CN106118229A - A kind of environment-friendly ink - Google Patents
A kind of environment-friendly ink Download PDFInfo
- Publication number
- CN106118229A CN106118229A CN201610755291.4A CN201610755291A CN106118229A CN 106118229 A CN106118229 A CN 106118229A CN 201610755291 A CN201610755291 A CN 201610755291A CN 106118229 A CN106118229 A CN 106118229A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- friendly ink
- kerosene
- pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environment-friendly ink, belong to technical field of environmental protection ink, technical points includes that this environment-friendly ink includes the raw material of following weight portion: rosin modified phenolic resin 30～40 parts；Alkyd resin 15～20 parts；Oligomerization oleum lini 5～10 parts；Banana aldehyde 1～5 parts；Colloid link stuff 2～8 parts；Kerosene 10～30 parts；Pigment 5～10 parts；Inserts 1～5 parts；Chitin 0.2～1 part；Other auxiliary agents 0.5～2 parts；Production technology of the present invention is simple, production cost is low, improve production efficiency, and benzene content is the one thousandth of common ink, and content of volatile organic compound is few, antibacterial and deodouring, has special Fructus Citri Limoniae, violet, Syringa oblata Lindl. mixed flavor, safety and environmental protection.
Description
Technical field
The present invention relates to a kind of ink, more specifically, particularly relate to a kind of environment-friendly ink.
Background technology
Ink is the important materials for packaging material printing, and it is by printing by pattern, literal table the most on the substrate
Ink includes main component and auxiliary element, and they mix equably and form a kind of viscosity colloidal fluid through repeat-rolling.
Printing-ink is by the dispersed pulpous state colloid mixed of colorant, link stuff and the material such as auxiliary agent and solvent.Solvent-borne type oil
The binder of ink is made up of hard resin and a large amount of volatile organic solvent.After hard resin is dissolved in solvent, colorant is equal
Even being dispersed in binder, ink is printed to printed medium, solvent rapid volatile dry conjunctiva.
Existing common ink typically contains the noxious substances such as benzene, health and environment is had destruction, not
Environmental protection, and the smell is awful.
Summary of the invention
Present invention aims to above-mentioned the deficiencies in the prior art, it is provided that a kind of environment-friendly ink.
The technical scheme is that and be achieved in that:
A kind of environment-friendly ink, described environment-friendly ink includes the raw material of following weight portion:
Rosin modified phenolic resin 30～40 parts；
Alkyd resin 15～20 parts；
Oligomerization oleum lini 5～10 parts；
Banana aldehyde 1～5 parts；
Colloid link stuff 2～8 parts；
Kerosene 10～30 parts；
Pigment 5～10 parts；
Inserts 1～5 parts；
Chitin 0.2～1 part；
Other auxiliary agents 0.5～2 parts；
Described banana aldehyde includes citral, ionoionone, terpineol, the wherein weight of citral, ionoionone, terpineol
Amount ratio is 3:2:1, and other auxiliary agents described include slip agent, desiccant, dispersant, anti skinning agent.
Preferably, described environment-friendly ink includes the raw material of following weight portion:
Rosin modified phenolic resin 32～38 parts；
Alkyd resin 16～19 parts；
Oligomerization oleum lini 6～9 parts；
Banana aldehyde 2～4 parts；
Colloid link stuff 4～6 parts；
Kerosene 15～25 parts；
Pigment 6～9 parts；
Inserts 2～4 parts；
Chitin 0.4～0.8 part；
Other auxiliary agents 0.8～1.2 parts.
Preferably, described environment-friendly ink includes the raw material of following weight portion:
Rosin modified phenolic resin 35 parts；
Alkyd resin 17 parts；
Oligomerization oleum lini 8 parts；
Banana aldehyde 3 parts；
Colloid link stuff 5 parts；
Kerosene 20 parts；
Pigment 7 parts；
Inserts 3 parts；
Chitin 0.6 part；
Other auxiliary agents 1.2 parts.
Further, described colloid link stuff uses isooctyl acid aluminum to be dissolved in Oleum Verniciae fordii and prepares, described isooctyl acid aluminum and Oleum Verniciae fordii
Weight ratio be 1:7.
