement of the above technical scheme, the ethyl cellulose resin solution and modified rosin resin solution
Solvent be absolute ethyl alcohol, the propellant be dimethyl ether.
As a further improvement of the above technical scheme, the ethyl cellulose resin solution is to carry out by the following method
It prepares：Ethyl cellulose resin is dissolved in absolute ethyl alcohol, stirs and evenly mixs up to mixed liquor I, is added into the mixed liquor I
Triethanolamine, mixing is up to ethyl cellulose resin solution；Ethyl cellulose resin 14%~25% and absolute ethyl alcohol 75%~
86%；The mass ratio of the triethanolamine and the mixed liquor I is 0.2%.
Preferably, the mixed liquor I is grouped as by the group of following mass percentage：Ethyl cellulose resin 20% and nothing
Water-ethanol 80%.
As a further improvement of the above technical scheme, the modified rosin resin solution is to be made by the following method
It is standby：Modified rosin resin is dissolved in absolute ethyl alcohol, is stirred and evenly mixed up to modified rosin resin solution；The modified rosin tree
Lipoprotein solution is grouped as by the group of following mass percentage：Modified rosin resin 25%~36% and absolute ethyl alcohol 64%~
75%.
Preferably, the modified rosin resin solution is grouped as by the group of following mass percentage：Modified rosin resin
30% and absolute ethyl alcohol 70%.
As a further improvement of the above technical scheme, the mill base is prepared by the following method：Add into toner
Enter the ethyl cellulose resin solution and the modified rosin resin solution, stirs evenly up to mill base magma；To the color
Slurry magma is ground to get mill base；Preferably, the toner is fluorescent powder or pearl powder.
As the further improvement of above-mentioned technical proposal, the grain size of particle in the mill base<10μm.
In addition, the present invention also provides a kind of preparation methods of the automobile air brushing spray comprising following steps：
1) ethyl cellulose resin solution, modified rosin resin solution and mill base are prepared；
2) by ethyl cellulose resin solution, waterborne polyurethane resin, modified rosin resin solution and absolute ethyl alcohol and stirring
Mixing, and dispersant is added, it stirs and evenly mixs up to mixed liquor II；
3) mill base is added into the mixed liquor II, up to mixed liquor Ш after toning；
4) filling to mixed liquor Ш progress, it is filled with propellant after sealing, is finally packed.
The beneficial effects of the present invention are：Method is put in a kind of automobile air brushing spray of present invention offer and its preparation, is sprayed
Agent includes ethyl cellulose resin, waterborne polyurethane resin and modified rosin resin；Wherein, ethyl cellulose resin is thermostabilization
Property good resin, there is excellent flexibility, can anti-aging, and resistance to good hygroscopicity；Waterborne polyurethane resin is main be situated between with water
Matter has low VOC values or non-environmental-pollution, and has excellent flexibility；Modified rosin resin has water-tolerant, hardness
High feature；The present invention is creatively by ethyl cellulose resin solution, waterborne polyurethane resin and modified rosin resin solution
It is combined, the spray prepared is environmentally friendly, will not damage vehicle body, and stable storing, drying time are short.
Specific implementation mode
For the object, technical solutions and advantages of the present invention are better described, below in conjunction with specific embodiment to the present invention
It is described further.
Embodiment 1
The present embodiment provides a kind of automobile air brushing sprays, and it includes the components of following mass percentage：Ethyl cellulose
Plain resin solution 3%, modified rosin resin solution 2%, mill base 4%, absolute ethyl alcohol 18.5%, divides waterborne polyurethane resin 7%
Powder 0.5% and propellant 65%；Ethyl cellulose resin is Ashland imported with original packaging, and dispersant is Bi Ke companies of Germany
BYK-104S, propellant are dimethyl ether.
In addition, the present embodiment also provides the preparation method of the automobile air brushing spray comprising following steps：
1) ethyl cellulose resin solution is prepared：Ethyl cellulose resin is dissolved in absolute ethyl alcohol, is stirred and evenly mixed i.e.
