CN106833214A - A kind of environment protection oil paint and preparation method thereof - Google Patents
A kind of environment protection oil paint and preparation method thereof Download PDFInfo
- Publication number
- CN106833214A CN106833214A CN201710151402.5A CN201710151402A CN106833214A CN 106833214 A CN106833214 A CN 106833214A CN 201710151402 A CN201710151402 A CN 201710151402A CN 106833214 A CN106833214 A CN 106833214A
- Authority
- CN
- China
- Prior art keywords
- parts
- acid
- resin
- environment protection
- protection oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environment protection oil paint and preparation method thereof.The environment protection oil paint includes the component of following parts by weight：30 40 parts of plastic propene's acid resin, 5 10 parts of cellulose acetate, 35 parts of limonene, 35 parts of polyalcohol, 24 parts of barium chromate, 10 15 parts of polyacrylate, 20 30 parts of alcohol-soluble resin, 5 10 parts of toluene di-isocyanate(TDI), 46 parts of isopropyl titanate, 24 parts of triethanolamine, 13 parts of sodium carboxymethylcellulose, 13 parts of zinc naphthenate, 46 parts of mill base, 13 parts of the smooth hard acid of sorb, 24 parts of cellulose derivative, 13 parts of hydracrylic acid, 13 parts of titanium dioxide, 13 parts of phenylalanine, 24 parts of 5 10 parts of defoamer and dimethyl sulfoxide (DMSO).Harmful substance is free of in raw material prepared by present invention paint, the air pollution in conventional paint drying process can be avoided, use safety.
Description
Technical field
Present invention relates particularly to a kind of environment protection oil paint and preparation method thereof.
Background technology
Paint English name：paint or coating.Paint is that one kind can firmly be covered in body surface, plays protection, dress
The chemical mixture coating of decorations, mark and other specific uses.Chinese coating circle is more authoritative《Coating process》One book is this
Sample definition：" coating is a kind of material, and this material can be coated in object surface, form adhesion with different construction technologies
Firmly, with some strength, continuous solid film.The film common name film for so being formed, also known as paint film or coating." coating one
As by film forming matter, filler（Color stuffing）, solvent, four parts such as auxiliary agent composition.According to performance requirement, composition can slightly become sometimes
Change, such as varnish can be without solvent in not having color stuffing, powdery paints.
Paint is that one kind can firmly be covered in body surface, and the chemistry for playing protection, decoration, mark and other specific uses is mixed
Compound coating.It is thickness oil colour to paint, it is not dry in the case of it is inflammable, it is water insoluble, be slightly soluble in fat, dissolve in alcohol, aldehyde,
Ether, benzene, alkane, are soluble in gasoline, kerosene, diesel oil.Paint species is many currently on the market, but mainly contains toluene, also there is a small amount of
Benzene, after being all chemicals especially application to the very big paint at present of human body influence, can constantly volatile organic compound
And episome (TDI) (VOC).Not only to the Nature produce ozone pollution, but also can make human body cause headache, general paralysis,
The various diseases such as anaemia, cancer, carry out serious threat, but be a kind of essential material being not fee to human body health care belt.
Therefore, industry is badly in need of providing a kind of environmentally-friendly sanitary, uses the paint of safety.
The content of the invention
The invention aims to solve defect present in prior art, there is provided a kind of environmentally-friendly sanitary, use safety
Paint.
In order to achieve the above object, the invention provides a kind of environment protection oil paint, including following parts by weight component：Plasticity
Acrylic resin 30-40 parts, cellulose acetate 5-10 parts, limonene 3-5 parts, polyalcohol 3-5 parts, barium chromate 2-4 parts, polypropylene
Acid esters 10-15 parts, alcohol-soluble resin 20-30 parts, toluene di-isocyanate(TDI) 5-10 parts, isopropyl titanate 4-6 parts, triethanolamine 2-
4 parts, sodium carboxymethylcellulose 1-3 parts, zinc naphthenate 1-3 parts, mill base 4-6 parts, smooth hard acid 1-3 parts of sorb, cellulose derivative
2-4 parts, hydracrylic acid 1-3 parts, titanium dioxide 1-3 parts, phenylalanine 1-3 parts, defoamer 5-10 parts and dimethyl sulfoxide (DMSO) 2-4 parts.
