CN108384314A - 一种uv凹印雪花油墨 - Google Patents
一种uv凹印雪花油墨 Download PDFInfo
- Publication number
- CN108384314A CN108384314A CN201810232635.2A CN201810232635A CN108384314A CN 108384314 A CN108384314 A CN 108384314A CN 201810232635 A CN201810232635 A CN 201810232635A CN 108384314 A CN108384314 A CN 108384314A
- Authority
- CN
- China
- Prior art keywords
- parts
- gravures
- printing ink
- snowflake printing
- ink
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种UV凹印雪花油墨，属于油墨印刷技术领域。本发明提出一种UV凹印雪花油墨，由以下重量份的物质组成：丙烯酸树脂20~30份，二缩三丙二醇二丙烯酸酯10~20份，1，6‑乙二醇二丙烯酸酯10~20份，光引发剂4~5份，树脂预聚物10~20份，稳定剂0.2~0.5份。本发明中添加剂的作用是为了增强油墨的着色性，添加剂为端氨基硅烷偶联剂和羧酸酯的羰基亲核取代产物，不影响油墨的印刷适性及储存性能，对中性纸张、PET薄膜等多种基材结合牢度性能提升较大，不含有芳烃溶剂，增强凹印雪花油墨的色彩效果和持久性。
Description
技术领域
本发明涉及油墨印刷技术领域，尤其涉及一种UV凹印雪花油墨。
背景技术
UV(紫外光固化)油墨是指在紫外线照射下，利用不同波长和能量的紫外光使油墨连接料中的单体聚合成聚合物，使油墨成膜和干燥的油墨。作为油墨，它们必须具备良好的印刷适性，艳丽的颜色(特殊情况除外)，适宜的固化干燥速率。同时有良好的附着力，并具备耐磨、耐蚀、耐候等特性。
在UV光的照射下，UV油墨光聚合引发剂吸收一定波长的光子，激发到激发态，形成自由基或离子。然后通过分子间能量转移，使聚合的预聚物和光敏感的单体和聚合物成为激发态，产生的电荷转移复合体。这些复杂的粒子不断交联聚合，固化成膜。
紫外光固化丝印雪花油墨是通过印刷机先将油墨印刷在印刷品的图案表面，再经过引爆起花固化呈现出冬天雪花般的品莹剔透纹理质感的过程，是结晶、裂变型的特殊工艺油墨。
现有技术中的油墨着色性差，为了实现雪花印油墨良好的立体效果往往需要多次印刷，2色次印刷，这样费时费力。
发明内容
为解决现有技术中一种UV凹印雪花油墨着色性差的缺陷，本发明提出一种UV凹印雪花油墨，由以下重量份的物质组成：丙烯酸树脂 20~30份，二缩三丙二醇二丙烯酸酯10~20份，1，6-乙二醇二丙烯酸酯10~20份，光引发剂4~5份，树脂预聚物10~20份，稳定剂0.2~0.5份。
在紫外光的照射下丙烯酸树脂、二缩三丙二醇二丙烯酸酯、1，6-乙二醇二丙烯酸酯单体和树脂预聚物发生交联反应，油墨中的颗粒由于接触或相距很近，造成相互吸引，快速向实体中间凝聚，形成规则的平面。光引发剂的作用是在近紫外的激发下产生自由基，它对光敏感而对热稳定。包括芳羰基化合物、有机硫化合物、有机过氧化物等， 它关系到光辐射时配方体系由液态转化为固态的交联固化时间。
进一步的，还包含消泡剂0.3~1.0份，润滑剂5~15份。
油墨中的气泡会严重影响承印制品的质量，消泡剂可为改性聚醚、聚硅氧烷消泡剂等。润滑剂可以使用聚乙二醇、聚乙烯蜡、甘油等。
进一步的，所述润滑剂为聚乙烯蜡。聚乙烯蜡又称高分子蜡，因其优良的耐寒性、耐热性、耐化学性和耐磨性而得到广泛的应用。正常生产中，这部分蜡作为一种添加剂可直接加到聚烯烃加工中，它可以增加产品的光泽和加工性能。作为润滑剂，其化学性质稳定、电性能良好，聚乙烯蜡具有更强的内部润滑作用。
进一步的，还包含0.5~0.9份的添加剂，所述添加剂为具有式Ⅰ所述结构式的物质：
（R2）z—Si(OR1)x(OCOR3)y （式Ⅰ）
其中，式Ⅰ中所述R1、R2 、R3为烷烃基，x、y、z均为自然数并且三者之和为4。
由式Ⅰ所示的结构式，可以很容易地想到添加剂由硅氧烷偶联剂R2—Si(OR1)3的硅氧基团和羧酸HOCOR3的氢发生取代反应，R1、R3同上述。该反应机理类似于硅氧烷的水解反应，硅氧烷偶联剂的硅氧键由于键能较烷氧基的C—O键的键能大因而能较容易断裂，较容易被羧酸的—COO所取代。该反应较佳地在非质子型溶剂，例如DMSO、丙酮、正己烷等，反应的温度较好地为80～105℃，反应时间为1～3h。至于反应加料顺序，可以采用连续加料法或者间隙性加料法。
前述，硅氧烷偶联剂可以使用例如二甲基二乙氧基硅烷、KH-550、KH-560等。至于羧酸，较好地为C10~C20的羧酸，例如十六碳酸等。
