CN108118424A - A kind of crease-resistant casual fabric and its preparation process - Google Patents

A kind of crease-resistant casual fabric and its preparation process Download PDF

Info

Publication number
CN108118424A
CN108118424A CN201611062180.1A CN201611062180A CN108118424A CN 108118424 A CN108118424 A CN 108118424A CN 201611062180 A CN201611062180 A CN 201611062180A CN 108118424 A CN108118424 A CN 108118424A
Authority
CN
China
Prior art keywords
parts
fixation
fabric
crease
round bar
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201611062180.1A
Other languages
Chinese (zh)
Inventor
张俊炎
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Danyang Danqi Textile Co Ltd
Original Assignee
Danyang Danqi Textile Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Danyang Danqi Textile Co Ltd filed Critical Danyang Danqi Textile Co Ltd
Priority to CN201611062180.1A priority Critical patent/CN108118424A/en
Publication of CN108118424A publication Critical patent/CN108118424A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of crease-resistant casual fabric and its preparation processes, it is related to fabric technical field；It by following component by weight：7 14 parts of embossing jeans flocking, 3 12 parts of acetate fiber, 5 10 parts of jeans flocking, 9 15 parts of polyester micro suede bounding with lamb fur, 4 11 parts of bast fibre spinning yarn, 24 parts of ceramic powder, 36 parts of biological enzyme, 23 parts of glass fibre；Its preparation process is as follows：Step 1：Base；Step 2：It pushes；Step 3：Cleaning treatment；Step 4：Fixation；Step 5：Braiding；Step 6：It impregnates；Step 7：Drying；The present invention has good snugness of fit, and fixation is good, is not easy to fade, service life is long.

Description

A kind of crease-resistant casual fabric and its preparation process
Technical field
The present invention relates to a kind of crease-resistant casual fabric and its preparation processes, belong to fabric technical field.
Background technology
Fabric is exactly the material for making clothes.As one of clothes three elements, fabric can not only annotate clothes Style and characteristic, and directly control the color of clothes, the expression effect of moulding.Different fabrics has different breathe freely Property, hygroscopicity, the performances such as warmth retention property, for example cotton fabric has good gas permeability and hygroscopicity, comfortable and easy to wear, warmth retention property is good, It is optimal children's garment fabric, cost of idleness during existing leisure fabric dispensing, and fabric feel is poor.
The content of the invention
In view of the above-mentioned problems, the technical problem to be solved in the present invention is to provide a kind of crease-resistant casual fabric and its prepare work Skill.
The present invention a kind of crease-resistant casual fabric, it by following component by weight：Embossing jeans flocking 7- 14 parts, 3-12 parts of acetate fiber, 5-10 parts of jeans flocking, 9-15 parts of polyester micro suede bounding with lamb fur, 4-11 parts of bast fibre spinning yarn, 2-4 parts of ceramic powder, 3-6 parts of biological enzyme, 2-3 parts of glass fibre.
Preferably, the biological enzyme is catalase, appointing in pectase, lipase, protease, cellulase Meaning is a kind of.
A kind of preparation process of crease-resistant casual fabric, its preparation process are as follows：
Step 1：Base：Material is pressed into the cylindrical base of Φ 120mm in advance at 40 DEG C~55 DEG C；
Step 2：It pushes：Cylindrical base is placed on pushing machine, 18~29mm of Φ are forced under the conditions of 55 DEG C~60 DEG C Round bar；
Step 3：Cleaning treatment：Round bar in step 2 is cleaned, is dyed after cleaning being immersed in pigment cylinder；
Step 4：Fixation：The round bar dyed in step 3 is subjected to fixation, is dried after fixation；
Step 5：Braiding：Round bar in step 4 is subjected to warp and weft formula braiding, is increased when weaving on warp bright Silk；
Step 6：It impregnates：Woven fabric is immersed in softening agent, when soaking time is 8-12 small；
Step 7：Drying：Cloth is dried, is rolled after drying by cylinder, is put in storage after the assay was approved.
Compared with prior art, beneficial effects of the present invention are：With good snugness of fit, and fixation is good, is not easy It fades, service life is long.
Specific embodiment
Present embodiment uses following technical scheme：It by following component by weight：Leather bottom of trench 7-14 parts of flocking, 3-12 parts of acetate fiber, 5-10 parts of jeans flocking, 9-15 parts of polyester micro suede bounding with lamb fur, bast fibre spinning yarn 4-11 parts, 2-4 parts of ceramic powder, 3-6 parts of biological enzyme, 2-3 parts of glass fibre.
Preferably, the biological enzyme is catalase, appointing in pectase, lipase, protease, cellulase Meaning is a kind of.
A kind of preparation process of crease-resistant casual fabric, its preparation process are as follows：
Step 1：Base：Material is pressed into the cylindrical base of Φ 120mm in advance at 40 DEG C~55 DEG C；
Step 2：It pushes：Cylindrical base is placed on pushing machine, 18~29mm of Φ are forced under the conditions of 55 DEG C~60 DEG C Round bar；
Step 3：Cleaning treatment：Round bar in step 2 is cleaned, is dyed after cleaning being immersed in pigment cylinder；
Step 4：Fixation：The round bar dyed in step 3 is subjected to fixation, is dried after fixation；
Step 5：Braiding：Round bar in step 4 is subjected to warp and weft formula braiding, is increased when weaving on warp bright Silk；
Step 6：It impregnates：Woven fabric is immersed in softening agent, when soaking time is 8-12 small；
Step 7：Drying：Cloth is dried, is rolled after drying by cylinder, is put in storage after the assay was approved.
Present embodiment has good snugness of fit, soft, wears well well-pressed, not wrinkled, not variable Shape, convenient for washing, and be not easy to fade.
The basic principles, main features and the advantages of the invention have been shown and described above.The technology of the industry Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its Equivalent thereof.

Claims (3)

1. a kind of crease-resistant casual fabric, it is characterised in that：It by following component by weight：Embossing jeans flocking 7- 14 parts, 3-12 parts of acetate fiber, 5-10 parts of jeans flocking, 9-15 parts of polyester micro suede bounding with lamb fur, 4-11 parts of bast fibre spinning yarn, 2-4 parts of ceramic powder, 3-6 parts of biological enzyme, 2-3 parts of glass fibre.
2. a kind of preparation process of crease-resistant casual fabric, its preparation process are as follows：
Step 1：Base：Material is pressed into the cylindrical base of Φ 120mm in advance at 40 DEG C~55 DEG C；
Step 2：It pushes：Cylindrical base is placed on pushing machine, 18~29mm of Φ are forced under the conditions of 55 DEG C~60 DEG C Round bar；
Step 3：Cleaning treatment：Round bar in step 2 is cleaned, is dyed after cleaning being immersed in pigment cylinder；
Step 4：Fixation：The round bar dyed in step 3 is subjected to fixation, is dried after fixation；
Step 5：Braiding：Round bar in step 4 is subjected to warp and weft formula braiding, is increased when weaving on warp bright Silk；
Step 6：It impregnates：Woven fabric is immersed in softening agent, when soaking time is 8-12 small；
Step 7：Drying：Cloth is dried, is rolled after drying by cylinder, is put in storage after the assay was approved.
It is 3. according to claim 1, it is characterised in that：The biological enzyme for catalase, pectase, lipase, Any one in protease, cellulase.
CN201611062180.1A 2016-11-28 2016-11-28 A kind of crease-resistant casual fabric and its preparation process Pending CN108118424A (en)