CN108017993A - 光致失黏胶组合物、光致失黏胶膜层的制备方法和应用 - Google Patents
光致失黏胶组合物、光致失黏胶膜层的制备方法和应用 Download PDFInfo
- Publication number
- CN108017993A CN108017993A CN201711486979.8A CN201711486979A CN108017993A CN 108017993 A CN108017993 A CN 108017993A CN 201711486979 A CN201711486979 A CN 201711486979A CN 108017993 A CN108017993 A CN 108017993A
- Authority
- CN
- China
- Prior art keywords
- photic
- viscose
- mistake
- functional group
- film layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种光致失黏胶组合物，其包括如下按质量百分数分配的各组分：5％～35％的丙烯酸酯类单体、5％～35％的多光敏官能团低聚物、1％～4％的光引发剂、1％～4％的热固化剂、0.2％～3％的功能添加剂、以及余量的溶解溶剂；其中，多光敏官能团低聚物中光敏官能团的数量至少为两个，聚合度不超过150。本发明还公开了基于上述光致失黏胶组合物的一种光致失黏胶膜层的制备方法及应用。根据本发明的光致失黏胶组合物在应用时，在UV照射前能够展现良好的粘着特性，以满足偏光片贴片制程和信赖性要求；而需剥离由其制成的光致失黏胶膜层时，仅需在UV光下照射一定时间后即可，展示了很好的失黏性能，便于拆离，而不对贴覆的基板表面产生破坏和残胶脏污。
Description
技术领域
本发明属于偏光片制作技术领域，具体来讲，涉及一种光致失黏胶组合物、基于该光致失黏胶组合物的光致失黏胶膜层的制备方法、以及该光致失黏胶膜层在偏光片中的应用。
背景技术
偏光片是液晶显示装置偏光片的重要组件之一，直接影响液晶显示装置的显示效果。偏光片吸收与偏光轴垂直方向上的光，使偏光轴方向的光通过，进而达到自然光与直线偏振光之间的转换，加上液晶分子扭转特性，控制光线的通过与否，使液晶显示装置得以正常显示图像。图1为常规市售偏光片的组成结构，该偏光片包括依次叠层设置的离型膜11、压敏胶层12、相位差膜13、偏光膜14和保护膜15。
在TFT-LCD研发生产制造中，通常需要经过贴片制程，将去除离型膜11后的偏光片分别贴付到TFT基板和CF基板侧，使液晶显示面板得以正常显示。压敏胶层12中的压敏胶材料是偏光片常用胶粘剂，其作用是使胶带具有对压力敏感粘付特性，从而通过贴片、脱泡工艺，使得偏光片得以平整的贴付在液晶显示面板上。
但在实际生产过程中，由于机台故障或者人为操作不当，在偏光片贴片制程中，会有脱泡不完全，表面刮伤，褶皱等不良现象发生，在进行不良品重做过程中，偏光片的移除工序费时费力，产生成本浪费；在实验室研发过程中，在盒厚测量、以及其他异常解析过程中，通常也都需要撕开偏光片，手动撕开偏光片是一项细致费时的工序，撕开时需要先用一把锋利的刀片从屏的一角小心切入，一手向上轻拉偏光片，另一只手用酒精棉球来回拭擦粘合面，以免显示屏面留下残胶及斑点，当用力稍大时，甚至会造成液晶显示面板的破损，给研发人员带来了很多不便和困扰。
发明内容
