CN107904958A - A kind of cotton ramie blended spinning fabric and its pre-treating method - Google Patents
A kind of cotton ramie blended spinning fabric and its pre-treating method Download PDFInfo
- Publication number
- CN107904958A CN107904958A CN201711240176.4A CN201711240176A CN107904958A CN 107904958 A CN107904958 A CN 107904958A CN 201711240176 A CN201711240176 A CN 201711240176A CN 107904958 A CN107904958 A CN 107904958A
- Authority
- CN
- China
- Prior art keywords
- parts
- bleaching
- fabric
- heated
- follows
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of cotton ramie blended spinning fabric and its pre-treating method, including pre-treating technology, carries out pre-treatment with cellulase, pectase, the mutual crop of polyoxyethylene carboxylate, lays the first stone for last phase tidying up technique.The cotton ramie blended spinning fabric of the present invention prepared has good flexibility, dye-uptake, and pretreatment process does not produce sewage, do not destroy natural environment, is environmentally protective technique；The method of the invention is simple, the process time is short, suitable for a large amount of productions.
Description
Technical field
Originally it is bright to belong to textile technology field, it is related to a kind of pre-treating technology of sodolin, is specially a kind of cotton ramie blended spinning
Fabric and its pre-treating method.
Background technology
Since Reformation and development, China's economic rapid development, pursuit of the people to quality of the life increasingly improves.Wherein spin
Fabric is closely bound up with people's lives, and the quality of textile has influenced pursuit of the people to comfortably living.Wherein sodolin
Liked using performances such as good air permeability, hygroscopicity and antibacterials by the people, but its impurity is more, it is necessary to which carrying out pre-treatment just makes
With late stage process, but long, seriously polluted, the unfavorable environmental protection of existing technical process；Cotton fiber as a kind of main textile, with
Its gas permeability, comfort, hygroscopicity liked by consumers in general, but commensal in its former cloth, synthetic fibers etc. have impact on
The appearance of cotton fabric, dye-uptake etc., in order to improve the needs of dress ornament performance and last phase tidying up technique, need to carry out pre-treatment processing.
With scientific and technological progress, cotton ramie blended spinning fabric is using degree of recognition that is increasingly extensive, and obtaining higher.Cotton ramie blended spinning combines
Both respective advantages, mutually make up the defects of respective.But its natural plant fibre inferior position of itself is limited by, cause it
Fabric creases easily, and needs to press after washing, and cloth cover gloss is poor, the shortcomings such as dye-uptake is low.Flax is the day in toughness fiber and cotton
Right fiber removal is always the problem of fabric pretreatment, and high-temperature concentrated alkali or sodium hypochlorite bleaching are used in traditional handicraft, more or
It is double boil double drifts or boil the technique floated more and handled, but its effect is not notable, also easily causes not colored, hemp skin and remove not
The problems such as net, while process time length, can also attach and produce pollution, destroy surrounding environment.
At present, in all kinds of natural fabrics, ramie cotton fabric enjoys high praise with its exclusive performance, and China cotton and numb resource
The defects of enriching, therefore improve the performance of ramie cotton fabric, reducing its pollution, dye-uptake, is that raising ramie cotton fabric commercial value is non-
An often important link.
The content of the invention
Present invention solves the technical problem that：In order to overcome ramie cotton fabric itself insufficient, reduce original technique and environment is broken
It is bad, a kind of ramie cotton fabric natural, flexibility is good is obtained, the present invention provides a kind of cotton ramie blended spinning fabric and its pre-treatment side
Method.
Technical solution：A kind of cotton ramie blended spinning fabric pretreatment method, comprises the steps of：
1st step：By weight, by 200~300 parts of purified cotton yarns and 15~35 parts of bast yarn and thread first through loose type coning
Plain weaving is carried out again, with 80~110g/m of plain surface density2, 20~40r/min of syringe revolution completion blended fabric A；
2nd step：By blended fabric A into the water, 90~100 DEG C are heated to, boils 4~8min；
3rd step：Enzymatic treatment is carried out, condition is as follows：Bath raio 1~2:17~29, by weight, cellulase 11~21
Part, 8~14 parts of pectase, 3~7 parts of polyoxyethylene carboxylate, adjusts pH to 6.5~7.3, is heated to 35~45 DEG C, heating
After 50~70min, it is heated to 90~100 DEG C and boils 9~15min, Zha Shui drying；
4th step：Bleaching, condition are as follows：Bath raio 1:10~15,20~35 parts of sodium perborate are added, bleach 20~30min
Afterwards, 5~7min is dried at 50~70 DEG C；
5th step：Multiple drift, condition are as follows：Bath raio 1:7~18,15~24 parts of hydrogen peroxide are added, after bleaching 15~30min,
5~7min is dried at 50~70 DEG C, then carries out finishing technique.
