CN108085117A - Concrete emulsion release agents - Google Patents

Concrete emulsion release agents Download PDF

Info

Publication number
CN108085117A
CN108085117A CN201711332734.XA CN201711332734A CN108085117A CN 108085117 A CN108085117 A CN 108085117A CN 201711332734 A CN201711332734 A CN 201711332734A CN 108085117 A CN108085117 A CN 108085117A
Authority
CN
China
Prior art keywords
parts
release agents
water
refers
reducing agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711332734.XA
Other languages
Chinese (zh)
Inventor
张会平
冯月娥
芮雪
吕锦辉
杨泽来
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GANSU ZHITONG SCIENCE & TECHNOLOGY ENGINEERING DETECTION CONSULTATION Co Ltd
Gansu Road and Bridge Construction Group Co Ltd
Original Assignee
GANSU ZHITONG SCIENCE & TECHNOLOGY ENGINEERING DETECTION CONSULTATION Co Ltd
Gansu Road and Bridge Construction Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GANSU ZHITONG SCIENCE & TECHNOLOGY ENGINEERING DETECTION CONSULTATION Co Ltd, Gansu Road and Bridge Construction Group Co Ltd filed Critical GANSU ZHITONG SCIENCE & TECHNOLOGY ENGINEERING DETECTION CONSULTATION Co Ltd
Priority to CN201711332734.XA priority Critical patent/CN108085117A/en
Publication of CN108085117A publication Critical patent/CN108085117A/en
Pending legal-status Critical Current

Abstract

The present invention relates to a kind of concrete emulsion release agents, the releasing agent be by the reacted kettle of raw material of following weight parts stir evenly and made of：700 ~ 900 parts of industrial soap lotion, 200 ~ 400 parts of water, 500 ~ 600 parts of miscella, 125 ~ 180 parts of organic siliconresin, 2.0 ~ 3.0 parts of water-reducing agent, 10 ~ 20 parts of emulsifier, 35 ~ 45 parts of preservative.Environmental protection and energy saving of the present invention are pollution-free, at low cost, while functional, can effectively shorten the maintenance demoulding cycle, and raise speed duration progress, applied widely.

