CN105483905A - Process for manufacturing waterproof, flame-retardant and breathable fabric - Google Patents
Process for manufacturing waterproof, flame-retardant and breathable fabric Download PDFInfo
- Publication number
- CN105483905A CN105483905A CN201510860910.1A CN201510860910A CN105483905A CN 105483905 A CN105483905 A CN 105483905A CN 201510860910 A CN201510860910 A CN 201510860910A CN 105483905 A CN105483905 A CN 105483905A
- Authority
- CN
- China
- Prior art keywords
- fibre
- parts
- fiber
- manufacture craft
- flame retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a process for manufacturing a waterproof, flame-retardant and breathable fabric. The process comprises the processes of fiber preparation, spinning and weaving. According to fiber preparation, natural plant materials are prepared into natural plant fibers, then flame-retardant treatment is carried out, and flame-retardant fibers are obtained. According to spinning, the flame-retardant fibers and composite fibers are blended and prepared into yarn, and the fineness of the yarn is 400 dtex. According to weaving, the blended yarn is spun, and the fabric with the warp density being 200 pieces/10 cm and the weft density being 250 pieces/10 cm is obtained. According to the process, the natural plant fibers are subjected to flame-retardant treatment, and compounded with fibers with flame-retardant performance and fibers with waterproofness performance, so that the fibers achieve flame-retardant performance, and meanwhile the manufactured fibers are smoother, elastic, good in breathability and convenient to manufacture.
Description
Technical field
The invention belongs to cloth and make field, particularly relate to a kind of manufacture craft of water proof fire retardant Ventilate cloth.
Background technology
Along with communications and transportation development and become more consummate day by day, people propose high requirement to ornaments in the vehicles, and particularly require higher for jewelry in the communal facilitys such as automobile, bullet train, aircraft, wherein seat-cover fabric is more outstanding.People wish that these fabrics can be comfortable, soft, attractive in appearance, also wish that these textiless being close to seat surface can have greater functionality, as antibacterial, deodorization, waterproof, fire-retardant etc.In numerous function, fire-retardant most important, the number of casualties caused because textiles catches fire every year is a lot, especially in the environment that the spaces such as automobile, bullet train, aircraft are less, must bring the heavy losses such as the person, property once catch fire.Therefore, the flame-proof treatment for these textiless is extremely important; Meanwhile, due to human contact, so water proofing property and gas permeability are also very good; But textile cloth is in the market difficult to meet waterproof, ventilative and fire-retardant requirement simultaneously.Therefore, the manufacture craft developing a kind of water proof fire retardant Ventilate cloth is necessary, to meet the demand in market.
Chinese patent CN201310498215.6 discloses a kind of corrosion-resistant waterproof fire-resistant cloth, comprise bottom surface fabric, also comprise watertight composition, anti-corrosion layer and flame retardant coating, bottom surface fabric is worked out by warp thread and weft yarn, bottom surface fabric is connected with watertight composition, anti-corrosion layer is connected with at watertight composition upper surface, anti-corrosion layer upper surface is provided with flame retardant coating, watertight composition is made up of polytetrafluoroethylene (PTFE), anti-corrosion layer adopts glass fabric to make, described flame retardant coating adopts CVC inflaming retarding fabric, described waterproofing layer thickness is 0.1mm, described anti-corrosion layer thickness is 0.2mm, described flame retardant coating thickness is 0.1mm.But this cloth is that watertight composition, anti-corrosion layer and flame retardant coating are composited, and in use easily comes off between each layer, be difficult to meet complicated user demand.
Chinese patent CN201210484848.7 discloses a kind of fire-proof and water-proof cloth, comprise bottom cloth layer, flame-retardant layer and watertight composition, flame-retardant layer is intermediate layer, the side of flame-retardant layer is bottom cloth layer, bottom cloth layer is connected by binder with flame-retardant layer, the opposite side of flame-retardant layer is watertight composition, and flame-retardant layer is connected by binder with watertight composition, and bottom cloth layer is made up of fiberglass yarn.But being connected by each layer by binder of this cloth, technological operation reliability is not high, obtained product quality is not high yet.
