CN107938309A - A kind of anti-fluffing and anti-pilling processing method of light and thin type hair terylene fabric - Google Patents
A kind of anti-fluffing and anti-pilling processing method of light and thin type hair terylene fabric Download PDFInfo
- Publication number
- CN107938309A CN107938309A CN201711238250.9A CN201711238250A CN107938309A CN 107938309 A CN107938309 A CN 107938309A CN 201711238250 A CN201711238250 A CN 201711238250A CN 107938309 A CN107938309 A CN 107938309A
- Authority
- CN
- China
- Prior art keywords
- fabric
- low
- fluffing
- pressure plasma
- processing method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of anti-fluffing and anti-pilling processing method of light and thin type hair terylene fabric, including:Selection wool content is 20%~99%, the wool-polyester yarn of 12.5~19.23tex is weaved, then fabric is carried out boiling cloth, dehydration, open-width, braying is carried out again, rinse, dehydration, is put into microwave drying sizing-low-temperature atmosphere-pressure plasma processing, microwave drying sizing is first carried out, then carries out low-temperature atmosphere-pressure plasma treatment;Finally carry out soft finish, to obtain the final product.In the present invention microwave heating have it is efficient, energy saving, temperature is low, drying is uniform, without advantages such as thermal inertias, and magnetron industrialized production, convenient maintenance and replacement, maintenance cost is low, low-temperature atmosphere-pressure plasma technology carries out surface modification treatment by dielectric barrier discharge to the wool fiber in fabric, reduce the dosage of chemical reagent and water during mao wool fabric final finishing, energy conservation and environmental protection, improves the anti-fluffing and anti-pilling performance of fabric.
Description
Technical field
The invention belongs to the fabric processing method field of hair clothes, more particularly to a kind of anti-fluffing of light and thin type hair terylene fabric
Balling-up processing method.
Background technology
Hair is a kind of natural animal protein fibre, by being coated on the scale layer of outside, forms the cortical layer of wool entity,
The medullary substance layer three parts composition opaque with hair shaft center.The scale layer covered outside hair shaft is made of sheet epithelial cells, its
Shape can be divided into ring-type covering, tiles covering or polygon covering;The inside of scale layer, is to determine wool Main physical chemically
The main part cortical layer of matter, due to having disulfide bond and more hydrophilic radical between its macromolecular chain, fiber crimp is larger,
It is soft and with elasticity, hygroscopicity is strong, and warmth retention property is good.Due to the particularity of hair, early stage people are begun to using fur as one kind
The instrument of keep warm, utilization of the mankind to hair even can trace back to the Neolithic Age, from Central Asia to the world other ground
Area propagates, and later hair is developing progressively as Asia-Europe main textile raw material.
The species of hair has very much, including sheep's wool, the rabbit hair, mohair yarn, camel hair etc., due to some particularity of wool fibre
Can, made fabric also has unique effect.The felting property of wool fiber is utilized in early stage people, passes through non-weaver
Felt is made in scattered wool fibre by skill, and felt is made carpet or cap etc., by development for many years, the production method of hair wool fabric
Be not only limited to it is non-knit, wool yarn knitting, it is woven on utilization it is also more and more extensive.But either which kind of method for weaving, mesh
Preceding most of maos of wool fabrics also still utilize the felting property of wool fiber, are obtained by fulling.Therefore, although gained hair
Fabric is more thick and solid, thermal property is preferable, but fabric lines is unintelligible, has prodding and itching feeling, its pilling performance is even more to become
Troubling problem.
