CN108085814A - A kind of flaxen fiber and synthetic fibers mixed yarn and preparation method thereof - Google Patents

A kind of flaxen fiber and synthetic fibers mixed yarn and preparation method thereof Download PDF

Info

Publication number
CN108085814A
CN108085814A CN201810147123.6A CN201810147123A CN108085814A CN 108085814 A CN108085814 A CN 108085814A CN 201810147123 A CN201810147123 A CN 201810147123A CN 108085814 A CN108085814 A CN 108085814A
Authority
CN
China
Prior art keywords
synthetic fibers
flaxen fiber
preparation
surfactant
mixed yarn
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810147123.6A
Other languages
Chinese (zh)
Inventor
郝新敏
刘辉
高明斋
张国君
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhan Hemp Biological Technology Co Ltd
Original Assignee
Wuhan Hemp Biological Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhan Hemp Biological Technology Co Ltd filed Critical Wuhan Hemp Biological Technology Co Ltd
Priority to CN201810147123.6A priority Critical patent/CN108085814A/en
Publication of CN108085814A publication Critical patent/CN108085814A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of flaxen fibers and synthetic fibers mixed yarn and preparation method thereof.The preparation method includes the following steps：(1) surface modification is carried out to flaxen fiber with surfactant I, obtains modified flaxen fiber；(2) surface modification is carried out to synthetic fibers with surfactant II, obtains modified synthetic fibers；(3) the modified flaxen fiber and the modified synthetic fibers are carried out blended obtaining the mixed yarn.In order to make up this deficiency of flaxen fiber, it is the best way that mixed yarn, which is made, using flaxen fiber of the present invention and the blended method of synthetic fibers.Synthetic fibers have softness, and Length Regularity is good, no staple fiber, no short flannel.The advantages of having gathered flaxen fiber using mixed yarn produced by the present invention, the shortcomings that improving synthetic fibers, therefore, it is preferred by, ornament that linen blended yarn increasingly becomes high-end dress ornament, bed necessaries towel.

