CN207697227U - One kind is energy saving, heat preservation, prevents fires and facing decorative integrated plate - Google Patents
One kind is energy saving, heat preservation, prevents fires and facing decorative integrated plate Download PDFInfo
- Publication number
- CN207697227U CN207697227U CN201721785419.8U CN201721785419U CN207697227U CN 207697227 U CN207697227 U CN 207697227U CN 201721785419 U CN201721785419 U CN 201721785419U CN 207697227 U CN207697227 U CN 207697227U
- Authority
- CN
- China
- Prior art keywords
- heat preservation
- energy saving
- lower plywood
- sandwich layer
- outside lower
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model belongs to energy saving one kind, heat preservation, fire prevention and facing decorative integrated plate；Including outside lower plywood, intermediate core layer and inner crest face layer, the outside of outside lower plywood is equipped with finish coat, the first adhesive linkage is equipped between outside lower plywood and intermediate core layer, intermediate core layer includes several sandwich layer items, is connected with inner crest face layer by the second adhesive linkage between the upper surface of sandwich layer item and adjacent sandwich layer item；The outside lower plywood is one of high-strength fabric cement plate, high-strength calcium silicate board, stone material or ceramic tile；The sandwich layer item is inorganic incombustible material, and thermal coefficient is 0.006~0.035W/ (M.K)；The material of sandwich layer item is one of unorganic glass sliver, rock wool, aeroge thermal insulation board or vacuum heat-insulating plate；With achievable exterior-wall heat insulation, finish coat integrated construction, the characteristics of saving of work and time.
Description
Technical field
The utility model belongs to energy-saving building material technical field, and in particular to one kind is energy saving, heat preservation, prevents fires and decorates one with facing
Body plate.
Background technology
China's wall thermal insulating safety high is serious.Recent State Council issues《Surely increase about building materials industry is promoted
Structure is adjusted to increase benefit》Instruction (Office of the State Council send out (2016) No. 34 text propose：Develop essential safety, energy conservation and environmental protection, high-strength light
Wall and roofing, external-wall heat-insulation material and structure and heat preservation decoration integrative Side fascia.Obviously, national and at different levels
Local government is encouraging to advocate new architectural energy saving techniques, the research and development of new product, promotion and application always, and building energy conservation, which has become, to be built
Build the grand strategy behave that industry implements national green development energy-saving and emission-reduction.And it researches and develops and promotes and applies integrated construction wall heat preservation
Power-saving technology is with product just at effective key for solving the problems, such as building industrialization and assembling.It is anti-to promote and apply integrated energy-saving
Fiery insulation system certainly will help to improve energy-saving projects quality, extend heat insulating work service life, ensure people's life wealth
The significant problem of production and safety.
Wall heat insulation technical measures at present substantially use external labeling type to keep the temperature, and mostly combustable organic material, deposit
In long in time limit, of high cost, easy to crack, easy to fall off, organic material easy firing, generate the critical defects such as public safety hidden danger, CCTV
The high buildings fire such as big fire is suffered from, and the insulating layer of external wall that takes place frequently falls off the tragedy hurted sb.'s feelings, it is sufficient to the drawbacks of illustrating conventional vacuum technology.
The sandwich class integration heat preservation technology system promoted, because of cost height, construction is difficult, and it is big to promote and apply difficulty；In the prior art
Have the materials such as rock wool and cement slurry Material cladding, buckling deformation easily occurs in this composite insulation boards poor mechanical property, easily inhales
Water causes heat-insulating property to decline, and this thermal insulation board complex manufacturing technology, and cement slurry material needs to solidify maintenance when making
It can dispatch from the factory within 28 days, cause the production cycle long, occupancy factory site is big, and commercial production level is low, and investment and production cost are larger；It is existing
There is adhesive temperature tolerance used in composite board in technology poor, generally 100 degree or so；Also there is a high-temperature resistance adhesive, but intolerant to
Water, interlaminar separation after water logging generate security risk.