Further, described pigment is the mixture of plant ash and white carbon black, and described plant ash is 1 with the weight ratio of white carbon black:
10。
Further, described inserts is barium sulfate, one or more in calcium carbonate, aluminium hydroxide.
Further, in other auxiliary agents described, slip agent, desiccant, dispersant, the weight ratio of anti skinning agent are: 2:0.5:
5:1.
The preparation method of a kind of environment-friendly ink, comprises the following steps:
According to formula quantity by the most standby for various measuring raw materials, by rosin modified phenolic resin, alkyd resin, oligomeric
Close oleum lini, banana aldehyde, colloid link stuff, pigment, account for kerosene weight 70% kerosene mixing put in dispersion cylinder, 300
～stir evenly under the rotating speed of 600rpm, be ground to fineness less than 55um, add inserts, chitin, residue kerosene and other
Auxiliary agent, disperses 15 minutes to pack to system bubble-free, discharging, i.e. obtain environment-friendly ink under 500～700rpm rotating speeds.
The invention provides a kind of environment-friendly ink, use rosin modified phenolic resin (bisphenol-A, tertiary butyl phenol, octyl phenol, nonyl
Base phenol, dodecyl fluosite) to improve set speed and the gloss of ink, it is favorably improved the set speed of ink,
Strengthen ink body bone, printing net-point is good, with aluminum become colloidality good；After alkyd resin film-forming, glossy and toughness, attachment
Power is strong, and has good wearability, weatherability and insulating properties, for improving the transfer performance of improving gloss ink；Oligomerization
Oleum lini can reduce ink viscosity, prevents stripping phenomenon, makes ink have operation adaptive；Banana aldehyde includes that weight ratio is
The citral of 3:2:1, ionoionone, terpineol, in special Fructus Citri Limoniae, violet, Syringa oblata Lindl. mixed flavor, dispel in ink
Bad smell, makes the spirit and QI cleaning that people hears；Using isooctyl acid aluminum to be dissolved in Oleum Verniciae fordii the colloid link stuff prepared makes ink in printing
The uniform thin layer of rear formation, is formed with the film layer of some strength after drying, and shields pigment so that it is be difficult to come off；
Pigment uses the mixture of plant ash and white carbon black, plant ash main component be potassium carbonate be alkalescence, can be used for adjusting ph value, have
The strongest effect killing pathogen and virus, prevents ink putrid and deteriorated, it is possible to decrease cost；In chitin rich in abundant ammonia
Base, its amino presents powerful effect adsorption-decomposition function organic harmful gas, decomposable asymmetric choice net formaldehyde, removal VOC, antibacterial and deodouring, sky
So nonhazardous, and thickening power can be played；The environment-friendly ink benzene content prepared is the one thousandth of common ink, and volatility is organic
Compounds content is few, antibacterial and deodouring, has special Fructus Citri Limoniae, violet, Syringa oblata Lindl. mixed flavor, and cost of manufacture is relatively low, safety
Environmental protection, processing technology is simple, also substantially increases production efficiency.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is described in further detail, but be not intended that the present invention any
Limit.
Embodiment 1
Present embodiments provide a kind of environment-friendly ink, including the raw material of following weight portion:
Rosin modified phenolic resin 30 parts；
Alkyd resin 15 parts；
Oligomerization oleum lini 5 parts；
Banana aldehyde 1 part；
Colloid link stuff 2 parts；
Kerosene 10 parts；
Pigment 5 parts；
Inserts 1 part；
Chitin 0.2 part；
Other auxiliary agents 0.5 part；
Described banana aldehyde includes citral, ionoionone, terpineol, the wherein weight of citral, ionoionone, terpineol
Amount ratio is 3:2:1, and other auxiliary agents described include slip agent, desiccant, dispersant, anti skinning agent, and described colloid link stuff uses
Isooctyl acid aluminum is dissolved in Oleum Verniciae fordii and preparing, and described isooctyl acid aluminum is 1:7 with the weight ratio of Oleum Verniciae fordii, and described pigment is plant ash and white carbon black
Mixture, the weight ratio of described plant ash and white carbon black is 1:10, and described inserts is barium sulfate, in calcium carbonate, aluminium hydroxide
One or more, in other auxiliary agents described, slip agent, desiccant, dispersant, the weight ratio of anti skinning agent are: 2:0.5:5:1.