Therefore a kind of good product quality, water proof fire retardant Ventilate cloth easy to make design is badly in need of, to meet the multi-functional demand of people for cloth.
Summary of the invention
The present invention is directed to the problems referred to above, there is provided a kind of manufacture craft of water proof fire retardant Ventilate cloth, technical process comprises fiber preparation, spins and weave, and fiber is prepared as: natural plant material is prepared natural plant fibre, then through flame treatment, fire resistance fibre is obtained; Spinning is: fire resistance fibre and composite fibre are carried out blending yarn, and the fineness of yarn is 400dtex; Be woven as: the yarn after blending is weaved, obtain through density be 200/10cm, weft density is the cloth of 250/10cm; There is good gas permeability, simultaneously due to the close contact between fiber, make hydrone be subject to very large skin resistance at fiber surface, hydrone not easily through, but easily breathe freely.Natural plant material comprises: cotton, sisal hemp, kapok, cocoanut shell, the weight portion composition of natural plant material comprises: 50 parts ~ 70 parts, cotton, 10 parts ~ 15 parts, sisal hemp, kapok 20 parts ~ 25 parts, cocoanut shell 1 part ~ 5 parts, the weight ratio of fire resistance fibre and composite fibre is 1:1 ~ 2.Adopt natural plants material to work out through the mode of flame treatment and composite fibre shuffling, class is high, reliable in quality, durable in use, is suitable as multifunctional textile product fabric and uses, have market prospects widely.
Further, flame treatment is: the fiber prepared by natural plant material soaks 5 hours ~ 6 hours in waterborne flame retardant liquid, then dries, then be immersed in oiliness fire resistant fluid soak 5 hours ~ 6 hours, again dry.To natural plant fibre through flame treatment, make fiber have anti-flammability, make the fiber that obtains more smooth, flexible simultaneously.
Further, oiliness fire resistant fluid is chlorinated paraffin wax.
Further, oiliness fire resistant fluid be described waterborne flame retardant liquid long-pending 1/4.
Further, the weight ratio of waterborne flame retardant liquid and natural plant fibre is 10:1.
Further, waterborne flame retardant liquid is: the mixed solution of ammonium phosphate salt, phosphamide, antimony chloride, pentachlorophenol.
Further, mixed solution is: the alkaline pentachlorophenol solution equal-volume mixing that the antimony chloride solution that the phosphamide solution that the ammonium phosphate salt solution that mass fraction is 8%, mass fraction are 10%, mass fraction are 12%, mass fraction are 6%.
Further, alkaline pentachlorophenol solution is: add in the pure water of metering by the pentachlorophenol of metering in proportion, drips and uses saturated NaOH solution, drips while stir, dissolves completely to pentachlorophenol.
Further, composite fibre is that waterproof fibre and composite flame retardant fiber are composited, waterproof fibre is: polyvinyl chloride, polyethylene, neoprene latex, polyurethane, the polytetrafluoroethylene (PTFE) fiber through being composited, composite flame retardant fiber is aramid fiber 1313, composite fibre be polyvinyl chloride, polyethylene, neoprene latex, polyurethane, polytetrafluoroethylene (PTFE) through compound again with aramid fiber 1313, the fiber obtained, in the fiber of compound, the weight ratio of waterproof fibre and composite flame retardant fiber is 2:3 ~ 5.Adopt composite fibre to be that the fiber with anti-flammability forms with the fiber composite with water proofing property, add the water proofing property of cloth, the flame resistance do not also not improved.
Further, the weight portion of waterproof fibre consists of: polyvinyl chloride 1 part ~ 5 parts, polyethylene 1 part ~ 5 parts, neoprene latex 2 parts ~ 7 parts, polyurethane 1 part ~ 5 parts, polytetrafluoroethylene (PTFE) 5 parts ~ 15 parts.
