CN108774894A - A kind of pre- pre-treating method of textile - Google Patents
A kind of pre- pre-treating method of textile Download PDFInfo
- Publication number
- CN108774894A CN108774894A CN201810663423.XA CN201810663423A CN108774894A CN 108774894 A CN108774894 A CN 108774894A CN 201810663423 A CN201810663423 A CN 201810663423A CN 108774894 A CN108774894 A CN 108774894A
- Authority
- CN
- China
- Prior art keywords
- textile
- technique
- fabric
- treating method
- cotton
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of pre- pre-treating methods of textile, including pre-treating technology, carry out pre-treatment with cellulase, pectase, the mutual crop of polyoxyethylene carboxylate, lay the first stone for last phase tidying up technique.There is the cotton ramie blended spinning fabric of the present invention prepared good flexibility, dye-uptake, pretreatment process not to generate sewage, not destroy natural environment, be environmentally protective technique;The method of the invention is simple, the process time is short, is suitable for mass production.
Description
Technical field
Originally bright to belong to textile technology field, it is related to a kind of pre- pre-treating method of textile.
Background technology
Since Reformation and development, China's economic rapid development, the people increasingly improve the pursuit of quality of the life.Wherein spin
Fabric is closely bound up with people's lives, and the quality of textile has influenced pursuit of the people to comfortably living.Wherein sodolin
Liked by the people with performances such as good air permeability, hygroscopicity and antibacterials, but its impurity is more, progress pre-treatment is needed just to make
With late stage process, but long, seriously polluted, the unfavorable environmental protection of existing technical process;Cotton fiber as a kind of main textile, with
Its gas permeability, comfort, hygroscopicity are liked by consumers in general, but commensal, the synthetic fibers etc. in its former cloth affect
Appearance, dye-uptake of cotton fabric etc. need to carry out pre-treatment processing to improve the needs of dress ornament performance and last phase tidying up technique.
With scientific and technological progress, cotton ramie blended spinning fabric obtains higher degree of recognition using increasingly extensive.Cotton ramie blended spinning combines
The two respective advantage, mutually makes up respective defect.But it is limited by its natural plant fibre disadvantage of itself, lead to it
The disadvantages such as fabric creases easily, and needs to press after washing, and cloth cover gloss is poor, and dye-uptake is low.Flax is the day in toughness fiber and cotton
Right fiber removal is always the problem of fabric pretreatment, uses high-temperature concentrated alkali or sodium hypochlorite bleaching in traditional handicraft, more or
It is double boil double drifts or boil the technique more floated and handled, but its effect is not notable, also easily cause not colored, hemp skin removal not
The problems such as net, while the process time is long, can also be attached to generating pollution, destroying ambient enviroment.
Currently, in all kinds of natural fabrics, ramie cotton fabric receives high praise with its exclusive performance, and China cotton and numb resource
The defects of enriching, therefore improve the performance of ramie cotton fabric, reducing its pollution, dye-uptake is that raising ramie cotton fabric commercial value is non-
An often important link.
Invention content
Present invention solves the technical problem that:In order to overcome ramie cotton fabric itself insufficient, reduces original technique and environment is broken
It is bad, a kind of natural, good ramie cotton fabric of flexibility is obtained, the present invention provides a kind of pre- pre-treating methods of textile.
Technical solution:A kind of pre- pre-treating method of textile, comprises the steps of:
1st step:Prepare blended fabric A.
2nd step:Into the water by blended fabric A, kiering is heated.
3rd step:Enzymatic treatment is carried out, 120 DEG C is heated to and boils 20min, Zha Shui drying.
4th step:Bleaching, 9min is dried at 80 DEG C.
5th step:Carry out finishing technique.
Advantageous effect:The cotton ramie blended spinning fabric of the present invention prepared has good flexibility, dye-uptake, preceding place
Reason process does not generate sewage, does not destroy natural environment, is environmentally protective technique;The method of the invention is simple, the process time is short,
Suitable for mass production.
Specific implementation mode
Below in conjunction with specific embodiment to further instruction of the present invention.
A kind of pre- pre-treating method of textile, which is characterized in that comprise the steps of:
1st step:Prepare blended fabric A.
2nd step:Into the water by blended fabric A, kiering is heated.
3rd step:Enzymatic treatment is carried out, 120 DEG C is heated to and boils 20min, Zha Shui drying.
4th step:Bleaching, 9min is dried at 80 DEG C.
5th step:Carry out finishing technique.
The above, only present pre-ferred embodiments, therefore cannot be limited the scope of implementation of the present invention with this, i.e., according to
Equivalent changes and modifications made by scope of the present invention patent and description all should still belong to the model that patent of the present invention covers
In enclosing.
Claims (1)
1. a kind of pre- pre-treating method of textile, which is characterized in that comprise the steps of:
1st step:Prepare blended fabric A;
2nd step:Into the water by blended fabric A, kiering is heated;
3rd step:Enzymatic treatment is carried out, 120 DEG C is heated to and boils 20min, Zha Shui drying;
4th step:Bleaching, 9min is dried at 80 DEG C;
5th step:Carry out finishing technique.