The preparation method of a kind of environment-friendly ink, comprises the following steps:
According to formula quantity by the most standby for various measuring raw materials, by rosin modified phenolic resin, alkyd resin, oligomeric
Close oleum lini, banana aldehyde, colloid link stuff, pigment, account for kerosene weight 70% kerosene mixing put in dispersion cylinder,
Stir evenly under the rotating speed of 300rpm, be ground to fineness less than 55um, add inserts, chitin, residue kerosene and other help
Agent, disperses 15 minutes to pack to system bubble-free, discharging, i.e. obtain environment-friendly ink under 500rpm rotating speed.
Embodiment 2
Present embodiments provide a kind of environment-friendly ink, including the raw material of following weight portion:
Rosin modified phenolic resin 32 parts；
Alkyd resin 16 parts；
Oligomerization oleum lini 6 parts；
Banana aldehyde 2 parts；
Colloid link stuff 4 parts；
Kerosene 15 parts；
Pigment 6 parts；
Inserts 2 parts；
Chitin 0.4 part；
Other auxiliary agents 0.8 part；
Described banana aldehyde includes citral, ionoionone, terpineol, the wherein weight of citral, ionoionone, terpineol
Amount ratio is 3:2:1, and other auxiliary agents described include slip agent, desiccant, dispersant, anti skinning agent, and described colloid link stuff uses
Isooctyl acid aluminum is dissolved in Oleum Verniciae fordii and preparing, and described isooctyl acid aluminum is 1:7 with the weight ratio of Oleum Verniciae fordii, and described pigment is plant ash and white carbon black
Mixture, the weight ratio of described plant ash and white carbon black is 1:10, and described inserts is barium sulfate, in calcium carbonate, aluminium hydroxide
One or more, in other auxiliary agents described, slip agent, desiccant, dispersant, the weight ratio of anti skinning agent are: 2:0.5:5:1.
The preparation method of a kind of environment-friendly ink, comprises the following steps:
According to formula quantity by the most standby for various measuring raw materials, by rosin modified phenolic resin, alkyd resin, oligomeric
Close oleum lini, banana aldehyde, colloid link stuff, pigment, account for kerosene weight 70% kerosene mixing put in dispersion cylinder,
Stir evenly under the rotating speed of 400rpm, be ground to fineness less than 55um, add inserts, chitin, residue kerosene and other help
Agent, disperses 15 minutes to pack to system bubble-free, discharging, i.e. obtain environment-friendly ink under 600rpm rotating speed.
Embodiment 3
Present embodiments provide a kind of environment-friendly ink, including the raw material of following weight portion:
Rosin modified phenolic resin 35 parts；
Alkyd resin 17 parts；
Oligomerization oleum lini 8 parts；
Banana aldehyde 3 parts；
Colloid link stuff 5 parts；
Kerosene 20 parts；
Pigment 7 parts；
Inserts 3 parts；
Chitin 0.6 part；
Other auxiliary agents 1.2 parts；
Described banana aldehyde includes citral, ionoionone, terpineol, the wherein weight of citral, ionoionone, terpineol
Amount ratio is 3:2:1, and other auxiliary agents described include slip agent, desiccant, dispersant, anti skinning agent, and described colloid link stuff uses
Isooctyl acid aluminum is dissolved in Oleum Verniciae fordii and preparing, and described isooctyl acid aluminum is 1:7 with the weight ratio of Oleum Verniciae fordii, and described pigment is plant ash and white carbon black
Mixture, the weight ratio of described plant ash and white carbon black is 1:10, and described inserts is barium sulfate, in calcium carbonate, aluminium hydroxide
One or more, in other auxiliary agents described, slip agent, desiccant, dispersant, the weight ratio of anti skinning agent are: 2:0.5:5:1.
