CN107828257A - A kind of strong paint formulation of anti-corrosion fire resistance property - Google Patents
A kind of strong paint formulation of anti-corrosion fire resistance property Download PDFInfo
- Publication number
- CN107828257A CN107828257A CN201711007183.XA CN201711007183A CN107828257A CN 107828257 A CN107828257 A CN 107828257A CN 201711007183 A CN201711007183 A CN 201711007183A CN 107828257 A CN107828257 A CN 107828257A
- Authority
- CN
- China
- Prior art keywords
- parts
- resin
- fire
- resistance property
- fire resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of strong paint formulation of anti-corrosion fire resistance property, including 12 ~ 18 parts of 6 ~ 8 parts of 10 ~ 12 parts of 5 ~ 7 parts of 1 ~ 2 part of 3 ~ 7 parts of 6 ~ 10 parts of 8 ~ 12 parts of 5 ~ 7 parts of 2 ~ 4 parts of 5 ~ 7 parts of 2 ~ 5 parts of 10 ~ 15 parts of 20 ~ 26 parts of titanium dioxide, glacial acetic acid, organic epoxy resin, glycol monoethyl ether, dimethyl sulfoxide (DMSO), trbasic zinc phosphate, barium chromate, aluminum oxide, rosin resin, anti-yellowing resin, hydroxyethyl cellulose, Ludox, methyl methacrylate, dehydrated castor oil and 3 ~ 5 parts of dimethyl malenate by weight.The beneficial effects of the invention are as follows：The present invention has the advantages of high temperature resistant, fire-resistant ability is strong, the risk for triggering fire can be reduced, consequently facilitating storage and managenent, and it is painted on after furniture, wall coverings, wall, can when fire occurs from fire retardation, loss caused by reduce fire, it has formula simple, low manufacture cost, applied widely, the advantages of being readily produced, is easy to promote the use of.
Description
Technical field
It is a kind of strong paint formulation of anti-corrosion fire resistance property specifically the present invention relates to paint field.
Background technology
Paint is that one kind can firmly be covered in body surface, and the chemistry for playing protection, decoration, mark and other specific uses mixes
Compound coating.Paint as viscous oily pigment, it is inflammable in the case of not dry, it is not soluble in water, be slightly soluble in fat, dissolve in alcohol, aldehyde,
Ether, benzene, alkane, it is soluble in gasoline, kerosene, diesel oil.
All it is by three kinds of film forming matter, subsidiary film forming matter and auxiliary film forming matter no matter painting kind or form
Base substance forms：
Film forming matter：Also referred to as binding agent, it is organic high molecular compound such as natural resin that film forming matter is most of（It is rosin, big
Paint）, coating（Tung oil, linseed oil, soya-bean oil, fish oil etc.）, the mix such as synthetic resin, form by pyroreaction, also whether there is
The paint of machine thing combination（Such as：Inorganic zinc rich paint）.Various film forming matters press the common xxx classes of national standard.It is the master for forming paint
Body, decide the performance of paint film.If without film forming matter, simple pigment and auxiliary material can not form paint film.
Subsidiary film forming matter：Including various pigment, extender pigment, rust resisting pigment.Pigment provides color and covering for paint film
Power, improves the protective value and decorative effect of paint, and the pigment of good weatherability can improve the service life of paint.Extender pigment can
It is folded multiple by the accumulation of pigment using the performance of itself " sheet, needle-like " structure to increase the thickness of paint film, form fish scale
The paint film of shape, the service life of paint film is improved, improve water proofing property and rust-proof effect.Rust resisting pigment passes through itself physics and chemistry
Anti-rust action, prevent that metal surface is by corrosion by air, chemicals attack for body surface.
Auxiliary film forming matter：Including various auxiliary agents, solvent, various auxiliary agents are in the production process of paint, storage process, use
Process and the forming process of paint film play very important effect.Although the amount used is all seldom, to the performance shadow of paint film
Ring very big.Even it can not form paint film such as：Do not do, sink to the bottom caking, skinning.
Under the conditions of prior art there is the shortcomings that inflammable perishable in the paint of liquid, and place existing for paint is dangerous high,
It is easy to trigger fire.