From mid-term the 1950s, various experts and scholars begin to study balling-up, and think that balling-up is one
A process, common statement are:Fluff-tangle-balling-up-come off.It is relatively more to influence balling-up factor, such as fiber surface morphology
And curling, the fineness of fiber, intensity etc., yarn twist, institutional framework, Density, processing method etc., and in woolens
Thing, since the particularity of wool fibre make it that its balling-up is even more serious.In order to meet current consumer to fabric quality and fashion
Property pursuit, many experts and scholars to improve the research that the landing-gear design of wool fabric has done series, also obtain it is certain into
Fruit.Improve the mode of woolen pilling property at present except having the twist for improving yarn, filoplume, fabric structure etc. more general
Time method outside, the technology of comparative maturity has resin finishing, wool modifying processing, ozone to arrange etc., although these methods are to changing
Kind wool fabric pilling property has certain effect, but mostly there is the problem of destroying fabric feeling and pollution.And 50 years this century
The low-temperature plasma processing textile techniques that generation starts to rise produce inert gas or oxygen-containing gas by using the method for electric discharge
Contain the plasma of a variety of high energy active particles such as various ions, excited state molecule, free radical and photon to textile surface
Processing is modified, not only almost fabric its intrinsic characteristic is not changed, also reduces the utilization of chemicals and water,
Be conducive to environmental protection, therefore, low-temperature atmosphere-pressure plasma technology on the textile with being increasingly becoming a kind of trend.
The content of the invention
The technical problems to be solved by the invention are to provide a kind of anti-fluffing and anti-pilling processing method of light and thin type hair terylene fabric,
This method energy conservation and environmental protection, it is efficient, fiber surface is modified, reduces the felting property of wool fibre, improves the anti-fluffing of fabric
Pilling property.
A kind of anti-fluffing and anti-pilling processing method of light and thin type hair terylene fabric of the present invention, comprises the following steps that:
(1) select wool content be 20%~99%, the wool-polyester yarn of 12.5~20.83tex weaved, by woven base
Fabric is carried out to boil cloth, dehydration after planting machine, then open-width;
(2) fabric of open-width is subjected to braying, removes the impurity such as natural impurity, dust, antistatic additive, rinsed, dehydration, puts
Enter in microwave drying and shaping-low-temperature atmosphere-pressure plasma processing, first carry out microwave drying sizing, then carry out low-temperature atmosphere-pressure
Plasma treatment;
(3) soft finish is carried out to the fabric after plasma treatment.
In the step (1) during weaving in order to during later stage plasma treatment than the more uniform density that can suitably increase fabric;
It is to infiltrate fabric and tentatively cleaned to boil cloth.
Braying is to accelerate wetting velocity and fully removal of impurities in the step (2).
Paregal O is added during braying in the step (2), does not influence later stage plasma treatment;The braying time for 20~
40min, braying temperature are room temperature.
The process conditions of microwave drying sizing are in the step (2):Setting temperature is 80-130 DEG C, and microwave frequency is
2450MHz, output power 100W, speed are 0.5~1m/min.
Low-temperature atmosphere-pressure plasma treatment is that fabric moisture regain is carried out at 10%~25% in the step (2);Low temperature is normal
Pressure plasma treatment process conditions be:Power is 300W~1000W, and speed is 0.5~1m/min.
Microwave drying sizing is consistent with the speed of low-temperature atmosphere-pressure plasma treatment in the step (2).
Microwave drying sizing-low-temperature atmosphere-pressure plasma processing is fixed by fabric feeding machine, microwave drying in the step (2)
Type equipment, low-temperature atmosphere-pressure plasma processing and control machine composition;
Fabric guide roll and expander are wherein equipped with fabric feeding machine, fabric is fed from fabric feeding machine, and fabric is transmitted to out by fabric guide roll
Fully unfolded after width roller;
Acupuncture axis, cloth pressing roller, deflector roll and deflector roll are equipped with microwave drying modular system, by the fabric of feeding by compress roll-in
In pricker into acupuncture axis, fabric is fixed on acupuncture axis by pricker, deflector roll guiding acupuncture axis and fabric movement;
Fabric guide roll, electrode dielectric pipe and grounding electrode medium tube, fabric guide roll are equipped with low-temperature atmosphere-pressure plasma processing
Fabric is imported, fabric is placed in electrode dielectric pipe and between grounding electrode medium tube mutually punctures the glow discharge layer of formation, connects
Dielectric barrier discharge produces plasma after indirect current, and fabric is handled;
The fabric export completed will be handled by controlling machine.
The distance between described deflector roll is 5-10m;2-4 electrode group is set between deflector roll.
The electrode dielectric pipe top layer is ceramics, and inside is metal powder;Grounding electrode medium tube by ground plane, metal layer and
Cooling device forms.
The radius of the grounding electrode medium tube is 3~10 times of electrode dielectric pipe.
