CN108455857A - 一种卫生陶瓷洁具柔光温润釉及其制备工艺 - Google Patents
一种卫生陶瓷洁具柔光温润釉及其制备工艺 Download PDFInfo
- Publication number
- CN108455857A CN108455857A CN201810053237.4A CN201810053237A CN108455857A CN 108455857 A CN108455857 A CN 108455857A CN 201810053237 A CN201810053237 A CN 201810053237A CN 108455857 A CN108455857 A CN 108455857A
- Authority
- CN
- China
- Prior art keywords
- glaze
- gentle
- sheen
- ceramic ware
- sanitary ceramic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种卫生陶瓷洁具柔光温润釉及其制备工艺。本发明涉及一种卫生洁具用柔光温润釉及其制备方法,所述柔光温润釉,其特征在于配方还包含有可产生钡、锶长石微晶结构的成分;组成配方按重量百分含量计为:SiO245.29~54.42%、Al2O313.01~22.88%、CaO 7.93~11.04%、MgO 0.12~3.98%、K2O 1.26~5.50%、Na2O 0.72~3.83%、ZrO20.05~10.50%、B2O30.56~1.89%、ZnO 2.76~8.95%、BaO 4.39~12.98%,SrO 0~5.35%,釉料经称量配料、球磨、除铁、陈腐、喷在卫生洁具厂常规组分的坯上,厚度为1mm左右,然后进行烧成步骤,将施釉的卫生洁具坯体放入隧道窑内,用常规明火焰1220~1280℃烧成,烧成后釉面具有观感柔和,触感细腻的效果。
Description
技术领域
本发明涉及一种卫生陶瓷洁具柔光温润釉及其制备方法,属于卫生陶瓷制备技术领域。所述柔光温润釉,其特征在于配方还包含有烧成时可产生长石微晶结构的材料;所述釉料具体涉及具有观感柔和,触感细腻、温润性能的卫生洁具用柔光温润釉及其制备工艺。
背景技术
根据人们的生活水平不断提高,卫生陶瓷洁具的应用场合越来越广泛应,使用量越来越多。同时对卫生陶瓷洁具釉面有了更高的装饰要求,对于使用价值及观赏价值的要求越来越高。目前市场上卫生陶瓷洁具有光泽的白色乳浊釉视觉、触觉效果单一,因此开发不同风格的卫生陶瓷洁具产品,是研发专业人员的目标之一。
低光泽度哑光釉料在建筑陶瓷砖生产中已经有所应用,但在卫生陶瓷洁具生产过程中,由于其特殊的造型结构及苛刻的烧成制度,较高烧成温度、较高烧成周期,造成颜色失真、釉面不平整等问题。并且现在市场卫生陶瓷洁具的质感冰冷坚硬,不够温馨,本发明通过烧成过程产生的非常细小粒度的晶体表面细腻、无强烈反光,给人一种柔和、安静的视觉感受和温润触觉感受。
发明内容
本发明克服了现有技术中的缺点,提供了一种卫生陶瓷洁具柔光温润釉及其制备工艺,具有烧成温度较低、烧成范围较宽、形成无光釉及微晶使白度较高、热膨胀系数稍小使机械性能更高的特点,而且可获得呈现出柔和丝状或绒状光泽具护目效果、细腻、温润感的卫生陶瓷洁具釉面。
为了解决上述技术问题,本发明是通过以下技术方案实现的:
一种卫生陶瓷洁具柔光温润釉,成分包括:SiO2 45.29~54.42%、Al2O3 13.01~22.88%、CaO 7.93~11.04%、MgO 0.12~3.98%、K2O 1.26~5.50%、Na2O 0.72~3.83%、ZrO2 0.05~10.50%、B2O3 0.56~1.89%、ZnO 2.76~8.95%、BaO 4.39~12.98%,SrO 0~5.35%。
其原料包括:粘土、长石、石英、滑石、白云石、石灰石、含硼熔块、硅酸锆、氧化锌、氧化铝、碳酸钡、碳酸锶,以及釉料性质调节剂;
一种卫生陶瓷洁具柔光温润釉的制备工艺,包括以下步骤:
