CN102815959A - Environment-friendly aerated concrete block - Google Patents
Environment-friendly aerated concrete block Download PDFInfo
- Publication number
- CN102815959A CN102815959A CN2012103172477A CN201210317247A CN102815959A CN 102815959 A CN102815959 A CN 102815959A CN 2012103172477 A CN2012103172477 A CN 2012103172477A CN 201210317247 A CN201210317247 A CN 201210317247A CN 102815959 A CN102815959 A CN 102815959A
- Authority
- CN
- China
- Prior art keywords
- tailings
- building block
- concrete building
- entrained concrete
- cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an environment-friendly aerated concrete block which at least comprises, by weight, 70%-82% of stone tailings and/or coal ash, 4%-10% of cement, 12%-19% of quicklime, 0.05-0.08% of powdered aluminum and 0.9%-2.7% of desulfurization gypsum. The environment-friendly aerated concrete block uses the stone tailings as a raw material, so that production cost is reduced, and the problem of difficulty in treatment of the stone tailings is further solved.
Description
Technical field
The present invention relates to a kind of concrete segment, be specifically related to the air-entrained concrete building block that a kind of light porous, heat insulating, fire resistance are good, can follow closely, can saw, can dig and have certain shock resistance, belong to building material field.
Background technology
Concrete is widely used in the building field, available coagulation soil be by gelling material and water according to certain mixed proportioning after, the artificial stone-like material that sclerosis forms with certain intensity.Along with present people's life requirement improves constantly, also increasingly high to the requirement of material of construction, available coagulation soil more and more can not satisfy the growing material life demand of people.Novel wall materials such as existing on the market at present all kinds of holllow building blocks, light wall board, but factors such as technology own, equipment all be limited to, exist all drawbacks.
Air-entrained concrete building block is the New Building Materials of a kind of less energy-consumption, environment-friendly type, have in light weight, thermal and insulating performance good, intensity is high, anti-seismic performance is good, good processability, high temperature resistant, advantage such as sound-proofing properties is good.Thereby the universal traditional concrete that replaces gradually.But because the production cost of air-entrained concrete building block is higher, thereby limited its development.
Lithotome such as marble, grouan is because the meliority of its performance and outward appearance is favored by people just more and more, along with increasing of its marketable value, also comes more popular to the exploitation of this type ore.Along with exploitation without restraint to these stone materials; Brought the destruction of a lot of environmental protection aspect thereupon; The stone material tailings (chip, powder, dust and mud etc.) that carries over after the stone material cutting can't be handled, and directly abandons accumulation usually, serious especially destruction ecotope.
Summary of the invention
The invention provides a kind of environment-friendly type air-entrained concrete building block, solved the deficiency in the above-mentioned background technology, the stone material tailings as the raw material of producing air-entrained concrete building block, has not only been reduced production cost, also solved a difficult problem of handling the stone material tailings simultaneously.
Realize that the technical scheme that above-mentioned purpose of the present invention adopted is:
A kind of environmental protection air-entrained concrete building block; The raw material of described air-entrained concrete building block comprises stone material tailings and/or flyash, cement, unslaked lime, aluminium powder and desulfurated plaster at least; The per-cent that each raw material accounts for the raw material gross weight is respectively stone material tailings and/or flyash 70%-82%, cement 4%-10%, unslaked lime 12%-19%; Aluminium powder 0.05%-0.08%, desulfurated plaster 0.9%-2.7%.
Described raw material is stone material tailings, flyash, cement, unslaked lime, aluminium powder and desulfurated plaster; The per-cent that each raw material accounts for the raw material gross weight is respectively: stone material tailings 72%-75%; Cement 4.8%-9.62%, unslaked lime 12%-18.7%, aluminium powder 0.07%-0.08%; Desulfurated plaster 0.96%-2.67%, flyash content is not more than 10%.
The fineness of said stone material tailings is more than 80 orders, comprises chip, powder, dust and the mud of stone material.
Said stone material tailings is marble tailings and/or grouan tailings.
The content of quicklime is greater than 80% in the described unslaked lime.
Described cement is the silicate cement of 42.5 grades.
Environment-friendly type air-entrained concrete building block provided by the invention compared with prior art has following advantage: 1. the present invention adopts the tailings that produces in grouan and the marble recovery process as raw material; Not only reduced manufacturing cost; And fully utilized salvage property, avoid environmental destruction.The air-entrained concrete building block that meanwhile makes among the present invention satisfies the GB requirement, can use widely.
Embodiment
Through specific embodiment the present invention is further described below, but protection content of the present invention is not limited to following examples.
Adopting said stone material tailings stone material tailings in following examples is marble tailings and/or grouan tailings, and its fineness is more than 80 orders, comprises chip, powder, dust and the mud of stone material.The content of quicklime is greater than 80% in the described unslaked lime.Described cement is the silicate cement of 42.5 grades.