硅氧烷偶联剂、羧酸二者的反应比可根据反应产生来设计的理论值，较好地，二者的质量之比为3：8~3：7。
本发明中添加剂的作用是为了增强油墨的着色性，所述的添加剂为端氨基硅烷偶联剂和羧酸酯的羰基亲核取代产物。本添加剂不影响油墨的印刷适性及储存性能，对中性纸张、PET薄膜等多种基材结合牢度性能提升较大，不含有芳烃溶剂，挥发性与毒性与重金属。
进一步的，所述光引发剂为2,4,6-三甲基苯甲酰基-二苯基氧化膦、苯基双(2,4,6-三甲基苯甲酰基)氧化膦、二苯甲酮衍生物中的一种或至少二种。
其中，所述的引发剂2,4,6-三甲基苯甲酰基-二苯基氧化膦（TPO），TPO为高效的光引发剂，吸收波长达430nm，特别适合于有色体系的光固化。其光解产物为三甲基苯甲酰自由基和二苯基膦酰自由基，都是引发活性很高的自由基。其光解产物的吸收波长向短波移动，具有光漂白效果，有利于紫外光透过，可用于厚涂层的固化。其热稳定性优良，加热至180℃无化学反应发生，贮存稳定性好。虽然自身带有浅黄色，但光解后变为无色，不发生黄变。苯基双(2,4,6-三甲基苯甲酰基)氧化膦的波长吸收峰在370nm和405nm处，最大吸收波长可达450nm。光解产物有两个三甲基苯甲酰基和一个苯基膦酰基自由基，都是引发活性很高的自由基，具有比TPO更高的引发活性。
本发明具有以下有益效果，加入添加剂增强油墨的附着性，增强凹印雪花油墨的色彩效果和持久性。
具体实施方式
下面根据实施例对发明内容进一步说明。
实施例一
本实施例的一种UV凹印雪花油墨，由以下重量份的物质组成：丙烯酸树脂 20份，二缩三丙二醇二丙烯酸酯10份，1，6-乙二醇二丙烯酸酯10份，光引发剂2,4,6-三甲基苯甲酰基-二苯基氧化膦4份，树脂预聚物10份，稳定剂0.2份。还包括消泡剂聚硅氧烷0.3份，润滑剂聚乙烯蜡5份。
还包含0.5份的添加剂，其中，硅氧烷偶联剂为二甲基二乙氧基硅烷，羧酸为十六碳酸，二者质量之比为3：8。
实施例二
本实施例的一种UV凹印雪花油墨，由以下重量份的物质组成：丙烯酸树脂 30份，二缩三丙二醇二丙烯酸酯20份，1，6-乙二醇二丙烯酸酯20份，光引发剂二苯甲酮衍生物5份，树脂预聚物20份，稳定剂0.5份。还包括消泡剂聚硅氧烷1.0份，润滑剂聚乙烯蜡15份。
还包含0.9份的添加剂，其中，硅氧烷偶联剂为二甲基二乙氧基硅烷，羧酸为二十碳酸，二者质量之比为3：7.5。
实施例三
本实施例的一种UV凹印雪花油墨，由以下重量份的物质组成：丙烯酸树脂 25份，二缩三丙二醇二丙烯酸酯15份，1，6-乙二醇二丙烯酸酯15份，光引发剂苯基双(2,4,6-三甲基苯甲酰基)氧化膦4.5份，树脂预聚物15份，稳定剂0.4份。还包括消泡剂聚硅氧烷0.7份，润滑剂聚乙烯蜡10份。
还包含0.9份的添加剂，其中，硅氧烷偶联剂为二甲基二乙氧基硅烷，羧酸为十七碳酸，二者质量之比为3：7。
实施例一、二、三的油墨承印效果很好，着色能力极佳。
本发明中添加剂的作用是为了增强油墨的着色性，添加剂为端氨基硅烷偶联剂和羧酸酯的羰基亲核取代产物，不影响油墨的印刷适性及储存性能，对中性纸张、PET薄膜等多种基材结合牢度性能提升较大，不含有芳烃溶剂，挥发性与毒性与重金属，增强凹印雪花油墨的色彩效果和持久性。
本发明不局限于上述具体的实施方式，本发明可以有各种更改和变化。凡是依据本发明的技术实质对以上实施方式所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围。
Claims (10)
1.一种UV凹印雪花油墨，其特征在于，由以下重量份的物质组成：丙烯酸树脂 20~30份，二缩三丙二醇二丙烯酸酯10~20份，1，6-乙二醇二丙烯酸酯10~20份，光引发剂4~5份，树脂预聚物10~20份，稳定剂0.2~0.5份。
2.根据权利要求1所述的UV凹印雪花油墨，其特征在于，还包含消泡剂0.3~1.0份。
3.根据权利要求1所述的UV凹印雪花油墨，其特征在于，还包含润滑剂5~15份。
4.根据权利要求3所述的UV凹印雪花油墨，其特征在于，所述润滑剂为聚乙烯蜡。
5.根据权利要求1所述的UV凹印雪花油墨，其特征在于，还包含0.5~0.9份的添加剂，所述添加剂为具有式Ⅰ所述结构式的物质：
（R2）z—Si(OR1)x(OCOR3)y （式Ⅰ）。
6.其中，式Ⅰ中所述R1、R2、R3为烷烃基，x、y、z均为自然数并且三者之和为4。
7.根据权利要求5所述的UV凹印雪花油墨，其特征在于，得到所述添加剂的硅氧烷偶联剂为二甲基二乙氧基硅烷。
8.根据权利要求6所述的UV凹印雪花油墨，其特征在于，得到所述添加剂的硅烷偶联剂和羧酸的质量之比为3：8~3：7。
9.根据权利要求7所述的UV凹印雪花油墨，其特征在于，所述R3为C10~C20的烷烃基。
10.根据权利要求1所述的UV凹印雪花油墨，其特征在于，所述光引发剂为2,4,6-三甲基苯甲酰基-二苯基氧化膦、苯基双(2,4,6-三甲基苯甲酰基)氧化膦、二苯甲酮衍生物中的一种或至少二种。