CN108032592A - A kind of energy saving, insulation, fire prevention and facing decorative integrated plate and preparation method - Google Patents

A kind of energy saving, insulation, fire prevention and facing decorative integrated plate and preparation method Download PDF

Info

Publication number
CN108032592A
CN108032592A CN201711374065.2A CN201711374065A CN108032592A CN 108032592 A CN108032592 A CN 108032592A CN 201711374065 A CN201711374065 A CN 201711374065A CN 108032592 A CN108032592 A CN 108032592A
Authority
CN
China
Prior art keywords
proof
fire
lower plywood
sandwich layer
outside lower
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711374065.2A
Other languages
Chinese (zh)
Inventor
徐振飞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201711374065.2A priority Critical patent/CN108032592A/en
Publication of CN108032592A publication Critical patent/CN108032592A/en
Pending legal-status Critical Current

Abstract

The invention belongs to a kind of energy saving, insulation, fire prevention and facing decorative integrated plate and preparation method；Including outside lower plywood, intermediate core layer and inner crest face layer, the outside of outside lower plywood is equipped with finish coat, the first adhesive linkage is equipped between outside lower plywood and intermediate core layer, intermediate core layer includes several sandwich layer bars, is connected between the upper surface of sandwich layer bar and adjacent sandwich layer bar by the second adhesive linkage with inner crest face layer；The outside lower plywood is one of high-strength fabric cement plate, high-strength calcium silicate board, stone material or ceramic tile；The sandwich layer bar is inorganic incombustible material, its thermal conductivity factor is 0.006~0.035W/ (M.K)；The material of sandwich layer bar is one of unorganic glass sliver, rock wool, aeroge thermal insulation board or vacuum heat-insulating plate；With can realize exterior-wall heat insulation, finish coat integrated construction, the advantages of saving of work and time.

Description

A kind of energy saving, insulation, fire prevention and facing decorative integrated plate and preparation method
Technical field
The invention belongs to energy-saving building material technical field, and in particular to a kind of energy saving, insulation, fire prevention and facing decorative integrated plate And preparation method.
Background technology
Wall heat insulation technical measures at present, are substantially kept the temperature using external labeling type, and mostly combustable organic material, are deposited In long in time limit, of high cost, easy to crack, easy to fall off, organic material easy firing, produce the critical defects such as public safety hidden danger, CCTV The high buildings such as big fire fire is suffered from, and the insulating layer of external wall to take place frequently comes off the tragedy hurted sb.'s feelings, it is sufficient to the drawbacks of illustrating conventional vacuum technology. The sandwich class integration heat preservation technology system promoted, because cost is high, construction is difficult, and it is big to promote and apply difficulty；In the prior art Have the materials such as rock wool and cement slurry Material cladding, buckling deformation, easily occurs in this composite insulation boards poor mechanical property, easily inhales Water causes heat-insulating property to decline, and this thermal insulation board complex manufacturing technology, and cement slurry material needs to solidify maintenance during making It can dispatch from the factory within 28 days, cause the production cycle to be grown, occupancy factory site is big, and commercial production level is low, and investment and production cost are larger； Adhesive temperature tolerance is poor used in composite board in the prior art, generally 100 degree or so；Also there is high-temperature resistance adhesive, but not Water-fast, interlaminar separation after water logging, produces security risk.
The content of the invention
The defects of it is an object of the invention to overcome in the prior art and provide a kind of more work(purposes, thermal conductivity factor it is small, It can not only be used for insulation to use but also as non-dismantling formwork, and have facing decorative effect；Using continuous production, industrialized production water Flat height；Do not crack, do not fall off in the application, fire safety, durable use；Cost is low, shortens the construction period, reduces hand labor Intensity and the energy saving of economy, insulation, fire prevention and facing decorative integrated plate and preparation method.
The object of the present invention is achieved like this：Including outside lower plywood, intermediate core layer and inner crest face layer, outside lower floor The outside of plate is equipped with finish coat, and the first adhesive linkage is equipped between outside lower plywood and intermediate core layer, and intermediate core layer includes several Sandwich layer bar, is connected between the upper surface of sandwich layer bar and adjacent sandwich layer bar by the second adhesive linkage with inner crest face layer；It is described outer Side lower plywood is one of high-strength fabric cement plate, high-strength calcium silicate board, stone material or ceramic tile；The sandwich layer bar is inorganic not fuel wood Material, its thermal conductivity factor is 0.006~0.035W/ (M.K)；The material of sandwich layer bar is unorganic glass sliver, rock wool, aeroge guarantor One of warm plate or vacuum heat-insulating plate；The inner crest face layer for high-strength fabric cement plate, high-strength calcium silicate board, cement roll felt-cloth or One of metal coiled material；First adhesive linkage is one of fire-proof and water-proof foamed glue or modified polyurethane hard bubble；Second bonding Layer is one of fire-proof and water-proof foamed glue or modified polyurethane hard bubble.
Preferably, the distance between described adjacent sandwich layer bar is 0mm~50mm.
Preferably, the unorganic glass sliver for forward cotton fiber cross section slitting, the thickness of slitting for 20mm~ 80mm, width are 60mm~300mm；The thickness of rock wool is 20mm~80mm, and width is 60mm~800mm；Aeroge thermal insulation board Thickness be 10mm~30mm, width is 300mm~1200mm；The thickness of vacuum heat-insulating plate is 2mm~20mm, and width is 300mm~1200mm.
Preferably, the thickness of the outside lower plywood is 5mm~15mm.
Present invention also offers a kind of energy saving, insulation, fire prevention and the preparation method of facing decorative integrated plate, its preparation method Including three kinds；
A kind of one of preparation method of energy saving, insulation, fire prevention and facing decorative integrated plate, includes the following steps：
Step 1：Prepare fire-proof and water-proof foamed glue, fire-proof and water-proof foamed glue by following raw materials according according to parts by weight prepare and Into：10~50 parts of polyphenylene polyphenyl cyanate, 20~120 parts of polyalcohol, 0.5~10 part of curing agent, solid melamine 3 ~30 parts and inorganic 1~20 part of ammonium polyphosphate；Its preparation method is：Polyalcohol is placed in dispensing containers, then to configuration Polyphenylene polyphenyl cyanate, solid melamine, inorganic ammonium polyphosphate and curing agent are sequentially added in container, is then stirred Mix, stir 10~50 minutes；The curing agent is one of polyisocyanate or tertiary amines curing agent；
Step 2：Outside lower plywood is placed on the crawler belt of thermal insulation board continuous producing apparatus conveying device, crawler belt is synchronous Mobile, outside lower plywood is delivered to gluing station by lower crawler belt, and the inside upper surface of outside lower plywood is sprayed by glue spreader Fire-proof and water-proof foamed glue or modified polyurethane hard bubble described in step 1, need to pass through thermal insulation board when environment temperature is less than 15 DEG C The heating unit set in production equipment heats it, and heating and temperature control is in 15 DEG C~60 DEG C；
Step 3：Outside lower plywood after gluing is delivered to intermediate core layer and is laid with filling station, on the outside lower plywood Upper surface is laid with sandwich layer bar, adjacent sandwich layer made of unorganic glass sliver, rock wool, aeroge thermal insulation board or vacuum heat-insulating plate The distance between bar is 0mm~50mm；
Step 4：Between sandwich layer bar upper surface, adjacent sandwich layer bar to laying and inner crest face layer lower surface sprays Fire-proof and water-proof foamed glue described in step 1, with being bonded as one after gluing, is made semi-finished product integrated board；The inner crest face Layer is cement roll felt-cloth；
Step 5：In thermal insulation board continuous producing apparatus conveying device by the semi-finished product integrated board described in step 4 according to After common process method carries out pressing, extrusion operation to plate, cutting work station is delivered to, the ruler of needs is cut into by cutter device It is very little, you can.
