CN107879728A - A kind of corrosion-resistant ceramic - Google Patents
A kind of corrosion-resistant ceramic Download PDFInfo
- Publication number
- CN107879728A CN107879728A CN201711043337.0A CN201711043337A CN107879728A CN 107879728 A CN107879728 A CN 107879728A CN 201711043337 A CN201711043337 A CN 201711043337A CN 107879728 A CN107879728 A CN 107879728A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- corrosion
- raw material
- resistant ceramic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of corrosion-resistant ceramic, include the raw material of parts by weight:The parts by weight of yellow ground 70 90, the parts by weight of clay 10 15, the parts by weight of jade powder 13 18, the parts by weight of volcanic rock 8 17, the parts by weight of zircon 35 55, the parts by weight of silica flour 24 26, the parts by weight of tricalcium phosphate 13, the parts by weight of calcium carbonate 2.5 3.6, the parts by weight of nanometer silicon carbide 0.9 2.7, the parts by weight of blast-furnace cinder 8 11.The invention has the advantages that on the basis of existing technology, there is provided a kind of corrosion-resistant ceramic.
Description
Technical field
The present invention relates to Material Field, specifically, is related to a kind of corrosion-resistant ceramic.
Background technology
Ceramics are by yellow ground, quartz sand and other inorganic non-metallic raw materials, through dispensing, ball milling, powder processed, shaping, sintering
Etc. the tabular or block elements of technique productions, it is widely used in decoration and protection building, the metope of structures and ground.With
Real estate is developed rapidly so that the production and consumption of ceramic tile is all got a larger development, while will to the performance of ceramics
Seek also more and more higher.But ceramic most low intensity in the market, not hard enough, frangible, usability is poor, can not meet city
Field demand.
Thus, how to obtain a kind of corrosion-resistant ceramic is current china industry urgent problem.
The content of the invention
The technical problems to be solved by the invention are to provide a kind of corrosion-resistant ceramic.
The technical scheme that the present invention solves above-mentioned technical problem is as follows:
A kind of corrosion-resistant ceramic, include the raw material of parts by weight:Yellow ground 70-90 parts by weight, clay 10-15 parts by weight, jade
Powder 13-18 parts by weight, volcanic rock 8-17 parts by weight, zircon 35-55 parts by weight, silica flour 24-26 parts by weight, tricalcium phosphate 1-3
Parts by weight, calcium carbonate 2.5-3.6 parts by weight, nanometer silicon carbide 0.9-2.7 parts by weight, blast-furnace cinder 8-11 parts by weight.
The beneficial effects of the invention are as follows:On the basis of existing technology, there is provided a kind of corrosion-resistant ceramic.
On the basis of above-mentioned technical proposal, the present invention can also do following improvement:
Further, it includes the raw material of parts by weight:The parts by weight of yellow ground 70, the parts by weight of clay 10, the parts by weight of jade powder 13, fire
The parts by weight of mountain rock 8, the parts by weight of zircon 35, the parts by weight of silica flour 24, the parts by weight of tricalcium phosphate 1, the parts by weight of calcium carbonate 2.5, nanometer
The parts by weight of carborundum 0.9, the parts by weight of blast-furnace cinder 8.
Further, it includes the raw material of parts by weight:The parts by weight of yellow ground 90, the parts by weight of clay 15, the parts by weight of jade powder 18, fire
The parts by weight of mountain rock 17, the parts by weight of zircon 55, the parts by weight of silica flour 26, the parts by weight of tricalcium phosphate 3, the parts by weight of calcium carbonate 3.6, nanometer
The parts by weight of carborundum 2.7, the parts by weight of blast-furnace cinder 11.
Further, it includes the raw material of parts by weight:The parts by weight of yellow ground 80, the parts by weight of clay 12, the parts by weight of jade powder 15, fire
The parts by weight of mountain rock 13, the parts by weight of zircon 42, the parts by weight of silica flour 25, the parts by weight of tricalcium phosphate 2.3, the parts by weight of calcium carbonate 3.2, receive
Rice carborundum 1.9 parts by weight, the parts by weight of blast-furnace cinder 9.
