CN108314343B - 一种用于制备地聚合物水泥土的拌合方法 - Google Patents
一种用于制备地聚合物水泥土的拌合方法 Download PDFInfo
- Publication number
- CN108314343B CN108314343B CN201810113924.0A CN201810113924A CN108314343B CN 108314343 B CN108314343 B CN 108314343B CN 201810113924 A CN201810113924 A CN 201810113924A CN 108314343 B CN108314343 B CN 108314343B
- Authority
- CN
- China
- Prior art keywords
- soil
- cement
- metakaolin
- geopolymer
- mixing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种用于制备地聚合物水泥土的拌合方法,制备时先将土体烘干粉碎过筛,再以最优含水率喷湿并拌匀且浸润一昼夜,然后将偏高岭土加入到湿土中并拌匀,再配制出碱激发剂,将碱激发剂喷入上述湿土中并拌匀,静置10min,将水泥加入上述土体中并拌匀,最后将水泥对应的水灰比喷入上述湿土中并拌匀。上述碱激发剂为浓度为50%的NaOH溶液与钠水玻璃混合而成。
Description
技术领域
本发明涉及一种制备地聚合物的拌合方法,尤其是在地聚合物部分代替水泥的应用。本发明通过与土混合中的地聚合物的制备,通过对不同材料的拌合方法,来达到拌合的均匀性。
技术背景
迄今为止,固化土的拌合方法因材料不同而有较大差异。Mo Zhang研究偏高岭土的掺量在对地聚合物固化土力学性能进行研究时,其首先配置出碱激发剂,然后将碱激发剂与偏高岭土混合制出地聚合物前体,最后将地聚合物前体与土均匀搅拌,制成试样。
高常辉在研究水泥砂浆固化土的力学特性时,先将土按最优含水率配置并侵润一昼夜,再加入砂与水泥,最后将水灰比所对应的水量均匀的喷洒在混合物中进行制样。
Mingtang Chai将偏高岭土以外加剂的形式加入到高温冻结水泥土中,其先将干土与水混合,低温冷冻24h,在冷冻室中压碎,加入水泥与偏高岭土,为确保水灰比而加入适量水,最后制成试块。
到目前为止,无法确保水泥、地聚合物和软土搅拌均匀,搅拌不均会影响地聚合物水泥土的各个性能。
发明内容
本发明提供了一种用于制备地聚合物水泥土的拌合方法。
为了达到上述发明目的,本发明采用的技术方案是:
a、土样预拌:将土样进行烘干、粉碎、筛分后,按最优含水率将筛分后的干土样和水拌合,浸润一昼夜,制成湿土;
b、制备偏高岭土与预拌湿土混合物:将偏高岭土加入步骤a所述的预拌好的湿土中,拌匀;
c、将制备好的碱激发剂加入步骤b中所述的偏高岭土与预拌湿土混合物中,拌匀,静置10min;
d、将计算所需的水泥加入步骤c所述的含有碱激发剂的偏高岭土与预拌湿土混合物中,然后边搅拌边加入水泥对应的水灰比的水,拌匀。
所述地聚合物为偏高岭土基地质聚合物,所述碱激发剂为浓度50%的NaOH溶液与钠水玻璃的混合物。
所述水泥为42.5级普通硅酸盐水泥。
所述偏高岭土的掺量为3%,所述水泥掺量为12%。
本发明的有益效果在于:
本发明关于制备地聚合物水泥土的拌合方法,其简单、易行,充分考虑到了地聚合物的物理特性,有效解决了地聚合物加入土体中时的成团现象,采用本方法拌合,可有效的提高地聚合物水泥土的强度和破坏应变,大大降低了工程建设成本。
附图说明
图1为本发明的地聚合物水泥土的拌合方法流程图;
图2为实施例1中地聚合物水泥土的无侧限抗压强度;
图3为实施例1中地聚合物水泥土的破坏应变。
具体实施方法
下面结合附图和实施例对本发明做进一步说明
实施例1
原材料准备
干土500g,以最优含水率喷湿,浸润一昼夜。
片状NaOH 3.15g,将NaOH固体溶于水中,配置成浓度为50%的溶液。
水玻璃溶液18.15g,将称量后的水玻璃溶液倒入NaOH溶液中,配置成碱激发剂。
水泥60g,为42.5级普通硅酸盐水泥。
偏高岭土15g。
本次试验选择的掺入比为偏高岭土3%,水泥掺量为12%。制成70.7×70.7×70.7mm的立方体试件
对比方法一为干土拌合,且先配制出地聚合物,再将地聚合物倒入干土中。
对比方法二为湿土拌合,且先配制出地聚合物,将地聚合物倒入湿土中。
如下表,地聚合物水泥土的拌合方法
其中,所述土体塑限为22.52%,液限为39.94%,塑性指数为17.42,最优含水率为20.24%的粉质粘土。
本拌合方法适用于地聚合物水泥土室内试验,试验测得地聚合物水泥土的无侧限抗压强度及破坏应变。
附图2为上述地聚合物水泥土的无侧限抗压强度,可以看出本发明的拌合方法所对应的无侧限抗压强度要优于同为湿土拌合的对比方法二的无侧限抗压强度。
附图3为上述地聚合物水泥土的破坏应变,可以看出本发明的拌合方法的破坏应变仅低于对比方法四,高于其他对比方法。
Claims (1)
1.一种用于制备地质聚合物水泥土的拌合方法,其特征在于,包括以下步骤:
a、土样预拌:将土样进行烘干、粉碎、筛分后,按最优含水率将筛分后的干土样和水拌合,浸润一昼夜,制成湿土;
b、制备偏高岭土与预拌湿土混合物:将偏高岭土加入步骤a所述的预拌好的湿土中,拌匀;
c、将制备好的碱激发剂加入步骤b中所述的偏高岭土与预拌湿土混合物中,拌匀,静置10min;
d、将计算所需的水泥加入步骤c所述的含有碱激发剂的偏高岭土与预拌湿土混合物中,然后边搅拌边加入水泥对应的水灰比的水,拌匀;
所述地质聚合物为偏高岭土基地质聚合物,所述碱激发剂为浓度50%的NaOH溶液和钠水玻璃溶液的混合物;
所述偏高岭土的掺量为3%,所述水泥的掺量为12%。