The content of the invention
It is an object of the invention to provide a kind of fire resistance property it is strong, can reduce and trigger the anti-corrosion fire resistance property of fire risk
Strong paint formulation.
The present invention is achieved through the following technical solutions：A kind of strong paint formulation of anti-corrosion fire resistance property, including by weight
5 ~ 7 parts of 2 ~ 5 parts of 10 ~ 15 parts of 20 ~ 26 parts of titanium dioxide, glacial acetic acid, organic epoxy resin, glycol monoethyl ether, the dimethyl of meter
2 ~ 4 parts of sulfoxide, 5 ~ 7 parts of trbasic zinc phosphate, 8 ~ 12 parts of barium chromate, 6 ~ 10 parts of aluminum oxide, 3 ~ 7 parts of rosin resin, 1 ~ 2 part of anti-yellowing resin,
5 ~ 7 parts of hydroxyethyl cellulose, 10 ~ 12 parts of Ludox, 6 ~ 8 parts of methyl methacrylate, 12 ~ 18 parts of dehydrated castor oil and malonic acid
3 ~ 5 parts of dimethyl ester.
Described 20 parts of titanium dioxide, 10 parts of glacial acetic acid, 2 parts of organic epoxy resin, 5 parts of glycol monoethyl ether, dimethyl
2 parts of sulfoxide, 5 parts of trbasic zinc phosphate, 8 parts of barium chromate, 6 parts of aluminum oxide, 3 parts of rosin resin, 1 part of anti-yellowing resin, hydroxyethyl cellulose 5
Part, 10 parts of Ludox, 6 parts of methyl methacrylate, 12 parts of dehydrated castor oil and 3 parts of dimethyl malenate.
Described 22 parts of titanium dioxide, 12 parts of glacial acetic acid, 2 parts of organic epoxy resin, 6 parts of glycol monoethyl ether, dimethyl
2 parts of sulfoxide, 5 parts of trbasic zinc phosphate, 9 parts of barium chromate, 7 parts of aluminum oxide, 4 parts of rosin resin, 1 part of anti-yellowing resin, hydroxyethyl cellulose 6
Part, 11 parts of Ludox, 6 parts of methyl methacrylate, 14 parts of dehydrated castor oil and 3 parts of dimethyl malenate.
Described 24 parts of titanium dioxide, 14 parts of glacial acetic acid, 4 parts of organic epoxy resin, 6 parts of glycol monoethyl ether, dimethyl
2 parts of sulfoxide, 5 parts of trbasic zinc phosphate, 10 parts of barium chromate, 8 parts of aluminum oxide, 4 parts of rosin resin, 1 part of anti-yellowing resin, hydroxyethyl cellulose 6
Part, 10 parts of Ludox, 7 parts of methyl methacrylate, 16 parts of dehydrated castor oil and 3 parts of dimethyl malenate.
Described 26 parts of titanium dioxide, 15 parts of glacial acetic acid, 5 parts of organic epoxy resin, 7 parts of glycol monoethyl ether, dimethyl
4 parts of sulfoxide, 7 parts of trbasic zinc phosphate, 12 parts of barium chromate, 10 parts of aluminum oxide, 7 parts of rosin resin, 2 parts of anti-yellowing resin, hydroxyethyl cellulose 7
Part, 12 parts of Ludox, 8 parts of methyl methacrylate, 18 parts of dehydrated castor oil and 5 parts of dimethyl malenate.
The present invention compared with prior art, has advantages below and beneficial effect：
The present invention has the advantages of high temperature resistant, fire-resistant ability is strong, can reduce the risk for triggering fire, consequently facilitating storage pipe
Reason, and is painted on after furniture, wall coverings, wall, can when fire occurs from fire retardation, caused by reducing fire
Loss, it has formula simple, low manufacture cost, applied widely, the advantages of being readily produced, is easy to promote the use of.
Embodiment
The present invention is described in further detail with reference to embodiment, but the implementation of the present invention is not limited to this.