Advantage of the present invention is:
1. the manufacture craft of cloth of the present invention, adopt natural plants material to work out through the mode of flame treatment and composite fibre shuffling, class is high, reliable in quality, durable in use, is suitable as multifunctional textile product fabric and uses, have market prospects widely;
2. the manufacture craft of cloth of the present invention, to natural plant fibre through flame treatment, makes fiber have anti-flammability, makes the fiber that obtains more smooth, flexible simultaneously;
3. the cloth that manufacture craft of the present invention makes adopts composite fibre to be that the fiber with anti-flammability forms with the fiber composite with water proofing property, adds the water proofing property of cloth, the flame resistance do not also not improved;
4. the fineness of the yarn of the cloth of manufacture craft making of the present invention is 400dtex, obtain cloth through density be 200/10cm, weft density is 250/10cm, there is good gas permeability, simultaneously due to the close contact between fiber, hydrone is made to be subject to very large skin resistance at fiber surface, hydrone not easily through, but easily breathe freely.
Except object described above, feature and advantage, the present invention also has other object, feature and advantage.Below with reference to detailed description of the invention, the present invention is further detailed explanation.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is described in detail, but the multitude of different ways that the present invention can be defined by the claims and cover is implemented.
Embodiment 1
A kind of manufacture craft of water proof fire retardant Ventilate cloth
Concrete steps are:
(1) fiber preparation: by cotton 50kg, sisal hemp 10kg, kapok 20kg, cocoanut shell 1kg, prepare natural plant fibre, then soaks 5 hours in 810kg waterborne flame retardant liquid, then dry, be immersed in again in 202.5L chlorinated paraffin wax and soak 5 hours, again dry, obtain fire resistance fibre; Waterborne flame retardant liquid is: the alkaline pentachlorophenol solution mixing that the antimony chloride solution that the phosphamide solution that the ammonium phosphate salt solution that 202.5kg mass fraction is 8%, 202.5kg mass fraction are 10%, 202.5kg mass fraction are 12%, 202.5kg mass fraction are 6%; Alkalescence pentachlorophenol solution is: add in the pure water of metering by the pentachlorophenol of metering in proportion, drip and use saturated NaOH solution, drip while stir, dissolve completely to pentachlorophenol.
(2) spin: fire resistance fibre and composite fibre are carried out blending yarn, and the fineness of yarn is 400dtex; The weight ratio of fire resistance fibre and composite fibre is 1:1, composite fibre is that waterproof fibre and composite flame retardant fiber are composited, waterproof fibre is: polyvinyl chloride 23.15kg, polyethylene 23.15kg, neoprene latex 46.30kg, polyurethane 23.15kg, the polytetrafluoroethylene (PTFE) 115.75kg fiber through being composited, composite flame retardant fiber is aramid fiber 1313 57.875kg, composite fibre be polyvinyl chloride, polyethylene, neoprene latex, polyurethane, polytetrafluoroethylene (PTFE) through compound again with aramid fiber 1313 compound, the fiber obtained.
(3) weave: the yarn after blending is weaved, obtain through density be 200/10cm, weft density is the cloth of 250/10cm.
Embodiment 2
A kind of manufacture craft of water proof fire retardant Ventilate cloth
Concrete steps are:
(1) fiber preparation: by cotton 70kg, sisal hemp 15kg, kapok 25kg, cocoanut shell 5kg, prepare natural plant fibre, then soaks 6 hours in 1150kg waterborne flame retardant liquid, then dry, soak 6 hours in 287.5L chlorinated paraffin wax again, again dry, obtain fire resistance fibre; Waterborne flame retardant liquid is: the alkaline pentachlorophenol solution mixing that the antimony chloride solution that the phosphamide solution that the ammonium phosphate salt solution that 287.5kg mass fraction is 8%, 287.5kg mass fraction are 10%, 287.5kg mass fraction are 12%, 287.5kg mass fraction are 6%; Alkalescence pentachlorophenol solution is: add in the pure water of metering by the pentachlorophenol of metering in proportion, drip and use saturated NaOH solution, drip while stir, dissolve completely to pentachlorophenol.
