CN101319422A - Production method of jhouta and dacron blended yarn - Google Patents

Production method of jhouta and dacron blended yarn Download PDF

Info

Publication number
CN101319422A
CN101319422A CNA2008101243908A CN200810124390A CN101319422A CN 101319422 A CN101319422 A CN 101319422A CN A2008101243908 A CNA2008101243908 A CN A2008101243908A CN 200810124390 A CN200810124390 A CN 200810124390A CN 101319422 A CN101319422 A CN 101319422A
Authority
CN
China
Prior art keywords
jute
spinning
comb
fibre
yarn
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2008101243908A
Other languages
Chinese (zh)
Inventor
孙道宽
严其明
季东岳
顾维康
孙亮晶
张兆奎
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
RUGAO RUXING TEXTILE CO Ltd
Original Assignee
RUGAO RUXING TEXTILE CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by RUGAO RUXING TEXTILE CO Ltd filed Critical RUGAO RUXING TEXTILE CO Ltd
Priority to CNA2008101243908A priority Critical patent/CN101319422A/en
Publication of CN101319422A publication Critical patent/CN101319422A/en
Pending legal-status Critical Current

Abstract

The invention discloses a method for producing the blended spinning of jute and terylene. The method comprises the following steps that: firstly, the jute is added with 10 percent of water and 5 percent of softener and preheated for 24 hours; the jute and the terylene are picked up according to a proportion and subjected to the working procedures of scutching, cotton carding, drawing, coarse spinning, fine spinning, and cheese winding; in the step of cotton carding, the striking times is 480 rmp and the carding time is twice; when impurities in the jute and chemical fibre are treated, a cotton-type sieve for cotton carding is A86C; a separation degree of the fibre is between 1.2 and 0.7 tex; in the step of coarse spinning, the twisting number of coarse yarn is between 80 and 85; and in the step of fine spinning, a relative humidity of fine yarn is between 65 and 70 percent. A jute product produced by adopting the technology changes the weakness of coarseness and hardness of jute fibre, improves the spinnability and softness of the fibre and has small production pollution.

Description

The production method of a kind of jute, dacron blended yarn
Technical field
The present invention relates to a kind of production method of blended yarn.Be specifically related to the production method of a kind of jute, the mixed yarn of terylene.
Background technology
Jute articles for use tool friction resistant, humidity absorption and release is fast, antibacterial, expelling parasite, anticorrosion, characteristics such as degradable are the first-selections of good grain, food, vegetables packing material.But at present the jute process technology falls behind, and exists in the production process such as living fiber crops to soak problems such as the higher and cleaner production degree of water environment pollution, the contained mineral oil of ripe retting emulsion in district is low.
Summary of the invention
The invention provides the production method of a kind of jute, the mixed yarn of terylene.
In order to solve above technical problem, the production method of a kind of jute of the present invention, dacron blended yarn, jute and terylene are got material in proportion, carry out scutching cotton, comb and parallel cotton fibers prior to spinning, drafting then, spin rove, spin spun yarn, winding procedure, its innovative point is: before above-mentioned operation, earlier jute is carried out preliminary treatment, during preliminary treatment jute added 10% water and added 5% softener preliminary treatment 24 hours; In the described comb and parallel cotton fibers prior to spinning step, 480 rev/mins, divide comb 2 times, during impurity in handling jute and chemical fibre, comb and parallel cotton fibers prior to spinning is A86C with the cotton type leakage end, the separating degree of fiber is 1.2tex-0.7tex; Described spinning in the rove step, the twisting count of rove is 80-85; The described relative humidity of spinning spun yarn in the spun yarn step is 65%-70%.
The advantage of above technology is: the jute products that adopts this technology to produce, changed the thick and stiff weakness of tossa, and improve the spinnability and the pliability of fiber, improve the added value of tossa; And the production of this technology is polluted little.
The specific embodiment
Earlier jute is carried out preliminary treatment, during preliminary treatment jute added 10% water and added 5% softener preliminary treatment 24 hours.
Get 45% jute and 55% terylene, put and carry out following processing on the scutcher:
After blowing finishes, enter the combing program, in this program, to carry out combing through the jute of blowing and the mixture of terylene, and, use comb and parallel cotton fibers prior to spinning to be A86C with the cotton type leakage end in order to make the impurity in jute and the chemical fibre still less residual, in this process, the separating degree that makes fiber is 1.2tex-0.7tex.Concrete operations are as shown in the table:
Fiber through combing enters the drafting program, and strip adoption three draftings, adopts the A272F drawing frame, finishes drafting work by following required precision operation to machinery:
Carry out slubbing after drafting finishes, in rove spinning process, adopt 81.3 low twisting count, finish by other relevant parameters are controlled in the following value:
Next be spun yarn spinning process, the relative humidity of spun yarn is 65%-70% in this process, and it is as shown in the table for other parameters:
Last winder, after winding procedure finished, the yarn finished product formed.

Claims (1)

1, the production method of a kind of jute, dacron blended yarn, jute and terylene are got material in proportion, carry out scutching cotton, comb and parallel cotton fibers prior to spinning, drafting then, spin rove, spin spun yarn, winding procedure, it is characterized in that: before above-mentioned operation, earlier jute is carried out preliminary treatment, during preliminary treatment jute added 10% water and added 5% softener preliminary treatment 24 hours; In the described comb and parallel cotton fibers prior to spinning step, 480 rev/mins of cycles divide comb 2 times, and during impurity in handling jute and chemical fibre, comb and parallel cotton fibers prior to spinning is A86C with the cotton type leakage end, and the separating degree of fiber is 1.2tex-0.7tex; Described spinning in the rove step, the twisting count of rove is 80-85; The described relative humidity of spinning spun yarn in the spun yarn step is 65%-70%.
CNA2008101243908A 2008-07-14 2008-07-14 Production method of jhouta and dacron blended yarn Pending CN101319422A (en)