CN108118421A - A kind of automotive fabric inner decoration facing and preparation method thereof - Google Patents
A kind of automotive fabric inner decoration facing and preparation method thereof Download PDFInfo
- Publication number
- CN108118421A CN108118421A CN201711127632.4A CN201711127632A CN108118421A CN 108118421 A CN108118421 A CN 108118421A CN 201711127632 A CN201711127632 A CN 201711127632A CN 108118421 A CN108118421 A CN 108118421A
- Authority
- CN
- China
- Prior art keywords
- inner decoration
- decoration facing
- parts
- preparation
- fire
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of automotive fabric inner decoration facings and preparation method thereof, and automobile inner decoration facing is weaved by polyester filament, and including veil layer, bottom silk layer and interlayer, three layers are all weaved by fire-retardant polyester filament yarn;Veil layer and bottom silk layer are interwoven using latitude and longitude level, and interlayer is made of the draught line of joint face yarn layer and bottom silk layer.Preparation method of the present invention is simple, is directly obtained with weaving, without gluing, impregnates, environmental-protecting performance is good;The sun-proof good flame resistance of polyester filament of use, intensity are high.
Description
Technical field
The present invention relates to automobile inner decoration facing preparing technical fields, are specially a kind of automotive fabric inner decoration facing and its preparation
Method.
Background technology
Internal decoration textile of automobile mainly includes:Seat-cover fabric, roof, door decorations, retaining wall, curtain, carpet etc..Existing automobile
Interior material is generally terylene and sponge is compound, and surface applying fire retardant or impregnation impregnate fire retardant, and easy aging uses the longevity
Order short, and production process is using a large amount of adhesives, and not environmentally friendly enough, technological process is complicated.
The content of the invention
It is an object of the invention to provide a kind of automotive fabric inner decoration facing and preparation method thereof, to solve above-mentioned background skill
The problem of being proposed in art.
To achieve the above object, the present invention provides following technical solution:A kind of automotive fabric inner decoration facing:Including veil
Layer, bottom silk layer and interlayer, three layers are all weaved by fire-retardant polyester filament yarn;Veil layer and bottom silk layer are handed over using latitude and longitude are horizontal
It knits, interlayer is made of the draught line of joint face yarn layer and bottom silk layer.
Preferably, the fire-retardant polyester filament yarn is made of flame-retardant color master batch grain;The flame-retardant color master batch grain is by PET, PBT, fire-retardant
Agent, toner and dispersant composition, and the component of its mass fraction is:PET is 10~40 parts;PBT is 10~30 parts;Fire retardant is
20~60 parts;Toner is 0~30 part;Dispersant is 0~10 part;The PET is bottle grade pet chip or big bright chip;PBT is
Engineering plastics;Fire retardant is phosphoric acid ester micromolecular compound;Toner is inorganic pigment or solvent dye;Dispersant is polarity
Wax.
Preferably, the fire-retardant polyester filament yarn component further includes wood-fibred, nano-sized magnesium hydroxide, nano silicon dioxide, receives
Meter level bamboo charcoal masterbatch;Each component parts by weight are:20~40 parts of flame-retardant color master batch grain, 10~20 parts of wood-fibred, nano-sized magnesium hydroxide
10~20 parts, 5~15 parts of nano silicon dioxide, 8~18 parts of nano bamboo master batch.
To realize the preparation method of above-mentioned automotive fabric inner decoration facing, comprise the following steps:
A, the method that melt blending is used after raw material is mixed carries out extruding pelletization and obtains mixture;Mixture is passed through afterwards
Melt spinning obtains fire-retardant polyester filament yarn;
B, weaved using fire-retardant polyester filament yarn, weaving veil layer, bottom silk layer and interlayer, and form overall structure, obtained
Semi-finished product;
C, the semi-finished product for obtaining step B carry out evaporating processing using high-temperature vapor;
D, the obtained semi-finished product of step C are washed;
E, the semi-finished product after step D is washed carry out drying and shaping processing;
F, the inner decoration facing after drying is subjected to bristle processing using brushing machine;
G, the inner decoration facing after bristle is carried out scalding skill processing;
H, sanding processing is carried out to get to inner decoration facing finished product using roughing-up machine to scalding the inner decoration facing after skill.
Preferably, melting temperature is 190 DEG C~210 DEG C in the step A.
Preferably, veil density is 200~400T, yarn count 200D/96F;Bottom silk density is 200~401T, and yarn count is
100D;Shed opening is 10~15mm, a height of 1.5~8mm of hair.
Preferably, the time is evaporated in step C for 5min~10min.
Preferably, washing temperature is 50 DEG C~70 DEG C in step D, washing time is 3min~6min.
Preferably, drying temperature is 80 DEG C~120 DEG C in step E.