Embodiment 1：
In the present embodiment, a kind of strong paint formulation of anti-corrosion fire resistance property, including 20 ~ 26 parts of titanium dioxide, ice by weight
10 ~ 15 parts of acetic acid, 2 ~ 5 parts of organic epoxy resin, 5 ~ 7 parts of glycol monoethyl ether, 2 ~ 4 parts of dimethyl sulfoxide (DMSO), trbasic zinc phosphate 5 ~ 7
Part, 8 ~ 12 parts of barium chromate, 6 ~ 10 parts of aluminum oxide, 3 ~ 7 parts of rosin resin, 1 ~ 2 part of anti-yellowing resin, 5 ~ 7 parts of hydroxyethyl cellulose, silicon
3 ~ 5 parts of 10 ~ 12 parts of colloidal sol, 6 ~ 8 parts of methyl methacrylate, 12 ~ 18 parts of dehydrated castor oil and dimethyl malenate.Present invention tool
There is the advantages of high temperature resistant, fire-resistant ability is strong, the risk for triggering fire can be reduced, consequently facilitating storage and managenent, and be painted on
After furniture, wall coverings, wall, can when fire occurs from fire retardation, caused by reduce fire loss, its have matches somebody with somebody
Side is simple, low manufacture cost, applied widely, the advantages of being readily produced, be easy to promote the use of.
Embodiment 2：
On the basis of above-described embodiment, in the present embodiment, a kind of strong paint formulation of anti-corrosion fire resistance property, including by weight
2 parts of 5 parts of 2 parts of 10 parts of 20 parts of titanium dioxide, glacial acetic acid, organic epoxy resin, glycol monoethyl ether, dimethyl sulfoxide (DMSO), the phosphorus of meter
Sour 5 parts of zinc, 8 parts of barium chromate, 6 parts of aluminum oxide, 3 parts of rosin resin, 1 part of anti-yellowing resin, 5 parts of hydroxyethyl cellulose, Ludox 10
Part, 6 parts of methyl methacrylate, 12 parts of dehydrated castor oil and 3 parts of dimethyl malenate.
Embodiment 3：
On the basis of above-described embodiment, in the present embodiment, a kind of strong paint formulation of anti-corrosion fire resistance property, including by weight
2 parts of 6 parts of 2 parts of 12 parts of 22 parts of titanium dioxide, glacial acetic acid, organic epoxy resin, glycol monoethyl ether, dimethyl sulfoxide (DMSO), the phosphorus of meter
Sour 5 parts of zinc, 9 parts of barium chromate, 7 parts of aluminum oxide, 4 parts of rosin resin, 1 part of anti-yellowing resin, 6 parts of hydroxyethyl cellulose, Ludox 11
Part, 6 parts of methyl methacrylate, 14 parts of dehydrated castor oil and 3 parts of dimethyl malenate.
Embodiment 4：
On the basis of above-described embodiment, in the present embodiment, a kind of strong paint formulation of anti-corrosion fire resistance property, including by weight
2 parts of 6 parts of 4 parts of 14 parts of 24 parts of titanium dioxide, glacial acetic acid, organic epoxy resin, glycol monoethyl ether, dimethyl sulfoxide (DMSO), the phosphorus of meter
Sour 5 parts of zinc, 10 parts of barium chromate, 8 parts of aluminum oxide, 4 parts of rosin resin, 1 part of anti-yellowing resin, 6 parts of hydroxyethyl cellulose, Ludox 10
Part, 7 parts of methyl methacrylate, 16 parts of dehydrated castor oil and 3 parts of dimethyl malenate.
Embodiment 5：
On the basis of above-described embodiment, in the present embodiment, a kind of strong paint formulation of anti-corrosion fire resistance property, including by weight
4 parts of 7 parts of 5 parts of 15 parts of 26 parts of titanium dioxide, glacial acetic acid, organic epoxy resin, glycol monoethyl ether, dimethyl sulfoxide (DMSO), the phosphorus of meter
Sour 7 parts of zinc, 12 parts of barium chromate, 10 parts of aluminum oxide, 7 parts of rosin resin, 2 parts of anti-yellowing resin, 7 parts of hydroxyethyl cellulose, Ludox
5 parts of 12 parts, 8 parts of methyl methacrylate, 18 parts of dehydrated castor oil and dimethyl malenate.