Description

A kind of flaxen fiber and synthetic fibers mixed yarn and preparation method thereof
Technical field
The present invention relates to a kind of mixed yarns and preparation method thereof, and in particular to a kind of flaxen fiber and synthetic fibers mixed yarn and Its preparation method.
Background technology
Flaxen fiber easily plays electrostatic in blended, causes sticky tight in carding process due to having good quick-drying Weight, be not easy to comb, in rolls, into item, resultant yarn, to flaxen fiber and other synthetic fibers are blended brings difficulty.And in synthetic fibers, such as Terylene, nylon, acrylic fibers, polypropylene fibre etc. are since regain is low, and electrostatic is serious when blended, and easy roll banding, makes in combing and spinning It is difficult into spinning.Therefore, it is necessary to be modified to flaxen fiber and synthetic fibers, to prevent from generating showing for electrostatic in blending process As.To solve the problems, such as flaxen fiber and the blended adhesion of synthetic fibers, winding, solve technical problem, improve spinning yarn quality.
The content of the invention
The object of the present invention is to provide a kind of flaxen fibers and synthetic fibers mixed yarn and preparation method thereof.
The preparation method of a kind of flaxen fiber provided by the present invention and synthetic fibers mixed yarn, includes the following steps：
(1) surface modification is carried out to flaxen fiber with surfactant I, obtains modified flaxen fiber；
(2) surface modification is carried out to synthetic fibers with surfactant II, obtains modified synthetic fibers；
(3) the modified flaxen fiber and the modified synthetic fibers are carried out blended obtaining the mixed yarn.
In above-mentioned preparation method, the surfactant I can be alkyl sulfonic acid, alkyl phosphoric acid and ethoxylated amine in extremely Few one kind；
The alkyl sulfonic acid concretely dodecyl sodium sulfate；
The alkyl phosphoric acid concretely alkyl phenol ether phosphate；
The ethoxylated amine concretely ethoxylated fat race alkylamine.
In above-mentioned preparation method, the surfactant II can be at least one of fatty amine and quaternary ammonium salt；
The fatty amine concretely cruel amine of ethyoxyl bay or lauryl amine；
The quaternary ammonium salt concretely dodecyl benzyl dimethyl ammonium chloride or dodecyl trimethyl ammonium chloride.
In above-mentioned preparation method, the method that surface described in step (1) is modified is as follows：
The surfactant I is configured to the aqueous solution that mass percentage is 0.5%~5%, by the aqueous solution It is sprayed on the flaxen fiber, standing, the mass percentage of the aqueous solution concretely 3%.
In above-mentioned preparation method, the fiber crops are arranged to be sprayed again after loose condition (of surface), the surfactant I Aqueous solution sprays quality as the 5%~10% of the flaxen fiber quality, such as 8%；
The step that sprays carries out under conditions of relative humidity is 70%~80%, temperature is 25 DEG C~30 DEG C, such as exists Humidity is 75%, temperature carries out under conditions of being 25 DEG C；
When the time of the standing is small not less than 72.
In above-mentioned preparation method, the method that surface described in step (2) is modified is as follows：
The surfactant II is configured to the aqueous solution that mass percentage is 0.5%~5%, by the aqueous solution It is sprayed on the synthetic fibers, standing, the mass percentage of the aqueous solution concretely 4%.
In above-mentioned preparation method, the synthesis is arranged to be sprayed again after loose condition (of surface), the surfactant II aqueous solution sprays quality as the 2%~5% of the synthetic fibers quality, such as 4%；
The step that sprays carries out under conditions of relative humidity is 70%~80%, temperature is 25 DEG C~30 DEG C, such as exists Humidity is 75%, temperature carries out under conditions of being 25 DEG C；
When the time of the standing is small not less than 72.
In above-mentioned preparation method, the flaxen fiber can be hemp, china-hemp fibers, flax fiber, ramee and At least one of jute-kenaf fibres.
In above-mentioned preparation method, the synthetic fibers can be at least one of terylene, polyamide fibre, acrylic fibers and polypropylene fibre.
In above-mentioned preparation method, the mass ratio of the flaxen fiber and the synthetic fibers can be 20~80：80~20, such as 50：50.
The present invention also provides the flaxen fibers being prepared by the above method and synthetic fibers mixed yarn.
The present invention has the advantages that：
Flaxen fiber belongs to environmentally protective ecology natural fiber, and characteristic also has in addition to other natural fiber characteristics Natural antibacterial, skin care are kept a public place clean, shield ultraviolet radiation, moisture absorbing and sweat releasing, soft comfortable, absorption peculiar smell and wear-resisting etc. unique Can, have both the styles such as honorable graceful, simple and unadorned, natural practicality.But flaxen fiber is bent and torsion stiffness is big, Length Regularity Difference, staple fiber is more, and short fibre content is high, and cohesive force is small, and spinnability is poor, and fiber head end easily pops up yarn body, and filoplume is more, grows firmly. In order to make up this deficiency of flaxen fiber, it is best that mixed yarn, which is made, using the flaxen fiber of the present invention method blended with synthetic fibers Method.Synthetic fibers have softness, and Length Regularity is good, no staple fiber, no short flannel.Using mixed yarn collection produced by the present invention The advantages of having gathered flaxen fiber, the shortcomings that improving synthetic fibers, therefore, linen blended yarn, increasingly become high-end dress ornament, bed necessaries towel Quilt, ornament are preferred.
Specific embodiment
Experimental method used in following embodiments is conventional method unless otherwise specified.
The materials, reagents and the like used in the following examples is commercially available unless otherwise specified.
Embodiment 1,
(1) surface modification is carried out to china-hemp fibers
Dodecyl sodium sulfate is configured to the aqueous solution that mass percentage is 3%, is loose by china-hemp fibers arrangement Then the aqueous solution of above-mentioned preparation is sprayed on the surface of china-hemp fibers by state, the quality that sprays of aqueous solution is 8%, opposite When standing 72 is small in the environment of humidity is 75%, temperature is 25 DEG C.
(2) surface modification is carried out to terylene
The cruel amine of ethyoxyl bay is configured to the aqueous solution that mass percentage is 4%, it is loose condition (of surface) that terylene, which is arranged, Then the aqueous solution of above-mentioned preparation is sprayed on to the surface of terylene, the quality that sprays of aqueous solution is 4%, is in relative humidity 75%th, when standing 72 is small in the environment of temperature is 25 DEG C.
(3) it is blended
The above-mentioned china-hemp fibers being modified by surface and terylene are subjected to blended, the wherein mass ratio of china-hemp fibers and terylene For 50：50, condition is as follows：
A, environmental condition of spinning is as shown in table 1.
The spinning environmental condition of table 1
Sequence number Process Temperature Relative humidity
1 Blowing 22—33 70 ± 3%
2 Cotton carding 22—33 68 ± 3%
3 Drafting 22—33 70 ± 3%
4 Rove 22—33 70 ± 3%
5 Spun yarn 25—33 72 ± 3%
6 Winder 25—33 72 ± 3%
B, Yarn spinning method：
Technological process is：Blowing → cotton carding → drafting → rove → spun yarn → winder
The mixed yarn principle of china-hemp fibers and terylene is as shown in table 2.
The mixed yarn principle of 2 china-hemp fibers of table and terylene
The quality index of mixed yarn manufactured in the present embodiment is as shown in table 3.
The quality index of 3 mixed yarn of table
The sliver evenness coefficient of variation of mixed yarn that it can be seen from the data in table 3 prepared by the present invention is good, single thread Fracture strength is high, stronger bacteriostasis property and fungicidal properties.