(1)按上述化学组成范围称取:粘土、长石、石英、滑石、白云石、石灰石、硅酸锆、氧化锌、氧化铝、碳酸钡和碳酸锶,含硼熔块1-10%及釉浆性能调节剂;
(2)将上述各原料按配比加入球磨机中,并加入上述各原料的总量的30-45%的水进行球磨,球磨后得到釉浆,要求过万孔筛余1%以下,充分球磨后得到柔光温润釉浆;
(3)将该釉浆喷涂在卫生陶瓷洁具日常生产的半成品坯体上,施釉层总厚度1mm左右;在隧道窑中1220~1280℃下烧成。
所述硼砂、氧化锌、氧化铝、碳酸钡、碳酸锶、羧甲基纤维素、三聚磷酸钠、聚乙烯醇为化工厂经过加工处理的工业纯原料。
釉浆性能调节剂为占重量总量低于1%的羧甲基纤维素、三聚磷酸钠或聚乙烯醇。
与现有技术相比,本发明的有益效果是:
本发明对配方组成微调变化,烧制得的釉面具有传统釉砖同样的强度、耐磨度、抗老化、使用寿命长的性能,釉面平整、细腻光滑无针孔;具有丝绢般或绒状光泽、釉面光泽度与现有产品比较更低,为3-5°,给人一种柔和、安静、舒服的护目感受;摸起来手感细嫩柔软,有温暖感的卫生陶瓷洁具柔光温润釉面。
本发明原料来源广泛,成本低廉、卫生洁具陶瓷厂不需对设备进行更新改造,易扩大生产,具有实际应用价值。
具体实施方式
以下对本发明的优选实施例进行说明,应当理解,此处所描述的优选实施例仅用于说明和解释本发明,并不用于限定本发明。
实施例1
本发明所述一种卫生陶瓷洁具柔光温润釉,釉原料组成配比,釉的组分包括:SiO246.39%、Al2O3 21.28%、CaO 8.03%、MgO 2.14%、K2O 4.52%、Na2O 1.62%、ZrO2 6.36%、B2O3 1.57%、ZnO 3.86%、BaO 5.44%,SrO 2.68%、Fe2O3 原料带入的杂质。
卫生陶瓷洁具柔光温润釉制备步骤如下:
(1)按上述化学组成范围称取目前卫生陶瓷洁具厂采用的通用无机原料:粘土、长石、石英、滑石、白云石、石灰石、硅酸锆、氧化锌、氧化铝、碳酸钡、碳酸锶等,含硼熔块3%及釉浆性能调节剂,将上述各原料按配比加入球磨机中,并加入上述各原料的总量的42%的水进行球磨,球磨后得到釉浆,要求过万孔筛余2%以下,充分球磨后得到柔光温润釉浆。
(2)将釉浆喷涂在卫生陶瓷洁具日常生产的半成品坯体上,施釉层总厚度1mm左右;在隧道窑中1250℃下烧成,可获得呈现出柔和丝状或绒状光泽具护目效果、细腻、温润感的卫生陶瓷洁具釉面,采用国家标准检测光泽度5°。
实施例2
本发明所述一种卫生陶瓷洁具柔光温润釉,釉原料组成配比,釉的组分包括:SiO254.02%、Al2O3 17.56%、CaO 10.12%、MgO 3.69%、K2O 5.34%、Na2O 3.69%、ZrO29.44%、B2O3 0.94%、ZnO 8.63%、BaO 12.15%,SrO 0%、Fe2O3 为原料带入的杂质成分。
卫生陶瓷洁具柔光温润釉制备步骤如下:
(1)按上述化学组成范围称取目前卫生陶瓷洁具厂采用的通用无机原料:粘土、长石、石英、滑石、白云石、石灰石、硅酸锆、氧化锌、氧化铝、碳酸钡、碳酸锶等,含硼熔块8%及釉浆性能调节剂,将上述各原料按配比加入球磨机中,并加入上述各原料的总量的40%的水进行球磨,球磨后得到釉浆,要求过万孔筛余3%以下,充分球磨后得到柔光温润釉浆。
(2)将釉浆喷涂在卫生陶瓷洁具日常生产的半成品坯体上,施釉层总厚度1mm左右;在隧道窑中1280℃下烧成,可获得呈现出柔和丝状或绒状光泽具护目效果、细腻、温润感的卫生陶瓷洁具釉面,采用国家标准检测光泽度7°。
实施例3
本发明所述一种卫生陶瓷洁具柔光温润釉,釉原料组成配比,釉的组分包括:SiO250.34%、Al2O3 15.34%、CaO 10.63%、MgO 0.86%、K2O 2.02%、Na2O 0.98%、ZrO25.25%、B2O3 1.62%、ZnO5.12%、BaO 7.43%,SrO 4.45%、Fe2O3 原料带入的杂质。
卫生陶瓷洁具柔光温润釉制备步骤如下:
(1)按上述化学组成范围称取目前卫生陶瓷洁具厂采用的通用无机原料:粘土、长石、石英、滑石、白云石、石灰石、硅酸锆、氧化锌、氧化铝、碳酸钡、碳酸锶等,含硼熔块8%及釉浆性能调节剂,将上述各原料按配比加入球磨机中,并加入上述各原料的总量的35%的水进行球磨,球磨后得到釉浆,要求过万孔筛余5%以下,充分球磨后得到柔光温润釉浆。