Utility model content
A kind of more work(purposes, thermal coefficient are provided the purpose of the utility model is to overcome defect in the prior art
It is small, can not only be used for heat preservation and used but also as non-dismantling formwork, and have facing decorative effect；Using continuous production, industrial metaplasia
Production is horizontal high；Do not crack, do not fall off in the application, fire safety, durable use；At low cost, the shortening construction period reduces manually
Labor intensity and the energy saving of economy, heat preservation, fire prevention and facing decorative integrated plate.
What the purpose of this utility model was realized in：Including outside lower plywood, intermediate core layer and inner crest face layer, outside
The outside of lower plywood is equipped with finish coat, and the first adhesive linkage is equipped between outside lower plywood and intermediate core layer, if intermediate core layer includes
Dry sandwich layer item, is connected by the second adhesive linkage with inner crest face layer between the upper surface of sandwich layer item and adjacent sandwich layer item；Institute
It is one of high-strength fabric cement plate, high-strength calcium silicate board, stone material or ceramic tile to state outside lower plywood；The sandwich layer item is inorganic non-ignitable
Material, thermal coefficient are 0.006~0.035W/ (M.K)；The material of sandwich layer item is unorganic glass sliver, rock wool, aeroge guarantor
One of warm plate or vacuum heat-insulating plate；The inner crest face layer be high-strength fabric cement plate, high-strength calcium silicate board, cement roll felt-cloth or
One of metal coiled material；First adhesive linkage is one of fire-proof and water-proof foamed glue or modified polyurethane hard bubble；Second bonding
Layer is one of fire-proof and water-proof foamed glue or modified polyurethane hard bubble.
Preferably, the distance between described adjacent sandwich layer item is 0mm~50mm.
Preferably, the unorganic glass sliver is the cross section slitting of forward cotton fiber, the thickness of slitting be 20mm~
80mm, width are 60mm~300mm；The thickness of rock wool is 20mm~80mm, and width is 60mm~800mm；Aeroge thermal insulation board
Thickness be 10mm~30mm, width be 300mm~1200mm；The thickness of vacuum heat-insulating plate is 2mm~20mm, and width is
300mm~1200mm.
Preferably, the thickness of the outside lower plywood is 5mm~15mm.
The utility model has the following advantages that：
1, insulated fire and building enclosure, facing decorative integrated plate continuous production.Completely eliminate operating environment and work
The uncertainty that people brings.Heat preservation with facing decorative integrated plate overcomes existing craft, and batch production efficiency is low, quality is nonstandard
Deficiency, stable quality, production capacity promoted.
2, the utility model can realize exterior-wall heat insulation, finish coat integrated construction, have the characteristics that saving of work and time.This reality
It is made suitable for batch production of novel product, assembling installation, makes the outer powder of wall thermal insulating, metope, exterior finish decoration scene one
Change synchronous formation, construction efficiency height, short time limit, expense is greatly lowered, reduces projects field management difficulty, has compressed
Duration.
3, the utility model disclosure satisfy that national higher energy conservation standard.The product insulating layer of the utility model is thin, and property
Can be excellent, it is only that can meet national higher completely between 0.006~0.034W/ (M.K) through authoritative institution's detection thermal coefficient
Energy conservation standard requirement.
4, the product fire-proof and water-proof performance of the utility model is good, through authoritative testing agency according to JG/T287-2013《Heat preservation
Decorative panel material for external thermal insulation system of external wall》Testing result is：Fire protecting performance reaches the non-ignitable standards of A1；Anti-impact force reaches 10J marks
It is accurate；Tensile bond strength original reaches 0.2Mpa by force, water-fast to reach 0.15Mpa by force；Bending resistance load reaches 2600N, is above standard
Prescribed requirement.Heat insulating decorative board firmly installs simultaneously, does not crack, does not fall off；Environmental protection index is better than through the detection of national testing agency
National standard, be it is a kind of green, environment-friendly products, so that occupant is trusted, be comfortable, the sorrow without any hidden danger, to significantly improve
The comfort level of residence enhances the market competitiveness in commercial residential buildings.