Preferably, it is 60 DEG C~80 DEG C that skill treatment temperature is scalded in step G, the time is 1min~3min.
Compared with prior art, the beneficial effects of the invention are as follows:The present invention starts with from the basic constituent of fabric, improves female
The ingredient of grain, with polyester filament made of the master batch, spinning efficiency is high, and the indexs such as toughness, elasticity, intensity are above general length
Silk, and flame-proof environmental protection, and then three-layer type fabric is directly prepared into the polyester filament, automotive trim is used directly for, without adding
Add sponge.The fabric preparation method is simple, is directly obtained with weaving, without gluing, impregnates, environmental-protecting performance is good;The terylene of use
The sun-proof good flame resistance of long filament, intensity are high;Furthermore, it is possible to pigment is directly added in master batch, i.e., it is colored, poststaining is not required, more
Add environmental protection;In addition, the preparation method that the present invention uses is easy to operation, and it is efficient, the intensity of automobile inner decoration facing can be improved, into
One step extends its service life.It, can also be in the closed manned work such as subway, elevator, high ferro due to the good characteristic of this fabric
It is used on tool.
Specific embodiment
The technical solution in the embodiment of the present invention is clearly and completely described below, it is clear that described embodiment
Only part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, the common skill in this field
Art personnel all other embodiments obtained without making creative work belong to the model that the present invention protects
It encloses.
The present invention provides following technical solution:A kind of automotive fabric inner decoration facing, including veil layer, bottom silk layer and centre
Layer, three layers are all weaved by fire-retardant polyester filament yarn;Veil layer and bottom silk layer be interwoven using latitude and longitude level, interlayer by
The draught line of joint face yarn layer and bottom silk layer is formed.Fire-retardant polyester filament yarn is made of flame-retardant color master batch grain;The flame-retardant color master batch grain by
PET, PBT, fire retardant, toner and dispersant composition, and the component of its mass fraction is:PET is 10~40 parts;PBT for 10~
30 parts;Fire retardant is 20~60 parts;Toner is 0~30 part;Dispersant is 0~10 part;The PET is bottle grade pet chip or has greatly
Light is cut into slices;PBT is engineering plastics;Fire retardant is phosphoric acid ester micromolecular compound;Toner is inorganic pigment or solvent dye;
Dispersant is polar waxes.The fire-retardant polyester filament yarn component further includes wood-fibred, nano-sized magnesium hydroxide, nano silicon dioxide, receives
Meter level bamboo charcoal masterbatch;Each component parts by weight are:20~40 parts of flame-retardant color master batch grain, 10~20 parts of wood-fibred, nano-sized magnesium hydroxide
10~20 parts, 5~15 parts of nano silicon dioxide, 8~18 parts of nano bamboo master batch.
Embodiment one:
Polyester filament component includes 20 parts of flame-retardant color master batch grain, 10 parts of wood-fibred, nano-sized magnesium hydroxide 10 part, nanometer in parts by weight
5 parts of silica, 8 parts of nano bamboo master batch.
The preparation method of the present embodiment comprises the following steps:
A, the method that melt blending is used after raw material is mixed carries out extruding pelletization and obtains mixture;Mixture is passed through afterwards
Melt spinning obtains fire-retardant polyester filament yarn;Melting temperature is 190 DEG C.
B, weaved using fire-retardant polyester filament yarn, weaving veil layer, bottom silk layer and interlayer, and form overall structure,
Obtain semi-finished product;Veil density is 310T, yarn count 200D/96F;Bottom silk density is 311T, yarn count 100D;Shed opening is
11mm, a height of 4.5mm of hair.
C, the semi-finished product for obtaining step B carry out evaporating processing using high-temperature vapor, evaporate the time for 8min.;
D, the obtained semi-finished product of step C are washed;Washing temperature is 60 DEG C, washing time 5min.
E, the semi-finished product after step D is washed carry out drying and shaping processing, and temperature is 120 DEG C.
F, the inner decoration facing after drying is subjected to bristle processing using brushing machine;
G, the inner decoration facing after bristle is carried out scalding skill processing, temperature is 80 DEG C, time 3min.
H, sanding processing is carried out to get to inner decoration facing finished product using roughing-up machine to scalding the inner decoration facing after skill.
Embodiment two:
Polyester filament component includes 40 parts of flame-retardant color master batch grain, 20 parts of wood-fibred, nano-sized magnesium hydroxide 20 part, nanometer in parts by weight
5 parts of silica 1,18 parts of nano bamboo master batch.
The preparation method of the present embodiment comprises the following steps:
A, the method that melt blending is used after raw material is mixed carries out extruding pelletization and obtains mixture;Mixture is passed through afterwards
Melt spinning obtains fire-retardant polyester filament yarn;Melting temperature is 200 DEG C.