Further, its preparation method includes:
(1) raw material is weighed in mass ratio, is well mixed, is crushed, wet ball grinding 5-10h, and 150-200 mesh sieves are crossed after drying,
It is stand-by;
(2) the waterglass mixing 20- that quality is compound weight 2-4% will be added in powder made from above-mentioned steps (1)
30min, 10-15h is stood, the solid content of the waterglass is 35%;
(3) by step (2) be well mixed powder be sent to forming machine under 60-80MPa it is compressing, then will suppress
Adobe deliver in dry kiln dry to water content be 3-5% dry body;
(4) dry body is warming up to 1160-1220 DEG C with 5-10 DEG C/min speed, is incubated 2-3h, then with 10-15 DEG C/min
Speed be cooled to 750-850 DEG C, be incubated 0.5-1h, be cooled to normal temperature, got product through edging, packaging.
Embodiment
The principle and feature of the present invention are described with reference to embodiments, the given examples are served only to explain the present invention,
It is not intended to limit the scope of the present invention.
Embodiment 1
A kind of corrosion-resistant ceramic, include the raw material of parts by weight:The parts by weight of yellow ground 70, the parts by weight of clay 10, the weight of jade powder 13
Measure part, the parts by weight of volcanic rock 8, the parts by weight of zircon 35, the parts by weight of silica flour 24, the parts by weight of tricalcium phosphate 1, the weight of calcium carbonate 2.5
Part, the parts by weight of nanometer silicon carbide 0.9, the parts by weight of blast-furnace cinder 8.
Its preparation method includes:
(1) raw material is weighed in mass ratio, is well mixed, is crushed, wet ball grinding 5h, and 150 mesh sieves are crossed after drying, it is stand-by;
(2) the waterglass mixing 20min that quality is compound weight 2% will be added in powder made from above-mentioned steps (1),
10h is stood, the solid content of the waterglass is 35%;
(3) by the powder that step (2) is well mixed be sent to forming machine under 60MPa it is compressing, then will suppress
The dry body dried to water content is 3% is delivered in dry kiln in adobe;
(4) dry body is warming up to 1160 DEG C with 5 DEG C/min speed, is incubated 3h, then be cooled to 10 DEG C/min speed
750 DEG C, 0.5h is incubated, is cooled to normal temperature, got product through edging, packaging.
Embodiment 2
A kind of corrosion-resistant ceramic, include the raw material of parts by weight:The parts by weight of yellow ground 90, the parts by weight of clay 15, the weight of jade powder 18
Measure part, the parts by weight of volcanic rock 17, the parts by weight of zircon 55, the parts by weight of silica flour 26, the parts by weight of tricalcium phosphate 3, the weight of calcium carbonate 3.6
Part, the parts by weight of nanometer silicon carbide 2.7, the parts by weight of blast-furnace cinder 11.
Its preparation method includes:
(1) raw material is weighed in mass ratio, is well mixed, is crushed, wet ball grinding 10h, and 200 mesh sieves are crossed after drying, it is stand-by;
(2) the waterglass mixing 30min that quality is compound weight 4% will be added in powder made from above-mentioned steps (1),
15h is stood, the solid content of the waterglass is 35%;
(3) by the powder that step (2) is well mixed be sent to forming machine under 80MPa it is compressing, then will suppress
The dry body dried to water content is 5% is delivered in dry kiln in adobe;
(4) dry body is warming up to 1220 DEG C with 10 DEG C/min speed, is incubated 3h, then be cooled to 15 DEG C/min speed
850 DEG C, 1h is incubated, is cooled to normal temperature, got product through edging, packaging.
Embodiment 3
A kind of corrosion-resistant ceramic, include the raw material of parts by weight:The parts by weight of yellow ground 80, the parts by weight of clay 12, the weight of jade powder 15
Measure part, the parts by weight of volcanic rock 13, the parts by weight of zircon 42, the parts by weight of silica flour 25, the parts by weight of tricalcium phosphate 2.3, the weight of calcium carbonate 3.2
Measure part, the parts by weight of nanometer silicon carbide 1.9, the parts by weight of blast-furnace cinder 9.