5, standard preresearch estimates, same construction item are expended according to existing construction project ration standard and construction auxiliary material
Mesh uses existing routine techniques product, duration that can shorten half with the product ratio of the utility model, and entire engineering is comprehensive
Conjunction expense is substantially reduced, and remarkable benefit increases.
6, the utility model has the characteristics that heat preservation, fire-proof and water-proof, decoration and fire-retardant, and can realize it is energy saving, save land, protect
Retaining ring border saves building cost, mitigates construction worker's labor intensity, energy saving overall working time and meet the single work(of China's building materials
Can be to complex function type developing direction the advantages of.
Description of the drawings
Fig. 1 is the structural schematic diagram of the utility model.
Fig. 2 is another structural schematic diagram of the utility model.
Specific implementation mode
For a clearer understanding of the technical features, objectives and effects of the utility model, existing control description of the drawings
Specific embodiment of the present utility model, in the various figures identical label indicate identical component.To make simplified form, in each figure
Only schematically show with the relevant part of utility model, they do not represent its practical structures as product.
As shown in Figure 1, 2, the utility model one kind is energy saving, heat preservation, prevents fires and facing decorative integrated plate and preparation method,
In, which includes outside lower plywood 1, intermediate core layer 2 and inner crest face layer 3, and the outside of outside lower plywood 1 is equipped with finish coat
4, the first adhesive linkage 5 is equipped between outside lower plywood 1 and intermediate core layer 2, intermediate core layer 2 includes several sandwich layer items, sandwich layer item
Upper surface and adjacent sandwich layer item between be connected with inner crest face layer 3 by the second adhesive linkage 6；The outside lower plywood 1 is
One of high-strength fabric cement plate, high-strength calcium silicate board, stone material or ceramic tile；The sandwich layer item is inorganic incombustible material, heat conduction system
Number is 0.006~0.035W/ (M.K)；The material of sandwich layer item is that unorganic glass sliver, rock wool, aeroge thermal insulation board or vacuum are exhausted
One of hot plate；The inner crest face layer 3 be high-strength fabric cement plate, high-strength calcium silicate board, cement roll felt-cloth or metal coiled material it
One；First adhesive linkage 5 is one of fire-proof and water-proof foamed glue or modified polyurethane hard bubble；Second adhesive linkage 6 is fire prevention
One of waterproof foamed glue or modified polyurethane hard bubble.The distance between described adjacent sandwich layer item is 0mm~50mm.It is described inorganic
Glass sliver is the cross section slitting of forward cotton fiber, and the thickness of slitting is 20mm~80mm, and width is 60mm~300mm；Rock
The thickness of cotton is 20mm~80mm, and width is 60mm~800mm；The thickness of aeroge thermal insulation board is 10mm~30mm, and width is
300mm~1200mm；The thickness of vacuum heat-insulating plate is 2mm~20mm, and width is 300mm~1200mm.The outside lower plywood 1
Thickness be 5mm~15mm.
