CN108328926A - A kind of starry sky series glaze formula - Google Patents
A kind of starry sky series glaze formula Download PDFInfo
- Publication number
- CN108328926A CN108328926A CN201810262392.7A CN201810262392A CN108328926A CN 108328926 A CN108328926 A CN 108328926A CN 201810262392 A CN201810262392 A CN 201810262392A CN 108328926 A CN108328926 A CN 108328926A
- Authority
- CN
- China
- Prior art keywords
- parts
- overglaze
- coat enamel
- ground
- feldspar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of starry sky series glaze formulas, it includes ground-coat enamel and overglaze；The ground-coat enamel is grouped as by the group of following parts by weight：35 40 parts of Jiangxi feldspar, 14 16 parts of Xianyou quartz, 14 16 parts of Longyan clay, 8 12 parts of barium carbonate, 23 27 parts of F320 frits, 24 26 parts of talcum, 46 parts of vanadic anhydride, 67 parts of iron oxide, 8 12 parts of manganese oxide, 46 parts of porcelain powder, 0.18 0.22 parts of nano-onions carbon；The overglaze is grouped as by the group of following parts by weight：78 82 parts of Jiangxi feldspar, 14 16 parts of coarse whiting, 8 12 parts of kaolin, 46 parts of barium, 46 parts of zinc oxide, 67 parts of water cyan high-temperature resisting pigment, quartzy 24 26 parts, 46 parts of porcelain powder；Starry sky pattern, glossiness height, low manufacture cost can be fired into.
Description
Technical field
The present invention relates to a kind of glaze, and in particular to a kind of starry sky series glaze formula.
Background technology
Glaze is a kind of silicate, and the glaze applied on ware is generally using quartz, feldspar, clay as raw material, ground plus water
After modulation, it is coated on billet surface, is melted through the roasting of certain temperature, when the temperature drops, forming the nature of glass of ceramic surface
Thin layer.It makes ware increase mechanical strength, thermal stability, dielectric strength and the erosion for preventing liquid, gas.Glaze, which also has, to be increased
Porcelain it is beautiful and convenient for wash wipe, be not sticky with by dust the effects that.
The difference of enamel formula, the color burnt out is also variant, and the glaze of few starry sky colors on the market, and
Modulated process is complex, and cost is higher.
Invention content
In view of the defects and deficiencies of the prior art, the present invention intends to provide a kind of starry sky series glaze formulas.
To achieve the above object, the technical solution adopted by the present invention is：It includes ground-coat enamel and overglaze；The ground-coat enamel by with
The group of lower parts by weight is grouped as：Feldspar 35-40 parts of Jiangxi, 14-16 parts of Xianyou quartz, 14-16 parts of Longyan clay, barium carbonate 8-12
Part, 23-27 parts of F320 frits, 24-26 parts of talcum, 4-6 parts of vanadic anhydride, 6-7 parts of iron oxide, 8-12 parts of manganese oxide, porcelain powder
4-6 parts, 0.18-0.22 parts of nano-onions carbon；The overglaze is grouped as by the group of following parts by weight：Feldspar 78-82 parts of Jiangxi,
14-16 parts of coarse whiting, 8-12 parts of kaolin, 4-6 parts of barium, 4-6 parts of zinc oxide, 6-7 parts of water cyan high-temperature resisting pigment, quartz 24-26
Part, 4-6 parts of porcelain powder；
Its glazing method is：It is comprised the following steps：
One, primary ground-coat enamel is first gone up on idiosome；
Two, an overglaze is sprayed again on the basis of ground-coat enamel；
Three, into klining system, natural cooling；
The temperature curve setting of its firing is as follows：Temperature is first increased to 300 DEG C from room temperature, takes 2 hours；It is continuously heating to
600 DEG C, take 2 hours；800 DEG C are warming up to, takes 1 hour；900 DEG C are warming up to, takes 1.5 hours；1200 DEG C are warming up to, consumption
When 1 hour；1330 DEG C are warming up to, takes 1.5 hours；Last 1330 DEG C keep the temperature 0.5 hour.
After adopting the above scheme, the present invention has the beneficial effect that：A kind of starry sky series glaze formula of the present invention, can burn
Starry sky pattern, glossiness height, low manufacture cost is made.
Specific implementation mode
The present invention is further illustrated below.
