CN107986622A - A kind of plum green color glaze and preparation method thereof - Google Patents
A kind of plum green color glaze and preparation method thereof Download PDFInfo
- Publication number
- CN107986622A CN107986622A CN201711142929.8A CN201711142929A CN107986622A CN 107986622 A CN107986622 A CN 107986622A CN 201711142929 A CN201711142929 A CN 201711142929A CN 107986622 A CN107986622 A CN 107986622A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- soil
- green color
- plum green
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of ceramic technology field, more particularly to a kind of plum green color glaze and preparation method thereof.The plum green color glaze is by major ingredient and auxiliary material in mass ratio 56:1 composition, the major ingredient are formed by the Raw material processing of following parts by weight：Profound 15 25 parts of the glaze soil of Huangshi, 10 15 parts of organobentonite, 20 30 parts of little Mei glaze soil, 20 30 parts of small stream mouth glaze soil, 15 25 parts of Zhou village glaze soil, 5 10 parts of kaolin, the auxiliary material is formed by the Raw material processing of following parts by weight：20 40 parts of Cab-O-sil, 6 12 parts of soda ash, 10 18 parts of feldspar powder, 10 ~ 15 parts of aluminium hydroxide, 58 parts of zinc oxide, 8 12 parts of calcium carbonate, 68 parts of borax, 26 parts of potassium carbonate, 6 10 parts of barium sulfate.The new plum green color glaze raw material selection is reasonable, temperature-controllable of cooking, and high yield rate, product homogeneity is good, and processing controllability is good.
Description
Technical field
The present invention relates to a kind of ceramic technology field, more particularly to a kind of plum green color glaze and preparation method thereof.
Background technology
Longquan, Zhejiang Province brother's kiln is one of Chinese five big kilns of Song Dynasty, its produce plum green glaze porcelain ware by generation treasure.Zhejiang
The preparation process of Jiang Longquan brother's kilns is：Celadon product is different with the shrinking percentage of tire using glaze in the cooling procedure after burning till, glaze
Irregular texture is cracked into, forms the celadon product of exquisiteness.
But plum green color glaze glaze of the prior art selection is harsh, and firing temperature is difficult to control, yield rate is low during klining, quality
Influenced greatly by processing qualification, homogeneity is poor, therefore urgently develops a kind of new plum green color glaze.
The content of the invention
A kind of deficiency it is an object of the present invention to the plum green color glaze for solving the prior art, there is provided new plum
Cyan glaze, the new plum green color glaze raw material selection is reasonable, firing temperature is controllable, and high yield rate, product homogeneity is good, and processing can
Control property is good.
The second object of the present invention is to provide a kind of preparation method of new plum green color glaze.
The third object of the present invention is to provide a kind of secret color glaze porcelain being process using the new plum green color glaze.
The technical solution adopted by the present invention to solve the technical problems is：
A kind of plum green color glaze, the plum green color glaze is by major ingredient and auxiliary material 5-6 in mass ratio:1 composition, the major ingredient is by following
The Raw material processing of parts by weight forms：15-25 parts of Huangshi profound glaze soil, 10-15 parts of organobentonite, 20-30 parts of little Mei glaze soil, small stream
Mouthful 20-30 parts of glaze soil, 15-25 parts of Zhou village glaze soil, 5-10 parts of kaolin, the auxiliary material by the Raw material processing of following parts by weight and
Into：20-40 parts of Cab-O-sil, 6-12 parts of soda ash, 10-18 parts of feldspar powder, 10 ~ 15 parts of aluminium hydroxide, 5-8 parts of zinc oxide, carbonic acid
8-12 parts of calcium, 6-8 parts of borax, 2-6 parts of potassium carbonate, 6-10 parts of barium sulfate.
Preferably, the plum green color glaze is by major ingredient and auxiliary material in mass ratio 6:1 composition, the major ingredient is by following parts by weight
Raw material processing form：Profound 20 parts of the glaze soil of Huangshi, 12 parts of organobentonite, 25 parts of little Mei glaze soil, 25 parts of small stream mouth glaze soil, Zhou village
20 parts of glaze soil, 8 parts of kaolin, the auxiliary material is formed by the Raw material processing of following parts by weight：30 parts of Cab-O-sil, 10 parts of soda ash are long
12 parts of mountain flour, 12 parts of aluminium hydroxide, 6 parts of zinc oxide, 10 parts of calcium carbonate, 6 parts of borax, 4 parts of potassium carbonate, 8 parts of barium sulfate.