为解决上述现有技术存在的问题，本发明提供了一种光致失黏胶组合物，该种光致失黏胶组合物在应用过程中，不仅可以展现良好的粘着特性，还可在UV光照射一定时间后，其中的多光敏官能团低聚物发生交联反应及与直链分子形成互穿网格状结构而易于剥离。
为了达到上述发明目的，本发明采用了如下的技术方案：
一种光致失黏胶组合物，包括如下按质量百分数分配的各组分：
余量为溶解溶剂；
其中，所述多光敏官能团低聚物中光敏官能团的数量至少为两个，聚合度不超过150。
进一步地，所述多光敏官能团低聚物中的光敏官能团选自丙烯酸基、甲基丙烯酸甲基、炔基、烯丙基、丙烯酰胺基、乙烯基醚基、乙烯基硫醚基、乙烯基胺基、环丙烷基中的至少一种。
进一步地，所述多光敏官能团低聚物选自二官能团聚氨酯丙烯酸酯、三官能团聚氨酯丙烯酸酯、四官能团聚氨酯丙烯酸酯、五官能团聚氨酯丙烯酸酯、六官能团聚氨酯丙烯酸酯中的至少一种。
进一步地，所述丙烯酸酯类单体选自丙烯酸十二酯、丙烯酸丁酯、丙烯酸-β-羟乙酯、丙烯酸、丙烯酸羟丙酯中的至少一种；所述光引发剂选自二苯甲酮、苯乙酮、α-羟基酮、α-氨基酮类中的至少一种；所述热固化剂为多异氰酸酯类固化剂；所述功能添加剂选自增塑剂、硅烷偶联剂、阻聚剂中的至少一种；所述溶解溶剂选自丙酮、甲苯、丙二醇、乙酸乙酯、二氯甲烷、N,N-二甲基甲酰胺、N-甲基吡咯烷酮、丙二醇甲醚醋酸酯中的至少一种。
进一步地，所述增塑剂选自邻苯二甲酸酯类、磷酸酯类、乙二酸酯类、葵二酸酯类中的至少一种；所述阻聚剂选自对苯二酚、蒽醌、对甲氧基苯酚中的至少一种。
本发明的另一目的在于提供一种光致失黏胶膜层的制备方法，包括步骤：
S1、将下述按质量百分数表示的各物质充分混合，获得光致失黏胶；
余量为溶解溶剂；
其中，所述多光敏官能团低聚物中光敏官能团的数量至少为两个，聚合度不超过150；
S2、将所述光致失黏胶涂覆于防粘纸上成膜，并置于110℃～150℃下烘烤5min～5min，获得光致失黏胶膜层。
进一步地，在所述步骤S2中，将所述光致失黏胶涂覆于所述防粘纸上成40μm～100μm厚度的膜。
进一步地，所述光致失黏胶膜层的厚度为5μm～40μm。
本发明的另一目的还在于提供一种如上任一所述的制备方法获得的光致失黏胶膜层在偏光片中的应用。
进一步地，所述应用还包括：采用UV光照射所述偏光片1min～1.5h，以将所述偏光片进行剥离。
本发明提供了一种以丙烯酸酯压敏胶为主、辅助以光引发剂及多光敏官能团低聚物的光致失黏胶组合物，当应用该光致失黏胶组合物时，在UV照射前，该光致失黏胶组合物能够展现良好的粘着特性，以满足偏光片贴片制程和信赖性要求；而需剥离由该光致失黏胶组合物制成的光致失黏胶膜层时，仅需在UV光下照射一定时间后即可，此时该光致失黏胶组合物中的多光敏官能团低聚物发生交联反应，与其他直链分子形成复杂的互穿网格状结构，导致180°剥离强度降至几乎为零，从而展示了很好的失黏性能，便于拆离，而不对贴覆的基板表面产生破坏和残胶脏污，从而应用于偏光片与基板的贴合与剥离时体现出良好的应用效果。
附图说明
通过结合附图进行的以下描述，本发明的实施例的上述和其它方面、特点和优点将变得更加清楚，附图中：
图1是现有技术中偏光片的结构示意图；
图2是根据本发明的偏光片的结构示意图；
图3是根据本发明的光致失黏胶组合物在应用过程中UV照射前的SEM图片；
图4是根据本发明的光致失黏胶组合物在应用过程中UV照射后的SEM图片。
具体实施方式
以下，将参照附图来详细描述本发明的实施例。然而，可以以许多不同的形式来实施本发明，并且本发明不应该被解释为限制于这里阐述的具体实施例。相反，提供这些实施例是为了解释本发明的原理及其实际应用，从而使本领域的其他技术人员能够理解本发明的各种实施例和适合于特定预期应用的各种修改。在附图中，为了清楚起见，可以夸大元件的形状和尺寸，并且相同的标号将始终被用于表示相同或相似的元件。