Claims (10)

1. the preparation method of a kind of flaxen fiber and synthetic fibers mixed yarn, includes the following steps：
(1) surface modification is carried out to flaxen fiber with surfactant I, obtains modified flaxen fiber；
(2) surface modification is carried out to synthetic fibers with surfactant II, obtains modified synthetic fibers；
(3) the modified flaxen fiber and the modified synthetic fibers are carried out blended obtaining the mixed yarn.
2. preparation method according to claim 1, it is characterised in that：The surfactant I is alkyl sulfonic acid, alkyl phosphorus At least one of acid and ethoxylated amine.
3. preparation method according to claim 1 or 2, it is characterised in that：The surfactant II is fatty amine and season At least one of ammonium salt.
4. preparation method according to any one of claim 1-3, it is characterised in that：Surface described in step (1) is modified Method it is as follows：
The surfactant I is configured to the aqueous solution that mass percentage is 0.5%~5%, the aqueous solution is sprayed In on the flaxen fiber, standing.
5. preparation method according to claim 4, it is characterised in that：By the flaxen fiber arrange for after loose condition (of surface) again into Row sprays, and the aqueous solution of the surfactant I sprays quality as the 5%~10% of the flaxen fiber quality；
The step that sprays carries out under conditions of relative humidity is 70%~80%, temperature is 25 DEG C~30 DEG C；
When the time of the standing is small not less than 72.
6. according to the preparation method any one of claim 1-5, it is characterised in that：Surface described in step (2) is modified Method it is as follows：
The surfactant II is configured to the aqueous solution that mass percentage is 0.5%~5%, the aqueous solution is sprayed In on the synthetic fibers, standing.
7. preparation method according to claim 6, it is characterised in that：By the synthetic fibers arrange for after loose condition (of surface) again It is sprayed, the aqueous solution of the surfactant II sprays quality as the 2%~5% of the synthetic fibers quality；
The step that sprays carries out under conditions of relative humidity is 70%~80%, temperature is 25 DEG C~30 DEG C；
When the time of the standing is small not less than 72.
8. according to the preparation method any one of claim 1-7, it is characterised in that：The flaxen fiber for hemp, At least one of china-hemp fibers, flax fiber, ramee and jute-kenaf fibres；
The synthetic fibers are at least one of terylene, polyamide fibre, polypropylene fibre and acrylic fibers.
9. according to the preparation method any one of claim 1-8, it is characterised in that：The flaxen fiber and the synthesis are fine The mass ratio of dimension is 20~80：80~20.
10. mixed yarn prepared by method any one of claim 1-9.
CN201810147123.6A 2018-02-12 2018-02-12 A kind of flaxen fiber and synthetic fibers mixed yarn and preparation method thereof Pending CN108085814A (en)