CN107880618A - A kind of formula of fire-retardant paint - Google Patents
A kind of formula of fire-retardant paint Download PDFInfo
- Publication number
- CN107880618A CN107880618A CN201711251194.2A CN201711251194A CN107880618A CN 107880618 A CN107880618 A CN 107880618A CN 201711251194 A CN201711251194 A CN 201711251194A CN 107880618 A CN107880618 A CN 107880618A
- Authority
- CN
- China
- Prior art keywords
- parts
- fire
- boric acid
- formula
- pentaerythrite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of formula of fire-retardant paint, including titanium dioxide, Boratex, methyl methacrylate, trimethylolpropane trimethacrylate, dipropylene glycol dibenzoate, titanium carbide, borax, aluminium powder, butyl stearate, pentaerythrite, sorbitan monostearate, Ludox, 4 morpholine phenyl boric acids, flame retardant and acrylic resin are configured by weight and is modified casein filming agent；Stirring is uniformly mixed and heated after solid matter is crushed with liquid.The beneficial effects of the invention are as follows：The present invention has the advantages of fire resistance property is strong, run into nonflammable after naked light, in the absence of any potential safety hazard so as to improving the security performance of the security performance that uses of paint and storage, and suitable for the adverse circumstances such as high temperature, humidity, pH-value be higher, it has formula simple, low manufacture cost, applied widely, the advantages of being readily produced, and is easy to promote the use of.
Description
Technical field
It is a kind of formula of fire-retardant paint specifically the present invention relates to paint field.
Background technology
Paint is that one kind can firmly be covered in body surface, and the chemistry for playing protection, decoration, mark and other specific uses mixes
Compound coating.Paint as viscous oily pigment, it is inflammable in the case of not dry, it is not soluble in water, be slightly soluble in fat, dissolve in alcohol, aldehyde,
Ether, benzene, alkane, it is soluble in gasoline, kerosene, diesel oil.
All it is by three kinds of film forming matter, subsidiary film forming matter and auxiliary film forming matter no matter painting kind or form
Base substance forms：
Film forming matter：Also referred to as binding agent, it is organic high molecular compound such as natural resin that film forming matter is most of（It is rosin, big
Paint）, coating（Tung oil, flame retardant, soya-bean oil, fish oil etc.）, the mix such as synthetic resin, form by pyroreaction, also have
The paint of inorganic matter combination（Such as：Inorganic zinc rich paint）.It is the main body for forming paint, decides the performance of paint film.If no
Film forming matter, simple pigment and auxiliary material can not form paint film.
Subsidiary film forming matter：Including various pigment, extender pigment, rust resisting pigment.Pigment provides color and covering for paint film
Power, improves the protective value and decorative effect of paint, and the pigment of good weatherability can improve the service life of paint.Extender pigment can
It is folded multiple by the accumulation of pigment using the performance of itself " sheet, needle-like " structure to increase the thickness of paint film, form fish scale
The paint film of shape, the service life of paint film is improved, improve water proofing property and rust-proof effect.Rust resisting pigment passes through itself physics and chemistry
Anti-rust action, prevent that metal surface is by corrosion by air, chemicals attack for body surface.
Auxiliary film forming matter：Including various auxiliary agents, solvent, various auxiliary agents are in the production process of paint, storage process, use
Process and the forming process of paint film play very important effect.Although the amount used is all seldom, to the performance shadow of paint film
Ring very big.Even it can not form paint film such as：Do not do, sink to the bottom caking, skinning.
The content of the invention
It is an object of the invention to provide a kind of formula of long, the strong aging of fire resistance property the fire-retardant paint of service life.
The present invention is achieved through the following technical solutions：A kind of formula of fire-retardant paint, including titanium dioxide by weight
19 ~ 27 parts, 9 ~ 16 parts of Boratex, 3 ~ 6 parts of methyl methacrylate, 5 ~ 7 parts of trimethylolpropane trimethacrylate, DPG
2 ~ 4 parts of dibenzoate, 5 ~ 7 parts of titanium carbide, 8 ~ 12 parts of borax, 5 ~ 11 parts of aluminium powder, 3 ~ 7 parts of butyl stearate, pentaerythrite 1 ~ 2
Part, 5 ~ 7 parts of sorbitan monostearate, 10 ~ 12 parts of Ludox, 6 ~ 8 parts of 4- morpholines phenyl boric acid, 11 ~ 19 parts of flame retardant and
Acrylic resin is modified 3 ~ 5 parts of casein filming agent.
