CN108341633A - 一种瓷砖胶 - Google Patents

一种瓷砖胶 Download PDF

Info

Publication number
CN108341633A
CN108341633A CN201710203856.2A CN201710203856A CN108341633A CN 108341633 A CN108341633 A CN 108341633A CN 201710203856 A CN201710203856 A CN 201710203856A CN 108341633 A CN108341633 A CN 108341633A
Authority
CN
China
Prior art keywords
parts
tile
powder
glue
ethylene
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710203856.2A
Other languages
English (en)
Inventor
黄飞豹
胡建连
池万松
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wenzhou Innovative New Materials Ltd By Share Ltd
Original Assignee
Wenzhou Innovative New Materials Ltd By Share Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wenzhou Innovative New Materials Ltd By Share Ltd filed Critical Wenzhou Innovative New Materials Ltd By Share Ltd
Priority to CN201710203856.2A priority Critical patent/CN108341633A/zh
Publication of CN108341633A publication Critical patent/CN108341633A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种瓷砖胶,其特征在于：所以重量百分比包括以下组分：水泥35‑42份；砂45‑55份；重钙粉4‑12份；乳胶粉1‑6份；纤维素醚0.1‑09份；缓凝剂0.1‑0.3份；消泡剂0.5‑1份，本发明的有益效果在于：所述缓凝剂可以提高涂抹性和延长可操作时间，能使浆料在涂抹后不会因干得太快而龟裂，增强硬化后强度，通过聚合物分子的扩散，乳胶颗粒在砂将中形成不溶于水的连续膜，从而提高了对界面的粘结性和对砂浆本身的改性，提高搞冻融性与憎水性、降低吸水率、防止开裂。以乙烯为主，起到胶粘剂的作用，提高瓷砖胶的粘贴强度。

Description

一种瓷砖胶
技术领域
本发明涉及建筑材料领域，尤其是指一种瓷砖胶。
背景技术
随着建筑装饰行业的蓬勃发展，人们对瓷砖装饰要求也越来越高，传统的瓷砖粘结材料主要采用现场配制的水泥砂浆(厚度一般为2厘米左右)，这种方法是将砂与水泥现场混合制成简单的水泥砂浆，把这种砂浆涂在预浸或预润湿的瓷砖背面，涂有砂浆的瓷砖压到预先润湿的墙(地)面上，然后轻敲瓷砖，以保证瓷砖具有一定的平整度。但这传统的水泥砂浆已被瓷砖胶所取代，瓷砖胶又称陶瓷砖粘合剂，主要用于粘贴瓷砖、面砖、地砖等装饰材料，广泛适用于内外墙面、地面、浴室、厨房等建筑的饰面装饰场所。其主要特点是粘接强度高、耐水、耐冻融、耐老化性能好及施工方便，是一种非常理想的粘结材料。目前市面上的瓷砖胶品种繁多、标准各不相同、应用领域、功能各不相同，普通消费人群对此并不了解。虽然很多普通消费都就算是选购瓷砖胶用来粘贴瓷砖、面砖、地砖也会出现大块瓷砖空鼓甚至脱落。
发明内容
本发明的目的在于提供一种瓷砖胶。
一种瓷砖胶,其特征在于：所以重量百分比包括以下组分：
所述重钙粉的细度为300-400目。
所述乳胶粉为醋酸乙烯酯与乙烯的共聚胶粉，乙烯与氯乙烯及月桂酸乙烯醋三元共聚粉，醋酸乙烯酯与乙烯及高级脂肪酸乙烯脂三元共聚粉，醋酸乙烯酸均聚胶粉，苯乙烯与丁二烯共聚胶粉。
本发明的有益效果在于：所述缓凝剂可以提高涂抹性和延长可操作时间，能使浆料在涂抹后不会因干得太快而龟裂，增强硬化后强度，通过聚合物分子的扩散，乳胶颗粒在砂将中形成不溶于水的连续膜，从而提高了对界面的粘结性和对砂浆本身的改性，提高搞冻融性与憎水性、降低吸水率、防止开裂。以乙烯为主，起到胶粘剂的作用，提高瓷砖胶的粘贴强度。
具体实施方式
一种瓷砖胶,其特征在于：所以重量百分比包括以下组分：
所述重钙粉的细度为300-400目。
所述乳胶粉为醋酸乙烯酯与乙烯的共聚胶粉，乙烯与氯乙烯及月桂酸乙烯醋三元共聚粉，醋酸乙烯酯与乙烯及高级脂肪酸乙烯脂三元共聚粉，醋酸乙烯酸均聚胶粉，苯乙烯与丁二烯共聚胶粉。
所述水泥为P.O42.5普通硅酸盐水泥
实施例1：各组分的具体重量(KG)配比如下：
此中配比瓷砖胶的粘结强度≥1.2Mpa，适合尺寸小的瓷砖。
实施例2：各组分的具体重量(KG)配比如下：
此中配比瓷砖胶的粘结强度≥1.5Mpa，适合中等尺寸的瓷砖。
实施例3：各组分的具体重量(KG)配比如下：
此中配比瓷砖胶的粘结强度≥2Mpa，适合尺寸大的瓷砖。
本发明的有益效果在于：所述缓凝剂可以提高涂抹性和延长可操作时间，能使浆料在涂抹后不会因干得太快而龟裂，增强硬化后强度，通过聚合物分子的扩散，乳胶颗粒在砂将中形成不溶于水的连续膜，从而提高了对界面的粘结性和对砂浆本身的改性，提高搞冻融性与憎水性、降低吸水率、防止开裂。以乙烯为主，起到胶粘剂的作用，提高瓷砖胶的粘贴强度。

Claims (3)

1.一种瓷砖胶,其特征在于：所以重量百分比包括以下组分：
2.根据权利要求1所述的一种瓷砖胶,其特征在于：所述重钙粉的细度为300-400目。
3.根据权利要求1所述的一种瓷砖胶,其特征在于：所述乳胶粉为醋酸乙烯酯与乙烯的共聚胶粉，乙烯与氯乙烯及月桂酸乙烯醋三元共聚粉，醋酸乙烯酯与乙烯及高级脂肪酸乙烯脂三元共聚粉，醋酸乙烯酸均聚胶粉，苯乙烯与丁二烯共聚胶粉。
CN201710203856.2A 2017-03-30 2017-03-30 一种瓷砖胶 Pending CN108341633A (zh)