(2)将釉浆喷涂在卫生陶瓷洁具日常生产的半成品坯体上,施釉层总厚度1mm左右;在隧道窑中1220℃下烧成,可获得呈现出柔和丝状或绒状光泽具护目效果、细腻、温润感的卫生陶瓷洁具釉面,采用国家标准检测光泽度3°。
本发明基本采用通用传统陶瓷原料,但是特别的在于锶元素部分替代钡元素。钡、锶同钙、镁一起组成碱土金属族中的主要常用元素(铍因为本身毒,且量小价高而不予采用)。氧化锶、氧化钡均是良好的助熔剂,与氧化钙、氧化镁不同的是,它们的助熔范围较宽。一般来说,从900℃起,氧化钡、氧化锶就可以发挥助熔作用,而对于加入了锶元素来说,加热下形成的偏硅酸锶的熔点比偏硅酸钡的熔点低,因此可以预期,锶元素的助熔效果应该高于钡元素,故可以降低烧温度,降低燃料成本。氧化锶、氧化钡有利于降低釉料的粘度。而且,它们与氧化钙、氧化镁相比,降低粘度的温度范围较宽,而且随着温度的变化,降低粘度大小的变化也较小。这也表明,烧成范围较宽。氧化钡则对热膨胀系数增加的作用要稍大一些,而氧化锶稍小一些,故釉砖有较高的耐磨性与坚韧性。氧化钡、氧化锶作为较重的元素可以增加釉料及微晶玻璃的玻璃相的折光率,氧化钡比氧化锶的作用更为明显提高光泽度、故加入锶部分替代钡可以降低釉的光泽度,更具哑光效果、更具卫生洁具所需的遮盖效果。在无光釉及微晶玻璃的配方组成中,有BaO-Al2O3-SiO2和SrO-Al2O3-SiO2体系的特征配方种类,这种类别的无光釉及微晶玻璃的特征析晶相分别为钡长石和锶长石。
与CaO-Al2O3-SiO2体系的无光釉及微晶玻璃相比较,添加SrO替代部分BaO,具有烧成温度较低、降低燃料消耗;烧成范围较宽、烧成更易控制;更易形成哑光釉微晶使光泽度低,更柔和护目、白度较高;热膨胀系数稍小使耐磨性与坚韧性更高、适应快烧的特点。
最后应说明的是:以上仅为本发明的优选实施例而已,并不用于限制本发明,尽管参照实施例对本发明进行了详细的说明,对于本领域的技术人员来说,其依然可以对前述各实施例所记载的技术方案进行修改,或者对其中部分技术特征进行等同替换,但是凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (6)
1.一种卫生陶瓷洁具柔光温润釉,其特征在于,按照重量比,成分包括:SiO2 45.29~54.42%、Al2O3 13.01~22.88%、CaO 7.93~11.04%、MgO 0.12~3.98%、K2O 1.26~5.50%、Na2O 0.72~3.83%、ZrO2 0.05~10.50%、B2O3 0.56~1.89%、ZnO 2.76~8.95%、BaO 4.39~12.98%,SrO 0~5.35%。
2.根据权利要求1所述一种卫生陶瓷洁具柔光温润釉,其特征在于,其原料包括:粘土、长石、石英、滑石、白云石、石灰石、硅酸锆、氧化锌、氧化铝、碳酸钡、碳酸锶,含硼熔块以及釉料性质调节剂。
3.根据权利要求1或2所述一种卫生陶瓷洁具柔光温润釉的制备工艺,其特征在于,包括以下步骤:
1)按上述化学组成范围称取:粘土、长石、石英、滑石、白云石、石灰石、硅酸锆、氧化锌、氧化铝、碳酸钡和碳酸锶,含硼熔块1-10%及釉浆性能调节剂;
2)将上述各原料按配比加入球磨机中,并加入上述各原料的总量的30-45%的水进行球磨,球磨后得到釉浆,要求过万孔筛余1~5%以下,充分球磨后得到柔光温润釉浆,该釉在1220~1280℃下烧成。
4.根据权利要求3所述一种卫生陶瓷洁具柔光温润釉的制备工艺,其特征在于,所述粘土采用黑泥、硅酸锆采用锆英石、滑石采用蛇纹石。
5.根据权利要求3所述一种卫生陶瓷洁具柔光温润釉的制备工艺,其特征在于,所述含硼熔块、氧化锌、氧化铝、碳酸钡、碳酸锶、羧甲基纤维素、三聚磷酸钠、聚乙烯醇为化工厂经过加工处理的工业纯原料。
6.根据权利要求3所述一种卫生陶瓷洁具柔光温润釉的制备工艺,其特征在于,所述釉浆性能调节剂为占重量总量低于1%的羧甲基纤维素、三聚磷酸钠或聚乙烯醇。