Its preparation method includes:
(1) raw material is weighed in mass ratio, is well mixed, is crushed, wet ball grinding 10h, and 200 mesh sieves are crossed after drying, it is stand-by;
(2) the waterglass mixing 30min that quality is compound weight 4% will be added in powder made from above-mentioned steps (1),
15h is stood, the solid content of the waterglass is 35%;
(3) by the powder that step (2) is well mixed be sent to forming machine under 80MPa it is compressing, then will suppress
The dry body dried to water content is 5% is delivered in dry kiln in adobe;
(4) dry body is warming up to 1220 DEG C with 10 DEG C/min speed, is incubated 3h, then be cooled to 15 DEG C/min speed
850 DEG C, 1h is incubated, is cooled to normal temperature, got product through edging, packaging.
Comparative example 1
Commercially available general ceramic material.
Comparative sample 1 in the sample 1-3 and comparative example that are obtained in embodiment 1-3 is carried out to the test of performance respectively, surveyed
Its breakdown strength, the modulus of rupture and decay resistance are tried, it is as a result as shown in the table.
The foregoing is only presently preferred embodiments of the present invention, be not intended to limit the invention, it is all the present invention spirit and
Within principle, any modification, equivalent substitution and improvements made etc., it should be included in the scope of the protection.
Claims (5)
- A kind of 1. corrosion-resistant ceramic, it is characterised in that the raw material including parts by weight:Yellow ground 70-90 parts by weight, clay 10-15 weights Measure part, jade powder 13-18 parts by weight, volcanic rock 8-17 parts by weight, zircon 35-55 parts by weight, silica flour 24-26 parts by weight, phosphorus Sour DFP 1-3 parts by weight, calcium carbonate 2.5-3.6 parts by weight, nanometer silicon carbide 0.9-2.7 parts by weight, blast-furnace cinder 8-11 weight Part.
- A kind of 2. corrosion-resistant ceramic according to claim 1, it is characterised in that the raw material including parts by weight:The weight of yellow ground 70 Part, the parts by weight of clay 10, the parts by weight of jade powder 13, the parts by weight of volcanic rock 8, the parts by weight of zircon 35, the parts by weight of silica flour 24, phosphoric acid The parts by weight of DFP 1, the parts by weight of calcium carbonate 2.5, the parts by weight of nanometer silicon carbide 0.9, the parts by weight of blast-furnace cinder 8.
- A kind of 3. corrosion-resistant ceramic according to claim 1, it is characterised in that the raw material including parts by weight:The weight of yellow ground 90 Part, the parts by weight of clay 15, the parts by weight of jade powder 18, the parts by weight of volcanic rock 17, the parts by weight of zircon 55, the parts by weight of silica flour 26, phosphorus The sour parts by weight of DFP 3, the parts by weight of calcium carbonate 3.6, the parts by weight of nanometer silicon carbide 2.7, the parts by weight of blast-furnace cinder 11.
- A kind of 4. corrosion-resistant ceramic according to claim 1, it is characterised in that the raw material including parts by weight:The weight of yellow ground 80 Part, the parts by weight of clay 12, the parts by weight of jade powder 15, the parts by weight of volcanic rock 13, the parts by weight of zircon 42, the parts by weight of silica flour 25, phosphorus The sour parts by weight of DFP 2.3, the parts by weight of calcium carbonate 3.2, the parts by weight of nanometer silicon carbide 1.9, the parts by weight of blast-furnace cinder 9.
- 5. according to a kind of any corrosion-resistant ceramics of claim 1-4, it is characterised in that its preparation method includes:(1) raw material is weighed in mass ratio, is well mixed, is crushed, wet ball grinding 5-10h, and 150-200 mesh sieves are crossed after drying, it is stand-by;(2) the waterglass mixing 20- that quality is compound weight 2-4% will be added in powder made from above-mentioned steps (1) 30min, 10-15h is stood, the solid content of the waterglass is 35%;(3) powder that step (2) is well mixed is sent to forming machine compressing, brick that then will be suppressed under 60-80MPa Base delivers in dry kiln the dry body dried to water content is 3-5%;(4) dry body is warming up to 1160-1220 DEG C with 5-10 DEG C/min speed, is incubated 2-3h, then the speed with 10-15 DEG C/min Rate is cooled to 750-850 DEG C, is incubated 0.5-1h, is cooled to normal temperature, is got product through edging, packaging.