A kind of energy saving, insulation, fire prevention and the two of the preparation method of facing decorative integrated plate, include the following steps：
Step 1：Prepare fire-proof and water-proof foamed glue, fire-proof and water-proof foamed glue by following raw materials according according to parts by weight prepare and Into：10~50 parts of polyphenylene polyphenyl cyanate, 20~120 parts of polyalcohol, 0.5~10 part of curing agent, solid melamine 3 ~30 parts and inorganic 1~20 part of ammonium polyphosphate；Its preparation method is：Polyalcohol is placed in dispensing containers, then to configuration Polyphenylene polyphenyl cyanate, solid melamine, inorganic ammonium polyphosphate and curing agent are sequentially added in container, is then stirred Mix, stir 10~50 minutes；The curing agent is one of polyisocyanate or tertiary amines curing agent；
Step 2：Outside lower plywood is placed on the crawler belt of thermal insulation board continuous producing apparatus conveying device, crawler belt is synchronous Mobile, outside lower plywood is delivered to gluing station by lower crawler belt, and the inside upper surface of outside lower plywood is sprayed by glue spreader Fire-proof and water-proof foamed glue or modified polyurethane hard bubble described in step 1, need to pass through thermal insulation board when environment temperature is less than 15 DEG C The heating unit set in production equipment heats it, and heating and temperature control is in 15 DEG C~60 DEG C；
Step 3：Outside lower plywood after gluing is delivered to intermediate core layer and is laid with filling station, on the outside lower plywood Upper surface is laid with sandwich layer bar, adjacent sandwich layer made of unorganic glass sliver, rock wool, aeroge thermal insulation board or vacuum heat-insulating plate The distance between bar is 0mm~50mm；
Step 4：Between sandwich layer bar upper surface, adjacent sandwich layer bar to laying and inner crest face layer lower surface sprays Modified polyurethane hard bubble, then makes inner crest face layer by modified polyurethane hard bubble and intermediate core layer compound sticking, be made half into Product integrated board；The inner crest face layer for high-strength fabric cement plate, high-strength calcium silicate board, cement roll felt-cloth or metal coiled material it One；
Step 5：It is in thermal insulation board continuous producing apparatus conveying device that the semi-finished product integrated board described in step 4 is continuous Cutting work station is delivered to, the size of needs is cut into by cutter device, you can.
A kind of energy saving, insulation, fire prevention and the three of the preparation method of facing decorative integrated plate, include the following steps：
Step 1：Prepare fire-proof and water-proof foamed glue, fire-proof and water-proof foamed glue by following raw materials according according to parts by weight prepare and Into：10~50 parts of polyphenylene polyphenyl cyanate, 20~120 parts of polyalcohol, 0.5~10 part of curing agent, solid melamine 3~ 30 parts and inorganic 1~20 part of ammonium polyphosphate；Its preparation method is：Polyalcohol is placed in dispensing containers, is then held to configuration Polyphenylene polyphenyl cyanate, solid melamine, inorganic ammonium polyphosphate and curing agent are sequentially added in device, is then stirred Mix, stir 10~50 minutes；The curing agent is one of polyisocyanate or tertiary amines curing agent；
Step 2：Outside lower plywood is placed on pre-fabricated template frame, using glue sprayer on the outside in lower plywood Fire-proof and water-proof foamed glue or modified polyurethane hard bubble described in side upper surface spraying process one, by manually on glue-line be laid with by Unorganic glass sliver, rock wool, aeroge thermal insulation board or sandwich layer bar made of vacuum heat-insulating plate are simultaneously bonded, adjacent sandwich layer bar The distance between be 0mm~50mm；
Step 3：Sprayed fire proofing waterproof foamed glue sprays between sandwich layer bar upper surface and adjacent sandwich layer bar to laying Fire-proof and water-proof foamed glue described in step 1, and inner crest face layer is placed at the top of fire-proof and water-proof foamed glue and is bonded, Semi-finished product integrated board is made；The inner crest face layer is high-strength fabric cement plate, high-strength calcium silicate board, cement roll felt-cloth or metal One of coiled material；
Step 4：Semi-finished product integrated board is made by above-mentioned steps one and step 2 in a manner of laminating on mould bases, extremely Semi-finished product integrated board carries out curing molding after building long-pending to 15~25 layers, and the temperature of the curing molding is outdoor environment temperature, Gu Changing the molding time is：1h~5h；
Step 5：Semi-finished product integrated board after above-mentioned curing molding is layered using hanging device and is seated in thermal insulation board In the conveying device of production equipment, continuous conveying to cutting work station, the sizes of needs is cut into by cutter device, you can.
The invention has the advantages that：
1st, insulated fire and building enclosure, facing decorative integrated plate continuous production.Completely eliminate operating environment and work The uncertainty that people brings, insulation overcome that existing craft batch production efficiency is low, quality is nonstandard with facing decorative integrated plate Deficiency, stable quality, production capacity lifting.
2nd, the present invention can realize exterior-wall heat insulation, finish coat integrated construction, have the characteristics that saving of work and time.The present invention's Product makes suitable for batch production, assembling installation, makes the outer powder of wall thermal insulating, metope, the live Integral synchronous shape of exterior finish decoration Into construction efficiency is high, short time limit, and expense is greatly lowered, reduces projects field management difficulty, have compressed the duration.
3rd, the present invention disclosure satisfy that national higher energy conservation standard.The product insulating layer of the present invention is thin, and excellent performance, warp Authoritative institution's detection thermal conductivity factor is only between 0.006~0.034W/ (M.K), can meet national higher energy conservation standard completely It is required that.