The preparation method of a kind of environment-friendly ink, comprises the following steps:
According to formula quantity by the most standby for various measuring raw materials, by rosin modified phenolic resin, alkyd resin, oligomeric
Close oleum lini, banana aldehyde, colloid link stuff, pigment, account for kerosene weight 70% kerosene mixing put in dispersion cylinder,
Stir evenly under the rotating speed of 500rpm, be ground to fineness less than 55um, add inserts, chitin, residue kerosene and other help
Agent, disperses 15 minutes to pack to system bubble-free, discharging, i.e. obtain environment-friendly ink under 650rpm rotating speed.
Embodiment 4
Present embodiments provide a kind of environment-friendly ink, including the raw material of following weight portion:
Rosin modified phenolic resin 38 parts；
Alkyd resin 19 parts；
Oligomerization oleum lini 9 parts；
Banana aldehyde 4 parts；
Colloid link stuff 6 parts；
Kerosene 25 parts；
Pigment 9 parts；
Inserts 4 parts；
Chitin 0.8 part；
Other auxiliary agents 1.2 parts；
Described banana aldehyde includes citral, ionoionone, terpineol, the wherein weight of citral, ionoionone, terpineol
Amount ratio is 3:2:1, and other auxiliary agents described include slip agent, desiccant, dispersant, anti skinning agent, and described colloid link stuff uses
Isooctyl acid aluminum is dissolved in Oleum Verniciae fordii and preparing, and described isooctyl acid aluminum is 1:7 with the weight ratio of Oleum Verniciae fordii, and described pigment is plant ash and white carbon black
Mixture, the weight ratio of described plant ash and white carbon black is 1:10, and described inserts is barium sulfate, in calcium carbonate, aluminium hydroxide
One or more, in other auxiliary agents described, slip agent, desiccant, dispersant, the weight ratio of anti skinning agent are: 2:0.5:5:1.
The preparation method of a kind of environment-friendly ink, comprises the following steps:
According to formula quantity by the most standby for various measuring raw materials, by rosin modified phenolic resin, alkyd resin, oligomeric
Close oleum lini, banana aldehyde, colloid link stuff, pigment, account for kerosene weight 70% kerosene mixing put in dispersion cylinder,
Stir evenly under the rotating speed of 550rpm, be ground to fineness less than 55um, add inserts, chitin, residue kerosene and other help
Agent, disperses 15 minutes to pack to system bubble-free, discharging, i.e. obtain environment-friendly ink under 600rpm rotating speed.
Embodiment 5
Present embodiments provide a kind of environment-friendly ink, including the raw material of following weight portion:
Rosin modified phenolic resin 40 parts；
Alkyd resin 20 parts；
Oligomerization oleum lini 10 parts；
Banana aldehyde 5 parts；
Colloid link stuff 8 parts；
Kerosene 30 parts；
Pigment 10 parts；
Inserts 5 parts；
Chitin 1 part；
Other auxiliary agents 2 parts；
Described banana aldehyde includes citral, ionoionone, terpineol, the wherein weight of citral, ionoionone, terpineol
Amount ratio is 3:2:1, and other auxiliary agents described include slip agent, desiccant, dispersant, anti skinning agent, and described colloid link stuff uses
Isooctyl acid aluminum is dissolved in Oleum Verniciae fordii and preparing, and described isooctyl acid aluminum is 1:7 with the weight ratio of Oleum Verniciae fordii, and described pigment is plant ash and white carbon black
Mixture, the weight ratio of described plant ash and white carbon black is 1:10, and described inserts is barium sulfate, in calcium carbonate, aluminium hydroxide
One or more, in other auxiliary agents described, slip agent, desiccant, dispersant, the weight ratio of anti skinning agent are: 2:0.5:5:1.
