CN105440885A - Board coating paint for strong lights and preparation method thereof - Google Patents
Board coating paint for strong lights and preparation method thereof Download PDFInfo
- Publication number
- CN105440885A CN105440885A CN201510925150.8A CN201510925150A CN105440885A CN 105440885 A CN105440885 A CN 105440885A CN 201510925150 A CN201510925150 A CN 201510925150A CN 105440885 A CN105440885 A CN 105440885A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- paint
- add
- hour
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses board coating paint for strong lights and a preparation method thereof. The board coating paint comprises 60-65 parts of natural plant oleoresin, 10-15 parts of natural plant oil-based color paste, 1-2 parts of a dispersing aid, 1-2 parts of an antifoaming agent, 2-3 parts of a diluent, 2-3 parts of herba schizonepetae, 2-3 parts of fried balloonflower root, 2-3 parts of steamed radix stemonae, 2-3 parts of steamed willowleaf swallowwort rhizome, 2-3 parts of steamed radix asteris, 2-3 parts of pear peel, 3-5 parts of fried licorice root, 4-5 scented tea particles, 100-150 parts of modified epoxy resin, 1-3 parts of KH-560, 6-9 parts of rutile type titanium dioxide, 1-5 parts of fumed silica, 120-150 parts of polyethylene polyamine, 5-10 parts of bismaleimide, 3-5 parts of tertiary amine, 90-99 parts of polythioether rubber and 12-15 parts of TED-85 epoxy resin. The drugs are used, ground and mixed and the organic compounds and episomes released through the paint are diluted so that the damage to the air and human body is reduced. Through mixing of the natural plant paint and a gummy liquid, mixing uniformity is guaranteed, paint volatilization is reduced and a protection layer is formed so that goo paint preservation effects are obtained.
Description
Technical field:
The present invention relates to a kind of coating, be specifically related to for plank japanning under high light and preparation method thereof.
Background technology:
Paint is that one firmly can cover body surface, plays protection, decoration, mark and the chemical mixture coating of other special purposes.China's coating circle more authoritative " coating process " book is definition like this: " coating is a kind of material, and this material can be coated in article surface by different construction technologies, forms adhere well, has some strength, continuous print solid film.The film common name film of such formation, also known as paint film or coating."
Coating is generally made up of four parts such as filmogen, filler (color stuffing), solvent, auxiliary agents.According to performance requriements sometimes composition can slightly change, as varnish does not have can not have solvent in color stuffing, powder coating.
Belong to organic chemical industry's macromolecular material, the film formed belongs to macromolecular compound type.The classification of the Chemicals of passing through according to the modern times, coating belongs to fine chemical product.Modern coating is progressively becoming the polyfunctional engineering materials of a class, is an important industry in chemical industry.
Existing coating mostly is chemical coating, continuous volatile organic compound and episome in the process of smearing, and not only produces ozone pollution to air, people also can be made to produce headache, general paralysis, the harm such as anaemia.
Summary of the invention:
Technical problem to be solved by this invention is the defect overcoming prior art, provides a kind of for plank japanning under high light and preparation method thereof.
Technical problem to be solved by this invention realizes by the following technical solutions.
For the plank japanning under high light, it is characterized in that: comprise natural phant oiliness resin 60-65 part, natural phant oiliness mill base 10-15 part, dispersing auxiliary 1-2 part, defoamer 1-2 part, thinner 2-3 part, schizonepeta 2-3 part, fry balloonflower root 2-3 part, steam tuber of stemona 2-3 part, steam Cynanchum glaucescens 2-3 part, steam aster 2-3 part, pears skin 2-3 part, fry Radix Glycyrrhizae 3-5 part, jasmine tea 4-5 grain, modified epoxy: 100-150 part, KH-560:1-3 part, Rutile type Titanium Dioxide: 6-9 part, aerosil: 1-5 part, polyethylene polyamine: 120-150 part, bismaleimides: 5-10 part, tertiary amine: 3-5 part, polythioether rubber: 90-99 part, TED-85 epoxy resin: 12-15 part.
