CN107326656A - A kind of antibacterial window curtain fabric and preparation method thereof - Google Patents
A kind of antibacterial window curtain fabric and preparation method thereof Download PDFInfo
- Publication number
- CN107326656A CN107326656A CN201710399053.9A CN201710399053A CN107326656A CN 107326656 A CN107326656 A CN 107326656A CN 201710399053 A CN201710399053 A CN 201710399053A CN 107326656 A CN107326656 A CN 107326656A
- Authority
- CN
- China
- Prior art keywords
- fabric
- parts
- antibacterial
- window curtain
- curtain fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of antibacterial window curtain fabric and preparation method thereof, the antibacterial window curtain fabric is formed by mixed knit of fiber of following parts by weight：30 50 parts of cotton fibers, 20 40 parts of polyacrylonitrile fibres, 10 20 parts of bamboo fibres, 10 20 parts of acetate fibers；Above-mentioned fabric is added into 24 parts of antiseptic processing while finishing process in printing and dye-ing.Microcapsule method is used in Final finishing antimicrobial treatment, can during fabric Final finishing by antiseptic it is more efficient be diffused into fiber surface, the anti-microbial property of fabric is more stablized.The antibacterial window curtain fabric of the present invention has good mould proof, mothproof, anti-microbial property, and the characteristics of its stability is high also causes curtain more durable in itself.
Description
Technical field
The invention belongs to field of textile, and in particular to a kind of antibacterial window curtain fabric and preparation method thereof.
Background technology
With the development of society, the raising of living standards of the people, the curtain that traditional fabric is made can not be fully met
The need for people's daily life.The textile fabric being made up of fiber, due to its porous type body form and high molecular polymer
Chemical constitution beneficial to microorganism adhere to, easily become microbe survival, breeding good parasitic body.And parasitic body is except to people
Fiber can be also polluted outside the harm of body, so Curtain suspension device is long to produce peculiar smell because of bacterium, and busy people may be simultaneously
There is no the time often to be cleaned to this kind of ornament of curtain, releasing one kind can keep clean and tidy, can eliminate and be produced because of bacterium
Peculiar smell the curtain that is made of antibiotic facing material it is just imperative.
In microorganism field, the effect for killing microbial nutrition body and brood body is called sterilization, prevents or suppresses micro- life
The effect of thing growth and breeding is called antibacterial, and antibacterial is antibacterial and bactericidal action general name.Antibiotic facing material is a kind of with good
Security, can efficiently remove bacterium, fungi and the mould on fabric completely, keep clean fabric, and bacterium can be prevented again
Raw and breeding fabric.
The content of the invention
There is excellent mould proof, mothproof, anti-microbial property window curtain fabric and its system it is an object of the invention to provide a kind of
Preparation Method.
To achieve the above object, technical scheme is as follows：
A kind of antibacterial window curtain fabric, is formed by mixed knit of the fiber of following parts by weight：30-50 parts of cotton fibers, 20-40 parts poly- third
Alkene nitrile fiber, 10-20 parts of bamboo fibres, 10-20 parts of acetate fibers；Above-mentioned fabric is added 2-4 parts while finishing process in printing and dye-ing
Antiseptic processing.
The antiseptic is nano silver-supported antibacterial finishing agent.
The preparation method of above-mentioned antibacterial window curtain fabric, comprises the following steps：
Step 1) the fiber carded sliver is made in the fibrous raw material of each component, by each fiber carded sliver is on gilling machine and closes, it is made
Ripe bar, drawing-off and twisting are carried out by ripe bar on fly frame, then are made after spinning frame, bobbin-winding machine, doubling frame, twisting machine mixed
Spinning, is finally made fabric using the woven method of rapier loom weft insertion；
Step 2) microcapsules are made in antiseptic, the microcapsules and coating agent are mixed and made into antibiotic finishing solution, will be walked
It is rapid 1) made from fabric be placed at normal temperatures in the antibiotic finishing solution impregnate；
Step 3) by step 2) in the fabric of dipping be dehydrated, dried at a temperature of 100 DEG C, the obtained antibacterial curtain
Fabric.
The coating agent is aqueous solution type polyacrylate.
It is preferred that, the time impregnated under normal temperature in antibiotic finishing solution is 30-40 minutes.
The antibacterial window curtain fabric of the present invention has good mould proof, mothproof, anti-microbial property, using new Final finishing antibacterial
Method --- microcapsule method, can during fabric Final finishing by antiseptic it is more efficient be diffused into fiber surface, make the anti-of fabric
Bacterium performance is more stablized.The window curtain fabric of the present invention is by washing anti-microbial property test, it was demonstrated that the fabric is by repeatedly washing
Anti-microbial property is still protruded afterwards.Not only there is good anti-microbial property using curtain made from fabric of the present invention, it is stable
The characteristics of property is high also causes curtain more durable in itself.
Embodiment
With reference to embodiment, the embodiment to the present invention is further described.Following examples are only used for more
Plus technical scheme is clearly demonstrated, and can not be limited the scope of the invention with this.