4th, product fire-proof and water-proof performance of the invention is good, through authoritative testing agency according to JG/T287-2013《Insulation and decoration Plate exterior wall external heat preservation system material》Testing result is：Fire protecting performance reaches the non-ignitable standards of A1；Anti-impact force reaches 10J standards；Draw Stretch adhesion strength original and reach 0.2Mpa by force, it is water-fast to reach 0.15Mpa by force；Bending resistance load reaches 2600N, and the regulation that is above standard will Ask.Heat insulating decorative board firmly installs at the same time, does not crack, does not fall off；Environmental protection index is through the detection of national testing agency better than country's mark Standard, is a kind of green, environment-friendly products, trusts occupant, is comfortable, the sorrow without any hidden danger, so as to significantly improve relaxing for house Appropriateness, enhances the market competitiveness in commercial residential buildings.
5th, standard preresearch estimates, same construction item are expended according to existing construction project ration standard and construction auxiliary material Mesh, uses existing routine techniques product, the duration can shorten half, and whole engineering comprehensive takes with the product ratio of the present invention Reduced with obvious, remarkable benefit increase.
6th, the present invention has the characteristics that insulation, fire-proof and water-proof, decoration and fire-retardant, and can realize it is energy saving, save land, protection ring Border, save building cost, mitigate construction worker labor intensity, energy saving overall working time and meet China's building materials simple function to The advantages of complex function type developing direction.
Brief description of the drawings
Fig. 1 is the structure diagram of the present invention.
Fig. 2 is another structure diagram of the present invention.
Embodiment
In order to which the technical features, objects and effects of the present invention are more clearly understood, now control illustrates this hair Bright embodiment, in the various figures identical label represent identical component.To make simplified form, in each figure only schematically Ground is indicated with inventing relevant part, they do not represent its practical structures as product.
As shown in Figure 1, 2, a kind of energy saving, insulation of the present invention, fire prevention and facing decorative integrated plate and preparation method, wherein, The integrated board includes outside lower plywood 1, intermediate core layer 2 and inner crest face layer 3, and the outside of outside lower plywood 1 is equipped with finish coat 4, The first adhesive linkage 5 is equipped between outside lower plywood 1 and intermediate core layer 2, intermediate core layer 2 includes several sandwich layer bars, sandwich layer bar It is connected between upper surface and adjacent sandwich layer bar by the second adhesive linkage 6 with inner crest face layer 3；The outside lower plywood 1 is height One of strong fiber cement board, high-strength calcium silicate board, stone material or ceramic tile；The sandwich layer bar is inorganic incombustible material, its thermal conductivity factor For 0.006~0.035W/ (M.K)；The material of sandwich layer bar is unorganic glass sliver, rock wool, aeroge thermal insulation board or vacuum insulation One of plate；The inner crest face layer 3 is one of high-strength fabric cement plate, high-strength calcium silicate board, cement roll felt-cloth or metal coiled material； First adhesive linkage 5 is one of fire-proof and water-proof foamed glue or modified polyurethane hard bubble；Second adhesive linkage 6 is fire-proof and water-proof One of foamed glue or modified polyurethane hard bubble.The distance between described adjacent sandwich layer bar is 0mm~50mm.The unorganic glass Sliver is the cross section slitting of forward cotton fiber, and the thickness of slitting is 20mm~80mm, and width is 60mm~300mm；Rock wool Thickness is 20mm~80mm, and width is 60mm~800mm；The thickness of aeroge thermal insulation board is 10mm~30mm, width 300mm ~1200mm；The thickness of vacuum heat-insulating plate is 2mm~20mm, and width is 300mm~1200mm.The thickness of the outside lower plywood 1 Spend for 5mm~15mm.
Present invention also offers a kind of energy saving, insulation, fire prevention and the preparation method of facing decorative integrated plate, its preparation method Including three kinds；
A kind of one of preparation method of energy saving, insulation, fire prevention and facing decorative integrated plate, includes the following steps：
Step 1：Prepare fire-proof and water-proof foamed glue, fire-proof and water-proof foamed glue by following raw materials according according to parts by weight prepare and Into：10~50 parts of polyphenylene polyphenyl cyanate, 20~120 parts of polyalcohol, 0.5~10 part of curing agent, solid melamine 3~ 30 parts and inorganic 1~20 part of ammonium polyphosphate；Its preparation method is：Polyalcohol is placed in dispensing containers, is then held to configuration Polyphenylene polyphenyl cyanate, solid melamine, inorganic ammonium polyphosphate and curing agent are sequentially added in device, is then stirred Mix, stir 10~50 minutes；The curing agent is one of polyisocyanate or tertiary amines curing agent；
Step 2：Outside lower plywood 1 is placed on the crawler belt of thermal insulation board continuous producing apparatus conveying device, crawler belt is synchronous Mobile, outside lower plywood 1 is delivered to gluing station by lower crawler belt, and the inside upper surface of outside lower plywood 1 is sprayed by glue spreader The fire-proof and water-proof foamed glue or modified polyurethane hard bubble described in step 1 are applied, need to pass through insulation when environment temperature is less than 15 DEG C The heating unit set in plate production equipment heats it, and heating and temperature control is in 15 DEG C~60 DEG C；
Step 3：Outside lower plywood 1 after gluing is delivered to intermediate core layer and is laid with filling station, on the outside lower plywood 1 Upper surface be laid with made of unorganic glass sliver, rock wool, aeroge thermal insulation board or vacuum heat-insulating plate sandwich layer bar, adjacent core The distance between layer bar is 0mm~50mm；
Step 4：Between sandwich layer bar upper surface, adjacent sandwich layer bar to laying and 3 lower surface of inner crest face layer sprays Fire-proof and water-proof foamed glue described in step 1, with being bonded as one after gluing, is made semi-finished product integrated board；The inner crest face Layer 3 is cement roll felt-cloth；
Step 5：In thermal insulation board continuous producing apparatus conveying device by the semi-finished product integrated board described in step 4 according to After common process method carries out pressing, extrusion operation to plate, cutting work station is delivered to, the ruler of needs is cut into by cutter device It is very little, you can.