The utility model additionally provides a kind of energy saving, heat preservation, fire prevention and facing decorative integrated plate preparation method, prepares
Method includes three kinds；
A kind of energy saving, heat preservation, fire prevention and facing decorative integrated plate one of preparation method, includes the following steps：
Step 1：Prepare fire-proof and water-proof foamed glue, fire-proof and water-proof foamed glue by following raw materials according according to parts by weight prepare and
At：10~50 parts of polyphenylene polyphenyl cyanate, 20~120 parts of polyalcohol, 0.5~10 part of curing agent, solid melamine 3~
30 parts and 1~20 part of inorganic ammonium polyphosphate；Preparation method is：Polyalcohol is placed in dispensing containers, is then held to configuration
Polyphenylene polyphenyl cyanate, solid melamine, inorganic ammonium polyphosphate and curing agent are sequentially added in device, are then stirred
It mixes, stirs 10~50 minutes；The curing agent is one of polyisocyanate or tertiary amines curing agent；
Step 2：Outside lower plywood 1 is placed on the crawler belt of thermal insulation board continuous producing apparatus conveying device, crawler belt synchronizes
Mobile, outside lower plywood 1 is delivered to gluing station by lower crawler belt, is sprayed to the inside upper surface of outside lower plywood 1 by glue spreader
The fire-proof and water-proof foamed glue or modified polyurethane hard bubble described in step 1 are applied, need to pass through heat preservation when environment temperature is less than 15 DEG C
The heating device being arranged in plate production equipment heats it, and heating and temperature control is in 15 DEG C~60 DEG C；
Step 3：Outside lower plywood 1 after gluing is delivered to intermediate core layer and is laid with filling station, on the outside lower plywood 1
Upper surface be laid with the sandwich layer item made of unorganic glass sliver, rock wool, aeroge thermal insulation board or vacuum heat-insulating plate, adjacent core
The distance between layer item is 0mm~50mm；
Step 4：Between the sandwich layer upper surface of laying, adjacent sandwich layer item and the spraying of 3 lower surface of inner crest face layer
Fire-proof and water-proof foamed glue described in step 1, after gluing be bonded as one, semi-finished product integrated board is made；The inner crest face
Layer 3 is cement roll felt-cloth；
Step 5：In thermal insulation board continuous producing apparatus conveying device by the semi-finished product integrated board described in step 4 according to
After common process method carries out pressing, extrusion operation to plank, it is delivered to cutting work station, the ruler of needs is cut by cutter device
It is very little, you can.
A kind of energy saving, heat preservation, fire prevention and the two of the preparation method of facing decorative integrated plate, include the following steps：
Step 1：Prepare fire-proof and water-proof foamed glue, fire-proof and water-proof foamed glue by following raw materials according according to parts by weight prepare and
At：10~50 parts of polyphenylene polyphenyl cyanate, 20~120 parts of polyalcohol, 0.5~10 part of curing agent, solid melamine 3~
30 parts and 1~20 part of inorganic ammonium polyphosphate；Preparation method is：Polyalcohol is placed in dispensing containers, is then held to configuration
Polyphenylene polyphenyl cyanate, solid melamine, inorganic ammonium polyphosphate and curing agent are sequentially added in device, are then stirred
It mixes, stirs 10~50 minutes；The curing agent is one of polyisocyanate or tertiary amines curing agent；
Step 2：Outside lower plywood 1 is placed on the crawler belt of thermal insulation board continuous producing apparatus conveying device, crawler belt synchronizes
Mobile, outside lower plywood 1 is delivered to gluing station by lower crawler belt, is sprayed to the inside upper surface of outside lower plywood 1 by glue spreader
The fire-proof and water-proof foamed glue or modified polyurethane hard bubble described in step 1 are applied, need to pass through heat preservation when environment temperature is less than 15 DEG C
The heating device being arranged in plate production equipment heats it, and heating and temperature control is in 15 DEG C~60 DEG C；
Step 3：Outside lower plywood 1 after gluing is delivered to intermediate core layer and is laid with filling station, on the outside lower plywood 1
Upper surface be laid with the sandwich layer item made of unorganic glass sliver, rock wool, aeroge thermal insulation board or vacuum heat-insulating plate, adjacent core
The distance between layer item is 0mm~50mm；
Step 4：Between the sandwich layer upper surface of laying, adjacent sandwich layer item and the spraying of 3 lower surface of inner crest face layer
Then modified polyurethane hard bubble makes inner crest face layer 3 by modified polyurethane hard bubble and 2 compound sticking of intermediate core layer, be made half
Finished product integrated board；The inner crest face layer 3 is high-strength fabric cement plate, high-strength calcium silicate board, cement roll felt-cloth or metal coiled material
One of；
Step 5：It is in thermal insulation board continuous producing apparatus conveying device that the semi-finished product integrated board described in step 4 is continuous
It is delivered to cutting work station, the size of needs is cut by cutter device, you can.