本发明提供了一种光致失黏胶组合物，其包括如下按质量百分数分配的各组分：5％～35％的丙烯酸酯类单体、5％～35％的多光敏官能团低聚物、1％～4％的光引发剂、1％～4％的热固化剂、0.2％～3％的功能添加剂，余量为溶解溶剂。
具体来讲，多光敏官能团低聚物中光敏官能团的数量至少为两个，且聚合度不超过150。
更为具体地，多光敏官能团低聚物中的光敏官能团可以选自丙烯酸基、甲基丙烯酸甲基、炔基、烯丙基、丙烯酰胺基、乙烯基醚基、乙烯基硫醚基、乙烯基胺基、环丙烷基等具有双键、三键或环等官能团的基团中的至少一种。
如此，多光敏官能团低聚物优选自二官能团聚氨酯丙烯酸酯、三官能团聚氨酯丙烯酸酯、四官能团聚氨酯丙烯酸酯、五官能团聚氨酯丙烯酸酯、六官能团聚氨酯丙烯酸酯中的至少一种。
为了配合上述多光敏官能团低聚物，在该光致失黏胶组合物中，光引发剂优选自二苯甲酮、苯乙酮、α-羟基酮、α-氨基酮类中的至少一种。
一般地，丙烯酸酯类单体、热固化剂以及功能添加剂的选择较为常规，如丙烯酸酯类单体可选自丙烯酸十二酯、丙烯酸丁酯、丙烯酸-β-羟乙酯、丙烯酸、丙烯酸羟丙酯中的至少一种，热固化剂可以为多异氰酸酯类固化剂，功能添加剂可以分为增塑剂、硅烷偶联剂、阻聚剂等，并且增塑剂可以选自邻苯二甲酸酯类、磷酸酯类、乙二酸酯类、葵二酸酯类中的至少一种，而阻聚剂可以选自对苯二酚、蒽醌、对甲氧基苯酚中的至少一种。
同时，溶解溶剂也可以选自丙酮、甲苯、丙二醇、乙酸乙酯、二氯甲烷、N,N-二甲基甲酰胺、N-甲基吡咯烷酮、丙二醇甲醚醋酸酯中的至少一种。
上述丙烯酸酯类单体、热固化剂、功能添加剂以及溶解溶剂的具体选择，本领域技术人员参照现有技术即可，此处不再一一赘述。
以下将结合具体的实施例来表示上述光致失黏胶组合物的组成，当然，下述实施例的组成仅是具体的示例，并不能限定上述光致失黏胶组合物的全部组成；实施例1～实施例4以表格形式表示。
表1实施例1～实施例4的光致失黏胶组合物的组成
基于上述光致失黏胶组合物的组分，本发明还提供了一种光致失黏胶膜层的制备方法，其包括下述步骤：
在步骤S1中，将按质量百分数表示的各原料充分混合，获得光致失黏胶。
具体来讲，原料包括5％～35％的丙烯酸酯类单体、5％～35％的多光敏官能团低聚物、1％～4％的光引发剂、1％～4％的热固化剂、0.2％～3％的功能添加剂、以及余量的溶解溶剂；换句话说，即该光致失黏胶膜层是以上述光致失黏胶组合物为原料来制备的，或者说，该光致失黏胶膜层是上述光致失黏胶组合物的具体使用形式。
更为具体地，多光敏官能团低聚物中光敏官能团的数量至少为两个，且聚合度不超过150。
在该光致失黏胶膜层的原料中，各组分的选择参照上述光致失黏胶组合物的选择即可，此处不再一一赘述。
一般地，将上述各原料混合后，充分搅拌1h～3h后即可获得光致失黏胶。
在步骤S2中，将光致失黏胶涂覆于防粘纸上成膜，并置于110℃～150℃下烘烤5min～5min，获得光致失黏胶膜层。
具体来讲，在该步骤中，将光致失黏胶涂覆于防粘纸上形成40μm～100μm厚度的膜，该膜经烘烤处理，即获得厚度为5μm～40μm的光致失黏胶膜层。
经上述制备方法制备获得的光致失黏胶膜层能够应用于偏光片中，即将上述光致失黏胶膜层与离型膜、相位差膜、偏光膜、保护膜等叠层，即获得偏光片。如图2所示的偏光片，其包括依次叠层设置的离型膜21、光致失黏胶膜层22、相位差膜23、偏光膜24和保护膜25。