The present invention provides a kind of sizing of microwave drying and the light and thin type hair terylene fabric of low-temperature atmosphere-pressure plasma Combined Treatment
Method, select the appropriate Gao Zhimao of wool content to wash yarn first and weaved on fabric manufacture equipment, then through over-cooking cloth and braying
After processing, handled in microwave drying sizing-low-temperature plasma equipment, finally carry out soft finish, by force being stretched property,
The preferable light and thin type hair terylene fabric of feel, and improve the anti-fluffing and anti-pilling performance of fabric.Microwave heating be develop in recent years it is fast
Speed, very potential novel dried technology, it realizes the drying of material using the selectivity heating and penetrability of microwave,
With it is efficient, energy saving, temperature is low, drying is uniform, without advantages such as thermal inertias, and magnetron replace by industrialized production, maintenance
Convenient, maintenance cost is low;Low-temperature atmosphere-pressure plasma technology is carrying out table by dielectric barrier discharge to the wool fiber in fabric
Face modification, reduces the dosage of chemical reagent and water during mao wool fabric final finishing, energy conservation and environmental protection.And microwave treatment
Afterwards, the crystallinity of wool fiber and the degree of orientation all increase, and the intensity of fiber also makes moderate progress, and the scale of fiber surface
It is subject to certain destruction, into after rear road plasma processing, the Covalent bonding together from wool surfaces can be effectively removes
Lipid layer, so as to improve wool fabric wetability, and reduce the scale on its surface, reduce the felting property of wool fabric, change
It is apt to its pilling performance.And soft finish can be improved the feel of fabric.
Microwave drying sizing can carry out fabric in the case where temperature is relatively low drying and shaping in the present invention, and fine to wool
The scale in dimension table face has certain destruction, and the fabric shaped by microwave drying carries out plasma treatment again, carries significantly
The high effect of plasma treatment, and the power setting of microwave drying and plasma treatment is within the specific limits so that wool table
While the scale in face is sufficiently destroyed, not too much destroy polyester fiber surface, therefore, the felting property of hair terylene fabric and rise
While hair pilling property obtains improving, the physical mechanical property of fabric is not damaged;The selection of the higher count of yarn and fabric
The improvement of felting performance make it that fabric is also more frivolous.
Beneficial effect
Microwave heating has that efficient, energy saving, temperature is low, drying is uniform, without advantages such as thermal inertias in the present invention, and magnetic control
Industrialized production is managed, convenient maintenance and replacement, maintenance cost is low, and the fabric shaped by microwave drying is carried out at plasma again
Reason, substantially increases the effect of plasma treatment, low-temperature atmosphere-pressure plasma technology is by dielectric barrier discharge to the sheep in fabric
Wool fibre carries out surface modification treatment, reduces the dosage of chemical reagent and water during mao wool fabric final finishing, energy conservation and environmental protection,
Improve the anti-fluffing and anti-pilling performance of fabric.
Brief description of the drawings
Fig. 1 is the overall structure diagram of present device;
Fig. 2 is the structure diagram of microwave drying modular system of the present invention;
Fig. 3 is the structure diagram of low-temperature atmosphere-pressure plasma apparatus of the present invention;
Fig. 4 is Conventional cryogenic in microwave drying sizing-low-temperature atmosphere-pressure plasma processing in embodiment 1 and comparative example 1
The Circular test pilling experimental result comparison diagram of the fabric of atmospheric plasma processing equipment processing.
Embodiment
With reference to specific embodiment, the present invention is further explained.It is to be understood that these embodiments are merely to illustrate the present invention
Rather than limit the scope of the invention.In addition, it should also be understood that, after reading the content taught by the present invention, people in the art
Member can make various changes or modifications the present invention, and such equivalent forms equally fall within the application the appended claims and limited
Scope.
Embodiment 1
As shown in Figure 1-Figure 3, present embodiments provide microwave drying sizing-low-temperature atmosphere-pressure plasma processing, by into
Cloth machine 1, microwave drying modular system 2, low-temperature atmosphere-pressure plasma processing 3 and control machine 4 and form, wherein set in fabric feeding machine 1
There are fabric guide roll 6 and expander 7, acupuncture axis 11, cloth pressing roller 12, deflector roll 13 and deflector roll 20 are equipped with microwave drying modular system 2, it is low
Fabric guide roll 14, electrode dielectric pipe 9 and grounding electrode medium tube 10 are equipped with normal temperature and pressure plasma processing 3.