A kind of preparation method of plum green color glaze, the preparation method step are as follows：
（1）The profound glaze soil of the Huangshi of formula ratio, organobentonite, little Mei glaze soil, small stream mouth glaze soil, Zhou village glaze soil and kaolin are mixed
Conjunction obtains major ingredient；
（2）By the Cab-O-sil of formula ratio, soda ash, feldspar powder, aluminium hydroxide, zinc oxide, calcium carbonate, borax, potassium carbonate and sulfuric acid
Barium is mixed to get auxiliary material；
（3）Major ingredient and auxiliary material are mixed in proportion, mixture is mixed with ballstone, water 1 ﹕ 0.8-0.9 of 1.3-1.5 ﹕ in mass ratio, is filled
Glaze slip is obtained after dividing grinding；
（4）, in 750~850 DEG C of biscuitings, it will be cooled down after secret color glaze porcelain body drying；
（5）By step（3）Glaze slip to be modulated into water content be 30-35%, interior glaze is applied to the color glaze porcelain billet body using glaze method is swung,
Then outer glaze is applied to color glaze porcelain billet body using dipping in glaze method；
（6）Color glaze porcelain billet body after glazing is fired by glaze, obtains plum green color glaze.
Preferably, step（6）Described in be fired by glaze and include evaporation stage, reduction phase successively, into porcelain stage and holding stage,
The temperature of the evaporation stage is 400-480 DEG C；
The temperature of the reduction phase is 950-1000 DEG C；
The temperature into the porcelain stage is 1080-1150 DEG C；
The temperature of the holding stage is 1080-1150 DEG C, 5-8min.
The beneficial effects of the invention are as follows：The new plum green color glaze raw material selection is reasonable, temperature-controllable of cooking, yield rate
Height, product homogeneity is good, and processing controllability is good.
Embodiment
Below by specific embodiment, technical scheme is described in further detail.
Embodiment 1：
A kind of plum green color glaze, the plum green color glaze is by major ingredient and auxiliary material in mass ratio 5:1 composition, the major ingredient is by following heavy
The Raw material processing of amount part forms：Profound 15 parts of the glaze soil of Huangshi, 10 parts of organobentonite, 20 parts of little Mei glaze soil, 20 parts of small stream mouth glaze soil,
15 parts of Zhou village glaze soil, 5 parts of kaolin, the auxiliary material is formed by the Raw material processing of following parts by weight：20 parts of Cab-O-sil, soda ash 6
Part, 10 parts of feldspar powder, 10 parts of aluminium hydroxide, 5 parts of zinc oxide, 8 parts of calcium carbonate, 6 parts of borax, 2 parts of potassium carbonate, barium sulfate 6
Part；
Its preparation methods steps are as follows：
（1）The profound glaze soil of the Huangshi of formula ratio, organobentonite, little Mei glaze soil, small stream mouth glaze soil, Zhou village glaze soil and kaolin are mixed
Conjunction obtains major ingredient；
（2）By the Cab-O-sil of formula ratio, soda ash, feldspar powder, aluminium hydroxide, zinc oxide, calcium carbonate, borax, potassium carbonate and sulfuric acid
Barium is mixed to get auxiliary material；
（3）Major ingredient and auxiliary material are mixed in proportion, mixture is mixed with 1 ﹕ 0.8 of ballstone, water 1.3 ﹕ in mass ratio, after being fully ground
Obtain glaze slip；
（4）, in 750-780 DEG C of biscuiting, it will be cooled down after secret color glaze porcelain body drying；
（5）By step（3）Glaze slip be modulated into water content as 30%, interior glaze is applied to the color glaze porcelain billet body using glaze method is swung, so
Outer glaze is applied to color glaze porcelain billet body using dipping in glaze method afterwards；
（6）Color glaze porcelain billet body after glazing is fired by glaze, obtains plum green color glaze, step（6）Described in be fired by glaze and include successively
Evaporation stage, reduction phase, into porcelain stage and holding stage,
The temperature of the evaporation stage is 400-420 DEG C；
The temperature of the reduction phase is 950-980 DEG C；
The temperature into the porcelain stage is 1080-1100 DEG C；
The temperature of the holding stage is 1080-1100 DEG C, 8min.