Description

Concrete emulsion release agents
Technical field
The present invention relates to a kind of releasing agent more particularly to concrete emulsion release agents.
Background technology
Concrete parting agent is also known as concrete isolation agent, is sprayed at its lubrication of concrete blinding inner wall and buffer action, makes Form removal is smooth.Concrete parting agent is broadly divided into seven classes, is respectively：Pure oils releasing agent, emulsification oils releasing agent, saponification oils Releasing agent, paraffin class and metal soap releasing agent, chemism releasing agent, paint class releasing agent and synthetic resin releasing agent. And pure oils releasing agent is also easy to produce greasy dirt, has certain influence to concrete surface and inherent quality；Using soaps releasing agent, although It is cheap but easily putrid and deteriorated after storage, and concrete surface shedding can be caused more serious；Use paint class and synthetic fat Class releasing agent can cause coating damage to be not easy coating and clear mould difficulty.Emulsification oils releasing agent demoulding effect currently on the market Preferably, but function is single, is unfavorable for storing for a long time.
The content of the invention
The technical problems to be solved by the invention are to provide a kind of at low cost, working performance and are well easy to industrialized production Concrete emulsion release agents.
To solve the above problems, concrete emulsion release agents of the present invention, it is characterised in that：The releasing agent be by The reacted kettle of raw material of following weight parts stirs evenly and manufactured：700 ~ 900 parts of industrial soap lotion, 200 ~ 400 parts of water, mixing 500 ~ 600 parts of oil, 125 ~ 180 parts of organic siliconresin, 2.0 ~ 3.0 parts of water-reducing agent, 10 ~ 20 parts of emulsifier, 35 ~ 45 parts of preservative.
The solid content of the industrial soap lotion is 2.2% ~ 3.5%.
The miscella refers to decolourize one or more of used oil, diesel oil, silicone oil, vegetable oil.
The organic silicon resin refers to industrial grade resins.
The water-reducing agent refers to amidosulfonic acid salt water-reducing agent or aliphatic high-efficiency water reducing agent.
The emulsifier refers to the two or more mixtures in OP-10, AEO-9, CR260U, sorbester p17, Tween 80.
The preservative refers to one or more of sodium benzoate, potassium sorbate, calcium propionate.
The present invention has the following advantages compared with prior art：
1st, raw material of the present invention are easy to get, are formulated reasonable and easy to process, and environmental protection and energy saving are pollution-free, at low cost, it is easy to accomplish industry Metaplasia is produced.
2nd, added with miscella and industrial soap type of latex type in the present invention, therefore, working performance is good, can effectively shorten maintenance The cycle is demoulded, raise speed duration progress；Meanwhile it is easy to the demoulding, irrelevant arrisdefect etc..
3rd, added with organic siliconresin in the present invention, therefore, surface of concrete structure has certain waterproof, anti-Cl-, resists The performance of ultraviolet light and with gas permeability.It can effectively prevent base material due to the erosion of infiltration, sunshine, acid rain and seawater to concrete And the burn into of internal bar construction is loose, the lesion peeling off, go mouldy and trigger, improves the service life of concrete.
4th, slurries viscosity at template face can be reduced added with water-reducing agent in the present invention, reduces surface tension, be conducive to The exclusion of interior formwork.
5th, properties of product of the present invention are stablized, and can store for a long time, not stratified to never degenerate.
Specific embodiment
1 concrete emulsion release agents of embodiment, which is by following weight parts（kg）The reacted kettle of raw material stir It mixes uniform and manufactured：700 parts of industrial soap lotion, 200 parts of water, 550 parts of miscella, 125 parts of organic siliconresin, water-reducing agent 2.0 Part, 10 parts of emulsifier, 35 parts of preservative.
Wherein：The solid content of industrial soap lotion is 2.2%.
Miscella refers to decolourize used oil, vegetable oil by 5：3 weight ratio mixes.
Organic silicon resin refers to industrial grade resins.
Water-reducing agent refers to amidosulfonic acid salt water-reducing agent.
Emulsifier refers to OP-10, Tween 80 by 2：1 weight ratio mixes.
Preservative refers to sodium benzoate.
2 concrete emulsion release agents of embodiment, which is by following weight parts（kg）The reacted kettle of raw material stir It mixes uniform and manufactured：750 parts of industrial soap lotion, 280 parts of water, 500 parts of miscella, 150 parts of organic siliconresin, water-reducing agent 3.0 Part, 13 parts of emulsifier, 40 parts of preservative.
Wherein：The solid content of industrial soap lotion is 2.5%.
Miscella refers to decolourize used oil, diesel oil, vegetable oil by 2:1:1 weight ratio mixes.
Organic silicon resin refers to industrial grade resins.
Water-reducing agent refers to amidosulfonic acid salt water-reducing agent.
Emulsifier refers to OP-10, AEO-9, Tween 80 by 2:1:1 weight ratio mixes.
Preservative refers to potassium sorbate, calcium propionate by 1：1 weight ratio mixes.
3 concrete emulsion release agents of embodiment, which is by following weight parts（kg）The reacted kettle of raw material stir It mixes uniform and manufactured：800 parts of industrial soap lotion, 320 parts of water, 540 parts of miscella, 140 parts of organic siliconresin, water-reducing agent 2.5 Part, 15 parts of emulsifier, 38 parts of preservative.
Wherein：The solid content of industrial soap lotion is 2.8%.
Miscella refers to silicone oil, vegetable oil by 2:1 weight ratio mixes.
Organic silicon resin refers to industrial grade resins.
Water-reducing agent refers to aliphatic high-efficiency water reducing agent.
Emulsifier refers to OP-10, sorbester p17, Tween 80 by 1:1:1 weight ratio mixes.
Preservative refers to sodium benzoate, potassium sorbate by 1:1 weight ratio mixes.
4 concrete emulsion release agents of embodiment, which is by following weight parts（kg）The reacted kettle of raw material stir It mixes uniform and manufactured：850 parts of industrial soap lotion, 330 parts of water, 570 parts of miscella, 160 parts of organic siliconresin, water-reducing agent 2.0 Part, 16 parts of emulsifier, 35 parts of preservative.
Wherein：The solid content of industrial soap lotion is 3.2%.
Miscella refers to decolourize used oil, diesel oil, silicone oil, vegetable oil by 3:2:1:1 weight ratio mixes.
Organic silicon resin refers to industrial grade resins.
Water-reducing agent refers to amidosulfonic acid salt water-reducing agent.
Emulsifier refers to OP-10, sorbester p17, Tween 80 by 2:1:1 weight ratio mixes.
Preservative refers to sodium benzoate, potassium sorbate, calcium propionate by 1:1:1 weight ratio mixes.
5 concrete emulsion release agents of embodiment, which is by following weight parts（kg）The reacted kettle of raw material stir It mixes uniform and manufactured：800 parts of industrial soap lotion, 300 parts of water, 5600 parts of miscella, 150 parts of organic siliconresin, water-reducing agent 3.0 Part, 15 parts of emulsifier, 35 parts of preservative.
Wherein：The solid content of industrial soap lotion is 3.0%.
Miscella refers to decolourize used oil, diesel oil by 2:1 weight ratio mixes.
Organic silicon resin refers to industrial grade resins.
Water-reducing agent refers to aliphatic high-efficiency water reducing agent.
Emulsifier refers to sorbester p17, Tween 80 by 2:1 weight ratio mixes.
Preservative refers to calcium propionate.
6 concrete emulsion release agents of embodiment, which is by following weight parts（kg）The reacted kettle of raw material stir It mixes uniform and manufactured：900 parts of industrial soap lotion, 400 parts of water, 600 parts of miscella, 180 parts of organic siliconresin, water-reducing agent 2.8 Part, 20 parts of emulsifier, 45 parts of preservative.
Wherein：The solid content of industrial soap lotion is 3.5%.
Miscella refers to vegetable oil.
Organic silicon resin refers to industrial grade resins.
Water-reducing agent refers to aliphatic high-efficiency water reducing agent.
Emulsifier refers to OP-10, CR260U, Tween 80 by 2:1:1 weight ratio mixes.
Preservative refers to sodium benzoate, calcium propionate by 1:1 weight ratio mixes.
7 concrete emulsion release agents of embodiment, which is by following weight parts（kg）The reacted kettle of raw material stir It mixes uniform and manufactured：860 parts of industrial soap lotion, 360 parts of water, 580 parts of miscella, 155 parts of organic siliconresin, water-reducing agent 2.8 Part, 18 parts of emulsifier, 43 parts of preservative.
Wherein：The solid content of industrial soap lotion is 3.3%.
Miscella refers to diesel oil, silicone oil by 5:3 weight ratio mixes.
Organic silicon resin refers to industrial grade resins.
Water-reducing agent refers to amidosulfonic acid salt water-reducing agent.
Emulsifier refers to AEO-9, CR260U by 2:1 weight ratio mixes.
Preservative refers to sodium benzoate.