Embodiment 1
The proportioning raw materials of the environmental protection air-entrained concrete building block that is provided in the present embodiment is following: stone material tailings 74.5%, cement 8%, unslaked lime 15%, aluminium powder 0.07%, desulfurated plaster 2.43%.
The preparation method of the environmental protection air-entrained concrete building block that present embodiment provided is following: with various raw materials respectively from the logical compounding plant that is delivered to of former feed bin separately; After electronic scale is according to the proportion speed metering; With raw material pulverizing and add water and stir and make slip; In mould vehicle and send into the precuring chamber and rest, slip is delivered to the upset boat and is lifted up into capable base substrate cutting after sclerosis forms qualified blank with slip casting, and it is steam-cured through boiler gas that order is put the back; Steam-cured technical process is following: emptying, intensification, draining, ftercompction thermostatic curing, pressure release, go out still, go out still after the salable product that detect are prepared environmental protection air-entrained concrete building block.
Prepared environmental protection air-entrained concrete building block check in building engineering quality supervision verification test center, 2011 07 month 22 Nikkei Hubei Province among the present invention, product meets GB11968-2006 and GB/T11969-2008 standard-required.The environmental protection air-entrained concrete building block that makes in the present embodiment is through detecting, and its density is 770Kg/m
3, ultimate compression strength is 74Kg/cm
2, drying shrinkage value is 0.7, thermal conductivity is 0.18W/ (mK).
Embodiment 2
The proportioning raw materials of the environmental protection air-entrained concrete building block that is provided in the present embodiment is following: stone material tailings 72%, and cement 6%, unslaked lime 13%, aluminium powder 0.08%, desulfurated plaster 1.8%, flyash content are 7.12%.
Preparing method in the present embodiment is identical with embodiment 1, has added part flyash in the environmental protection air-entrained concrete building block that makes in the present embodiment, can not impact performance of products equally.Through detecting, the density of the environmental protection air-entrained concrete building block that makes in the present embodiment is 760Kg/m
3, ultimate compression strength is 78Kg/cm
2, drying shrinkage value is 0.7, thermal conductivity is 0.17W/ (mK).
Embodiment 3
The proportioning raw materials of the environmental protection air-entrained concrete building block that is provided in the present embodiment is following: stone material tailings 20%, flyash 60%, cement 5%, unslaked lime 13%, aluminium powder 0.07%, desulfurated plaster 1.93%.
Preparing method in the present embodiment is identical with embodiment 1, has added a small amount of stone material tailings in the environmental protection air-entrained concrete building block that makes in the present embodiment, and prepared product is through detecting, and its density is 723Kg/m
3, ultimate compression strength is 80Kg/cm
2, drying shrinkage value is 0.7, thermal conductivity is 0.18W/ (mK).
Embodiment 4
The proportioning raw materials of the environmental protection air-entrained concrete building block that is provided in the present embodiment is following: flyash 75%, cement 4.5%, unslaked lime 18.5%, aluminium powder 0.06%, desulfurated plaster 1.94%.
Preparing method in the present embodiment is identical with embodiment 1, only is added with flyash in the environmental protection air-entrained concrete building block that makes in the present embodiment, and prepared product is through detecting, and its density is 703Kg/m
3, ultimate compression strength is 81Kg/cm
2, drying shrinkage value is 0.7, thermal conductivity is 0.18W/ (mK).
Claims (6)
1. environmental protection air-entrained concrete building block; The raw material that it is characterized in that described air-entrained concrete building block comprises stone material tailings and/or flyash, cement, unslaked lime, aluminium powder and desulfurated plaster at least; The per-cent that each raw material accounts for the raw material gross weight is respectively stone material tailings and/or flyash 70%-82%, cement 4%-10%, unslaked lime 12%-19%; Aluminium powder 0.05%-0.08%, desulfurated plaster 0.9%-2.7%.
2. environmental protection air-entrained concrete building block according to claim 1; It is characterized in that: described raw material is stone material tailings, flyash, cement, unslaked lime, aluminium powder and desulfurated plaster, and the per-cent that each raw material accounts for the raw material gross weight is respectively: stone material tailings 72%-75%, cement 4.8%-9.62%; Unslaked lime 12%-18.7%; Aluminium powder 0.07%-0.08%, desulfurated plaster 0.96%-2.67%, flyash content is not more than 10%.
3. environmental protection air-entrained concrete building block according to claim 1 and 2 is characterized in that: the fineness of said stone material tailings is more than 80 orders, comprises chip, powder, dust and the mud of stone material.
4. environmental protection air-entrained concrete building block according to claim 1 and 2 is characterized in that: said stone material tailings is marble tailings and/or grouan tailings.
5. environmental protection air-entrained concrete building block according to claim 1 and 2 is characterized in that: the content of quicklime is greater than 80% in the described unslaked lime.
6. environmental protection air-entrained concrete building block according to claim 1 and 2 is characterized in that: described cement is the silicate cement of 42.5 grades.