It is described above, be only presently preferred embodiments of the present invention, any formal limitation not done to the present invention, it is every according to
Any simply modification, the equivalent variations made according to the technical spirit of the present invention to above example, each fall within the protection of the present invention
Within the scope of.
Claims (5)
- A kind of 1. strong paint formulation of anti-corrosion fire resistance property, it is characterised in that：Including 20 ~ 26 parts of titanium dioxide by weight, 10 ~ 15 parts of glacial acetic acid, 2 ~ 5 parts of organic epoxy resin, 5 ~ 7 parts of glycol monoethyl ether, 2 ~ 4 parts of dimethyl sulfoxide (DMSO), trbasic zinc phosphate 5 ~ 7 Part, 8 ~ 12 parts of barium chromate, 6 ~ 10 parts of aluminum oxide, 3 ~ 7 parts of rosin resin, 1 ~ 2 part of anti-yellowing resin, 5 ~ 7 parts of hydroxyethyl cellulose, silicon 3 ~ 5 parts of 10 ~ 12 parts of colloidal sol, 6 ~ 8 parts of methyl methacrylate, 12 ~ 18 parts of dehydrated castor oil and dimethyl malenate.
- A kind of 2. strong paint formulation of anti-corrosion fire resistance property according to claim 1, it is characterised in that：Described titanium dioxide 20 parts, 10 parts of glacial acetic acid, 2 parts of organic epoxy resin, 5 parts of glycol monoethyl ether, 2 parts of dimethyl sulfoxide (DMSO), 5 parts of trbasic zinc phosphate, chromium Sour 8 parts of barium, 6 parts of aluminum oxide, 3 parts of rosin resin, 1 part of anti-yellowing resin, 5 parts of hydroxyethyl cellulose, 10 parts of Ludox, metering system 3 parts of sour 6 parts of methyl esters, 12 parts of dehydrated castor oil and dimethyl malenate.
- A kind of 3. strong paint formulation of anti-corrosion fire resistance property according to claim 1, it is characterised in that：Described titanium dioxide 22 parts, 12 parts of glacial acetic acid, 2 parts of organic epoxy resin, 6 parts of glycol monoethyl ether, 2 parts of dimethyl sulfoxide (DMSO), 5 parts of trbasic zinc phosphate, chromium Sour 9 parts of barium, 7 parts of aluminum oxide, 4 parts of rosin resin, 1 part of anti-yellowing resin, 6 parts of hydroxyethyl cellulose, 11 parts of Ludox, metering system 3 parts of sour 6 parts of methyl esters, 14 parts of dehydrated castor oil and dimethyl malenate.
- A kind of 4. strong paint formulation of anti-corrosion fire resistance property according to claim 1, it is characterised in that：Described titanium dioxide 24 parts, 14 parts of glacial acetic acid, 4 parts of organic epoxy resin, 6 parts of glycol monoethyl ether, 2 parts of dimethyl sulfoxide (DMSO), 5 parts of trbasic zinc phosphate, chromium Sour 10 parts of barium, 8 parts of aluminum oxide, 4 parts of rosin resin, 1 part of anti-yellowing resin, 6 parts of hydroxyethyl cellulose, 10 parts of Ludox, methyl-prop 3 parts of 7 parts of e pioic acid methyl ester, 16 parts of dehydrated castor oil and dimethyl malenate.
- A kind of 5. strong paint formulation of anti-corrosion fire resistance property according to claim 1, it is characterised in that：Described titanium dioxide 26 parts, 15 parts of glacial acetic acid, 5 parts of organic epoxy resin, 7 parts of glycol monoethyl ether, 4 parts of dimethyl sulfoxide (DMSO), 7 parts of trbasic zinc phosphate, chromium Sour 12 parts of barium, 10 parts of aluminum oxide, 7 parts of rosin resin, 2 parts of anti-yellowing resin, 7 parts of hydroxyethyl cellulose, 12 parts of Ludox, methyl-prop 5 parts of 8 parts of e pioic acid methyl ester, 18 parts of dehydrated castor oil and dimethyl malenate.