The preparation method of a kind of environment-friendly ink, comprises the following steps:
According to formula quantity by the most standby for various measuring raw materials, by rosin modified phenolic resin, alkyd resin, oligomeric
Close oleum lini, banana aldehyde, colloid link stuff, pigment, account for kerosene weight 70% kerosene mixing put in dispersion cylinder,
Stir evenly under the rotating speed of 600rpm, be ground to fineness less than 55um, add inserts, chitin, residue kerosene and other help
Agent, disperses 15 minutes to pack to system bubble-free, discharging, i.e. obtain environment-friendly ink under 700rpm rotating speed.
The above, the only present invention preferably detailed description of the invention, but protection scope of the present invention is not limited thereto,
Any those familiar with the art in the technical scope that the invention discloses, according to technical scheme and
Inventive concept equivalent or change in addition, all should contain within protection scope of the present invention.
Claims (8)
1. an environment-friendly ink, it is characterised in that described environment-friendly ink includes the raw material of following weight portion:
Rosin modified phenolic resin 30～40 parts；
Alkyd resin 15～20 parts；
Oligomerization oleum lini 5～10 parts；
Banana aldehyde 1～5 parts；
Colloid link stuff 2～8 parts；
Kerosene 10～30 parts；
Pigment 5～10 parts；
Inserts 1～5 parts；
Chitin 0.2～1 part；
Other auxiliary agents 0.5～2 parts；
Described banana aldehyde includes citral, ionoionone, terpineol, the wherein weight ratio of citral, ionoionone, terpineol
For 3:2:1, other auxiliary agents described include slip agent, desiccant, dispersant, anti skinning agent.
A kind of environment-friendly ink the most according to claim 1, it is characterised in that described environment-friendly ink includes following weight portion
Raw material:
Rosin modified phenolic resin 32～38 parts；
Alkyd resin 16～19 parts；
Oligomerization oleum lini 6～9 parts；
Banana aldehyde 2～4 parts；
Colloid link stuff 4～6 parts；
Kerosene 15～25 parts；
Pigment 6～9 parts；
Inserts 2～4 parts；
Chitin 0.4～0.8 part；
Other auxiliary agents 0.8～1.2 parts.
A kind of environment-friendly ink the most according to claim 1, it is characterised in that described environment-friendly ink includes following weight portion
Raw material:
Rosin modified phenolic resin 35 parts；
Alkyd resin 17 parts；
Oligomerization oleum lini 8 parts；
Banana aldehyde 3 parts；
Colloid link stuff 5 parts；
Kerosene 20 parts；
Pigment 7 parts；
Inserts 3 parts；
Chitin 0.6 part；
Other auxiliary agents 1.2 parts.
4. according to a kind of environment-friendly ink described in claim 1 or 2 or 3, it is characterised in that described colloid link stuff uses different pungent
Acid aluminum is dissolved in Oleum Verniciae fordii and preparing, and described isooctyl acid aluminum is 1:7 with the weight ratio of Oleum Verniciae fordii.
5. according to a kind of environment-friendly ink described in claim 1 or 2 or 3, it is characterised in that described pigment is plant ash and white carbon black
Mixture, the weight ratio of described plant ash and white carbon black is 1:10.
6. according to a kind of environment-friendly ink described in claim 1 or 2 or 3, it is characterised in that described inserts is barium sulfate, carbon
One or more in acid calcium, aluminium hydroxide.
7. according to a kind of environment-friendly ink described in claim 1 or 2 or 3, it is characterised in that slip agent in other auxiliary agents described,
Desiccant, dispersant, the weight ratio of anti skinning agent be: 2:0.5:5:1.
8. the preparation method of a kind of environment-friendly ink described in any one of claim 1～7, it is characterised in that comprise the following steps:
According to formula quantity by the most standby for various measuring raw materials, by rosin modified phenolic resin, alkyd resin, oligomerization Asia
Oleum Sesami, banana aldehyde, colloid link stuff, pigment, the kerosene mixing that accounts for kerosene weight 70% are put in dispersion cylinder, 300～
Stir evenly under the rotating speed of 600rpm, be ground to fineness less than 55um, add inserts, chitin, residue kerosene and other help
Agent, disperses 15 minutes to pack to system bubble-free, discharging, i.e. obtain environment-friendly ink under 500～700rpm rotating speeds.