CN103243436A - Bamboo fiber and terylene blended yarn - Google Patents
Bamboo fiber and terylene blended yarn Download PDFInfo
- Publication number
- CN103243436A CN103243436A CN2013101912062A CN201310191206A CN103243436A CN 103243436 A CN103243436 A CN 103243436A CN 2013101912062 A CN2013101912062 A CN 2013101912062A CN 201310191206 A CN201310191206 A CN 201310191206A CN 103243436 A CN103243436 A CN 103243436A
- Authority
- CN
- China
- Prior art keywords
- yarn
- terylene
- blended yarn
- bamboo fibre
- test
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a bamboo fiber and terylene blended yarn which contains components of 2D*51mm bamboo fibers and 2D*51mm terylene with weight ratio to be 1:1. According to the bamboo fiber and terylene blended yarn, characteristics of bamboo fibers and terylene are relatively complemented and advantages of bamboo fibers and terylene are fully developed.
Description
Technical field
The present invention relates to the blended yarn of a kind of bamboo fibre and terylene, belong to the spinning engineering field.
Background technology
At present, the development trend of international clothes is " Machine Washable, wash and wear, easy maintenance, crease-resistant, uvioresistants, mothproof ", and traditional pure spinning as single varieties such as cotton textiles, pure wools all more or less exists such-and-such deficiency, brought the defective in the design.
Blended yarn is the yarn that is spun into by two or more fiber, as fiber crops/cotton, hair/cotton, hair/fiber crops/thin,tough silk, wash/cotton, wash/hair etc., broken the boundary between original cotton, fiber crops, hair, silk, the chemical fibre, can remedy the deficiency of single certain textile material, embody the superiority of each component fibre, to improve the einnehmen function of fabric, enlarge the scope of application.
Summary of the invention
The objective of the invention is to overcome the deficiencies in the prior art part, the blended yarn of a kind of bamboo fibre and terylene is provided.
The blended yarn of bamboo fibre of the present invention and terylene comprises following ingredients: the bamboo fibre of 2D*51mm and 2D*51mm terylene, its weight ratio is for being 1:1.
The blended yarn of bamboo fibre of the present invention and terylene with the advantage complementation of bamboo fibre and terylene, is brought into play both advantages.
The specific embodiment
" the spinning experiment study course " that test method in the present embodiment is all edited with reference to the Yang Suoting that in July, 2007, China Textiles Press published.
Embodiment 1
Bamboo fibre in the present embodiment and the blended yarn of terylene comprise following ingredients: the bamboo fibre of 2D*51mm and 2D*51mm terylene, its weight ratio is for being 1:1.
The production method step is as follows:
(1) blowing: the mixed raw materials dimension is made volume by scutcher;
(2) comb and parallel cotton fibers prior to spinning: will roll into the carded sliver by carding machine;
(3) drafting: the carded sliver is merged ripe bar by drawing frame;
(4) rove: stretching oneself and yawn to attenuate for ripe that will merge by Speed frames becomes the rove bar;
(5) spun yarn: rove is stretched oneself and yawn yarn into certain number by fine spining machine;
(6) winder: by bobbin winder with spinning volume cheese coning;
(7) the packing finished product blended yarn of weighing.
Embodiment 2
The yarn property of the bamboo fibre of detection embodiment 1 and the blended yarn of terylene.
1) yarn linear density test
The line density of yarn is one of yarn most important characteristic index, and it directly has influence on fabric property and appearance style, as stiffness, gloss, lines, ABRASION RESISTANCE etc.
The bamboo fibre of embodiment 1 and the blended yarn of terylene are carried out the yarn linear density test.Its test result is as follows:
Table 1 yarn linear density result of the test
| Project | Embodiment 1 |
| Yarn linear density (tex) | 19.7 |
2) yarn strength test
The end breakage rate of operation was closely related under yarn strength and this operation reached, and was the important references index that product waited and evaluated the spun yarn quality surely.
The bamboo fibre of embodiment 1 and the blended yarn of terylene are carried out the yarn strength test.Its test result such as following table:
Table 2 yarn strength result of the test
| Project | Embodiment 1 |
| Yarn strength (N) | 550 |
3) yarn twist test
Yarn twist is to weigh an important parameter of yarn qualities, and what of yarn twist directly influence outward appearance and many physical properties of performance such as the brute force, ABRASION RESISTANCE, weight, elasticity, filoplume, shrinkage of yarn and product.
The bamboo fibre of embodiment 1 and the blended yarn of terylene are carried out the yarn twist test.Its test result such as following table:
Table 3 yarn twist result of the test
| Project | Embodiment 1 |
| Yarn twist 10CM/ | 75 |
4) irregularity test
Bar evenness is the important indicator of evaluation yarn qualities, whether the thickness of bar evenness reflection yarn is consistent, this numerical value is more big, yarn is more inhomogeneous with regard to thickness so, directly influence outward appearance uniformity, durability of fabric etc., and the superfine place of the yarn twist concentrates intensity to descend, and brings many difficulties for the processing of later process, as winder, weave in broken end and stop platform and increase.
The bamboo fibre of embodiment 1 and the blended yarn of terylene are carried out the yarn evenness test.Its test result such as following table:
Table 4 yarn Ubbelohde irregularity test result
From table 1 to table 4 as can be seen, the blended yarn of bamboo fibre of the present invention and terylene has good yarn property.
Claims (1)
1. the blended yarn of a bamboo fibre and terylene is characterized in that, comprises following ingredients: the bamboo fibre of 2D*51mm and 2D*51mm terylene, its weight ratio is for being 1:1.