For the plank japanning preparation method under high light, it is characterized in that: specifically comprise the following steps:
Add in reactor by natural oil resin, under the effect of orgnometallic catalyst, heating and controlling crosslinking temperature is 110 DEG C-130 DEG C, and pressure is 0.2MPa-0.25MPa, stirring velocity is 30-50 rev/min, and mixing 30-60 minute, to color even, transparent, viscosity obviously increases, then lowers the temperature;
Add dispersing auxiliary and natural phant oiliness mill base is uniformly mixed, obtain mixture;
By the schizonepeta in constitutive material, fry balloonflower root, the steaming tuber of stemona, steaming Cynanchum glaucescens, steaming aster, pears skin and fry Radix Glycyrrhizae, put into matrass, add the clear water of 5 times, boiling, to the water evaporate to dryness in matrass, collect water vapour, water vapour liquefies again; Jasmine tea is put into boiling water to soak, the water yield is 300ml simultaneously, and soak 5-8 minute, filtered water, obtains jasmine tea water; Again the water vapour collected is mixed with jasmine tea water;
Pour into after mixing in mixture, leave standstill 2 hours, heat 1 hour for 60-70 DEG C, cool 1 hour, heat 20 minutes for 66-72 DEG C, then leave standstill 1 hour, add thinner, stand-by;
Modified modified epoxy resin, KH-560, Rutile type Titanium Dioxide and aerosil are added in mixing machine, is uniformly mixed and obtains component A;
In 150 DEG C of reactions 1 hour after polyethylene polyamine, bismaleimides and tertiary amine being mixed, obtain B component;
React after polythioether rubber and the mixing of TED-85 epoxy resin 1 hour in 180 DEG C, obtain component C;
3 components press 3:2.6:2.2 preparation, add 1-5 part promotor in process for preparation; Mix 20 minutes with 90 DEG C, add defoamer, obtain required paint.
Beneficial effect of the present invention is: natural phant oiliness resin reduces micromolecular content after crosslinking Treatment, improves macromolecular content, and water tolerance and thermotolerance are all applauded; Add medicine ground and mixed simultaneously; the organic compound of dilution paint release and episome; reduce the harm to air and human body; colloidal liquid mixing is added in crude vegetal paint; while guarantee mixes; for the volatilization reducing paint strengthens layer protecting film, make paint preservation effect better, the time is longer.
Embodiment:
The technique means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with specific embodiment, setting forth the present invention further.
Specific embodiment 1: for the plank japanning under high light, comprise natural phant oiliness resin 60 parts, natural phant oiliness mill base 10 parts, dispersing auxiliary 1 part, defoamer 1 part, thinner 2 parts, schizonepeta 2 parts, fry balloonflower root 2 parts, steam the tuber of stemona 2 parts, steam Cynanchum glaucescens 2 parts, steam aster 2 parts, pears skin 2 parts, fry 3 parts, Radix Glycyrrhizae, jasmine tea 4, modified epoxy: 100 parts, KH-560:1 part, Rutile type Titanium Dioxide: 6 parts, aerosil: 1 part, polyethylene polyamine: 120 parts, bismaleimides: 5 parts, tertiary amine: 3 parts, polythioether rubber: 90 parts, TED-85 epoxy resin: 12 parts.
Specific embodiment 2: for the plank japanning under high light, comprise natural phant oiliness resin 65 parts, natural phant oiliness mill base 15 parts, dispersing auxiliary 2 parts, defoamer 2 parts, thinner 3 parts, schizonepeta 3 parts, fry balloonflower root 3 parts, steam the tuber of stemona 3 parts, steam Cynanchum glaucescens 3 parts, steam aster 3 parts, pears skin 3 parts, fry 5 parts, Radix Glycyrrhizae, jasmine tea 5, modified epoxy: 150 parts, KH-560:3 part, Rutile type Titanium Dioxide: 9 parts, aerosil: 5 parts, polyethylene polyamine: 150 parts, bismaleimides: 10 parts, tertiary amine: 5 parts, polythioether rubber: 99 parts, TED-85 epoxy resin: 15 parts.