The distance between described deflector roll 13 and deflector roll 20 are 5-10m;3 electrode groups 8 are set between deflector roll 13 and deflector roll 20.
9 top layer of electrode dielectric pipe is ceramics 15, and inside is metal powder 16;Grounding electrode medium tube 10 is by ground plane
17th, metal layer 18 and cooling device 19 form.
A diameter of 1.12m of the grounding electrode medium tube 10, a diameter of 0.37m of electrode dielectric pipe 9.
The present embodiment additionally provides a kind of anti-fluffing and anti-pilling processing method of light and thin type hair terylene fabric, comprises the following steps that:
(1) 20.83tex, 70/30 hair is selected to wash yarn and weaved on circular knitting machine, the line length of fabric is 10.5mm/50
Coil.Room temperature is first carried out in kier after machine under fabric to soap, and fabric is infiltrated and is tentatively cleaned;Dehydration can incite somebody to action after soaping
Fabric carries out open-width along open-width line.
(2) fabric of open-width is put into rope-form washing dolly, add paregal O braying 30min, fully by antistatic additive,
The impurity such as machine oil, grass cuttings remove, and added paregal O is nonionic surfactant, does not influence plasma treatment below;Wash
It is rear to be rinsed well with clear water, be dehydrated on dryer, then fed microwave drying sizing-low-temperature atmosphere-pressure etc. from
In fabric feeding machine 1 in subprocessing equipment, fabric is transmitted to after expander 7 by fabric guide roll 6 is fully unfolded, then microwave drying
Cloth pressing roller 12 in modular system 2 is pressed in the pricker in acupuncture axis 11, and fabric is fixed on acupuncture axis 11 by pricker, deflector roll 13
With 20 collective effect of deflector roll, guiding acupuncture axis 11 and fabric movement, (speed 1m/min, microwave frequency 2450MHz, output
Power is 100W, and setting temperature is 80 DEG C, and 10% or so, the fabric arranged through microwave drying sizing is straight for processing material moisture regain below
Connected fabric guide roll 14 to import in low-temperature atmosphere-pressure plasma apparatus 3, fabric is placed in electrode dielectric pipe 9 and grounding electrode medium tube 10
Between the glow discharge layer that mutually breakdown is formed, its operating power is arranged to 400W, speed 1m/min, can after powering on
Carry out glow discharge and plasma treatment is carried out to fabric, then exported fabric by controlling machine 4.
(3) soft finish is carried out to the fabric after plasma treatment.Obtained fabric is subjected to Circular test pilling survey
Examination.
Comparative example 1
(1) 20.83tex, 70/30 hair is selected to wash yarn and weaved on circular knitting machine, the line length of fabric is 10.5mm/50
Coil.Room temperature is first carried out in kier after machine under fabric to soap, and fabric is infiltrated and is tentatively cleaned;Dehydration can incite somebody to action after soaping
Fabric carries out open-width along open-width line.
(2) fabric of open-width is put into rope-form washing dolly, add paregal O braying 30min, fully by antistatic additive,
The impurity such as machine oil, grass cuttings remove, and added paregal O is nonionic surfactant, does not influence plasma treatment below;Braying
Rinsed well with clear water, be dehydrated on dryer afterwards, air flow dryer drying and shaping, drying temperature is 80 DEG C, then is used
The processing of Conventional cryogenic atmospheric plasma processing equipment, speed 1m/min, power 400W.
(3) soft finish is carried out to the fabric after plasma treatment.Obtained fabric is subjected to Circular test pilling survey
Examination.
Fig. 4 shows:The anti-fluffing and anti-pilling series of Conventional cryogenic atmospheric plasma processing equipment processing fabric in this comparative example
For 2 grades, the anti-fluffing and anti-pilling of microwave drying sizing-low-temperature atmosphere-pressure plasma processing processing fabric is 3 grades in embodiment 1,
Understand by contrast, the fabric anti-fluffing and anti-pilling performance of microwave drying sizing-low-temperature atmosphere-pressure plasma processing processing is better than normal
Advise the fabric of low-temperature atmosphere-pressure plasma processing processing.