Preferably, in the 1st step, by weight, by 260 parts of purified cotton yarns and 30 parts of bast yarn and thread first through loose type coning
Plain weaving is carried out again, with plain surface density 98g/m2, syringe revolution 35r/min completion blended fabric A.
Preferably, in the 2nd step, 100 DEG C are heated to, boils 5min by blended fabric A into the water.
Preferably, in the 3rd step, enzymatic treatment is carried out, condition is as follows：Bath raio 1:22, by weight, 16 parts of cellulase,
11 parts of pectase, 5 parts of polyoxyethylene carboxylate, adjusts pH to 6.9, is heated to 39 DEG C, after heating 60min, is heated to 98 DEG C
Boil 11min, Zha Shui drying.
Preferably, in the 4th step, bleach, condition is as follows：Bath raio 1:12,33 parts of sodium perborate are added, after bleaching 25min,
6min is dried at 65 DEG C.
Preferably, multiple to float in the 5th step, condition is as follows：Bath raio 1:11,19 parts of hydrogen peroxide are added, after bleaching 21min,
7min is dried at 60 DEG C, then carries out finishing technique.
The cotton ramie blended spinning fabric that any the method prepares.
Beneficial effect：The cotton ramie blended spinning fabric of the present invention prepared has good flexibility, dye-uptake, preceding place
Reason process does not produce sewage, does not destroy natural environment, is environmentally protective technique；The method of the invention is simple, the process time is short,
Suitable for a large amount of productions.
Embodiment
Embodiment 1
1st step：By weight, 260 parts of purified cotton yarns and 30 parts of bast yarn and thread are first put down again through loose type coning
Knitting is made, with plain surface density 98g/m2, syringe revolution 35r/min completion blended fabric A.
2nd step：By blended fabric A into the water, 100 DEG C are heated to, boils 5min.
3rd step：Enzymatic treatment is carried out, condition is as follows：Bath raio 1:22, by weight, 16 parts of cellulase, pectase 11
Part, 5 parts of polyoxyethylene carboxylate, adjusts pH to 6.9, is heated to 39 DEG C, after heating 60min, is heated to 98 DEG C and boils 11min,
Zha Shui is dried.
4th step：Bleaching, condition are as follows：Bath raio 1:12,33 parts of sodium perborate are added, after bleaching 25min, are dried at 65 DEG C
Dry 6min.
5th step：Multiple drift, condition are as follows：Bath raio 1:11,19 parts of hydrogen peroxide are added, after bleaching 21min, are dried at 60 DEG C
Dry 7min, then carry out finishing technique.
Embodiment 2
1st step：By weight, 230 parts of purified cotton yarns and 21 parts of bast yarn and thread are first put down again through loose type coning
Knitting is made, with plain surface density 98g/m2, syringe revolution 33r/min completion blended fabric A；
2nd step：By blended fabric A into the water, 98 DEG C are heated to, boils 6min；
3rd step：Enzymatic treatment is carried out, condition is as follows：Bath raio 1:21, by weight, 18 parts of cellulase, pectase 11
Part, 6 parts of polyoxyethylene carboxylate, adjusts pH to 7.1, is heated to 41 DEG C, after heating 65min, is heated to 95 DEG C and boils 11min,
Zha Shui is dried；
4th step：Bleaching, condition are as follows：Bath raio 1:12,28 parts of sodium perborate are added, after bleaching 27min, are dried at 65 DEG C
Dry 6min；
5th step：Multiple drift, condition are as follows：Bath raio 1:11,21 parts of hydrogen peroxide are added, after bleaching 22min, are dried at 63 DEG C
Dry 6min, then carry out finishing technique.