Present embodiment the technical solution adopted is that：It includes ground-coat enamel and overglaze；The ground-coat enamel is by following weight
The group of part is grouped as：37 parts of Jiangxi feldspar, 15 parts of Longyan clay, 10 parts of barium carbonate, 25 parts of F320 frits, is slided 15 parts of Xianyou quartz
25 parts of stone, 5 parts of vanadic anhydride, 7 parts of iron oxide, 10 parts of manganese oxide, 5 parts of porcelain powder, 0.2 part of nano-onions carbon；The overglaze
It is grouped as by the group of following parts by weight：80 parts of Jiangxi feldspar, 15 parts of coarse whiting, 10 parts of kaolin, 5 parts of barium, 5 parts of zinc oxide, water are green
6 parts of color high-temperature resisting pigment, quartzy 25 parts, 5 parts of porcelain powder；
Its glazing method is：It is comprised the following steps：
One, primary ground-coat enamel is first gone up on idiosome；
Two, an overglaze is sprayed again on the basis of ground-coat enamel；
Three, into klining system, natural cooling；
The temperature curve setting of firing is as follows：Temperature is first increased to 300 DEG C from room temperature, takes 2 hours；It is continuously heating to 600
DEG C, take 2 hours；800 DEG C are warming up to, takes 1 hour；900 DEG C are warming up to, takes 1.5 hours；1200 DEG C are warming up to, is taken
1 hour；1330 DEG C are warming up to, takes 1.5 hours；Last 1330 DEG C keep the temperature 0.5 hour.
The above is merely illustrative of the technical solution of the present invention and unrestricted, and those of ordinary skill in the art are to this hair
The other modifications or equivalent replacement that bright technical solution is made, as long as it does not depart from the spirit and scope of the technical scheme of the present invention,
It is intended to be within the scope of the claims of the invention.
Claims (3)
1. a kind of starry sky series glaze formula, it is characterised in that it includes ground-coat enamel and overglaze；The ground-coat enamel is by following parts by weight
Group be grouped as：Feldspar 35-40 parts of Jiangxi, 14-16 parts of Xianyou quartz, 14-16 parts of Longyan clay, 8-12 parts of barium carbonate, F320 are molten
23-27 parts of block, 24-26 parts of talcum, 4-6 parts of vanadic anhydride, 6-7 parts of iron oxide, 8-12 parts of manganese oxide, 4-6 parts of porcelain powder, nanometer
0.18-0.22 parts of onion carbon；The overglaze is grouped as by the group of following parts by weight：Feldspar 78-82 parts of Jiangxi, coarse whiting 14-16
Part, 8-12 parts of kaolin, 4-6 parts of barium, 4-6 parts of zinc oxide, 6-7 parts of water cyan high-temperature resisting pigment, 24-26 parts of quartz, porcelain powder 4-6
Part.
2. a kind of starry sky series glaze formula according to claim 1, it is characterised in that it includes ground-coat enamel and overglaze；It is described
Ground-coat enamel be grouped as by the group of following parts by weight：37 parts of Jiangxi feldspar, Xianyou quartz 15 parts, 15 parts of Longyan clay, 10 parts of barium carbonate,
25 parts of F320 frits, 25 parts of talcum, 5 parts of vanadic anhydride, 7 parts of iron oxide, 10 parts of manganese oxide, 5 parts of porcelain powder, nano-onions carbon
0.2 part；The overglaze is grouped as by the group of following parts by weight：80 parts of Jiangxi feldspar, 15 parts of coarse whiting, 10 parts of kaolin, barium 5
Part, 5 parts of zinc oxide, 6 parts of water cyan high-temperature resisting pigment, quartzy 25 parts, 5 parts of porcelain powder.
3. a kind of starry sky series glaze formula according to claim 1 or 2, it is characterised in that its glazing method is：It
It comprises the following steps：
One, primary ground-coat enamel is first gone up on idiosome；
Two, an overglaze is sprayed again on the basis of ground-coat enamel；
Three, into klining system, natural cooling；The temperature curve setting of firing is as follows：Temperature is first increased to 300 DEG C from room temperature, consumption
When 2 hours；600 DEG C are continuously heating to, takes 2 hours；800 DEG C are warming up to, takes 1 hour；900 DEG C are warming up to, it is small to take 1.5
When；1200 DEG C are warming up to, takes 1 hour；1330 DEG C are warming up to, takes 1.5 hours；Last 1330 DEG C keep the temperature 0.5 hour.