A kind of energy saving, heat preservation, fire prevention and the three of the preparation method of facing decorative integrated plate, include the following steps：
Step 1：Prepare fire-proof and water-proof foamed glue, fire-proof and water-proof foamed glue by following raw materials according according to parts by weight prepare and
At：10~50 parts of polyphenylene polyphenyl cyanate, 20~120 parts of polyalcohol, 0.5~10 part of curing agent, solid melamine 3~
30 parts and 1~20 part of inorganic ammonium polyphosphate；Preparation method is：Polyalcohol is placed in dispensing containers, is then held to configuration
Polyphenylene polyphenyl cyanate, solid melamine, inorganic ammonium polyphosphate and curing agent are sequentially added in device, are then stirred
It mixes, stirs 10~50 minutes；The curing agent is one of polyisocyanate or tertiary amines curing agent；
Step 2：Outside lower plywood 1 is placed on pre-fabricated template frame, utilizes glue sprayer lower plywood 1 on the outside
Fire-proof and water-proof foamed glue described in inside upper surface spraying process one or modified polyurethane hard bubble, by being manually laid on glue-line
The sandwich layer item made of unorganic glass sliver, rock wool, aeroge thermal insulation board or vacuum heat-insulating plate is simultaneously bonded, adjacent sandwich layer
The distance between item is 0mm~50mm；
Step 3：Sprayed fire proofing waterproof foamed glue sprays between sandwich layer upper surface and adjacent sandwich layer item to laying
Fire-proof and water-proof foamed glue described in step 1, and inner crest face layer 3 is placed at the top of fire-proof and water-proof foamed glue and is bonded,
Semi-finished product integrated board is made；The inner crest face layer 3 is high-strength fabric cement plate, high-strength calcium silicate board, cement roll felt-cloth or gold
Belong to one of coiled material；
Step 4：On mould bases in a manner of laminating through the above steps one and step 2 make semi-finished product integrated board, until
Semi-finished product integrated board carries out curing molding after building long-pending to 15~25 layers, the temperature of the curing molding is outdoor environment temperature, Gu
Changing the molding time is：1h~5h；
Step 5：Semi-finished product integrated board after above-mentioned curing molding is layered using hanging device and is seated in thermal insulation board
In the conveying device of production equipment, continuous conveying to cutting work station is cut into the size of needs by cutter device, you can.
Fire-proof and water-proof foamed glue described in the utility model can not decompose in 300 degree or so of hot environment, and
Have the characteristics that strong with water-proof binding power；Modified polyurethane hard bubble described in the utility model is patented product, Patent
Number it is 201620101185.X, patent name is：A kind of low heat conduction A grades of non-ignitable sandwich thermal insulation boards have in the 25th section of specification
It records in detail, and number of patent application is：201610070856.9 patent of invention right require 1 in recorded related content.This
Outside lower plywood 1 described in utility model is with having made or generating naturally, unlike material and different color
Finish coat, stone material or ceramic tile specifically refer to ultrathin lithotome, slim porcelain plate, sheet metal, fluorine carbon metal paint decorative panel, reality
Colored paint decorative panel, imitative stone material, marble lacquer decorative panel or flexible porcelain tendre.Tertiary amines curing agent described in the utility model includes
Aliphatic tertiary amine and aromatic nitrile base, aliphatic tertiary amine include triethylamine and triethanolamine etc., and aromatic nitrile base includes benzyl two
Methylamine, methylbenzyl dimethylamine, DMP-10 and DMP-30 etc..Polyisocyanate described in the utility model or tertiary amines solidification
Agent can directly be purchased in market.Metal coiled material described in the utility model is aluminium sheet or color steel.Described in the utility model
Fire-proof and water-proof foamed glue and modified polyurethane hard bubble can be replaced, but the first adhesive linkage 5 is preferably by fire-proof and water-proof
Foamed glue.