Obtain mixed liquor I (due to the volatilization of ethyl alcohol, ethyl alcohol is supplied in whipping process)；Triethanolamine, mixing are added into the mixed liquor I
Up to ethyl cellulose resin solution；The mixed liquor I is grouped as by the group of following mass percentage：Ethyl cellulose resin
20% and absolute ethyl alcohol 80%；The mass ratio of the triethanolamine and the mixed liquor I is 0.2%；
2) modified rosin resin solution is prepared：Modified rosin resin is dissolved in absolute ethyl alcohol, stir and evenly mix can (by
Ethyl alcohol is supplied in the volatilization of ethyl alcohol, whipping process)；The modified rosin resin solution by following mass percentage component
Composition：Modified rosin resin 30% and absolute ethyl alcohol 70%；
3) mill base is prepared：Ethyl cellulose resin solution and modified rosin resin solution are added into toner, stirs evenly
Up to mill base magma；The mill base magma is ground to get mill base, the grain size of solid particle in mill base<10μm；
4) by ethyl cellulose resin solution, waterborne polyurethane resin, modified rosin resin solution and absolute ethyl alcohol and stirring
Mixing, and dispersant is added, it stirs and evenly mixs up to mixed liquor II；
3) mill base is added into the mixture II, up to mixed liquor Ш after toning；
4) filling to mixed liquor Ш progress, it is filled with propellant after sealing, is finally packed.
Embodiment 2
The present embodiment provides a kind of automobile air brushing sprays, and it includes the components of following mass percentage：Ethyl cellulose
Plain resin solution 2%, waterborne polyurethane resin 8%, modified rosin resin solution 3%, mill base 3%, absolute ethyl alcohol 18%, dispersion
Agent 1% and propellant 65%；Ethyl cellulose resin is Ashland imported with original packaging, and dispersant is Bi Ke companies of Germany BYK-
104, propellant is dimethyl ether.
In addition, the present embodiment also provides the preparation method of the automobile air brushing spray comprising following steps：
1) ethyl cellulose resin solution is prepared：Ethyl cellulose resin is dissolved in absolute ethyl alcohol, is stirred and evenly mixed i.e.
Mixed liquor I (due to the volatilization of ethyl alcohol, ethyl alcohol is supplied in whipping process) is obtained, triethanolamine, mixing are added into the mixed liquor I
Up to ethyl cellulose resin solution；The mixed liquor I is grouped as by the group of following mass percentage：Ethyl cellulose resin
14% and absolute ethyl alcohol 86%；The mass ratio of the triethanolamine and the mixed liquor I is 0.2%；
2) modified rosin resin solution is prepared：Modified rosin resin is dissolved in absolute ethyl alcohol, stir and evenly mix can (by
Ethyl alcohol is supplied in the volatilization of ethyl alcohol, whipping process)；The modified rosin resin solution by following mass percentage component
Composition：Modified rosin resin 25% and absolute ethyl alcohol 75%；
3) mill base is prepared：Ethyl cellulose resin solution and modified rosin resin solution are added into toner, stirs evenly
Up to mill base magma；The mill base magma is ground to get mill base, the grain size of solid particle in mill base<10μm；
4) by ethyl cellulose resin solution, waterborne polyurethane resin, modified rosin resin solution and absolute ethyl alcohol and stirring
Mixing, and dispersant is added, it stirs and evenly mixs up to mixed liquor II；
3) mill base is added into the mixture II, up to mixed liquor Ш after toning；
4) filling to mixed liquor Ш progress, it is filled with propellant after sealing, is finally packed.
Embodiment 3
The present embodiment provides a kind of automobile air brushing sprays, and it includes the components of following mass percentage：Ethyl cellulose
Plain resin solution 5%, modified rosin resin solution 2.2%, mill base 5%, absolute ethyl alcohol 20%, divides waterborne polyurethane resin 7%
Powder 0.8% and propellant 60%；Ethyl cellulose resin is Ashland imported with original packaging, and dispersant is Bi Ke companies of Germany
BYK-2008, propellant are dimethyl ether.
In addition, the present embodiment also provides the preparation method of the automobile air brushing spray comprising following steps：
1) ethyl cellulose resin solution is prepared：Ethyl cellulose resin is dissolved in absolute ethyl alcohol, is stirred and evenly mixed i.e.
Mixed liquor I (due to the volatilization of ethyl alcohol, ethyl alcohol is supplied in whipping process) is obtained, triethanolamine, mixing are added into the mixed liquor I
Up to ethyl cellulose resin solution；The mixed liquor I is grouped as by the group of following mass percentage：Ethyl cellulose resin
25% and absolute ethyl alcohol 75%；The mass ratio of the triethanolamine and the mixed liquor I is 0.2%；
2) modified rosin resin solution is prepared：Modified rosin resin is dissolved in absolute ethyl alcohol, stir and evenly mix can (by
Ethyl alcohol is supplied in the volatilization of ethyl alcohol, whipping process)；The modified rosin resin solution by following mass percentage component
Composition：Modified rosin resin 36% and absolute ethyl alcohol 64%；
3) mill base is prepared：Ethyl cellulose resin solution and modified rosin resin solution are added into toner, stirs evenly
Up to mill base magma；The mill base magma is ground to get mill base, the grain size of solid particle in mill base<10μm；
4) by ethyl cellulose resin solution, waterborne polyurethane resin, modified rosin resin solution and absolute ethyl alcohol and stirring
Mixing, and dispersant is added, it stirs and evenly mixs up to mixed liquor II；
3) mill base is added into the mixture II, up to mixed liquor Ш after toning；
4) filling to mixed liquor Ш progress, it is filled with propellant after sealing, is finally packed.