Claims (7)

1. concrete emulsion release agents, it is characterised in that：The releasing agent is the reacted kettle stirring of raw material by following weight parts It is uniform and manufactured：700 ~ 900 parts of industrial soap lotion, 200 ~ 400 parts of water, 500 ~ 600 parts of miscella, organic siliconresin 125 ~ 180 parts, 2.0 ~ 3.0 parts of water-reducing agent, 10 ~ 20 parts of emulsifier, 35 ~ 45 parts of preservative.
2. concrete emulsion release agents as described in claim 1, it is characterised in that：The solid content of the industrial soap lotion is 2.2%~3.5%。
3. concrete emulsion release agents as described in claim 1, it is characterised in that：The miscella refers to the useless machine that decolourizes One or more of oil, diesel oil, silicone oil, vegetable oil.
4. concrete emulsion release agents as described in claim 1, it is characterised in that：The organic silicon resin refers to industry Grade resins.
5. concrete emulsion release agents as described in claim 1, it is characterised in that：The water-reducing agent refers to amidosulfonic acid salt Water-reducing agent or aliphatic high-efficiency water reducing agent.
6. concrete emulsion release agents as described in claim 1, it is characterised in that：The emulsifier refers to OP-10, AEO- 9th, the two or more mixtures in CR260U, sorbester p17, Tween 80.
7. concrete emulsion release agents as described in claim 1, it is characterised in that：The preservative refer to sodium benzoate, One or more of potassium sorbate, calcium propionate.
CN201711332734.XA 2017-12-13 2017-12-13 Concrete emulsion release agents Pending CN108085117A (en)