The preferred ingredient weight proportion of environment protection oil paint of the present invention is：35 parts of plastic propene's acid resin, 7 parts of cellulose acetate,
4 parts of limonene, 4 parts of polyalcohol, 3 parts of barium chromate, 12 parts of polyacrylate, 25 parts of alcohol-soluble resin, toluene di-isocyanate(TDI) 7
Part, 5 parts of isopropyl titanate, 3 parts of triethanolamine, 2 parts of sodium carboxymethylcellulose, 2 parts of zinc naphthenate, 5 parts of mill base, the smooth hard acid of sorb
2 parts, 3 parts of cellulose derivative, 2 parts of hydracrylic acid, 2 parts of titanium dioxide, 2 parts of phenylalanine, 7 parts of defoamer and dimethyl sulfoxide (DMSO) 3
Part.
Wherein, polyalcohol uses propane diols；Alcohol-soluble resin uses rosin modified alkyd resin；Mill base uses resin color
Slurry；Cellulose derivative uses methylcellulose；Defoamer uses polypropylene glycerol aether.
Present invention also offers the preparation method of above-mentioned environment protection oil paint, it is characterised in that comprise the following steps：
（1）By plastic propene's acid resin, cellulose acetate, limonene, polyalcohol, barium chromate, polyacrylate, alcohol-soluble tree
After the mixing of fat, toluene di-isocyanate(TDI), isopropyl titanate, triethanolamine and sodium carboxymethylcellulose, 70 DEG C are heated to, stirring is straight
To being completely dissolved and be well mixed；
（2）By zinc naphthenate, mill base, the smooth hard acid of sorb, cellulose derivative, hydracrylic acid, titanium dioxide, phenylalanine, froth breaking
After agent and dimethyl sulfoxide (DMSO) mixing, it is heated to 100 DEG C and is stirred, to being completely dissolved and be well mixed；
（3）By step（1）And step（2）The two kinds of solution for obtaining are stirred at room temperature uniformly, and being subsequently adding in grinder is carried out
Grinding 40 minutes.
The present invention has advantages below compared to existing technology：Nuisance is not contained in raw material prepared by present invention paint
Matter, can avoid the air pollution in conventional paint drying process, using safety, to the basic non-hazardous of operating personnel, realize clear
Clean production.And obtained environment protection oil paint tinting strength, tinting power is high, strong covering power, have nontoxic fragrance, environmental protection can also be effectively deodorant.
Specific embodiment
With reference to specific embodiment, the present invention is described in detail.
Embodiment one：
A kind of environment protection oil paint, including following parts by weight composition：30 parts of plastic propene's acid resin, 5 parts of cellulose acetate, lemon
3 parts of alkene, 3 parts of propane diols, 2 parts of barium chromate, 10 parts of polyacrylate, 20 parts of rosin modified alkyd resin, toluene di-isocyanate(TDI) 5
Part, 4 parts of isopropyl titanate, 2 parts of triethanolamine, 1 part of sodium carboxymethylcellulose, 1 part of zinc naphthenate, 4 parts of resin mill base, sorb are smooth
1 part of hard acid, 2 parts of methyl cellulose derivatives, 1 part of hydracrylic acid, 1 part of titanium dioxide, 1 part of phenylalanine, polypropylene glycerol aether 5
2 parts of part and dimethyl sulfoxide (DMSO).
A kind of preparation method of environment protection oil paint, comprises the following steps：
1）By 30 parts of plastic propene's acid resin, 5 parts of cellulose acetate, 3 parts of limonene, 3 parts of propane diols, 2 parts of barium chromate, polypropylene
10 parts of acid esters, 20 parts of rosin modified alkyd resin, 5 parts of toluene di-isocyanate(TDI), 4 parts of isopropyl titanate, 2 parts of triethanolamine and carboxylic
1 part of sodium carboxymethylcellulose pyce is placed on a container for stirring, is heated to 70 DEG C, until being completely dissolved；
2）By 1 part of zinc naphthenate, 4 parts of resin mill base, 1 part of the smooth hard acid of sorb, 2 parts of methyl cellulose derivatives, hydracrylic acid 1
Part, 1 part of titanium dioxide, 1 part of phenylalanine, 5 parts of polypropylene glycerol aether and 2 parts of dimethyl sulfoxide (DMSO) are placed on another vessel in heating
It is stirred to 100 DEG C；
3）By step 1）With step 2）The two kinds of solution for obtaining are stirred at room temperature uniformly, are subsequently adding in grinder and are ground
40 minutes.
