CN103266377A - Cationic dacron-cotton fiber blended yarn - Google Patents
Cationic dacron-cotton fiber blended yarn Download PDFInfo
- Publication number
- CN103266377A CN103266377A CN2013101925310A CN201310192531A CN103266377A CN 103266377 A CN103266377 A CN 103266377A CN 2013101925310 A CN2013101925310 A CN 2013101925310A CN 201310192531 A CN201310192531 A CN 201310192531A CN 103266377 A CN103266377 A CN 103266377A
- Authority
- CN
- China
- Prior art keywords
- cotton fiber
- yarn
- cation terylene
- blended yarn
- fiber blended
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a cationic dacron-cotton fiber blended yarn. The cationic dacron-cotton fiber blended yarn comprises the following components, by weight percentage, 55-65 percent of 2.2D*38mm cationic dacron and 35-45 percent of cotton fibers. By means of the cationic dacron-cotton fiber blended yarn, the advantages of the cationic dacron and the advantages of the cotton fibers are complemented and exerted.
Description
Technical field
The present invention relates to a kind of CATION terylene cotton fiber mixed yarn, belong to the spinning engineering field.
Background technology
At present, the development trend of international clothes is " Machine Washable, wash and wear, easily maintenances, lightening ", and traditional pure spinning as single varieties such as cotton textiles, pure wools all more or less exists such-and-such deficiency, brought the defective in the design.
Blended yarn is the yarn that is spun into by two or more fiber, as fiber crops/cotton, hair/cotton, hair/fiber crops/thin,tough silk, wash/cotton, wash/hair etc., broken the boundary between original cotton, fiber crops, hair, silk, the chemical fibre, can remedy the deficiency of single certain textile material, embody the superiority of each component fibre, to improve the einnehmen function of fabric, enlarge the scope of application.
Summary of the invention
The objective of the invention is to overcome the deficiencies in the prior art part, a kind of CATION terylene cotton fiber mixed yarn is provided.
CATION terylene cotton fiber mixed yarn of the present invention comprises following ingredients according to percentage by weight: the CATION terylene 55-65% of 2.2D*38mm and cotton fiber 35-45%.
Described CATION terylene cotton fiber mixed yarn comprises following ingredients according to percentage by weight: the CATION terylene 60% of 2.2D*38mm and cotton fiber 40%.
CATION terylene cotton fiber mixed yarn of the present invention with the advantage complementation of CATION terylene and cotton fiber, is brought into play both advantages.
The specific embodiment
" the spinning experiment study course " that test method in the present embodiment is all edited with reference to the Yang Suoting that in July, 2007, China Textiles Press published.
Embodiment 1
In the present embodiment, CATION terylene cotton fiber mixed yarn comprises following ingredients according to percentage by weight: the CATION terylene 60% of 2.2D*38mm and cotton fiber 40%.
The production method step is as follows:
(1) blowing: the raw material dimension is made two kinds of volumes by scutcher;
(2) comb and parallel cotton fibers prior to spinning: two kinds of volumes are made the carded sliver respectively by carding machine;
(3) drafting: the different carded slivers is merged ripe bar by drawing frame;
(4) rove: stretching oneself and yawn to attenuate for ripe that will merge by Speed frames becomes the rove bar;
(5) spun yarn: rove is stretched oneself and yawn yarn into certain number by fine spining machine;
(6) winder: by bobbin winder with spinning volume cheese coning;
(7) the packing finished product cationic polyester synthetic fibre cotton fiber mixed yarn of weighing.
Embodiment 2
In the present embodiment, CATION terylene cotton fiber mixed yarn comprises following ingredients according to percentage by weight: the CATION terylene 55% of 2.2D*38mm and cotton fiber 45%.
The production method step is identical with embodiment 1.
Embodiment 3
In the present embodiment, CATION terylene cotton fiber mixed yarn comprises following ingredients according to percentage by weight: the CATION terylene 65% of 2.2D*38mm and cotton fiber 35%.
The production method step is identical with embodiment 1.
Reference examples 1
In this reference examples, CATION terylene cotton fiber mixed yarn comprises following ingredients according to percentage by weight: the CATION terylene 40% of 2.2D*38mm, cotton fiber 60%.
The production method step is identical with embodiment 1.
Reference examples 2
In this reference examples, CATION terylene cotton fiber mixed yarn comprises following ingredients according to percentage by weight: the CATION terylene 70% of 2.2D*38mm, cotton fiber 30%.
The production method step is identical with embodiment 1.
Embodiment 4
The yarn property of 1~2 CATION terylene cotton fiber mixed yarn of comparing embodiment 1~3 and reference examples.
1) yarn linear density test
The line density of yarn is one of yarn most important characteristic index, and it directly has influence on fabric property and appearance style, as stiffness, gloss, lines, ABRASION RESISTANCE etc.
1~2 CATION terylene cotton fiber mixed yarn that obtains to embodiment 1~3 and reference examples carries out the yarn linear density test.Its test result such as following table:
Table 1 yarn linear density experimental control table
Project | Embodiment 1 | Embodiment 2 | Embodiment 3 | Reference examples 1 | Reference examples 2 |
Yarn linear density (tex) | 21 | 21 | 21 | 21 | 21 |
2) yarn strength test
The end breakage rate of operation was closely related under yarn strength and this operation reached, and was the important references index that product waited and evaluated the spun yarn quality surely.
1~2 CATION terylene cotton fiber mixed yarn that obtains to embodiment 1~3 and reference examples carries out the yarn strength test.Its test result such as following table:
Table 2 yarn strength experimental control table
Project | Embodiment 1 | Embodiment 2 | Embodiment 3 | Reference examples 1 | Reference examples 2 |
Yarn strength (N) | 490 | 520 | 550 | 450 | 590 |
3) yarn twist test
Yarn twist is to weigh an important parameter of yarn qualities, and what of yarn twist directly influence outward appearance and many physical properties of performance such as the brute force, ABRASION RESISTANCE, weight, elasticity, filoplume, shrinkage of yarn and product.
1~2 CATION terylene cotton fiber mixed yarn that obtains to embodiment 1~3 and reference examples carries out the yarn twist test.Its test result such as following table:
Table 3 yarn twist experimental control table
Project | Embodiment 1 | Embodiment 2 | Embodiment 3 | Reference examples 1 | Reference examples 2 |
Yarn twist 10CM/ | 62 | 62 | 62 | 62 | 62 |
4) irregularity test
Bar evenness is the important indicator of evaluation yarn qualities, whether the thickness of bar evenness reflection yarn is consistent, this numerical value is more big, yarn is more inhomogeneous with regard to thickness so, directly influence outward appearance uniformity, durability of fabric etc., and the superfine place of the yarn twist concentrates intensity to descend, and brings many difficulties for the processing of later process, as winder, weave in broken end and stop platform and increase.
1~2 CATION terylene cotton fiber mixed yarn that obtains to embodiment 1~3 and reference examples carries out the yarn evenness test.Its test result such as following table:
The table 4 yarn Ubbelohde irregularity test table of comparisons
From table 1 to table 4 as can be seen, CATION terylene cotton fiber mixed yarn of the present invention has better yarn property with respect to existing CATION terylene cotton fiber mixed yarn.
Claims (2)
1. a CATION terylene cotton fiber mixed yarn is characterized in that, comprises following ingredients according to percentage by weight: the CATION terylene 55-65% of 2.2D*38mm and cotton fiber 35-45%.
2. CATION terylene cotton fiber mixed yarn according to claim 1 is characterized in that, comprises following ingredients according to percentage by weight: the CATION terylene 60% of 2.2D*38mm and cotton fiber 40%.