For the plank japanning preparation method under high light, specifically comprise the following steps:
Add in reactor by natural oil resin, under the effect of orgnometallic catalyst, heating and controlling crosslinking temperature is 110 DEG C-130 DEG C, and pressure is 0.2MPa-0.25MPa, stirring velocity is 30-50 rev/min, and mixing 30-60 minute, to color even, transparent, viscosity obviously increases, then lowers the temperature;
Add dispersing auxiliary and natural phant oiliness mill base is uniformly mixed, obtain mixture;
By the schizonepeta in constitutive material, fry balloonflower root, the steaming tuber of stemona, steaming Cynanchum glaucescens, steaming aster, pears skin and fry Radix Glycyrrhizae, put into matrass, add the clear water of 5 times, boiling, to the water evaporate to dryness in matrass, collect water vapour, water vapour liquefies again; Jasmine tea is put into boiling water to soak, the water yield is 300ml simultaneously, and soak 5-8 minute, filtered water, obtains jasmine tea water; Again the water vapour collected is mixed with jasmine tea water;
Pour into after mixing in mixture, leave standstill 2 hours, heat 1 hour for 60-70 DEG C, cool 1 hour, heat 20 minutes for 66-72 DEG C, then leave standstill 1 hour, add thinner, stand-by;
Modified modified epoxy resin, KH-560, Rutile type Titanium Dioxide and aerosil are added in mixing machine, is uniformly mixed and obtains component A;
In 150 DEG C of reactions 1 hour after polyethylene polyamine, bismaleimides and tertiary amine being mixed, obtain B component;
React after polythioether rubber and the mixing of TED-85 epoxy resin 1 hour in 180 DEG C, obtain component C;
3 components press 3:2.6:2.2 preparation, add 1-5 part promotor in process for preparation; Mix 20 minutes with 90 DEG C, add defoamer, obtain required paint.
More than show and describe ultimate principle of the present invention, principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (2)
1. for the plank japanning under high light, it is characterized in that: comprise natural phant oiliness resin 60-65 part, natural phant oiliness mill base 10-15 part, dispersing auxiliary 1-2 part, defoamer 1-2 part, thinner 2-3 part, schizonepeta 2-3 part, fry balloonflower root 2-3 part, steam tuber of stemona 2-3 part, steam Cynanchum glaucescens 2-3 part, steam aster 2-3 part, pears skin 2-3 part, fry Radix Glycyrrhizae 3-5 part, jasmine tea 4-5 grain, modified epoxy: 100-150 part, KH-560:1-3 part, Rutile type Titanium Dioxide: 6-9 part, aerosil: 1-5 part, polyethylene polyamine: 120-150 part, bismaleimides: 5-10 part, tertiary amine: 3-5 part, polythioether rubber: 90-99 part, TED-85 epoxy resin: 12-15 part.
2. according to claim 1, for the plank japanning under high light, it is characterized in that: specifically comprise the following steps:
Add in reactor by natural oil resin, under the effect of orgnometallic catalyst, heating and controlling crosslinking temperature is 110 DEG C-130 DEG C, and pressure is 0.2MPa-0.25MPa, stirring velocity is 30-50 rev/min, and mixing 30-60 minute, to color even, transparent, viscosity obviously increases, then lowers the temperature;
Add dispersing auxiliary and natural phant oiliness mill base is uniformly mixed, obtain mixture;
By the schizonepeta in constitutive material, fry balloonflower root, the steaming tuber of stemona, steaming Cynanchum glaucescens, steaming aster, pears skin and fry Radix Glycyrrhizae, put into matrass, add the clear water of 5 times, boiling, to the water evaporate to dryness in matrass, collect water vapour, water vapour liquefies again; Jasmine tea is put into boiling water to soak, the water yield is 300ml simultaneously, and soak 5-8 minute, filtered water, obtains jasmine tea water; Again the water vapour collected is mixed with jasmine tea water;
Pour into after mixing in mixture, leave standstill 2 hours, heat 1 hour for 60-70 DEG C, cool 1 hour, heat 20 minutes for 66-72 DEG C, then leave standstill 1 hour, add thinner, stand-by;
Modified modified epoxy resin, KH-560, Rutile type Titanium Dioxide and aerosil are added in mixing machine, is uniformly mixed and obtains component A;
In 150 DEG C of reactions 1 hour after polyethylene polyamine, bismaleimides and tertiary amine being mixed, obtain B component;
React after polythioether rubber and the mixing of TED-85 epoxy resin 1 hour in 180 DEG C, obtain component C;
3 components press 3:2.6:2.2 preparation, add 1-5 part promotor in process for preparation; Mix 20 minutes with 90 DEG C, add defoamer, obtain required paint.