Embodiment two：
A kind of environment protection oil paint, including following parts by weight composition：40 parts of plastic propene's acid resin, 10 parts of cellulose acetate, lemon
5 parts of lemon alkene, 5 parts of propane diols, 4 parts of barium chromate, 15 parts of polyacrylate, 30 parts of rosin modified alkyd resin, toluene diisocynate
10 parts of ester, 6 parts of isopropyl titanate, 4 parts of triethanolamine, 3 parts of sodium carboxymethylcellulose, 3 parts of zinc naphthenate, 6 parts of resin mill base, mountain
3 parts of the smooth hard acid of pears, 4 parts of methyl cellulose derivatives, 3 parts of hydracrylic acid, 3 parts of titanium dioxide, phenylalanine-3,4-quinone part, polyoxypropylene are sweet
4 parts of 10 parts of oily ether and dimethyl sulfoxide (DMSO).
A kind of preparation method of environment protection oil paint, comprises the following steps：
1）By 40 parts of plastic propene's acid resin, 10 parts of cellulose acetate, 5 parts of limonene, 5 parts of propane diols, 4 parts of barium chromate, poly- third
15 parts of olefin(e) acid ester, 30 parts of rosin modified alkyd resin, 10 parts of toluene di-isocyanate(TDI), 6 parts of isopropyl titanate, 4 parts of triethanolamine
3 parts are placed on a container for stirring with sodium carboxymethylcellulose, 70 DEG C are heated to, until being completely dissolved；
2）By 3 parts of zinc naphthenate, 6 parts of resin mill base, 3 parts of the smooth hard acid of sorb, 4 parts of methyl cellulose derivatives, hydracrylic acid 3
4 parts of part, 3 parts of titanium dioxide, phenylalanine-3,4-quinone part, 10 parts of polypropylene glycerol aether and dimethyl sulfoxide (DMSO) add in being placed on another container
Heat is stirred to 100 DEG C；
3）By step 1）With step 2）The two kinds of solution for obtaining are stirred at room temperature uniformly, are subsequently adding in grinder and are ground
40 minutes.
Embodiment three：
A kind of environment protection oil paint, including following parts by weight composition：35 parts of plastic propene's acid resin, 7 parts of cellulose acetate, lemon
4 parts of alkene, 4 parts of propane diols, 3 parts of barium chromate, 12 parts of polyacrylate, 25 parts of rosin modified alkyd resin, toluene di-isocyanate(TDI) 7
Part, 5 parts of isopropyl titanate, 3 parts of triethanolamine, 2 parts of sodium carboxymethylcellulose, 2 parts of zinc naphthenate, 5 parts of resin mill base, sorb are smooth
2 parts of hard acid, 3 parts of methylcellulose, 2 parts of hydracrylic acid, 2 parts of titanium dioxide, 2 parts of phenylalanine, 7 parts of polypropylene glycerol aether and two
3 parts of methyl sulfoxide.
A kind of preparation method of environment protection oil paint, comprises the following steps：
1）By 35 parts of plastic propene's acid resin, 7 parts of cellulose acetate, 4 parts of limonene, 4 parts of propane diols, 3 parts of barium chromate, polypropylene
12 parts of acid esters, 25 parts of rosin modified alkyd resin, 7 parts of toluene di-isocyanate(TDI), 5 parts of isopropyl titanate, 3 parts of triethanolamine and carboxylic
2 parts of sodium carboxymethylcellulose pyce is placed on a container for stirring, is heated to 70 DEG C, until being completely dissolved；
2）By 2 parts of zinc naphthenate, 5 parts of resin mill base, 2 parts of the smooth hard acid of sorb, 3 parts of methylcellulose, 2 parts of hydracrylic acid, titanium white
3 parts of 2 parts of powder, 2 parts of phenylalanine, 7 parts of polypropylene glycerol aether and dimethyl sulfoxide (DMSO) are placed on another vessel in heating to 100 DEG C
It is stirred；
3）By step 1）With step 2）The two kinds of solution for obtaining are stirred at room temperature uniformly, are subsequently adding in grinder and are ground
40 minutes.