(2) spin: fire resistance fibre and composite fibre are carried out blending yarn, and the fineness of yarn is 400dtex; The weight ratio of fire resistance fibre and composite fibre is 1:1, composite fibre is that waterproof fibre and composite flame retardant fiber are composited, waterproof fibre is: polyvinyl chloride 15kg, polyethylene 23.15kg, neoprene latex 46.30kg, polyurethane 23.15kg, the polytetrafluoroethylene (PTFE) 115.75kg fiber through being composited, composite flame retardant fiber is aramid fiber 1313 57.875kg, composite fibre be polyvinyl chloride, polyethylene, neoprene latex, polyurethane, polytetrafluoroethylene (PTFE) through compound again with aramid fiber 1313, the fiber obtained.
(2) spin: fire resistance fibre and composite fibre are carried out blending yarn, and the fineness of yarn is 400dtex; The weight ratio of fire resistance fibre and composite fibre is 230kg, composite fibre is that waterproof fibre and composite flame retardant fiber are composited, waterproof fibre is: polyvinyl chloride 11.66kg, polyethylene 11.66kg, neoprene latex 16.32kg, polyurethane 11.66kg, the polytetrafluoroethylene (PTFE) 34.98kg fiber through being composited, composite fibre be polyvinyl chloride, polyethylene, neoprene latex, polyurethane, polytetrafluoroethylene (PTFE) through compound again with aramid fiber 1313 compound, the fiber obtained.
(3) weave: the yarn after blending is weaved, obtain through density be 200/10cm, weft density is the cloth of 250/10cm.
Embodiment 3
A kind of manufacture craft of water proof fire retardant Ventilate cloth
Concrete steps are:
(1) fiber preparation: by cotton 60kg, sisal hemp 12.5kg, kapok 22.5kg, cocoanut shell 3kg, prepare natural plant fibre, then soaks 5.5 hours in 980kg waterborne flame retardant liquid, then dry, be immersed in again in 245L chlorinated paraffin wax and soak 5.5 hours, again dry, obtain fire resistance fibre; Waterborne flame retardant liquid is: the alkaline pentachlorophenol solution that the antimony chloride solution that the phosphamide solution that the ammonium phosphate salt solution that 245kg mass fraction is 8%, 245kg mass fraction are 10%, 245kg mass fraction are 12%, 245kg mass fraction are 6%, alkalescence pentachlorophenol solution is: add in the pure water of metering by the pentachlorophenol of metering in proportion, drip and use saturated NaOH solution, drip while stir, dissolve completely to pentachlorophenol.
(2) spin: fire resistance fibre and composite fibre are carried out blending yarn, and the fineness of yarn is 400dtex; The weight ratio of fire resistance fibre and composite fibre is 230kg, composite fibre is that waterproof fibre and composite flame retardant fiber are composited, waterproof fibre is: polyvinyl chloride 11.66kg, polyethylene 11.66kg, neoprene latex 16.32kg, polyurethane 11.66kg, the polytetrafluoroethylene (PTFE) 34.98kg fiber through being composited, composite flame retardant fiber is aramid fiber 1313 143.75kg, composite fibre be polyvinyl chloride, polyethylene, neoprene latex, polyurethane, polytetrafluoroethylene (PTFE) through compound again with aramid fiber 1313 compound, the fiber obtained.
(3) weave: the yarn after blending is weaved, obtain through density be 200/10cm, weft density is the cloth of 250/10cm.