Embodiment 2：
A kind of plum green color glaze, the plum green color glaze is by major ingredient and auxiliary material in mass ratio 6:1 composition, the major ingredient is by following heavy
The Raw material processing of amount part forms：Profound 25 parts of the glaze soil of Huangshi, 15 parts of organobentonite, 30 parts of little Mei glaze soil, 30 parts of small stream mouth glaze soil,
25 parts of Zhou village glaze soil, 10 parts of kaolin, the auxiliary material is formed by the Raw material processing of following parts by weight：40 parts of Cab-O-sil, soda ash 12
Part, 18 parts of feldspar powder, 15 parts of aluminium hydroxide, 8 parts of zinc oxide, 12 parts of calcium carbonate, 8 parts of borax, 6 parts of potassium carbonate, barium sulfate 10
Part, magnetic order mesoporous 15 parts of nickel ferrite based magnetic loaded.
Its preparation methods steps are as follows：
（1）The profound glaze soil of the Huangshi of formula ratio, organobentonite, little Mei glaze soil, small stream mouth glaze soil, Zhou village glaze soil and kaolin are mixed
Conjunction obtains major ingredient；
（2）By the Cab-O-sil of formula ratio, soda ash, feldspar powder, aluminium hydroxide, zinc oxide, calcium carbonate, borax, potassium carbonate and sulfuric acid
Barium is mixed to get auxiliary material；
（3）Major ingredient and auxiliary material are mixed in proportion, mixture is mixed with 1 ﹕ 0.9 of ballstone, water 1.5 ﹕ in mass ratio, after being fully ground
Obtain glaze slip；
（4）, in 820~850 DEG C of biscuitings, it will be cooled down after secret color glaze porcelain body drying；
（5）By step（3）Glaze slip be modulated into water content as 35%, interior glaze is applied to the color glaze porcelain billet body using glaze method is swung, so
Outer glaze is applied to color glaze porcelain billet body using dipping in glaze method afterwards；
（6）Color glaze porcelain billet body after glazing is fired by glaze, obtains plum green color glaze, step（6）Described in be fired by glaze and include successively
Evaporation stage, reduction phase, into porcelain stage and holding stage,
The temperature of the evaporation stage is 460-480 DEG C；
The temperature of the reduction phase is 980-1000 DEG C；
The temperature into the porcelain stage is 1130-1150 DEG C；
The temperature of the holding stage is 1130-1150 DEG C, 5min.
Embodiment 3：
A kind of plum green color glaze, the plum green color glaze is by major ingredient and auxiliary material in mass ratio 6:1 composition, the major ingredient is by following heavy
The Raw material processing of amount part forms：Profound 20 parts of the glaze soil of Huangshi, 12 parts of organobentonite, 25 parts of little Mei glaze soil, 25 parts of small stream mouth glaze soil,
20 parts of Zhou village glaze soil, 8 parts of kaolin, the auxiliary material is formed by the Raw material processing of following parts by weight：30 parts of Cab-O-sil, soda ash 10
Part, 12 parts of feldspar powder, 12 parts of aluminium hydroxide, 6 parts of zinc oxide, 10 parts of calcium carbonate, 6 parts of borax, 4 parts of potassium carbonate, barium sulfate 8
Part, magnetic order mesoporous 10 parts of nickel ferrite based magnetic loaded.
Its preparation methods steps are as follows：
（1）The profound glaze soil of the Huangshi of formula ratio, organobentonite, little Mei glaze soil, small stream mouth glaze soil, Zhou village glaze soil and kaolin are mixed
Conjunction obtains major ingredient；
（2）By the Cab-O-sil of formula ratio, soda ash, feldspar powder, aluminium hydroxide, zinc oxide, calcium carbonate, borax, potassium carbonate and sulfuric acid
Barium is mixed to get auxiliary material；
（3）Major ingredient and auxiliary material are mixed in proportion, mixture is mixed with 1 ﹕ 0.85 of ballstone, water 1.4 ﹕ in mass ratio, is fully ground
After obtain glaze slip；
（4）, in 800-820 DEG C of biscuiting, it will be cooled down after secret color glaze porcelain body drying；
（5）By step（3）Glaze slip be modulated into water content as 32%, interior glaze is applied to the color glaze porcelain billet body using glaze method is swung, so
Outer glaze is applied to color glaze porcelain billet body using dipping in glaze method afterwards；
（6）Color glaze porcelain billet body after glazing is fired by glaze, obtains plum green color glaze, step（6）Described in be fired by glaze and include successively
Evaporation stage, reduction phase, into porcelain stage and holding stage,
The temperature of the evaporation stage is 450-460 DEG C；
The temperature of the reduction phase is 980-990 DEG C；
The temperature into the porcelain stage is 1110-1120 DEG C；
The temperature of the holding stage is 1110-1120 DEG C, 6min.
