Summary of the invention
The deficiency existed for prior art, it is an object of the present invention to provide one and grows flax waterproof anticorrosion fabric, to solve
The problem proposed in above-mentioned background technology, the present invention designs ingenious, improves the market competitiveness, has reached simple in construction and design
Reasonably purpose
To achieve these goals, the present invention is to realize by the following technical solutions: one grows flax waterproof anticorrosion fabric,
Including waterproof layer, burlap layer, anti-corrosion layer and contact layer, waterproof layer is made up of PVC, PUR and elastic fiber, wherein
The mass ratio of PVC is 20-30%, and the mass ratio of PUR is 10-20%, and the mass ratio of elastic fiber is 50-60%;Burlap layer by
Pure hemp weaving is constituted;Anti-corrosion layer is made up of aqueous polyurethane anti-flaming dope and fire-retardant polyurethane, and wherein aqueous polyurethane is fire-retardant
The mass ratio of coating is 30-40%, and the mass ratio of fire-retardant polyurethane is 60-70%;Contact layer is by bamboo carbon fiber, mint fibers and sticks
Glue fiber is constituted, and wherein the mass ratio of bamboo carbon fiber is 50-65%, and the mass ratio of mint fibers is 25-40%, the matter of viscose fiber
Amount ratio is 7-13%.
Further, waterproof layer covers the outer surface at burlap layer, and burlap layer covers the outer surface at anti-corrosion layer, corrosion resistant
Erosion layer covers the outer surface at contact layer.
Further, waterproof layer covers the outer surface at anti-corrosion layer, and anti-corrosion layer covers the outer surface at burlap layer, fiber crops
Layer of cloth covers the outer surface at contact layer.
A kind of technique making Caulis et Folium Lini waterproof anticorrosion fabric, comprises the following steps:
A) make waterproof layer, PVC powder is dissolved in oil-based solvent, obtains PVC solution;Under conditions of temperature is 50 °
PVC solution is stirred;By the PVC solution left standstill deaeration after stirring, pour PUR and elastic fiber into, import spray webbing and set
Standby, then, by solution slow cooling in 60 DEG C of warm water of mixing, after taking-up, at a temperature of 120 DEG C-130 DEG C, it is dried place
Reason, strikes off with scraper plate, and then using longitude and latitude woven fabric, longitude and latitude number of share of stock ratio is 2: 1, forms fabric.
B) prepare burlap layer, pure hemp weaving is woven into the size of needs;
C) prepare anti-corrosion layer, aqueous polyurethane anti-flaming dope is sufficiently stirred for, rise viscous, when viscosity reaches the feelings of room temperature 50 DEG C
When viscosity number is 500-600pa.s under condition, adds fire-retardant polyurethane, stir simultaneously, stop when viscosity number reaches 200pa.s
Only stirring, after mixed solution is cooled to room temperature, strikes off with scraper plate, dries it under 120-150 DEG C of temperature conditions;
D) prepare contact layer, select viscose fiber as warp, make parallel with mint fibers and bamboo carbon fiber, use 14 to combine
Frame one, along wearing, uses 14*14 alternative construction intertexture rule, floats long alternate by longitude and latitude, forms fabric, dry
In the environment of temperature is 200 DEG C, dry 2 min.
E) connect, waterproof layer, burlap layer, anti-corrosion layer and contact layer sizing are bonded together.
Beneficial effects of the present invention: the one of the present invention grows flax waterproof anticorrosion fabric, overcomes that tradition fabric washability is poor, resists
The drawbacks such as electrostatic capacity is weak, dress is not easypro, non-watertight, thus expanded the development space that fabric is broader, and functional tool
There is good environmental protection characteristic, production operation safety and final products are nontoxic, have no side effect and good function persistency.
Detailed description of the invention
For the technological means making the present invention realize, creation characteristic, reach purpose and be easy to understand with effect, below in conjunction with
Detailed description of the invention, is expanded on further the present invention.
The present invention provides a kind of technical scheme: one grows flax waterproof anticorrosion fabric, including waterproof layer, burlap layer, corrosion resistant
Erosion layer and contact layer, waterproof layer is made up of PVC, PUR and elastic fiber, and wherein the mass ratio of PVC is 20-30%, heat
The mass ratio of melten gel is 10-20%, and the mass ratio of elastic fiber is 50-60%.
Burlap layer is made up of pure hemp weaving;Anti-corrosion layer is made up of aqueous polyurethane anti-flaming dope and fire-retardant polyurethane, its
The mass ratio of middle aqueous polyurethane anti-flaming dope is 30-40%, and the mass ratio of fire-retardant polyurethane is 60-70%.
Contact layer is made up of bamboo carbon fiber, mint fibers and viscose fiber, and wherein the mass ratio of bamboo carbon fiber is 50-65%,
The mass ratio of mint fibers is 25-40%, and the mass ratio of viscose fiber is 7-13%.
