CN108176726A - 一种直丝管用镀铜钢丝生产工艺 - Google Patents

一种直丝管用镀铜钢丝生产工艺 Download PDF

Info

Publication number
CN108176726A
CN108176726A CN201711361098.3A CN201711361098A CN108176726A CN 108176726 A CN108176726 A CN 108176726A CN 201711361098 A CN201711361098 A CN 201711361098A CN 108176726 A CN108176726 A CN 108176726A
Authority
CN
China
Prior art keywords
steel wire
diameter
raw silk
silk rings
effective
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711361098.3A
Other languages
English (en)
Inventor
陈斌
姜继书
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guizhou Steel Rope Co Ltd
Original Assignee
Guizhou Steel Rope Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guizhou Steel Rope Co Ltd filed Critical Guizhou Steel Rope Co Ltd
Priority to CN201711361098.3A priority Critical patent/CN108176726A/zh
Publication of CN108176726A publication Critical patent/CN108176726A/zh
Pending legal-status Critical Current

Abstract

一种直丝管用镀铜钢丝生产工艺，原料选用直径6.5mm、钢号为80#或82B优质碳素钢热轧盘条，半成品钢丝直径2.3mm，成品钢丝直径0.8mm，钢丝弦高≤600mm/3m，翘高＜3mm，保证钢丝有足够好的平直度，钢丝表面镀紫铜＞0.3 kg/mm2，在温度为130—170℃进行烘干收线。本发明直丝管用镀铜钢丝与直丝管之间的结合力良好，外形美观。

Description

一种直丝管用镀铜钢丝生产工艺
技术领域
本发明涉及一种直丝管用镀铜钢丝生产工艺，属于金属制品加工工艺技术领域。
背景技术
直丝管用镀铜钢丝主要应用于汽车、客车、装载车、电动车、自行车等上的直丝管领域，本发明直丝管用镀铜钢丝从选料上能保证钢丝的回复弹力，并能有效提升钢丝与直丝管的结合，从而与普通的直丝管用钢丝进行区分和使用，在针对直丝管的生产过程中，对钢丝与直丝管的结合力、钢丝本身的平整度和回复弹性进行多方面考虑，因此，自主制定了此种工艺。
该直丝管用镀铜钢丝生产工艺，它是保整钢丝有足够好的平直度（弦高≤600mm/3m，翘高＜3mm）和回复弹性、钢丝抗拉强度（≥1600Mpa），钢丝表面镀紫铜（＞0.3 kg/mm2）等重要参数，并选用80#优质高强度碳素钢。不但满足用户要求、外形美观，还保证了直丝管用钢丝与直丝管之间的结合力。
在相关直丝管用钢丝产品生产上未见有相同的工艺技术内容报道。
发明内容
本发明提供一种直丝管用镀铜钢丝生产工艺，解决直丝管用镀铜钢丝质量差技术问题。
本发明直丝管用镀铜钢丝生产工艺的目的是生产一种使用在直丝管内的钢丝产品，使该类产品更美观、与直丝管结合力更强、回复弹力更好的生产工艺。本生产工艺所生产的新型产品，它由对产品的选料、一次拉拔、热处理磷化、二次拉拔、镀铜上线、钢丝表面清洗、镀铜处理、表面处理、烘干、收线、包装等步骤组成。
本发明的生产0.8mm直丝管用镀铜钢丝，其生产工艺包括如下实施步骤：
（1）原料选择，原料选用钢号为80#或82B优质碳素钢热轧盘条，盘条直径6.5mm；
（2）对原料进行表面处理；
（3）一次拉拔，将直径6.5mm盘条拉拔成直径2.3mm半成品钢丝；
（4）对直径2.3mm半成品钢丝进行热处理及磷化涂层处理；
（5）钢丝二次拉拔，直径2.3mm半成品钢丝拉拔成直径0.8mm，钢丝弦高≤600mm/3m，翘高＜3mm，保证钢丝有足够好的平直度；
（6）镀铜上线，不进行回火处理；然后将钢丝进行电解酸、碱洗表面清洗；再进行焦磷酸铜电镀铜，钢丝表面镀紫铜＞0.3 kg/mm2；
（7）表面处理，加乙醇20kg/24h，添加剂0.5kg/24h；
（8）用温度130—170℃进行烘干，收线速度135—145米/分；
（9）包装，采用单盘独立编织袋软包装。
本以明不但满足用户使用要求、外形美观，还保证了直丝管用钢丝与直丝管之间的结合力。
具体实施方式
以生产0.8mm直丝管用镀铜钢丝工艺为例进行说明：
本发明的直丝管用镀铜钢丝生产工艺，包括如下实施步骤：
（1）原料选择，原料选用钢号为80#或82B优质碳素钢热轧盘条，盘条直径6.5mm；
（2）对原料进行表面处理；
（3）一次拉拔，将直径6.5mm盘条拉拔成直径2.3mm半成品钢丝；
（4）对直径2.3mm半成品钢丝进行热处理及磷化涂层处理；
（5）钢丝二次拉拔，直径2.3mm半成品钢丝拉拔成直径0.8mm，钢丝弦高≤600mm/3m，翘高＜3mm，保证钢丝有足够好的平直度；
（6）镀铜上线，不进行回火处理；然后将钢丝进行电解酸、碱洗表面清洗；再进行焦磷酸铜电镀铜，钢丝表面镀紫铜＞0.3 kg/mm2；
（7）表面处理，加乙醇20kg/24h，添加剂0.5kg/24h；
（8）用温度130—170℃进行烘干，收线速度135—145米/分；
（9）包装，采用单盘独立编织袋软包装。
本发明直丝管用镀铜钢丝与直丝管之间的结合力良好，外形美观。

Claims (1)

1.一种直丝管用镀铜钢丝生产工艺，其特征是包括如下实施步骤：
（1）原料选择，原料选用钢号为80#或82B优质碳素钢热轧盘条，盘条直径6.5mm；
（2）对原料进行表面处理；
（3）一次拉拔，将直径6.5mm盘条拉拔成直径2.3mm半成品钢丝；
（4）对直径2.3mm半成品钢丝进行热处理及磷化涂层处理；
（5）钢丝二次拉拔，直径2.3mm半成品钢丝拉拔成直径0.8mm，钢丝弦高≤600mm/3m，翘高＜3mm，保证钢丝有足够好的平直度；
（6）镀铜上线，不进行回火处理；然后将钢丝进行电解酸、碱洗表面清洗；再进行焦磷酸铜电镀铜，钢丝表面镀紫铜＞0.3 kg/mm2；
（7）表面处理，加乙醇20kg/24h，添加剂0.5kg/24h；
（8）用温度130—170℃进行烘干，收线速度135—145米/分；
（9）包装，采用单盘独立编织袋软包装。
CN201711361098.3A 2017-12-18 2017-12-18 一种直丝管用镀铜钢丝生产工艺 Pending CN108176726A (zh)