Claims (8)
1. a kind of anti-fluffing and anti-pilling processing method of light and thin type hair terylene fabric, comprises the following steps that:
(1) select wool content be 20%~99%, the wool-polyester yarn of 12.5~20.83tex weaved, by under woven fabric
Fabric is carried out after machine to boil cloth, dehydration, then open-width;
(2) fabric of open-width is subjected to braying, rinsed, dehydration, is put into microwave drying sizing-low-temperature atmosphere-pressure plasma treatment and sets
In standby, microwave drying sizing is first carried out, then carries out low-temperature atmosphere-pressure plasma treatment;
(3) soft finish is carried out to the fabric after plasma treatment.
A kind of 2. anti-fluffing and anti-pilling processing method of light and thin type hair terylene fabric described in accordance with the claim 1, it is characterised in that institute
Paregal O is added when stating braying in step (2);The braying time is 20~40min, and braying temperature is room temperature.
A kind of 3. anti-fluffing and anti-pilling processing method of light and thin type hair terylene fabric described in accordance with the claim 1, it is characterised in that institute
Stating the process conditions that microwave drying is shaped in step (2) is:Setting temperature is 80-130 DEG C, microwave frequency 2450MHz, output
Power is 100W, and speed is 0.5~1m/min.
A kind of 4. anti-fluffing and anti-pilling processing method of light and thin type hair terylene fabric described in accordance with the claim 1, it is characterised in that institute
It is that fabric moisture regain is carried out at 10%~25% to state low-temperature atmosphere-pressure plasma treatment in step (2);At low-temperature atmosphere-pressure plasma
The power of reason is 300W~1000W, and speed is identical with the speed that microwave drying is shaped.
A kind of 5. anti-fluffing and anti-pilling processing method of light and thin type hair terylene fabric described in accordance with the claim 1, it is characterised in that institute
Microwave drying sizing-low-temperature atmosphere-pressure plasma processing is stated in step (2) by fabric feeding machine (1), microwave drying modular system
(2), low-temperature atmosphere-pressure plasma processing (3) and control machine (4) composition;
Wherein is equipped with fabric guide roll (6) and expander (7) in fabric feeding machine (1), fabric is from fabric feeding machine (1) feeding, and fabric guide roll (6) is by face
Material is fully unfolded after being transmitted to expander (7);
Acupuncture axis (11), cloth pressing roller (12), deflector roll (13) and deflector roll (20) are equipped with microwave drying modular system (2), will be fed
Fabric pressed to by cloth pressing roller (12) in the pricker in acupuncture axis (11), fabric is fixed on acupuncture axis (11) by pricker, deflector roll
(13) moved with deflector roll (20) collective effect, guiding acupuncture axis (11) and fabric;
Fabric guide roll (14), electrode dielectric pipe (9) and grounding electrode medium tube are equipped with low-temperature atmosphere-pressure plasma processing (3)
(10), fabric guide roll (14) imports fabric, and fabric is placed in electrode dielectric pipe (9) and grounding electrode medium tube (10) mutually punctures shape
Into glow discharge layer between, connect alternating current after dielectric barrier discharge produce plasma, fabric is handled;
The fabric export completed will be handled by controlling machine (4).
6. according to a kind of anti-fluffing and anti-pilling processing method of light and thin type hair terylene fabric described in claim 5, it is characterised in that institute
It is 5-10m to state the distance between deflector roll (13) and deflector roll (20);2-4 electrode group is set between deflector roll (13) and deflector roll (20)
(8)。
7. according to a kind of anti-fluffing and anti-pilling processing method of light and thin type hair terylene fabric described in claim 5, it is characterised in that institute
It is ceramic (15) to state electrode dielectric pipe (9) top layer, and inside is metal powder (16);Grounding electrode medium tube (10) is by ground plane
(17), metal layer (18) and cooling device (19) composition.
8. according to a kind of anti-fluffing and anti-pilling processing method of light and thin type hair terylene fabric described in claim 5, it is characterised in that institute
The radius for stating grounding electrode medium tube (10) is 3~10 times of electrode dielectric pipe (9).