A kind of energy saving, insulation, fire prevention and the two of the preparation method of facing decorative integrated plate, include the following steps：
Step 1：Prepare fire-proof and water-proof foamed glue, fire-proof and water-proof foamed glue by following raw materials according according to parts by weight prepare and Into：10~50 parts of polyphenylene polyphenyl cyanate, 20~120 parts of polyalcohol, 0.5~10 part of curing agent, solid melamine 3 ~30 parts and inorganic 1~20 part of ammonium polyphosphate；Its preparation method is：Polyalcohol is placed in dispensing containers, then to configuration Polyphenylene polyphenyl cyanate, solid melamine, inorganic ammonium polyphosphate and curing agent are sequentially added in container, is then stirred Mix, stir 10~50 minutes；The curing agent is one of polyisocyanate or tertiary amines curing agent；
Step 2：Outside lower plywood 1 is placed on the crawler belt of thermal insulation board continuous producing apparatus conveying device, crawler belt is synchronous Mobile, outside lower plywood 1 is delivered to gluing station by lower crawler belt, and the inside upper surface of outside lower plywood 1 is sprayed by glue spreader The fire-proof and water-proof foamed glue or modified polyurethane hard bubble described in step 1 are applied, need to pass through insulation when environment temperature is less than 15 DEG C The heating unit set in plate production equipment heats it, and heating and temperature control is in 15 DEG C~60 DEG C；
Step 3：Outside lower plywood 1 after gluing is delivered to intermediate core layer and is laid with filling station, on the outside lower plywood 1 Upper surface be laid with made of unorganic glass sliver, rock wool, aeroge thermal insulation board or vacuum heat-insulating plate sandwich layer bar, adjacent core The distance between layer bar is 0mm~50mm；
Step 4：Between sandwich layer bar upper surface, adjacent sandwich layer bar to laying and 3 lower surface of inner crest face layer sprays Modified polyurethane hard bubble, then makes inner crest face layer 3 be made half by modified polyurethane hard bubble and 2 compound sticking of intermediate core layer Finished product integrated board；The inner crest face layer 3 is high-strength fabric cement plate, high-strength calcium silicate board, cement roll felt-cloth or metal coiled material One of；
Step 5：It is in thermal insulation board continuous producing apparatus conveying device that the semi-finished product integrated board described in step 4 is continuous Cutting work station is delivered to, the size of needs is cut into by cutter device, you can.
A kind of energy saving, insulation, fire prevention and the three of the preparation method of facing decorative integrated plate, include the following steps：
Step 1：Prepare fire-proof and water-proof foamed glue, fire-proof and water-proof foamed glue by following raw materials according according to parts by weight prepare and Into：10~50 parts of polyphenylene polyphenyl cyanate, 20~120 parts of polyalcohol, 0.5~10 part of curing agent, solid melamine 3 ~30 parts and inorganic 1~20 part of ammonium polyphosphate；Its preparation method is：Polyalcohol is placed in dispensing containers, then to configuration Polyphenylene polyphenyl cyanate, solid melamine, inorganic ammonium polyphosphate and curing agent are sequentially added in container, is then stirred Mix, stir 10~50 minutes；The curing agent is one of polyisocyanate or tertiary amines curing agent；
Step 2：Outside lower plywood 1 is placed on pre-fabricated template frame, utilizes glue sprayer lower plywood 1 on the outside Fire-proof and water-proof foamed glue or modified polyurethane hard bubble described in inside upper surface spraying process one, by being manually laid with glue-line Sandwich layer bar and it is bonded, adjacent sandwich layer made of unorganic glass sliver, rock wool, aeroge thermal insulation board or vacuum heat-insulating plate The distance between bar is 0mm~50mm；
Step 3：Sprayed fire proofing waterproof foamed glue sprays between sandwich layer bar upper surface and adjacent sandwich layer bar to laying Fire-proof and water-proof foamed glue described in step 1, and inner crest face layer 3 is placed at the top of fire-proof and water-proof foamed glue and is bonded, Semi-finished product integrated board is made；The inner crest face layer 3 is high-strength fabric cement plate, high-strength calcium silicate board, cement roll felt-cloth or gold Belong to one of coiled material；
Step 4：Semi-finished product integrated board is made by above-mentioned steps one and step 2 in a manner of laminating on mould bases, extremely Semi-finished product integrated board carries out curing molding after building long-pending to 15~25 layers, and the temperature of the curing molding is outdoor environment temperature, Gu Changing the molding time is：1h~5h；
Step 5：Semi-finished product integrated board after above-mentioned curing molding is layered using hanging device and is seated in thermal insulation board In the conveying device of production equipment, continuous conveying to cutting work station, the sizes of needs is cut into by cutter device, you can.
Heretofore described fire-proof and water-proof foamed glue can not decompose in 300 degree or so of hot environment, and have With water-proof binding power it is strong the characteristics of；Heretofore described modified polyurethane hard bubble is patented product, wherein Patent No. 201620101185.X patent name is：A kind of low heat conduction A grades of non-ignitable sandwich thermal insulation boards, have in the 25th section of specification in detail Record, and number of patent application is：201610070856.9 patent of invention right requirement 1 in recorded related content.The present invention Described in outside lower plywood 1 be the finish coat with having made or generating naturally, unlike material and different color, stone Material or ceramic tile specifically refer to ultrathin lithotome, slim porcelain plate, sheet metal, fluorine carbon metal paint decorative panel, solid color enamel decoration Plate, imitative stone material, marble lacquer decorative panel or flexible porcelain tendre.Heretofore described tertiary amines curing agent include aliphatic tertiary amine and Aromatic nitrile base, aliphatic tertiary amine include triethylamine and triethanolamine etc., and aromatic nitrile base includes benzyl dimethylamine, methyl-benzyl Dimethylamine, DMP-10 and DMP-30 etc..Heretofore described polyisocyanate or tertiary amines curing agent can be direct in market Purchase.Heretofore described metal coiled material is aluminium sheet or color steel.Heretofore described fire-proof and water-proof foamed glue gathers with modified Urethane hard bubble can be replaced, but the first adhesive linkage 5 is preferably by fire-proof and water-proof foamed glue.
For the more detailed explanation present invention, the present invention is further elaborated in conjunction with embodiment.Specific embodiment It is as follows：
Embodiment one
A kind of energy saving, insulation, fire prevention and the preparation method of facing decorative integrated plate, include the following steps：
Step 1：Prepare fire-proof and water-proof foamed glue, fire-proof and water-proof foamed glue by following raw materials according according to parts by weight prepare and Into：10 parts of polyphenylene polyphenyl cyanate, 20 parts of polyalcohol, 0.5 part of curing agent, 3 parts of solid melamine and inorganic polyphosphoric acid 1 part of ammonium；Its preparation method is：Polyalcohol is placed in dispensing containers, poly- methylene is then sequentially added into dispensing containers and is gathered Phenylcyanate, solid melamine, inorganic ammonium polyphosphate and curing agent, are then stirred, and stir 10 minutes；It is described Curing agent is polyisocyanate；
Step 2：Outside lower plywood 1 is placed on the crawler belt of thermal insulation board continuous producing apparatus conveying device, crawler belt is synchronous Mobile, outside lower plywood 1 is delivered to gluing station by lower crawler belt, and the inside upper surface of outside lower plywood 1 is sprayed by glue spreader The fire-proof and water-proof foamed glue described in step 1 is applied, need to be by being set on equipment for producing heat preservation plate when environment temperature is less than 15 DEG C Heating unit it is heated, heating and temperature control is in 15 DEG C；
Step 3：Outside lower plywood 1 after gluing is delivered to intermediate core layer and is laid with filling station, on the outside lower plywood 1 Upper surface be laid with made of unorganic glass sliver, rock wool, aeroge thermal insulation board or vacuum heat-insulating plate sandwich layer bar, adjacent core The distance between layer bar is 0mm；
Step 4：It is anti-described in 3 lower surface spraying process one of sandwich layer bar upper surface and inner crest face layer to laying Fiery waterproof foamed glue, with being bonded as one after gluing, is made semi-finished product integrated board；The inner crest face layer 3 is cement roll felt-cloth；
Step 5：In thermal insulation board continuous producing apparatus conveying device by the semi-finished product integrated board described in step 4 according to After common process method carries out pressing, extrusion operation to plate, cutting work station is delivered to, the ruler of needs is cut into by cutter device It is very little, you can.