Under standard environment, environment protection oil paint obtained in various embodiments of the present invention is entered with existing paint as a control group
Row performance comparison detects that the former paint viscosity of the paint that the present invention is prepared is 100-200, and working viscosity is 50-65, surface drying time
≤ 1h, does solid work the time≤24h, content of volatile organic compound≤200g/L, covering power≤40 g/m2, thickness of dry film >=
50um, concrete outcome is as follows：
As can be seen from the above table, its tinting strength, tinting power of the environment protection oil paint of the application, covering power are all better than existing paint on the market, and its
Content of volatile organic compound is also significant lower, while also with nontoxic fragrance.
The present invention can avoid the air in conventional paint drying process dirty using harmful substance is not contained in raw material
Dye, using safety, to the basic non-hazardous of operating personnel, realizes clean manufacturing；Tinting strength, tinting power is high, strong covering power, have nontoxic fragrance
Smell, environmental protection can also be effectively deodorant.
The above, specific embodiment only of the invention, but protection scope of the present invention is not limited thereto, and it is any
The change or replacement expected without creative work, should all cover and be defined in the new protection domain of this practicality.
Claims (4)
1. a kind of environment protection oil paint, it is characterised in that the component including following parts by weight：30-40 parts of plastic propene's acid resin, vinegar
Acid cellulose 5-10 parts, limonene 3-5 parts, polyalcohol 3-5 parts, barium chromate 2-4 parts, polyacrylate 10-15 parts, alcohol-soluble tree
Fat 20-30 parts, toluene di-isocyanate(TDI) 5-10 parts, isopropyl titanate 4-6 parts, triethanolamine 2-4 parts, sodium carboxymethylcellulose 1-
3 parts, zinc naphthenate 1-3 parts, mill base 4-6 parts, smooth hard acid 1-3 parts of sorb, cellulose derivative 2-4 parts, hydracrylic acid 1-3 parts,
Titanium dioxide 1-3 parts, phenylalanine 1-3 parts, defoamer 5-10 parts and dimethyl sulfoxide (DMSO) 2-4 parts.
2. environment protection oil paint according to claim 1, it is characterised in that the component including following parts by weight：Plastic propene
35 parts of acid resin, 7 parts of cellulose acetate, 4 parts of limonene, 4 parts of polyalcohol, 3 parts of barium chromate, 12 parts of polyacrylate, alcohol-soluble
25 parts of resin, 7 parts of toluene di-isocyanate(TDI), 5 parts of isopropyl titanate, 3 parts of triethanolamine, 2 parts of sodium carboxymethylcellulose, aphthenic acids
2 parts of zinc, 5 parts of mill base, 2 parts of the smooth hard acid of sorb, 3 parts of cellulose derivative, 2 parts of hydracrylic acid, 2 parts of titanium dioxide, phenylalanine 2
3 parts of part, 7 parts of defoamer and dimethyl sulfoxide (DMSO).
3. environment protection oil paint according to claim 2, it is characterised in that：The polyalcohol uses propane diols；The alcohol-soluble
Resin uses rosin modified alkyd resin；The mill base uses resin mill base；The cellulose derivative uses methylcellulose；
The defoamer uses polypropylene glycerol aether.
4. the preparation method of any environment protection oil paint of claims 1 to 3, it is characterised in that comprise the following steps：
（1）By plastic propene's acid resin, cellulose acetate, limonene, polyalcohol, barium chromate, polyacrylate, alcohol-soluble tree
After the mixing of fat, toluene di-isocyanate(TDI), isopropyl titanate, triethanolamine and sodium carboxymethylcellulose, 70 DEG C are heated to, stirring is straight
To being completely dissolved and be well mixed；
（2）By zinc naphthenate, mill base, the smooth hard acid of sorb, cellulose derivative, hydracrylic acid, titanium dioxide, phenylalanine, froth breaking
After agent and dimethyl sulfoxide (DMSO) mixing, it is heated to 100 DEG C and is stirred, to being completely dissolved and be well mixed；
（3）By step（1）And step（2）The two kinds of solution for obtaining are stirred at room temperature uniformly, and being subsequently adding in grinder is carried out
Grinding 40 minutes.