Embodiment 4
A kind of manufacture craft of water proof fire retardant Ventilate cloth
Technical process comprises fiber preparation, spins and weave, and fiber is prepared as: natural plant material is prepared natural plant fibre, then through flame treatment, obtains fire resistance fibre; Flame treatment is: the fiber prepared by natural plant material soaks 5 hours ~ 6 hours in waterborne flame retardant liquid, then dries, then be immersed in oiliness fire resistant fluid soak 5 hours ~ 6 hours, again dry; Oiliness fire resistant fluid is chlorinated paraffin wax, oiliness fire resistant fluid be waterborne flame retardant liquid long-pending 1/4, the weight ratio of waterborne flame retardant liquid and natural plant fibre is 10:1; Waterborne flame retardant liquid is: the alkaline pentachlorophenol solution equal-volume mixing that the antimony chloride solution that the phosphamide solution that the ammonium phosphate salt solution that mass fraction is 8%, mass fraction are 10%, mass fraction are 12%, mass fraction are 6%; Alkalescence pentachlorophenol solution is: add in the pure water of metering by the pentachlorophenol of metering in proportion, drip and use saturated NaOH solution, drip while stir, dissolve completely to pentachlorophenol.Spinning is: fire resistance fibre and composite fibre are carried out blending yarn, and the fineness of yarn is 400dtex; Composite fibre is that waterproof fibre and composite flame retardant fiber are composited; The weight portion of waterproof fibre consists of: the fiber that polyvinyl chloride 1 part ~ 5 parts, polyethylene 1 part ~ 5 parts, neoprene latex 2 parts ~ 7 parts, polyurethane 1 part ~ 5 parts, polytetrafluoroethylene (PTFE) 5 parts ~ 15 parts of processes are composited, composite flame retardant fiber is aramid fiber 1313, composite fibre be polyvinyl chloride, polyethylene, neoprene latex, polyurethane, polytetrafluoroethylene (PTFE) through compound again with aramid fiber 1313, the fiber obtained, in the fiber of compound, the weight ratio of waterproof fibre and composite flame retardant fiber is 2:3 ~ 5.Be woven as: the yarn after blending is weaved, obtain through density be 200/10cm, weft density is the cloth of 250/10cm; Natural plant material comprises: cotton, sisal hemp, kapok, cocoanut shell, the weight portion composition of natural plant material comprises: 50 parts ~ 70 parts, cotton, 10 parts ~ 15 parts, sisal hemp, kapok 20 parts ~ 25 parts, cocoanut shell 1 part ~ 5 parts, the weight ratio of fire resistance fibre and composite fibre is 1:1 ~ 2.
Experimental example
In this experimental example, test the performance of the present invention 1 ~ 3 cloth by experiment.
1. test material
Experimental group: the embodiment of the present invention 1 ~ 3 cloth;
Control group: with common water proof fire retardant cloth.
2. test method
The test embodiment of the present invention 1 ~ 3 cloth, indices performance with common water proof fire retardant cloth.
3. result of the test
By the embodiment of the present invention 1 ~ 3 cloth, analyze with after the indices performance test of common water proof fire retardant cloth, experimental result is in table 1.
Table 1. test result
| Material | Cloth performance | The scope of application | Average life/year |
| Embodiment 1 cloth | Smooth, flexible, good flame resistance, waterproof effect is good, good permeability, rapid heat dissipation | Dress ornament, high-grade decoration, fire-fighting equipment | 5 |
| Embodiment 2 cloth | Smooth, flexible, good flame resistance, waterproof effect is good, good permeability, rapid heat dissipation | Dress ornament, high-grade decoration, fire-fighting equipment | 5 |
| Embodiment 3 cloth | Smooth, flexible, good flame resistance, waterproof effect is good, good permeability, rapid heat dissipation | Dress ornament, high-grade decoration, fire-fighting equipment | 5 |
| Common water proof fire retardant cloth | Rough, elasticity is general, and good flame resistance, waterproof effect is good, poor air permeability | Labour protection equipment, fire-fighting equipment | 2 |
Experimental result shows, compared with common water proof fire retardant cloth, the cloth performance of the embodiment of the present invention 1 ~ 3 cloth under square one, the results of property of average life measure and are better than common water proof fire retardant cloth, the fabric of preparation is more high-grade, the scope of application is wider more high-end, preparation method is applicable to promoting, and product quality is better.