Embodiment two
A kind of energy saving, insulation, fire prevention and the preparation method of facing decorative integrated plate, include the following steps：
Step 1：Prepare fire-proof and water-proof foamed glue, fire-proof and water-proof foamed glue by following raw materials according according to parts by weight prepare and Into：50 parts of polyphenylene polyphenyl cyanate, 120 parts of polyalcohol, 10 parts of curing agent, 30 parts of solid melamine and inorganic polyphosphoric acid 20 parts of ammonium；Its preparation method is：Polyalcohol is placed in dispensing containers, poly- methylene is then sequentially added into dispensing containers and is gathered Phenylcyanate, solid melamine, inorganic ammonium polyphosphate and curing agent, are then stirred, and stir 30 minutes；It is described Curing agent is tertiary amines curing agent；
Step 2：Outside lower plywood 1 is placed on the crawler belt of thermal insulation board continuous producing apparatus conveying device, crawler belt is synchronous Mobile, outside lower plywood 1 is delivered to gluing station by lower crawler belt, and the inside upper surface of outside lower plywood 1 is sprayed by glue spreader Modified polyurethane hard bubble is applied, need to be by the heating unit that is set on equipment for producing heat preservation plate to it when environment temperature is less than 15 DEG C Heated, heating and temperature control is in 60 DEG C；
Step 3：Outside lower plywood 1 after gluing is delivered to intermediate core layer and is laid with filling station, on the outside lower plywood 1 Upper surface be laid with made of unorganic glass sliver, rock wool, aeroge thermal insulation board or vacuum heat-insulating plate sandwich layer bar, adjacent core The distance between layer bar is 50mm；
Step 4：Between sandwich layer bar upper surface, adjacent sandwich layer bar to laying and 3 lower surface of inner crest face layer sprays Fire-proof and water-proof foamed glue described in step 1, with being bonded as one after gluing, is made semi-finished product integrated board；The inner crest face Layer 3 is cement roll felt-cloth；
Step 5：In thermal insulation board continuous producing apparatus conveying device by the semi-finished product integrated board described in step 4 according to After common process method carries out pressing, extrusion operation to plate, cutting work station is delivered to, the ruler of needs is cut into by cutter device It is very little, you can.
Embodiment three
A kind of energy saving, insulation, fire prevention and the preparation method of facing decorative integrated plate, include the following steps：
Step 1：Prepare fire-proof and water-proof foamed glue, fire-proof and water-proof foamed glue by following raw materials according according to parts by weight prepare and Into：30 parts of polyphenylene polyphenyl cyanate, 70 parts of polyalcohol, 5.25 parts of curing agent, 16.5 parts of solid melamine and inorganic poly- 10.5 parts of ammonium phosphate；Its preparation method is：Polyalcohol is placed in dispensing containers, is then sequentially added into dispensing containers poly- Methylene polyphenylene cyanate, solid melamine, inorganic ammonium polyphosphate and curing agent, are then stirred, and stir 50 minutes i.e. Can；The curing agent is tertiary amines curing agent；
Step 2：Outside lower plywood 1 is placed on the crawler belt of thermal insulation board continuous producing apparatus conveying device, crawler belt is synchronous Mobile, outside lower plywood 1 is delivered to gluing station by lower crawler belt, and the inside upper surface of outside lower plywood 1 is sprayed by glue spreader The fire-proof and water-proof foamed glue described in step 1 is applied, need to be by being set on equipment for producing heat preservation plate when environment temperature is less than 15 DEG C Heating unit it is heated, heating and temperature control is in 37.5 DEG C；
Step 3：Outside lower plywood 1 after gluing is delivered to intermediate core layer and is laid with filling station, on the outside lower plywood 1 Upper surface be laid with made of unorganic glass sliver, rock wool, aeroge thermal insulation board or vacuum heat-insulating plate sandwich layer bar, adjacent core The distance between layer bar is 25mm；
Step 4：Between sandwich layer bar upper surface, adjacent sandwich layer bar to laying and 3 lower surface of inner crest face layer sprays Modified polyurethane hard bubble, with being bonded as one after gluing, is made semi-finished product integrated board；The inner crest face layer 3 is cement roll felt Cloth；
Step 5：In thermal insulation board continuous producing apparatus conveying device by the semi-finished product integrated board described in step 4 according to After common process method carries out pressing, extrusion operation to plate, cutting work station is delivered to, the ruler of needs is cut into by cutter device It is very little, you can.
Example IV
A kind of energy saving, insulation, fire prevention and the preparation method of facing decorative integrated plate, include the following steps：
Step 1：Prepare fire-proof and water-proof foamed glue, fire-proof and water-proof foamed glue by following raw materials according according to parts by weight prepare and Into：10 parts of polyphenylene polyphenyl cyanate, 20 parts of polyalcohol, 0.5 part of curing agent, 3 parts of solid melamine and inorganic polyphosphoric acid 1 part of ammonium；Its preparation method is：Polyalcohol is placed in dispensing containers, poly- methylene is then sequentially added into dispensing containers and is gathered Phenylcyanate, solid melamine, inorganic ammonium polyphosphate and curing agent, are then stirred, and stir 30 minutes；It is described Curing agent is polyisocyanate；
Step 2：Outside lower plywood 1 is placed on the crawler belt of thermal insulation board continuous producing apparatus conveying device, crawler belt is synchronous Mobile, outside lower plywood 1 is delivered to gluing station by lower crawler belt, and the inside upper surface of outside lower plywood 1 is sprayed by glue spreader The fire-proof and water-proof foamed glue described in step 1 is applied, need to be by being set on equipment for producing heat preservation plate when environment temperature is less than 15 DEG C Heating unit it is heated, heating and temperature control is in 60 DEG C；
Step 3：Outside lower plywood 1 after gluing is delivered to intermediate core layer and is laid with filling station, on the outside lower plywood 1 Upper surface be laid with made of unorganic glass sliver, rock wool, aeroge thermal insulation board or vacuum heat-insulating plate sandwich layer bar, adjacent core The distance between layer bar is 50mm；
Step 4：Between sandwich layer bar upper surface, adjacent sandwich layer bar to laying and 3 lower surface of inner crest face layer sprays Modified polyurethane hard bubble, then makes inner crest face layer 3 be made half by modified polyurethane hard bubble and 2 compound sticking of intermediate core layer Finished product integrated board；The inner crest face layer 3 is one of cement felt-cloth or metal coiled material；
Step 5：It is in thermal insulation board continuous producing apparatus conveying device that the semi-finished product integrated board described in step 4 is continuous Cutting work station is delivered to, the size of needs is cut into by cutter device, you can.
