CN108410099A - 抗静电复合pvc板材配方 - Google Patents
抗静电复合pvc板材配方 Download PDFInfo
- Publication number
- CN108410099A CN108410099A CN201810346648.2A CN201810346648A CN108410099A CN 108410099 A CN108410099 A CN 108410099A CN 201810346648 A CN201810346648 A CN 201810346648A CN 108410099 A CN108410099 A CN 108410099A
- Authority
- CN
- China
- Prior art keywords
- parts
- antistatic
- agent
- composite pvc
- pvc plank
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种抗静电复合PVC板材配方,包括如下组分和含量(重量份数):树脂100份、氯化聚乙烯(CPE)8份、抗静电剂1份、钙锌复合稳定剂5份、碳酸氢钠0.5份、发泡调节剂4份、硬脂酸甘油脂0.5份、聚乙烯蜡0.6份;进一步改进在于:所述抗静电剂为纳米氧化硅。本发明添加纳米氧化硅,显著改善抗静电性能。
Description
技术领域
本发明涉及一种复合高分子材料配方,特别是一种复合PVC板材配方。
背景技术
人们的生活水平越来越高,也越来越关注健康和安全,特别是噪声对人们生活的影响。现有复合PVC板材具有无甲醇、防腐蚀、重量轻、隔音、隔热等特点,在装饰行业得到越来越多的应用,但现有复合PVC板材抗静电性能差,无法满足抗静电场所的需要。
发明内容
本发明针对现有技术的不足,提出一种能显著提高抗静电性能的抗静电复合PVC板材配方。
本发明通过下述技术方案实现技术目标。
抗静电复合PVC板材配方,其改进之处在于:包括如下组分和含量(重量份数):树脂100份、氯化聚乙烯(CPE)8份、抗静电剂1份、钙锌复合稳定剂5份、碳酸氢钠0.5份、发泡调节剂4份、硬脂酸甘油脂0.5份、聚乙烯蜡0.6份。
进一步改进在于:所述抗静电剂为纳米氧化硅。
本发明与现有技术相比,具有以下积极效果:
1、添加抗静电剂,显著提高本发明抗静电性能。
2、抗静电剂为纳米氧化硅,使本发明具有较高的抗静电性能。
具体实施方式
下面结合实施例对本发明作进一步说明。
抗静电复合PVC板材配方,包括如下组分和含量(重量份数):树脂100份、氯化聚乙烯(CPE)8份、抗静电剂1份、钙锌复合稳定剂5份、碳酸氢钠0.5份、发泡调节剂4份、硬脂酸甘油脂0.5份、聚乙烯蜡0.6份,本实施例中,抗静电剂为纳米氧化硅。
Claims (2)
1.一种抗静电复合PVC板材配方,其特征在于:包括如下组分和含量(重量份数):树脂100份、氯化聚乙烯(CPE)8份、抗静电剂1份、钙锌复合稳定剂5份、碳酸氢钠0.5份、发泡调节剂4份、硬脂酸甘油脂0.5份、聚乙烯蜡0.6份。
2.根据权利要求1所述的抗静电复合PVC板材配方,其特征在于:所述抗静电剂为纳米氧化硅。