CN106477884A - A kind of rust red glaze and preparation method thereof - Google Patents
A kind of rust red glaze and preparation method thereof Download PDFInfo
- Publication number
- CN106477884A CN106477884A CN201610833738.5A CN201610833738A CN106477884A CN 106477884 A CN106477884 A CN 106477884A CN 201610833738 A CN201610833738 A CN 201610833738A CN 106477884 A CN106477884 A CN 106477884A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- preparation
- rust red
- red glaze
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to pottery glaze technical field is and in particular to a kind of rust red glaze and preparation method thereof, it is to be prepared from by the raw material of following parts by weight：SiO280 to 100 parts, Al2O315 to 20 parts, 4 to 10 parts of CaO, CaCO325 to 30 parts, Na25 to 10 parts of 4 to 8 parts of O, MgO, K26 to 9 parts of O, Fe2O320 to 30 parts, the applied range of preparation method of described rust red glaze disclosed by the invention and should be readily appreciated that, goodish effect is all played in reduction to production cost and the training to technical staff, rust red glaze of the present invention is that colored glaze adds a new color, and the innovation for colored glaze enhances a step again.
Description
Technical field
The invention belongs to pottery glaze technical field is and in particular to a kind of rust red glaze and preparation method thereof.
Background technology
China's pottery has a long history, and is the outstanding representative of human civilization progress, spread all over now we life each
Field, improves our quality of life.With the progress of technique, the quality of pottery is also lifted constantly, various on market
Pottery system various in style tinkling of jades meet the eye on every side, its practicality and dicoration are all stronger, but are from making more than the dicoration of existing pottery
To innovate in type, its color is also relatively single few, colored glaze still awaits innovating hyperchromic, to meet creation and decoration demand.
Content of the invention
For the deficiencies in the prior art, the present invention proposes a kind of rust red glaze and preparation method thereof, existing in order to make up
The deficiency of technology.
The technical scheme is that and be achieved in that：A kind of rust red glaze, it is by the raw material of following parts by weight
It is prepared from：SiO280 to 100 parts, Al2O315 to 20 parts, 4 to 10 parts of CaO, CaCO325 to 30 parts, Na2O 4 to 8
Part, 5 to 10 parts of MgO, K26 to 9 parts of O, Fe2O320 to 30 parts.
It is to be prepared from by the raw material of following parts by weight：SiO290 parts, Al2O318 parts, 8 parts of CaO, CaCO3
28 parts, Na28 parts of 6 parts of O, MgO, K28 parts of O, Fe2O325 parts.
Its preparation method is as follows：
1）Choose each component of above-mentioned weight portion, mix homogeneously, obtain compound；
2）Compound is crossed after 80 mesh sieves, melting 1 to 1 .5 hour at 900 to 1000 DEG C, then at 1300 to 1500 DEG C,
Melting 2 hours, then water quenching, obtain block glaze；
3）By block glaze after wet ball grinding, remove impurity of sieving obtains glaze slip, and the concentration of glaze slip is 1 .5 to 1.8g/mL, by glaze
Slurry imposes on billet surface, after the moisture being dried to glaze slip is less than 1%, respectively at 1000 to 1100 DEG C and 1200 to 1250 DEG C
Alternately fire 2 times, each firing time is 20 to 30 minutes, after cooling, obtains rust red glaze.
Described drying is to dry at 80 to 160 DEG C.
Described melting is carried out in box siliconits resistance furnace.
Described it is cooled to naturally cool to room temperature with stove.
The present invention has following beneficial effect：The application model of the preparation method of described rust red glaze disclosed by the invention
Enclose extensively and it can be readily appreciated that goodish effect is all played in the reduction to production cost and the training to technical staff；The present invention's
In preparation process, fusion process adopts stagewise to rust red glaze, and sintering procedure is alternately fired using high and low temperature, by this
The melting of kind of form and fire each component of guarantee and effectively combine, and then the acquisition uniformity preferable rust red glaze；Ferrum of the present invention
The red glaze that becomes rusty is that colored glaze adds a new color, and the innovation for colored glaze enhances a step again.
Specific embodiment
A kind of rust red glaze, it is to be prepared from by the raw material of following parts by weight：SiO280 to 100 parts, Al2O3
15 to 20 parts, 4 to 10 parts of CaO, CaCO325 to 30 parts, Na25 to 10 parts of 4 to 8 parts of O, MgO, K26 to 9 parts of O, Fe2O3
20 to 30 parts.It is to be prepared from by the raw material of following parts by weight：SiO290 parts, Al2O318 parts, 8 parts of CaO, CaCO3
28 parts, Na28 parts of 6 parts of O, MgO, K28 parts of O, Fe2O325 parts.Its preparation method is as follows：1）Choose each of above-mentioned weight portion
Component, mix homogeneously, obtain compound；2）Compound is crossed after 80 mesh sieves, at 900 to 1000 DEG C, melting 1 to 1 .5 hour, connects
At 1300 to 1500 DEG C, melting 2 hours, then water quenching, obtain block glaze；3）By block glaze after wet ball grinding,
Remove impurity of sieving obtains glaze slip, and the concentration of glaze slip is 1 .5 to 1.8g/mL, glaze slip is imposed on billet surface, is dried to glaze slip
After moisture is less than 1%, alternately fire at 1000 to 1100 DEG C and 1200 to 1250 DEG C 2 times respectively, each firing time is 20
To 30 minutes, after cooling, obtain rust red glaze.Described drying is to dry at 80 to 160 DEG C.Described melting is in case
Carry out in formula siliconits resistance furnace.Described it is cooled to naturally cool to room temperature with stove.