Embodiment five
A kind of energy saving, insulation, fire prevention and the preparation method of facing decorative integrated plate, include the following steps：
Step 1：Outside lower plywood 1 is placed on the crawler belt of thermal insulation board continuous producing apparatus conveying device, crawler belt is synchronous Mobile, outside lower plywood 1 is delivered to gluing station by lower crawler belt, and the inside upper surface of outside lower plywood 1 is sprayed by glue spreader Apply modified polyurethane hard bubble；
Step 2：Outside lower plywood 1 after gluing is delivered to intermediate core layer and is laid with filling station, on the outside lower plywood 1 Upper surface be laid with made of unorganic glass sliver, rock wool, aeroge thermal insulation board or vacuum heat-insulating plate sandwich layer bar, adjacent core The distance between layer bar is 0mm；
Step 3：Sandwich layer bar upper surface and 3 lower surface of inner crest face layer spraying modified polyurethane hard bubble to laying, so After make inner crest face layer 3 that semi-finished product integrated board be made by modified polyurethane hard bubble and 2 compound sticking of intermediate core layer；In described Side upper layer 3 is one of cement felt-cloth or metal coiled material；
Step 4：It is in thermal insulation board continuous producing apparatus conveying device that the semi-finished product integrated board described in step 4 is continuous Cutting work station is delivered to, the size of needs is cut into by cutter device, you can.
Embodiment six
A kind of energy saving, insulation, fire prevention and the preparation method of facing decorative integrated plate, include the following steps：
Step 1：Prepare fire-proof and water-proof foamed glue, fire-proof and water-proof foamed glue by following raw materials according according to parts by weight prepare and Into：30 parts of polyphenylene polyphenyl cyanate, 70 parts of polyalcohol, 5.25 parts of curing agent, 16.5 parts of solid melamine and inorganic poly- 10.5 parts of ammonium phosphate；Its preparation method is：Polyalcohol is placed in dispensing containers, is then sequentially added into dispensing containers poly- Methylene polyphenylene cyanate, solid melamine, inorganic ammonium polyphosphate and curing agent, are then stirred, and stir 10 minutes i.e. Can；The curing agent is polyisocyanate；
Step 2：Outside lower plywood 1 is placed on the crawler belt of thermal insulation board continuous producing apparatus conveying device, crawler belt is synchronous Mobile, outside lower plywood 1 is delivered to gluing station by lower crawler belt, and the inside upper surface of outside lower plywood 1 is sprayed by glue spreader The fire-proof and water-proof foamed glue described in step 1 is applied, need to be by being set on equipment for producing heat preservation plate when environment temperature is less than 15 DEG C Heating unit it is heated, heating and temperature control is in 37.5 DEG C；
Step 3：Outside lower plywood 1 after gluing is delivered to intermediate core layer and is laid with filling station, on the outside lower plywood 1 Upper surface be laid with made of unorganic glass sliver, rock wool, aeroge thermal insulation board or vacuum heat-insulating plate sandwich layer bar, adjacent core The distance between layer bar is 25mm；
Step 4：Between sandwich layer bar upper surface, adjacent sandwich layer bar to laying and 3 lower surface of inner crest face layer sprays Modified polyurethane hard bubble, then makes inner crest face layer 3 be made half by modified polyurethane hard bubble and 2 compound sticking of intermediate core layer Finished product integrated board；The inner crest face layer 3 is one of cement felt-cloth or metal coiled material；
Step 5：It is in thermal insulation board continuous producing apparatus conveying device that the semi-finished product integrated board described in step 4 is continuous Cutting work station is delivered to, the size of needs is cut into by cutter device, you can.
Embodiment seven
The preparation method of a kind of energy-saving heat preserving fire prevention, building enclosure and facing decorative integrated plate, includes the following steps：
Step 1：Prepare fire-proof and water-proof foamed glue, fire-proof and water-proof foamed glue by following raw materials according according to parts by weight prepare and Into：10 parts of polyphenylene polyphenyl cyanate, 20 parts of polyalcohol, 0.5 part of curing agent, 3 parts of solid melamine and inorganic polyphosphoric acid 1 part of ammonium；Its preparation method is：Polyalcohol is placed in dispensing containers, poly- methylene is then sequentially added into dispensing containers and is gathered Phenylcyanate, solid melamine, inorganic ammonium polyphosphate and curing agent, are then stirred, and stir 10 minutes；It is described Curing agent is tertiary amines curing agent；
Step 2：Outside lower plywood 1 is placed on pre-fabricated template frame, utilizes glue sprayer lower plywood 1 on the outside Fire-proof and water-proof foamed glue described in inside upper surface spraying process one, by manually on glue-line be laid with by unorganic glass sliver, Rock wool, aeroge thermal insulation board or sandwich layer bar made of vacuum heat-insulating plate are simultaneously bonded, and the distance between adjacent sandwich layer bar is 25mm；
Step 3：The fire prevention described in sandwich layer bar upper surface sprayed fire proofing waterproof foamed glue spraying process one to laying is prevented Water blown glue, and inner crest face layer 3 is placed at the top of fire-proof and water-proof foamed glue and is bonded, semi-finished product integrated board is made；Institute Inner crest face layer 3 is stated as one of cement felt-cloth or metal coiled material；
Step 4：Semi-finished product integrated board is made by above-mentioned steps one and step 2 in a manner of laminating on mould bases, extremely Semi-finished product integrated board carries out curing molding after building long-pending to 20 layers, and the temperature of the curing molding is outdoor environment temperature, is solidified into The time of type is：3h；
Step 5：Semi-finished product integrated board after above-mentioned curing molding is layered using hanging device and is seated in thermal insulation board In the conveying device of production equipment, continuous conveying to cutting work station, the sizes of needs is cut into by cutter device, you can.