The plum green color glaze raw material of embodiment 1-3 selects reasonable, temperature-controllable of cooking, and high yield rate, product homogeneity is good,
It is good to process controllability.Embodiment described above is a kind of preferable scheme of the present invention, not makees any shape to the present invention
Limitation in formula, also has other variations and remodeling on the premise of without departing from the technical solution described in claim.
Claims (4)
1. a kind of plum green color glaze, it is characterised in that the plum green color glaze is by major ingredient and auxiliary material 5-6 in mass ratio:1 composition,
The major ingredient is formed by the Raw material processing of following parts by weight：15-25 parts of Huangshi profound glaze soil, 10-15 parts of organobentonite, little Mei
20-30 parts of glaze soil, 20-30 parts of small stream mouth glaze soil, 15-25 parts of Zhou village glaze soil, 5-10 parts of kaolin, the auxiliary material is by following parts by weight
Raw material processing form：20-40 parts of Cab-O-sil, 6-12 parts of soda ash, 10-18 parts of feldspar powder, 10 ~ 15 parts of aluminium hydroxide, oxidation
5-8 parts of zinc, 8-12 parts of calcium carbonate, 6-8 parts of borax, 2-6 parts of potassium carbonate, 6-10 parts of barium sulfate.
A kind of 2. plum green color glaze according to claim 1, it is characterised in that：The plum green color glaze is by major ingredient and auxiliary material
In mass ratio 6:1 composition, the major ingredient are formed by the Raw material processing of following parts by weight：Profound 20 parts of the glaze soil of Huangshi, organobentonite
12 parts, 25 parts of little Mei glaze soil, 25 parts of small stream mouth glaze soil, 20 parts of Zhou village glaze soil, 8 parts of kaolin, the auxiliary material is by following parts by weight
Raw material processing forms：30 parts of Cab-O-sil, 10 parts of soda ash, 12 parts of feldspar powder, 12 parts of aluminium hydroxide, 6 parts of zinc oxide, calcium carbonate 10
Part, 6 parts of borax, 4 parts of potassium carbonate, 8 parts of barium sulfate.
A kind of 3. preparation method of the plum green color glaze described in claim 1 or 2, it is characterised in that：The preparation method step
It is as follows：
（1）The profound glaze soil of the Huangshi of formula ratio, organobentonite, little Mei glaze soil, small stream mouth glaze soil, Zhou village glaze soil and kaolin are mixed
Conjunction obtains major ingredient；
（2）By the Cab-O-sil of formula ratio, soda ash, feldspar powder, aluminium hydroxide, zinc oxide, calcium carbonate, borax, potassium carbonate and sulfuric acid
Barium is mixed to get auxiliary material；
（3）Major ingredient and auxiliary material are mixed in proportion, mixture is mixed with ballstone, water 1 ﹕ 0.8-0.9 of 1.3-1.5 ﹕ in mass ratio, is filled
Glaze slip is obtained after dividing grinding；
（4）, in 750~850 DEG C of biscuitings, it will be cooled down after secret color glaze porcelain body drying；
（5）By step（3）Glaze slip to be modulated into water content be 30-35%, interior glaze is applied to the color glaze porcelain billet body using glaze method is swung,
Then outer glaze is applied to color glaze porcelain billet body using dipping in glaze method；
（6）Color glaze porcelain billet body after glazing is fired by glaze, obtains plum green color glaze.
4. the preparation method of plum green color glaze according to claim 1, it is characterised in that：Step（6）Described in glaze firing according to
It is secondary including evaporation stage, reduction phase, into porcelain stage and holding stage,
The temperature of the evaporation stage is 400-480 DEG C；
The temperature of the reduction phase is 950-1000 DEG C；
The temperature into the porcelain stage is 1080-1150 DEG C；
The temperature of the holding stage is 1080-1150 DEG C, 5-8min.