B, weaved using fire-retardant polyester filament yarn, weaving veil layer, bottom silk layer and interlayer, and form overall structure,
Obtain semi-finished product;Veil density is 210T, yarn count 200D/96F;Bottom silk density is 211T, yarn count 100D;Shed opening is
10mm, a height of 2.5mm of hair.
C, the semi-finished product for obtaining step B carry out evaporating processing using high-temperature vapor, evaporate the time for 5min.;
D, the obtained semi-finished product of step C are washed;Washing temperature is 50 DEG C, washing time 4min.
E, the semi-finished product after step D is washed carry out drying and shaping processing, and temperature is 110 DEG C.
F, the inner decoration facing after drying is subjected to bristle processing using brushing machine;
G, the inner decoration facing after bristle is carried out scalding skill processing, temperature is 70 DEG C, time 2min.
H, sanding processing is carried out to get to inner decoration facing finished product using roughing-up machine to scalding the inner decoration facing after skill.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
Understanding without departing from the principles and spirit of the present invention can carry out these embodiments a variety of variations, modification, replace
And modification, the scope of the present invention is defined by the appended.
Claims (10)
1. a kind of automotive fabric inner decoration facing, it is characterised in that:Including veil layer, bottom silk layer and interlayer, three layers all by fire-retardant
Polyester filament is weaved;Veil layer and bottom silk layer are interwoven using latitude and longitude level, and interlayer is by joint face yarn layer and bottom
The draught line of silk layer is formed.
2. a kind of automotive fabric inner decoration facing according to claim 1, it is characterised in that:The fire-retardant polyester filament yarn is by hindering
Combustion Masterbatch is made;The flame-retardant color master batch grain is made of PET, PBT, fire retardant, toner and dispersant, and the group of its mass fraction
It is divided into:PET is 10~40 parts;PBT is 10~30 parts;Fire retardant is 20~60 parts;Toner is 0~30 part;Dispersant is 0~10
Part;The PET is bottle grade pet chip or big bright chip;PBT is engineering plastics;Fire retardant is phosphoric acid ester small molecule chemical combination
Object;Toner is inorganic pigment or solvent dye;Dispersant is polar waxes.
3. a kind of automotive fabric inner decoration facing according to claim 2, it is characterised in that:The fire-retardant polyester filament yarn component
Further include wood-fibred, nano-sized magnesium hydroxide, nano silicon dioxide, nano bamboo master batch;Each component parts by weight are:Fire-retardant color
20~40 parts of master batch, 10~20 parts of wood-fibred, 10~20 parts of nano-sized magnesium hydroxide, 5~15 parts of nano silicon dioxide, nanoscale bamboo
8~18 parts of charcoal master batch.
4. realize a kind of preparation method of automotive fabric inner decoration facing described in claim 1, it is characterised in that:Its preparation method
Comprise the following steps:
A, the method that melt blending is used after raw material is mixed carries out extruding pelletization and obtains mixture;Mixture is passed through into melting
Spinning obtains fire-retardant polyester filament yarn;
B, weaved using fire-retardant polyester filament yarn, weaving veil layer, bottom silk layer and interlayer, and form overall structure, obtained
Semi-finished product;
C, the semi-finished product for obtaining step B carry out evaporating processing using high-temperature vapor;
D, the obtained semi-finished product of step C are washed;
E, the semi-finished product after step D is washed carry out drying and shaping processing;
F, the inner decoration facing after drying is subjected to bristle processing using brushing machine;
G, the inner decoration facing after bristle is carried out scalding skill processing;
H, sanding processing is carried out to get to inner decoration facing finished product using roughing-up machine to scalding the inner decoration facing after skill.
5. a kind of preparation method of automotive fabric inner decoration facing according to claim 4, it is characterised in that:The step A
Middle melting temperature is 190 DEG C~210 DEG C.
6. a kind of preparation method of automotive fabric inner decoration facing according to claim 4, it is characterised in that:Veil density is
200~400T, yarn count 200D/96F;Bottom silk density is 200~401T, yarn count 100D;Shed opening be 10~15mm, hair
A height of 1.5~8mm.
7. a kind of preparation method of automotive fabric inner decoration facing according to claim 4, it is characterised in that:It is steamed in step C
The change time is 5min~10min.
8. a kind of preparation method of automotive fabric inner decoration facing according to claim 4, it is characterised in that:Water in step D
Temperature is washed as 50 DEG C~70 DEG C, washing time is 3min~6min.
9. a kind of preparation method of automotive fabric inner decoration facing according to claim 4, it is characterised in that:It is dried in step E
Dry temperature is 80 DEG C~120 DEG C.
10. a kind of preparation method of automotive fabric inner decoration facing according to claim 4, it is characterised in that:It is scalded in step G
Skill treatment temperature is 60 DEG C~80 DEG C, and the time is 1min~3min.