Embodiment eight
The preparation method of a kind of energy-saving heat preserving fire prevention, building enclosure and facing decorative integrated plate, includes the following steps：
Step 1：Prepare fire-proof and water-proof foamed glue, fire-proof and water-proof foamed glue by following raw materials according according to parts by weight prepare and Into：50 parts of polyphenylene polyphenyl cyanate, 120 parts of polyalcohol, 10 parts of curing agent, 30 parts of solid melamine and inorganic polyphosphoric acid 20 parts of ammonium；Its preparation method is：Polyalcohol is placed in dispensing containers, poly- methylene is then sequentially added into dispensing containers and is gathered Phenylcyanate, solid melamine, inorganic ammonium polyphosphate and curing agent, are then stirred, and stir 50 minutes；It is described Curing agent is polyisocyanate；
Step 2：Outside lower plywood 1 is placed on pre-fabricated template frame, utilizes glue sprayer lower plywood 1 on the outside Fire-proof and water-proof foamed glue described in inside upper surface spraying process one, by manually on glue-line be laid with by unorganic glass sliver, Rock wool, aeroge thermal insulation board or sandwich layer bar made of vacuum heat-insulating plate are simultaneously bonded, and the distance between adjacent sandwich layer bar is 0mm；
Step 3：The fire prevention described in sandwich layer bar upper surface sprayed fire proofing waterproof foamed glue spraying process one to laying is prevented Water blown glue, and inner crest face layer 3 is placed at the top of fire-proof and water-proof foamed glue and is bonded, semi-finished product integrated board is made；Institute Inner crest face layer 3 is stated as one of cement felt-cloth or metal coiled material；
Step 4：Semi-finished product integrated board is made by above-mentioned steps one and step 2 in a manner of laminating on mould bases, extremely Semi-finished product integrated board carries out curing molding after building long-pending to 15 layers, and the temperature of the curing molding is outdoor environment temperature, is solidified into The time of type is：1h；
Step 5：Semi-finished product integrated board after above-mentioned curing molding is layered using hanging device and is seated in thermal insulation board In the conveying device of production equipment, continuous conveying to cutting work station, the sizes of needs is cut into by cutter device, you can.
Embodiment nine
The preparation method of a kind of energy-saving heat preserving fire prevention, building enclosure and facing decorative integrated plate, includes the following steps：
Step 1：Prepare fire-proof and water-proof foamed glue, fire-proof and water-proof foamed glue by following raw materials according according to parts by weight prepare and Into：30 parts of polyphenylene polyphenyl cyanate, 70 parts of polyalcohol, 5.25 parts of curing agent, 16.5 parts of solid melamine and inorganic poly- 10.5 parts of ammonium phosphate；Its preparation method is：Polyalcohol is placed in dispensing containers, is then sequentially added into dispensing containers poly- Methylene polyphenylene cyanate, solid melamine, inorganic ammonium polyphosphate and curing agent, are then stirred, and stir 30 minutes i.e. Can；The curing agent is tertiary amines curing agent；
Step 2：Outside lower plywood 1 is placed on pre-fabricated template frame, utilizes glue sprayer lower plywood 1 on the outside Inside upper surface sprays modified polyurethane hard bubble, is kept the temperature by being manually laid with glue-line by unorganic glass sliver, rock wool, aeroge Sandwich layer bar made of plate or vacuum heat-insulating plate is simultaneously bonded, and the distance between adjacent sandwich layer bar is 50mm；
Step 3：Sprayed fire proofing waterproof foamed glue sprays between sandwich layer bar upper surface and adjacent sandwich layer bar to laying Fire-proof and water-proof foamed glue described in step 1, and inner crest face layer 3 is placed at the top of fire-proof and water-proof foamed glue and is bonded, Semi-finished product integrated board is made；The inner crest face layer 3 is one of high-strength fabric cement plate or high-strength calcium silicate board；
Step 4：Semi-finished product integrated board is made by above-mentioned steps one and step 2 in a manner of laminating on mould bases, extremely Semi-finished product integrated board carries out curing molding after building long-pending to 25 layers, and the temperature of the curing molding is outdoor environment temperature, is solidified into The time of type is：5h；
Step 5：Semi-finished product integrated board after above-mentioned curing molding is layered using hanging device and is seated in thermal insulation board In the conveying device of production equipment, continuous conveying to cutting work station, the sizes of needs is cut into by cutter device, you can.
In the description of the present invention, it is necessary to illustrate, unless otherwise clearly defined and limited, term " connection ", " phase Company " etc. should be interpreted broadly, for example, it may be being fixedly connected, be integrally connected or be detachably connected；Can also It is the connection inside two elements；It can be directly connected, can also be indirectly connected by intermediary, for the general of this area For logical technical staff, the concrete meaning of above-mentioned term in the present invention can be understood as the case may be.Above specifically The bright feasibility embodiment only for the present invention illustrates, they are simultaneously not used to the protection model of the limitation present invention Enclose, all equivalent implementations made without departing from skill spirit of the present invention, change and transformation should be included in the protection of the present invention Within the scope of.

Claims (7)

1. a kind of energy saving, insulation, fire prevention and facing decorative integrated plate, it is characterised in that：The integrated board includes outside lower plywood (1), intermediate core layer (2) and inner crest face layer (3), the outside of outside lower plywood (1) are equipped with finish coat (4), outside lower plywood (1) The first adhesive linkage (5) is equipped between intermediate core layer (2), intermediate core layer (2) includes several sandwich layer bars, the upper surface of sandwich layer bar And it is connected between adjacent sandwich layer bar by the second adhesive linkage (6) with inner crest face layer (3)；
The outside lower plywood (1) is one of high-strength fabric cement plate, high-strength calcium silicate board, stone material or ceramic tile；
The sandwich layer bar is inorganic incombustible material, its thermal conductivity factor is 0.006~0.035W/ (M.K)；The material of sandwich layer bar is nothing One of machine glass sliver, rock wool, aeroge thermal insulation board or vacuum heat-insulating plate；
The inner crest face layer (3) is one of high-strength fabric cement plate, high-strength calcium silicate board, cement roll felt-cloth or metal coiled material；
First adhesive linkage (5) is one of fire-proof and water-proof foamed glue or modified polyurethane hard bubble；
Second adhesive linkage (6) is one of fire-proof and water-proof foamed glue or modified polyurethane hard bubble.
2. one kind according to claim 1 is energy saving, keeps the temperature, prevents fires and facing decorative integrated plate, it is characterised in that：The phase The distance between adjacent sandwich layer bar is 0mm~50mm.
3. one kind according to claim 1 is energy saving, keeps the temperature, prevents fires and facing decorative integrated plate, it is characterised in that：The nothing Machine glass sliver is the cross section slitting of forward cotton fiber, and the thickness of slitting is 20mm~80mm, and width is 60mm~300mm； The thickness of rock wool is 20mm~80mm, and width is 60mm~800mm；The thickness of aeroge thermal insulation board is 10mm~30mm, width For 300mm~1200mm；The thickness of vacuum heat-insulating plate is 2mm~20mm, and width is 300mm~1200mm.
4. one kind according to claim 1 is energy saving, keeps the temperature, prevents fires and facing decorative integrated plate, it is characterised in that：It is described outer The thickness of side lower plywood (1) is 5mm~15mm.