Described 20 parts of titanium dioxide, 10 parts of Boratex, 3 parts of methyl methacrylate, trimethylolpropane trimethacrylate 5
Part, 2 parts of dipropylene glycol dibenzoate, 5 parts of titanium carbide, 8 parts of borax, 6 parts of aluminium powder, 3 parts of butyl stearate, 5 parts of pentaerythrite,
5 parts of sorbitan monostearate, 10 parts of Ludox, 6 parts of 4- morpholines phenyl boric acid, 12 parts of flame retardant and acrylic resin are modified
3 parts of casein filming agent.
Described 22 parts of titanium dioxide, 12 parts of Boratex, 3 parts of methyl methacrylate, trimethylolpropane trimethacrylate 6
Part, 2 parts of dipropylene glycol dibenzoate, 5 parts of titanium carbide, 9 parts of borax, 7 parts of aluminium powder, 4 parts of butyl stearate, 6 parts of pentaerythrite,
6 parts of sorbitan monostearate, 11 parts of Ludox, 6 parts of 4- morpholines phenyl boric acid, 14 parts of flame retardant and acrylic resin are modified
3 parts of casein filming agent.
Described 24 parts of titanium dioxide, 14 parts of Boratex, 5 parts of methyl methacrylate, trimethylolpropane trimethacrylate 6
Part, 2 parts of dipropylene glycol dibenzoate, 5 parts of titanium carbide, 10 parts of borax, 8 parts of aluminium powder, 4 parts of butyl stearate, pentaerythrite 7
Part, 6 parts of sorbitan monostearate, 10 parts of Ludox, 7 parts of 4- morpholines phenyl boric acid, 16 parts of flame retardant and acrylic resin
Modified 3 parts of casein filming agent.
Described 26 parts of titanium dioxide, 15 parts of Boratex, 6 parts of methyl methacrylate, trimethylolpropane trimethacrylate 7
Part, 4 parts of dipropylene glycol dibenzoate, 7 parts of titanium carbide, 12 parts of borax, 10 parts of aluminium powder, 7 parts of butyl stearate, pentaerythrite 8
Part, 7 parts of sorbitan monostearate, 12 parts of Ludox, 8 parts of 4- morpholines phenyl boric acid, 18 parts of flame retardant and acrylic resin
Modified 5 parts of casein filming agent.
The present invention compared with prior art, has advantages below and beneficial effect：
The present invention has the advantages of fire resistance property is strong, run into it is nonflammable after naked light, in the absence of any potential safety hazard so as to improving
The security performance and the security performance of storage that paint uses, and suitable for the severe ring such as high temperature, humidity, pH-value be higher
Border, it has formula simple, low manufacture cost, applied widely, the advantages of being readily produced, is easy to promote the use of.
Embodiment
The present invention is described in further detail with reference to embodiment, but the implementation of the present invention is not limited to this.
Embodiment 1：
In the present embodiment, a kind of formula of fire-retardant paint, including 9 ~ 16 parts of 19 ~ 27 parts of titanium dioxide, Boratex by weight,
3 ~ 6 parts of methyl methacrylate, 5 ~ 7 parts of trimethylolpropane trimethacrylate, 2 ~ 4 parts of dipropylene glycol dibenzoate, carbonization
5 ~ 7 parts of titanium, 8 ~ 12 parts of borax, 5 ~ 11 parts of aluminium powder, 3 ~ 7 parts of butyl stearate, 1 ~ 2 part of pentaerythrite, sorbitol anhydride monostearate
5 ~ 7 parts of ester, 10 ~ 12 parts of Ludox, 6 ~ 8 parts of 4- morpholines phenyl boric acid, 11 ~ 19 parts of flame retardant and acrylic resin are modified casein
3 ~ 5 parts of film forming agent.Its collocation method includes following steps：
Step S1:19 ~ 27 parts of titanium dioxide, 9 ~ 16 parts of Boratex, 3 ~ 6 parts of methyl methacrylate, three hydroxyls are configured by weight
5 ~ 7 parts of propane tri, 2 ~ 4 parts of dipropylene glycol dibenzoate, 5 ~ 7 parts of titanium carbide, 8 ~ 12 parts of borax, aluminium powder 5 ~
11 parts, 3 ~ 7 parts of butyl stearate, 1 ~ 2 part of pentaerythrite, 5 ~ 7 parts of sorbitan monostearate, 10 ~ 12 parts of Ludox, 4-
6 ~ 8 parts of quinoline phenyl boric acid, 11 ~ 19 parts of flame retardant and acrylic resin are modified 3 ~ 5 parts of casein filming agent；
Step S2：Titanium dioxide, Boratex, titanium carbide, borax, aluminium powder, butyl stearate, Ludox are well mixed, will be uniform
Mixed mixture is crushed to more than 800 mesh；
Step S3：By the mixture after being crushed in step S2 and methyl methacrylate, trimethylolpropane trimethacrylate, two
Propylene glycol dibenzoate, pentaerythrite, hydroxy ethyl fiber, 4- morpholines phenyl boric acid, flame retardant and acrylic resin are modified junket
Albumen film forming agent is uniformly mixed and heated to 120 DEG C ~ 150 DEG C；
Step S4：The mixture in step S3 is set to be incubated 9 ~ 16 minutes in the environment of 120 DEG C ~ 150 DEG C, soaking time terminates
Afterwards, stirred 20 minutes ~ 35 minutes in the environment of 120 DEG C ~ 150 DEG C, mixing speed is 800 ~ 1200 revs/min；
Step S5：After stirring, Temperature fall is painted.The present invention has the advantages of high temperature resistant, fire-resistant ability is strong, can reduce
Trigger the risk of fire, consequently facilitating storage and managenent, and be painted on after furniture, wall coverings, wall, can be when fire occurs
Play fire retardation, loss caused by reduce fire, its have formula simple, low manufacture cost, it is applied widely, be easy to raw
The advantages of production, it is easy to promote the use of.