Embodiment 4
The present embodiment provides a kind of automobile air brushing sprays, and it includes the components of following mass percentage：Ethyl cellulose
Plain resin solution 3%, waterborne polyurethane resin 5%, modified rosin resin solution 1.6%, mill base 4.4%, absolute ethyl alcohol 25%,
Dispersant 1% and propellant 60%；Ethyl cellulose resin is Ashland imported with original packaging, and dispersant is Bi Ke companies of Germany
BYK-104S, propellant are dimethyl ether.
In addition, the present embodiment also provides the preparation method of the automobile air brushing spray comprising following steps：
1) ethyl cellulose resin solution is prepared：Ethyl cellulose resin is dissolved in absolute ethyl alcohol, is stirred and evenly mixed i.e.
Mixed liquor I (due to the volatilization of ethyl alcohol, ethyl alcohol is supplied in whipping process) is obtained, triethanolamine, mixing are added into the mixed liquor I
Up to ethyl cellulose resin solution；The mixed liquor I is grouped as by the group of following mass percentage：Ethyl cellulose resin
20% and absolute ethyl alcohol 80%；The mass ratio of the triethanolamine and the mixed liquor I is 0.2%；
2) modified rosin resin solution is prepared：Modified rosin resin is dissolved in absolute ethyl alcohol, stir and evenly mix can (by
Ethyl alcohol is supplied in the volatilization of ethyl alcohol, whipping process)；The modified rosin resin solution by following mass percentage group
Point：Modified rosin resin 30% and absolute ethyl alcohol 70%；
3) mill base is prepared：Ethyl cellulose resin solution and modified rosin resin solution are added into toner, stirs evenly
Up to mill base magma；The mill base magma is ground to get mill base, the grain size of solid particle in mill base<10μm；
4) by ethyl cellulose resin solution, waterborne polyurethane resin, modified rosin resin solution and absolute ethyl alcohol and stirring
Mixing, and dispersant is added, it stirs and evenly mixs up to mixed liquor II；
3) mill base is added into the mixture II, up to mixed liquor Ш after toning；
4) filling to mixed liquor Ш progress, it is filled with propellant after sealing, is finally packed.
Embodiment 5
The present embodiment provides a kind of automobile air brushing sprays, and it includes the components of following mass percentage：Ethyl cellulose
Plain resin solution 2%, waterborne polyurethane resin 5%, modified rosin resin solution 1%, mill base 3%, absolute ethyl alcohol 18%, dispersion
Agent 1% and propellant 70%；Ethyl cellulose resin is Ashland imported with original packaging, and dispersant is Bi Ke companies of Germany BYK-
104S, propellant are dimethyl ether.
In addition, the present embodiment also provides the preparation method of the automobile air brushing spray comprising following steps：
1) ethyl cellulose resin solution is prepared：Ethyl cellulose resin is dissolved in absolute ethyl alcohol, is stirred and evenly mixed i.e.
Mixed liquor I (due to the volatilization of ethyl alcohol, ethyl alcohol is supplied in whipping process) is obtained, triethanolamine, mixing are added into the mixed liquor I
Up to ethyl cellulose resin solution；The mixed liquor I is grouped as by the group of following mass percentage：Ethyl cellulose resin
20% and absolute ethyl alcohol 80%；The mass ratio of the triethanolamine and the mixed liquor I is 0.2%；
2) modified rosin resin solution is prepared：Modified rosin resin is dissolved in absolute ethyl alcohol, stir and evenly mix can (by
Ethyl alcohol is supplied in the volatilization of ethyl alcohol, whipping process)；The modified rosin resin solution by following mass percentage group
Point：Modified rosin resin 30% and absolute ethyl alcohol 70%；
3) mill base is prepared：Ethyl cellulose resin solution and modified rosin resin solution are added into toner, stirs evenly
Up to mill base magma；The mill base magma is ground to get mill base, the grain size of solid particle in mill base<10μm；
4) by ethyl cellulose resin solution, waterborne polyurethane resin, modified rosin resin solution and absolute ethyl alcohol and stirring
Mixing, and dispersant is added, it stirs and evenly mixs up to mixed liquor II；
3) mill base is added into the mixture II, up to mixed liquor Ш after toning；
4) filling to mixed liquor Ш progress, it is filled with propellant after sealing, is finally packed.