Embodiment 3
1st step：By weight, 280 parts of purified cotton yarns and 28 parts of bast yarn and thread are first put down again through loose type coning
Knitting is made, with plain surface density 101g/m2, syringe revolution 32r/min completion blended fabric A；
2nd step：By blended fabric A into the water, 99 DEG C are heated to, boils 5min；
3rd step：Enzymatic treatment is carried out, condition is as follows：Bath raio 1:22, by weight, 18 parts of cellulase, pectase 12
Part, 4 parts of polyoxyethylene carboxylate, adjusts pH to 7.0, is heated to 41 DEG C, after heating 65min, is heated to 92 DEG C and boils 11min,
Zha Shui is dried；
4th step：Bleaching, condition are as follows：Bath raio 1:12,31 parts of sodium perborate are added, after bleaching 29min, are dried at 60 DEG C
Dry 5min；
5th step：Multiple drift, condition are as follows：Bath raio 1:13,19 parts of hydrogen peroxide are added, after bleaching 28min, are dried at 55 DEG C
Dry 7min, then carry out finishing technique.
The fabric prepared to 1~3 the method for embodiment carries out follow-up soft finish and performance test after upper dye,
Acquired results are as follows：
| Twist (sth. made by twisting/10cm-1) | The remaining twist (sth. made by twisting/10cm-1) | Dye-uptake | |
| Embodiment 1 | 25 | 60.9 | 58.7% |
| Embodiment 2 | 25 | 54.4 | 51.6% |
| Embodiment 3 | 25 | 57.8 | 42.8% |
Claims (7)
- A kind of 1. cotton ramie blended spinning fabric pretreatment method, it is characterised in that comprise the steps of：1st step：By weight, by 200~300 parts of purified cotton yarns and 15~35 parts of bast yarn and thread first through loose type coning again into Row plain is weaved, with 80~110g/m of plain surface density2, 20~40r/min of syringe revolution completion blended fabric A；2nd step：By blended fabric A into the water, 90~100 DEG C are heated to, boils 4~8min；3rd step：Enzymatic treatment is carried out, condition is as follows：Bath raio 1~2:17~29, by weight, cellulase 11~21 part, fruit 8~14 parts of glue enzyme, 3~7 parts of polyoxyethylene carboxylate, adjusts pH to 6.5~7.3, is heated to 35~45 DEG C, and heating 50~ After 70min, it is heated to 90~100 DEG C and boils 9~15min, Zha Shui drying；4th step：Bleaching, condition are as follows：Bath raio 1:10~15,20~35 parts of sodium perborate are added, after bleaching 20~30min, 5~7min is dried at 50~70 DEG C；5th step：Multiple drift, condition are as follows：Bath raio 1:7~18,15~24 parts of hydrogen peroxide are added, after bleaching 15~30min, 50 5~7min is dried at~70 DEG C, then carries out finishing technique.
- 2. a kind of cotton ramie blended spinning fabric pretreatment method according to claim 1, it is characterised in that in the 1st step, by weight 260 parts of purified cotton yarns and 30 parts of bast yarn and thread are first carried out plain weaving, with plain surface density by part meter again through loose type coning 98g/m2, syringe revolution 35r/min completion blended fabric A.
- 3. a kind of cotton ramie blended spinning fabric pretreatment method according to claim 1, it is characterised in that, will be blended in the 2nd step Fabric A into the water, is heated to 100 DEG C, boils 5min.
- 4. a kind of cotton ramie blended spinning fabric pretreatment method according to claim 1, it is characterised in that in the 3rd step, carry out enzyme Processing, condition are as follows：Bath raio 1:22, by weight, 16 parts of cellulase, 11 parts of pectase, polyoxyethylene carboxylate 5 Part, pH to 6.9 is adjusted, is heated to 39 DEG C, after heating 60min, 98 DEG C is heated to and boils 11min, Zha Shui drying.
- A kind of 5. cotton ramie blended spinning fabric pretreatment method according to claim 1, it is characterised in that in the 4th step, bleaching, Condition is as follows：Bath raio 1:12,33 parts of sodium perborate are added, after bleaching 25min, 6min is dried at 65 DEG C.
- A kind of 6. cotton ramie blended spinning fabric pretreatment method and its application according to claim 1, it is characterised in that the 5th step In, multiple to float, condition is as follows：Bath raio 1:11,19 parts of hydrogen peroxide are added, after bleaching 21min, dry 7min at 60 DEG C, then into Row finishing technique.
- 7. the cotton ramie blended spinning fabric that any the method for claim 1~6 prepares.