Embodiment 1：Take SiO290 kg, Al2O318 kg, CaO 8 kg, CaCO328 kg, Na2O 6 kg, MgO 8
Kg, K2O 8 kg, Fe2O325 kg, their mix homogeneously obtain compound, compound are crossed after 80 mesh sieves, 900 to 1000
Melting 1 to 1 .5 hour at DEG C, then at 1300 to 1500 DEG C, melting 2 hours, then water quenching, obtain block glaze；By block
After wet ball grinding, remove impurity of sieving obtains glaze slip to shape glaze, and the concentration of glaze slip is 1 .5 to 1.8g/mL, and glaze slip is imposed on base substrate
Surface, after the moisture being dried to glaze slip is less than 1%, alternately fires 2 respectively at 1000 to 1100 DEG C and 1200 to 1250 DEG C
Secondary, each firing time is 20 to 30 minutes, after cooling, obtains rust red glaze.Described drying is to dry at 80 to 160 DEG C
Dry.Described melting is carried out in box siliconits resistance furnace.Described it is cooled to naturally cool to room temperature with stove.
Embodiment 2：Take SiO280 kg, Al2O315 kg, CaO 4 kg, CaCO325 kg, Na2O 4 kg, MgO 5
Kg, K2O 6 kg, Fe2O320 kg, their mix homogeneously obtain compound, compound are crossed after 80 mesh sieves, 900 to 1000
Melting 1 to 1 .5 hour at DEG C, then at 1300 to 1500 DEG C, melting 2 hours, then water quenching, obtain block glaze；By block
After wet ball grinding, remove impurity of sieving obtains glaze slip to shape glaze, and the concentration of glaze slip is 1 .5 to 1.8g/mL, and glaze slip is imposed on base substrate
Surface, after the moisture being dried to glaze slip is less than 1%, alternately fires 2 respectively at 1000 to 1100 DEG C and 1200 to 1250 DEG C
Secondary, each firing time is 20 to 30 minutes, after cooling, obtains rust red glaze.Described drying is to dry at 80 to 160 DEG C
Dry.Described melting is carried out in box siliconits resistance furnace.Described it is cooled to naturally cool to room temperature with stove.
Embodiment 3：Take SiO2100 kg, Al2O320 kg, CaO 10 kg, CaCO330 kg, Na2O 8 kg, MgO
10 kg, K2O 9 kg, Fe2O330 kg, their mix homogeneously obtain compound, and compound is crossed after 80 mesh sieves, 900 to
Melting 1 to 1 .5 hour at 1000 DEG C, then at 1300 to 1500 DEG C, melting 2 hours, then water quenching, obtain block glaze；
By block glaze after wet ball grinding, remove impurity of sieving obtains glaze slip, and the concentration of glaze slip is 1 .5 to 1.8g/mL, and glaze slip is imposed on
Billet surface, after the moisture being dried to glaze slip is less than 1%, alternately burns respectively at 1000 to 1100 DEG C and 1200 to 1250 DEG C
System 2 times, each firing time is 20 to 30 minutes, after cooling, obtains rust red glaze.Described drying is at 80 to 160 DEG C
Lower drying.Described melting is carried out in box siliconits resistance furnace.Described it is cooled to naturally cool to room temperature with stove.
Claims (6)
1. a kind of rust red glaze is it is characterised in that it is to be prepared from by the raw material of following parts by weight：SiO280 to
100 parts, Al2O315 to 20 parts, 4 to 10 parts of CaO, CaCO325 to 30 parts, Na25 to 10 parts of 4 to 8 parts of O, MgO, K2O 6
To 9 parts, Fe2O320 to 30 parts.
2. rust red glaze according to claim 1 is it is characterised in that it is by the raw material preparation of following parts by weight
Become：SiO290 parts, Al2O318 parts, 8 parts of CaO, CaCO328 parts, Na28 parts of 6 parts of O, MgO, K28 parts of O, Fe2O325
Part.
3. a kind of preparation method of rust red glaze as claimed in claim 1 or 2 is it is characterised in that its preparation method is as follows：
1）Choose each component of above-mentioned weight portion, mix homogeneously, obtain compound；
2）Compound is crossed after 80 mesh sieves, melting 1 to 1 .5 hour at 900 to 1000 DEG C, then at 1300 to 1500 DEG C,
Melting 2 hours, then water quenching, obtain block glaze；
3）By block glaze after wet ball grinding, remove impurity of sieving obtains glaze slip, and the concentration of glaze slip is 1 .5 to 1.8g/mL, by glaze
Slurry imposes on billet surface, after the moisture being dried to glaze slip is less than 1%, respectively at 1000 to 1100 DEG C and 1200 to 1250 DEG C
Alternately fire 2 times, each firing time is 20 to 30 minutes, after cooling, obtains rust red glaze.
4. rust red glaze according to claim 3 preparation method it is characterised in that described drying be 80 to
Dry at 160 DEG C.
5. the preparation method of rust red glaze according to claim 3 is it is characterised in that described melting is in box silicon
Carry out in kryptol stove.
6. the preparation method of rust red glaze according to claim 3 is it is characterised in that described being cooled to is natural with stove
It is cooled to room temperature.