In the description of the present invention, it should be noted that unless otherwise clearly defined and limited, term is " even
Connect ", " connected " etc. shall be understood in a broad sense, for example, it may be being fixedly connected, be integrally connected, may be a detachable connection；
It can also be the connection inside two elements；It can be directly connected, it can also indirectly connected through an intermediary, for ability
For the those of ordinary skill in domain, the concrete meaning of above-mentioned term in the present invention can be understood as the case may be.On
The detailed description of text is illustrated only for the feasible embodiment of the utility model, they are not limiting this
The protection domain of utility model, it is all equal without departing from equivalent implementations, change made by the utility model skill spirit and transformation
It should be included within the scope of protection of this utility model.
Claims (8)
1. a kind of energy saving, heat preservation, fire prevention and facing decorative integrated plate, it is characterised in that：The integrated board includes outside lower plywood
(1), the outside of intermediate core layer (2) and inner crest face layer (3), outside lower plywood (1) is equipped with finish coat (4), outside lower plywood (1)
The first adhesive linkage (5) is equipped between intermediate core layer (2), intermediate core layer (2) includes several sandwich layer items, the upper surface of sandwich layer item
And it is connected with inner crest face layer (3) by the second adhesive linkage (6) between adjacent sandwich layer item；
The outside lower plywood (1) is one of high-strength fabric cement plate, high-strength calcium silicate board, stone material or ceramic tile；
The sandwich layer item is inorganic incombustible material, and thermal coefficient is 0.006~0.035W/ (mK)；
The inner crest face layer (3) is one of high-strength fabric cement plate, high-strength calcium silicate board, cement roll felt-cloth or metal coiled material；
First adhesive linkage (5) is one of fire-proof and water-proof foamed glue or modified polyurethane hard bubble；
Second adhesive linkage (6) is one of fire-proof and water-proof foamed glue or modified polyurethane hard bubble.
2. one kind according to claim 1 is energy saving, heat preservation, prevents fires and facing decorative integrated plate, it is characterised in that：The phase
The distance between adjacent sandwich layer item is 0mm~50mm.
3. one kind according to claim 1 is energy saving, heat preservation, prevents fires and facing decorative integrated plate, it is characterised in that：The core
The material of layer item is one of unorganic glass sliver, rock wool, aeroge thermal insulation board or vacuum heat-insulating plate.
4. one kind according to claim 3 is energy saving, heat preservation, prevents fires and facing decorative integrated plate, it is characterised in that：The nothing
Machine glass sliver is the cross section slitting of forward cotton fiber, and the thickness of slitting is 20mm~80mm, and width is 60mm~300mm.
5. one kind according to claim 3 is energy saving, heat preservation, prevents fires and facing decorative integrated plate, it is characterised in that：The rock
The thickness of cotton is 20mm~80mm, and width is 60mm~800mm.
6. one kind according to claim 3 is energy saving, heat preservation, prevents fires and facing decorative integrated plate, it is characterised in that：The gas
The thickness of gel thermal insulation board is 10mm~30mm, and width is 300mm~1200mm.
7. one kind according to claim 3 is energy saving, heat preservation, prevents fires and facing decorative integrated plate, it is characterised in that：It is described true
The thickness of empty heat-insulating shield is 2mm~20mm, and width is 300mm~1200mm.
8. one kind according to claim 1 is energy saving, heat preservation, prevents fires and facing decorative integrated plate, it is characterised in that：It is described outer
The thickness of side lower plywood (1) is 5mm~15mm.