5. a kind of energy saving, insulation as described in right wants 1-4, fire prevention and the preparation method of facing decorative integrated plate, its feature exist In：The preparation method includes the following steps：
Step 1：Fire-proof and water-proof foamed glue is prepared, fire-proof and water-proof foamed glue is prepared by following raw materials according according to parts by weight：It is poly- 10~50 parts of methylene polyphenylene cyanate, 20~120 parts of polyalcohol, 0.5~10 part of curing agent, 3~30 parts of solid melamine With inorganic 1~20 part of ammonium polyphosphate；Its preparation method is：Polyalcohol is placed in dispensing containers, then into dispensing containers Polyphenylene polyphenyl cyanate, solid melamine, inorganic ammonium polyphosphate and curing agent are sequentially added, is then stirred, stirs Mix 10~50 minutes；The curing agent is one of polyisocyanate or tertiary amines curing agent；
Step 2：Outside lower plywood (1) is placed on the crawler belt of thermal insulation board continuous producing apparatus conveying device, crawler belt synchronously moves Dynamic, outside lower plywood (1) is delivered to gluing station by lower crawler belt, the inside upper surface by glue spreader to outside lower plywood (1) Fire-proof and water-proof foamed glue or modified polyurethane hard bubble described in spraying process one, need to pass through guarantor when environment temperature is less than 15 DEG C The heating unit set in warm plate production equipment heats it, and heating and temperature control is in 15 DEG C~60 DEG C；
Step 3：Outside lower plywood (1) after gluing is delivered to intermediate core layer and is laid with filling station, on the outside lower plywood (1) Upper surface be laid with made of unorganic glass sliver, rock wool, aeroge thermal insulation board or vacuum heat-insulating plate sandwich layer bar, adjacent core The distance between layer bar is 0mm~50mm；
Step 4：Between sandwich layer bar upper surface, adjacent sandwich layer bar to laying and inner crest face layer (3) lower surface spraying step Fire-proof and water-proof foamed glue described in rapid one, with being bonded as one after gluing, is made semi-finished product integrated board；The inner crest face layer (3) it is cement roll felt-cloth；
Step 5：By the semi-finished product integrated board described in step 4 according to routine in thermal insulation board continuous producing apparatus conveying device After process carries out pressing, extrusion operation to plate, cutting work station is delivered to, the size of needs is cut into by cutter device, .
6. a kind of energy saving, insulation, fire prevention and preparation method of facing decorative integrated plate as described in right wants 1-4, including it is as follows Step：
Step 1：Fire-proof and water-proof foamed glue is prepared, fire-proof and water-proof foamed glue is prepared by following raw materials according according to parts by weight：It is poly- 10~50 parts of methylene polyphenylene cyanate, 20~120 parts of polyalcohol, 0.5~10 part of curing agent, 3~30 parts of solid melamine With inorganic 1~20 part of ammonium polyphosphate；Its preparation method is：Polyalcohol is placed in dispensing containers, then into dispensing containers Polyphenylene polyphenyl cyanate, solid melamine, inorganic ammonium polyphosphate and curing agent are sequentially added, is then stirred, stirs Mix 10~50 minutes；The curing agent is one of polyisocyanate or tertiary amines curing agent；
Step 2：Outside lower plywood (1) is placed on the crawler belt of thermal insulation board continuous producing apparatus conveying device, crawler belt synchronously moves Dynamic, outside lower plywood (1) is delivered to gluing station by lower crawler belt, the inside upper surface by glue spreader to outside lower plywood (1) Fire-proof and water-proof foamed glue described in spraying process one, need to be by setting when environment temperature is less than 15 DEG C on equipment for producing heat preservation plate The heating unit put heats it, and heating and temperature control is in 15 DEG C~60 DEG C；
Step 3：Outside lower plywood (1) after gluing is delivered to intermediate core layer and is laid with filling station, on the outside lower plywood (1) Upper surface be laid with made of unorganic glass sliver, rock wool, aeroge thermal insulation board or vacuum heat-insulating plate sandwich layer bar, adjacent core The distance between layer bar is 0mm~50mm；
Step 4：The spraying of between sandwich layer bar upper surface, adjacent sandwich layer bar to laying and inner crest face layer (3) lower surface changes Property hard polyurethane foam, then makes inner crest face layer (3) be made up of modified polyurethane hard bubble and intermediate core layer (2) compound sticking Semi-finished product integrated board；The inner crest face layer (3) is high-strength fabric cement plate, high-strength calcium silicate board, cement roll felt-cloth or metal One of coiled material；
Step 5：By the semi-finished product integrated board continuous conveying described in step 4 in thermal insulation board continuous producing apparatus conveying device To cutting work station, the size of needs is cut into by cutter device, you can.
7. a kind of energy saving, insulation, fire prevention and preparation method of facing decorative integrated plate as described in right wants 1-4, including it is as follows Step：
Step 1：Fire-proof and water-proof foamed glue is prepared, fire-proof and water-proof foamed glue is prepared by following raw materials according according to parts by weight：It is poly- 10~50 parts of methylene polyphenylene cyanate, 20~120 parts of polyalcohol, 0.5~10 part of curing agent, 3~30 parts of solid melamine With inorganic 1~20 part of ammonium polyphosphate；Its preparation method is：Polyalcohol is placed in dispensing containers, then into dispensing containers Polyphenylene polyphenyl cyanate, solid melamine, inorganic ammonium polyphosphate and curing agent are sequentially added, is then stirred, stirs Mix 10~50 minutes；The curing agent is one of polyisocyanate or tertiary amines curing agent；
Step 2：Outside lower plywood (1) is placed on pre-fabricated template frame, utilizes glue sprayer lower plywood (1) on the outside Fire-proof and water-proof foamed glue or modified polyurethane hard bubble described in inside upper surface spraying process one, by being manually laid with glue-line Sandwich layer bar and it is bonded, adjacent sandwich layer made of unorganic glass sliver, rock wool, aeroge thermal insulation board or vacuum heat-insulating plate The distance between bar is 0mm~50mm；
Step 3：Sprayed fire proofing waterproof foamed glue spraying process between sandwich layer bar upper surface and adjacent sandwich layer bar to laying Fire-proof and water-proof foamed glue described in one, and inner crest face layer (3) is placed at the top of fire-proof and water-proof foamed glue and is bonded, make Into semi-finished product integrated board；The inner crest face layer (3) is high-strength fabric cement plate, high-strength calcium silicate board, cement roll felt-cloth or gold Belong to one of coiled material；
Step 4：Semi-finished product integrated board is made by above-mentioned steps one and step 2 in a manner of laminating on mould bases, to half into Product integrated board carries out curing molding after building long-pending to 15~25 layers, and the temperature of the curing molding is outdoor environment temperature, is solidified into The time of type is：1h~5h；
Step 5：Semi-finished product integrated board after above-mentioned curing molding is layered using hanging device and is seated in thermal insulation board production In the conveying device of equipment, continuous conveying to cutting work station, the sizes of needs is cut into by cutter device, you can.
CN201711374065.2A 2017-12-07 2017-12-07 A kind of energy saving, insulation, fire prevention and facing decorative integrated plate and preparation method Pending CN108032592A (en)