上述偏光片一般通过贴片制程得以应用，即将去除离型膜21后的偏光片分别贴付到TFT基板和CF基板侧，从而使液晶显示面板得以正常显示。
此时，基于上述光致失黏胶组合物的光致失黏胶膜层能够展现良好的粘着特性，以满足偏光片贴片制程和信赖性要求。
而当偏光片需要从液晶显示面板上剥离时，仅需要采用UV光照射上述偏光片1min～1.5h即可。
此处UV光具体指波长为365nm～420nm的光。
具体来讲，当在UV光下照射一定时间后，上述光致失黏胶组合物中的多光敏官能团低聚物发生交联反应，与其他直链分子形成复杂的互穿网格状结构，导致180°剥离强度降至几乎为零，从而展示了很好的失黏性能，便于拆离，而不对贴覆的基板表面产生破坏和残胶脏污。
图3和图4分别示出了UV光照前后的偏光片的SEM图片，对比图3和图4可以看出，经UV光照后的偏光片呈现褶皱状，将更易于剥离去除。
很显然，照射时间越长，则上述交联反应等进行的更加彻底，相对来说，也越易剥离。
虽然已经参照特定实施例示出并描述了本发明，但是本领域的技术人员将理解：在不脱离由权利要求及其等同物限定的本发明的精神和范围的情况下，可在此进行形式和细节上的各种变化。
Claims (10)
1.一种光致失黏胶组合物，其特征在于，包括如下按质量百分数分配的各组分：
余量为溶解溶剂；
其中，所述多光敏官能团低聚物中光敏官能团的数量至少为两个，聚合度不超过150。
2.根据权利要求1所述的光致失黏胶组合物，其特征在于，所述多光敏官能团低聚物中的光敏官能团选自丙烯酸基、甲基丙烯酸甲基、炔基、烯丙基、丙烯酰胺基、乙烯基醚基、乙烯基硫醚基、乙烯基胺基、环丙烷基中的至少一种。
3.根据权利要求2所述的光致失黏胶组合物，其特征在于，所述多光敏官能团低聚物选自二官能团聚氨酯丙烯酸酯、三官能团聚氨酯丙烯酸酯、四官能团聚氨酯丙烯酸酯、五官能团聚氨酯丙烯酸酯、六官能团聚氨酯丙烯酸酯中的至少一种。
4.根据权利要求1-3任一所述的光致失黏胶组合物，其特征在于，所述丙烯酸酯类单体选自丙烯酸十二酯、丙烯酸丁酯、丙烯酸-β-羟乙酯、丙烯酸、丙烯酸羟丙酯中的至少一种；
所述光引发剂选自二苯甲酮、苯乙酮、α-羟基酮、α-氨基酮类中的至少一种；
所述热固化剂为多异氰酸酯类固化剂；
所述功能添加剂选自增塑剂、硅烷偶联剂、阻聚剂中的至少一种；
所述溶解溶剂选自丙酮、甲苯、丙二醇、乙酸乙酯、二氯甲烷、N,N-二甲基甲酰胺、N-甲基吡咯烷酮、丙二醇甲醚醋酸酯中的至少一种。
5.根据权利要求4所述的光致失黏胶组合物，其特征在于，所述增塑剂选自邻苯二甲酸酯类、磷酸酯类、乙二酸酯类、葵二酸酯类中的至少一种；所述阻聚剂选自对苯二酚、蒽醌、对甲氧基苯酚中的至少一种。
6.一种光致失黏胶膜层的制备方法，其特征在于，包括步骤：
S1、将下述按质量百分数表示的各物质充分混合，获得光致失黏胶；
余量为溶解溶剂；
其中，所述多光敏官能团低聚物中光敏官能团的数量至少为两个，聚合度不超过150；
S2、将所述光致失黏胶涂覆于防粘纸上成膜，并置于110℃～150℃下烘烤5min～5min，获得光致失黏胶膜层。
7.根据权利要求6所述的制备方法，其特征在于，在所述步骤S2中，将所述光致失黏胶涂覆于所述防粘纸上成40μm～100μm厚度的膜。
8.根据权利要求6或7所述的制备方法，其特征在于，所述光致失黏胶膜层的厚度为5μm～40μm。
9.如权利要求6-8任一所述的制备方法获得的光致失黏胶膜层在偏光片中的应用。
10.根据权利要求9所述的应用，其特征在于，所述应用还包括：采用UV光照射所述偏光片1min～1.5h，以将所述偏光片进行剥离。