Embodiment 1
1st, 30 parts of cotton fibers, 30 parts of polyacrylonitrile fibres, 10 parts of bamboo fibres, 10 parts of acetate fibers are taken to carry out by weight pre-
Processing, the fiber carded sliver is made by the fibrous raw material of each component, by the fiber carded sliver is in gilling machine and closes, and ripe bar is made, by ripe bar
Drawing-off and twisting in coarse sand maker are placed in, spinning frame, bobbin-winding machine, doubling frame, twisting machine are sequentially passed through afterwards, mixed yarn is made, most
Fabric is made with wefting insertion hatching on rapier loom afterwards.
2nd, take 2 parts of nano silver-carrying antiseptics that microcapsules are made by weight, by microcapsules and the polyacrylic acid of aqueous solution type
Ester (coating agent) is mixed and made into antibacterial finishing agent, and above-mentioned fabric is placed under normal temperature (20 DEG C or so) in antibacterial finishing agent and impregnated
30 minutes, impregnated fabric is carried out being dried at a temperature of dewater treatment, last 100 DEG C afterwards, antibacterial curtain face is made
Material.
Embodiment 2
1st, 50 parts of cotton fibers, 40 parts of polyacrylonitrile fibres, 20 parts of bamboo fibres, 20 parts of acetate fibers are taken to carry out by weight pre-
Processing, the fiber carded sliver is made by the fibrous raw material of each component, by the fiber carded sliver is in gilling machine and closes, and ripe bar is made, by ripe bar
Drawing-off and twisting in coarse sand maker are placed in, spinning frame, bobbin-winding machine, doubling frame, twisting machine are sequentially passed through afterwards, mixed yarn is made, most
Fabric is made with wefting insertion hatching on rapier loom afterwards.
2nd, take 4 parts of nano silver-carrying antiseptics that microcapsules are made by weight, by microcapsules and the polyacrylic acid of aqueous solution type
Ester (coating agent) is mixed and made into antibacterial finishing agent, and above-mentioned fabric is placed under normal temperature (20 DEG C or so) in antibacterial finishing agent and impregnated
40 minutes, impregnated fabric is carried out being dried at a temperature of dewater treatment, last 100 DEG C afterwards, antibacterial curtain face is made
Material.
Embodiment 3
1st, 40 parts of cotton fibers, 30 parts of polyacrylonitrile fibres, 15 parts of bamboo fibres, 15 parts of acetate fibers are taken to carry out by weight pre-
Processing, the fiber carded sliver is made by the fibrous raw material of each component, by the fiber carded sliver is in gilling machine and closes, and ripe bar is made, by ripe bar
Drawing-off and twisting in coarse sand maker are placed in, spinning frame, bobbin-winding machine, doubling frame, twisting machine are sequentially passed through afterwards, mixed yarn is made, most
Fabric is made with wefting insertion hatching on rapier loom afterwards.
2nd, take 3 parts of nano silver-carrying antiseptics that microcapsules are made by weight, by microcapsules and the polyacrylic acid of aqueous solution type
Ester (coating agent) is mixed and made into antibacterial finishing agent, and above-mentioned fabric is placed under normal temperature (20 DEG C or so) in antibacterial finishing agent and impregnated
35 minutes, impregnated fabric is carried out being dried at a temperature of dewater treatment, last 100 DEG C afterwards, antibacterial curtain face is made
Material.
Test case 1
After antibacterial window curtain fabric made from embodiment 1-3 is washed 30 times, using the Chinese people's republicanisms of FZ/T01021-92
State's textile industry standard, fabric anti-interference bacterium method for testing performance carries out antibiotic property test, and test result refers to table 1.
The bacteriostasis rate of table 1 tests table
Claims (5)
1. a kind of antibacterial window curtain fabric, it is characterised in that formed by mixed knit of the fiber of following parts by weight：30-50 parts of cotton fibers,
20-40 parts of polyacrylonitrile fibres, 10-20 parts of bamboo fibres, 10-20 parts of acetate fibers；By above-mentioned fabric in the same of finishing process in printing and dye-ing
When add 2-4 part antiseptics and handle.
2. a kind of antibacterial window curtain fabric according to claim 1, it is characterised in that the antiseptic is nano silver-supported antibacterial
Finishing agent.
3. based on the preparation method of the antibacterial window curtain fabric described in claim 1, comprise the following steps：
Step 1) the fiber carded sliver is made in the fibrous raw material of each component, by each fiber carded sliver is on gilling machine and closes, ripe bar is made,
Ripe bar is subjected to drawing-off and twisting on fly frame, then mixed yarn is made after spinning frame, bobbin-winding machine, doubling frame, twisting machine,
Fabric is finally made using the woven method of rapier loom weft insertion；
Step 2) microcapsules are made in antiseptic, the microcapsules and coating agent are mixed and made into antibiotic finishing solution, by step 1)
Obtained fabric is placed in the antibiotic finishing solution at normal temperatures to be impregnated；
Step 3) by step 2) in the fabric of dipping be dehydrated, dried at a temperature of 100 DEG C, the obtained antibacterial curtain face
Material.
4. a kind of preparation method of antibacterial window curtain fabric according to claim 3, it is characterised in that step 2) described in apply
Layer agent is aqueous solution type polyacrylate.
5. a kind of preparation method of antibacterial window curtain fabric according to claim 3, it is characterised in that step 2) under normal temperature
The time impregnated in antibiotic finishing solution is 30-40 minutes.