As one embodiment of the present of invention: the present invention provides a kind of technique making Caulis et Folium Lini waterproof anticorrosion fabric, bag
Include following steps:
A) make waterproof layer, PVC powder is dissolved in oil-based solvent, obtains PVC solution;Under conditions of temperature is 50 °
PVC solution is stirred;By the PVC solution left standstill deaeration after stirring, pour PUR and elastic fiber into, import spray webbing and set
Standby, then, by solution slow cooling in 60 DEG C of warm water of mixing, after taking-up, at a temperature of 120 DEG C-130 DEG C, it is dried place
Reason, strikes off with scraper plate, and then using longitude and latitude woven fabric, longitude and latitude number of share of stock ratio is 2: 1, forms fabric.
B) prepare burlap layer, pure hemp weaving is woven into the size of needs;
C) prepare anti-corrosion layer, aqueous polyurethane anti-flaming dope is sufficiently stirred for, rise viscous, when viscosity reaches the feelings of room temperature 50 DEG C
When viscosity number is 500-600pa.s under condition, adds fire-retardant polyurethane, stir simultaneously, stop when viscosity number reaches 200pa.s
Only stirring, after mixed solution is cooled to room temperature, strikes off with scraper plate, dries it under 120-150 DEG C of temperature conditions;
D) prepare contact layer, select viscose fiber as warp, make parallel with mint fibers and bamboo carbon fiber, use 14 to combine
Frame one, along wearing, uses 14*14 alternative construction intertexture rule, floats long alternate by longitude and latitude, forms fabric, dry
In the environment of temperature is 200 DEG C, dry 2 min.
E) connect, waterproof layer, burlap layer, anti-corrosion layer and contact layer sizing are bonded together, wherein waterproof layer
Covering the outer surface at burlap layer, burlap layer covers the outer surface at anti-corrosion layer, and anti-corrosion layer covers the appearance at contact layer
Face.
As an alternative embodiment of the invention: the present invention provides a kind of technique making Caulis et Folium Lini waterproof anticorrosion fabric,
Comprise the following steps:
A) make waterproof layer, PVC powder is dissolved in oil-based solvent, obtains PVC solution;Under conditions of temperature is 50 °
PVC solution is stirred;By the PVC solution left standstill deaeration after stirring, pour PUR and elastic fiber into, import spray webbing and set
Standby, then, by solution slow cooling in 60 DEG C of warm water of mixing, after taking-up, at a temperature of 120 DEG C-130 DEG C, it is dried place
Reason, strikes off with scraper plate, and then using longitude and latitude woven fabric, longitude and latitude number of share of stock ratio is 2: 1, forms fabric.
B) prepare burlap layer, pure hemp weaving is woven into the size of needs;
C) prepare anti-corrosion layer, aqueous polyurethane anti-flaming dope is sufficiently stirred for, rise viscous, when viscosity reaches the feelings of room temperature 50 DEG C
When viscosity number is 500-600pa.s under condition, adds fire-retardant polyurethane, stir simultaneously, stop when viscosity number reaches 200pa.s
Only stirring, after mixed solution is cooled to room temperature, strikes off with scraper plate, dries it under 120-150 DEG C of temperature conditions;
D) prepare contact layer, select viscose fiber as warp, make parallel with mint fibers and bamboo carbon fiber, use 14 to combine
Frame one, along wearing, uses 14*14 alternative construction intertexture rule, floats long alternate by longitude and latitude, forms fabric, dry
In the environment of temperature is 200 DEG C, dry 2 min.
E) connect, waterproof layer, burlap layer, anti-corrosion layer and contact layer sizing are bonded together, wherein waterproof layer
Covering the outer surface at anti-corrosion layer, anti-corrosion layer covers the outer surface at burlap layer, and burlap layer covers the appearance at contact layer
Face.
The ultimate principle of the present invention and principal character and advantages of the present invention are more than shown and described, for this area skill
For art personnel, it is clear that the invention is not restricted to the details of above-mentioned one exemplary embodiment, and without departing substantially from the present invention spirit or
In the case of basic feature, it is possible to realize the present invention in other specific forms.Therefore, no matter from the point of view of which point, all should be by
Embodiment regards exemplary as, and is nonrestrictive, the scope of the present invention by claims rather than on state
Bright restriction, it is intended that include all changes fallen in the implication of equivalency and scope of claim in the present invention
In.
Although moreover, it will be appreciated that this specification is been described by according to embodiment, but the most each embodiment only wraps
Containing an independent technical scheme, this narrating mode of description is only that for clarity sake those skilled in the art should
Description can also be formed those skilled in the art through appropriately combined as an entirety, the technical scheme in each embodiment
May be appreciated other embodiments.