Comparative example 1
The present embodiment provides a kind of automobile air brushing sprays, and it includes the components of following mass percentage：Aqueous poly- ammonia
Ester resin 12%, modified rosin resin solution 2.2%, mill base 5%, absolute ethyl alcohol 20%, dispersant 0.8% and propellant
60%；Ethyl cellulose resin is Ashland imported with original packaging, and dispersant is Bi Ke companies of Germany BYK-2008, propellant two
Methyl ether.
In addition, the preparation method of automobile air brushing spray described in this comparative example, can refer to Examples 1 to 5.
Performance measurement is carried out to the spray of Examples 1 to 3, comparative example 1 and market purchase, measurement result is as shown in table 1：
The spray of the present invention is environmentally friendly, will not damage vehicle body, and stable storing, drying time are short.
Table 1
Finally, it should be noted that above example to illustrate technical scheme of the present invention rather than to the present invention protect
The limitation of range, although being explained in detail to the present invention with reference to preferred embodiment, those skilled in the art should manage
Solution, can modify to technical scheme of the present invention or replace on an equal basis, without departing from technical solution of the present invention essence and
Range.
Claims (10)
1. a kind of automobile air brushing spray, which is characterized in that include the component of following mass percentage：Ethyl cellulose resin
Solution 2%~5%, waterborne polyurethane resin 5%~8%, modified rosin resin solution 1%~3%, mill base 3%~5%, nothing
Water-ethanol 18%~25%, dispersant 0.5%~1% and propellant 60%~70%；The ethyl cellulose resin solution and
The solvent of modified rosin resin solution is organic solvent.
2. automobile air brushing spray as described in claim 1, which is characterized in that include the component of following mass percentage：
Ethyl cellulose resin solution 3%, waterborne polyurethane resin 7%, modified rosin resin solution 2%, mill base 4%, absolute ethyl alcohol
18.5%, dispersant 0.5% and propellant 65%.
3. automobile air brushing spray as claimed in claim 1 or 2, which is characterized in that the ethyl cellulose resin solution and
The solvent of modified rosin resin solution is absolute ethyl alcohol, and the propellant is dimethyl ether.
4. automobile air brushing spray as claimed in claim 1 or 2, which is characterized in that the ethyl cellulose resin solution is
It is prepared by the following method：Ethyl cellulose resin is dissolved in absolute ethyl alcohol, mixed liquor I to obtain the final product is stirred and evenly mixed, to
Triethanolamine is added in the mixed liquor I, mixing is up to ethyl cellulose resin solution；The mixed liquor I is by following quality hundred
The group of point content is grouped as：Ethyl cellulose resin 14%~25% and absolute ethyl alcohol 75%~86%；The triethanolamine with
The mass ratio of the mixed liquor I is 0.2%.
5. automobile air brushing spray as claimed in claim 4, which is characterized in that the mixed liquor I is contained by following quality percentage
The group of amount is grouped as：Ethyl cellulose resin 20% and absolute ethyl alcohol 80%.
6. automobile air brushing spray as claimed in claim 1 or 2, which is characterized in that the modified rosin resin solution is logical
Following methods are crossed to be prepared：Modified rosin resin is dissolved in absolute ethyl alcohol, is stirred and evenly mixed molten up to modified rosin resin
Liquid；The modified rosin resin solution is grouped as by the group of following mass percentage：25%~36% He of modified rosin resin
Absolute ethyl alcohol 64%~75%.
7. automobile air brushing spray as claimed in claim 6, which is characterized in that the modified rosin resin solution is by following matter
The group of amount percentage composition is grouped as：Modified rosin resin 30% and absolute ethyl alcohol 70%.
8. automobile air brushing spray as claimed in claim 1 or 2, which is characterized in that the mill base carries out by the following method
It prepares：The ethyl cellulose resin solution and the modified rosin resin solution are added into toner, mixes uniformly up to mill base
Magma；The mill base magma is ground to get mill base.
9. automobile air brushing spray as claimed in claim 8, which is characterized in that the grain size of particle in the mill base<10μm.
10. a kind of preparation method of such as claim 1~9 any one of them automobile air brushing spray, which is characterized in that including
Following steps：
1) ethyl cellulose resin solution, modified rosin resin solution and mill base are prepared；
2) ethyl cellulose resin solution, waterborne polyurethane resin, modified rosin resin solution and absolute ethyl alcohol and stirring are mixed,
And dispersant is added, it stirs and evenly mixs up to mixed liquor II；
3) mill base is added into the mixed liquor II, up to mixed liquor Ш after toning；
4) filling to mixed liquor Ш progress, it is filled with propellant after sealing, is finally packed.