These are only the preferred embodiments of the present invention and experimental example, be not limited to the present invention, for a person skilled in the art, the present invention can have various modifications and variations.Within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., within the protection domain that all should be included in invention.
Claims (10)
1. a manufacture craft for water proof fire retardant Ventilate cloth, technical process comprises fiber preparation, spins and weave, and it is characterized in that, described fiber is prepared as: natural plant material is prepared natural plant fibre, then through flame treatment, obtains fire resistance fibre; Described spinning is: fire resistance fibre and composite fibre are carried out blending yarn, and the fineness of described yarn is 400dtex; Describedly to be woven as: the yarn after blending is weaved, obtain through density be 200/10cm, weft density is the cloth of 250/10cm; Described natural plant material comprises: cotton, sisal hemp, kapok, cocoanut shell, the weight portion composition of described natural plant material comprises: 50 parts ~ 70 parts, cotton, 10 parts ~ 15 parts, sisal hemp, kapok 20 parts ~ 25 parts, cocoanut shell 1 part ~ 5 parts, the weight ratio of described fire resistance fibre and composite fibre is 1:1 ~ 2.
2. manufacture craft according to claim 1, it is characterized in that, described flame treatment is: the fiber prepared by natural plant material soaks 5 hours ~ 6 hours in waterborne flame retardant liquid, then dries, be immersed in again in oiliness fire resistant fluid and soak 5 hours ~ 6 hours, again dry.
3. manufacture craft according to claim 2, is characterized in that, described oiliness fire resistant fluid is chlorinated paraffin wax.
4. manufacture craft according to claim 2, is characterized in that, described oiliness fire resistant fluid be described waterborne flame retardant liquid long-pending 1/4.
5. manufacture craft according to claim 2, is characterized in that, the weight ratio of described waterborne flame retardant liquid and natural plant fibre is 10:1.
6. manufacture craft according to claim 2, is characterized in that, described waterborne flame retardant liquid is: the mixed solution of ammonium phosphate salt, phosphamide, antimony chloride, pentachlorophenol.
7. manufacture craft according to claim 6, it is characterized in that, described mixed solution is: the alkaline pentachlorophenol solution equal-volume mixing that the antimony chloride solution that the phosphamide solution that the ammonium phosphate salt solution that mass fraction is 8%, mass fraction are 10%, mass fraction are 12%, mass fraction are 6%.
8. manufacture craft according to claim 7, is characterized in that, described alkaline pentachlorophenol solution is: add in the pure water of metering by the pentachlorophenol of metering in proportion, drip and use saturated NaOH solution, drip while stir, dissolve completely to pentachlorophenol.
9. manufacture craft according to claim 1, it is characterized in that, described composite fibre is that waterproof fibre and composite flame retardant fiber are composited, described waterproof fibre is: polyvinyl chloride, polyethylene, neoprene latex, polyurethane, the fiber of polytetrafluoroethylene (PTFE) through being composited, described composite flame retardant fiber is aramid fiber 1313, described composite fibre is polyvinyl chloride, polyethylene, neoprene latex, polyurethane, polytetrafluoroethylene (PTFE) through compound again with aramid fiber 1313, the fiber obtained, in the fiber of described compound, the weight ratio of waterproof fibre and composite flame retardant fiber is 2:3 ~ 5.
10. manufacture craft according to claim 9, is characterized in that, the weight portion of described waterproof fibre consists of: polyvinyl chloride 1 part ~ 5 parts, polyethylene 1 part ~ 5 parts, neoprene latex 2 parts ~ 7 parts, polyurethane 1 part ~ 5 parts, polytetrafluoroethylene (PTFE) 5 parts ~ 15 parts.