CN108326468A - 一种钻探钻头用钎料 - Google Patents
一种钻探钻头用钎料 Download PDFInfo
- Publication number
- CN108326468A CN108326468A CN201711495589.7A CN201711495589A CN108326468A CN 108326468 A CN108326468 A CN 108326468A CN 201711495589 A CN201711495589 A CN 201711495589A CN 108326468 A CN108326468 A CN 108326468A
- Authority
- CN
- China
- Prior art keywords
- solder
- drill bit
- good
- manganese
- nickel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种钻探钻头用钎料,所述钎料的成分及质量百分比为:铜52~55%、镍8~9%、锰5~6%,余量为锌。本发明提供的钎料对结构钢和特硬合金粉末具有良好的浸润性,对金刚石单晶及复合片具有良好的包嵌及烧结性能,具有良好的强度。
Description
技术领域
本发明属于钎焊材料领用,具体为一种钻探钻头用钎料。
背景技术
地质勘探、钻井、采掘中使用的一个重要部件就是钻头,钻头直接影响到钻探的质量、成本和效率。钻头一般由钻体和钻齿通过钎焊成一个整体。钎焊是采用比母材熔点低的金属材料作钎料,将焊件和钎料加热到高于钎料熔点,低于母材熔化温度,利用液态钎料润湿母材,填充接头间隙并与母材相互扩散实现连接焊件的方法。钎焊时,只有熔化的液体钎料很好地润湿母材表面才能填满钎缝。钎焊接头的质量在很大程度上取决钎料。
发明内容
本发明的目的在于提供一种具有良好的浸润性和良好的强度的钻探钻头用钎料。
本发明的目的是通过以下技术方案实现的:一种钻探钻头用钎料,所述钎料的成分及质量百分比为:铜52~55%、镍8~9%、锰5~6%,余量为锌。
优选地,所述钎料的成分及质量百分比为:铜55%、镍7%、锰5%,锌33%。
本发明的有益效果是:本发明提供的钎料对结构钢和特硬合金粉末具有良好的浸润性,对金刚石单晶及复合片具有良好的包嵌及烧结性能,具有良好的强度。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施例,进一步阐述本发明。
一种钻探钻头用钎料,所述钎料的成分及质量百分比为:铜52~55%、镍8~9%、锰5~6%,余量为锌。
各组分的较佳质量百分比为:铜55%、镍7%、锰5%,锌33%。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (2)
1.一种钻探钻头用钎料,其特征在于,所述钎料的成分及质量百分比为:铜52~55%、镍8~9%、锰5~6%,余量为锌。
2.如权利要求1所述的一种钻探钻头用钎料,其特征在于,所述钎料的成分及质量百分比为:铜55%、镍7%、锰5%,锌33%。