Embodiment 2：
On the basis of above-described embodiment, in the present embodiment, a kind of formula of fire-retardant paint, including by weight described
20 parts of titanium dioxide, 10 parts of Boratex, 2 parts of methyl methacrylate, 5 parts of trimethylolpropane trimethacrylate, DPG two
2 parts of benzoic ether, 5 parts of titanium carbide, 8 parts of borax, 6 parts of aluminium powder, 3 parts of butyl stearate, 5 parts of pentaerythrite, sorbitol anhydride list are hard
5 parts of resin acid ester, 10 parts of Ludox, 6 parts of 4- morpholines phenyl boric acid, 12 parts of flame retardant and acrylic resin are modified casein filming agent
3 parts.In the present embodiment, other parts not described are identical with the content of above-described embodiment, therefore do not repeat.
Embodiment 3：
On the basis of above-described embodiment, in the present embodiment, a kind of formula of fire-retardant paint, including titanium dioxide by weight
20 parts, 10 parts of Boratex, 3 parts of methyl methacrylate, 5 parts of trimethylolpropane trimethacrylate, DPG dibenzoic acid
2 parts of ester, 5 parts of titanium carbide, 8 parts of borax, 6 parts of aluminium powder, 3 parts of butyl stearate, 6 parts of pentaerythrite, sorbitan monostearate 5
Part, 10 parts of Ludox, 6 parts of 4- morpholines phenyl boric acid, 12 parts of flame retardant and acrylic resin are modified 3 parts of casein filming agent.This
In embodiment, other parts not described are identical with the content of above-described embodiment, therefore do not repeat.
Embodiment 4：
On the basis of above-described embodiment, in the present embodiment, a kind of formula of fire-retardant paint, including titanium dioxide by weight
22 parts, 12 parts of Boratex, 3 parts of methyl methacrylate, 6 parts of trimethylolpropane trimethacrylate, DPG dibenzoic acid
2 parts of ester, 5 parts of titanium carbide, 9 parts of borax, 7 parts of aluminium powder, 4 parts of butyl stearate, 7 parts of pentaerythrite, sorbitan monostearate 6
Part, 11 parts of Ludox, 6 parts of 4- morpholines phenyl boric acid, 14 parts of flame retardant and acrylic resin are modified 3 parts of casein filming agent.This
In embodiment, other parts not described are identical with the content of above-described embodiment, therefore do not repeat.
Embodiment 5：
On the basis of above-described embodiment, in the present embodiment, a kind of formula of fire-retardant paint, including titanium dioxide by weight
24 parts, 14 parts of Boratex, 5 parts of methyl methacrylate, 6 parts of trimethylolpropane trimethacrylate, DPG dibenzoic acid
2 parts of ester, 5 parts of titanium carbide, 10 parts of borax, 8 parts of aluminium powder, 4 parts of butyl stearate, 8 parts of pentaerythrite, sorbitan monostearate
6 parts, 10 parts of Ludox, 7 parts of 4- morpholines phenyl boric acid, 16 parts of flame retardant and acrylic resin are modified 3 parts of casein filming agent.This
In embodiment, other parts not described are identical with the content of above-described embodiment, therefore do not repeat.
Embodiment 6：
On the basis of above-described embodiment, in the present embodiment, a kind of formula of fire-retardant paint, including titanium dioxide by weight
26 parts, 15 parts of Boratex, 6 parts of methyl methacrylate, 7 parts of trimethylolpropane trimethacrylate, DPG dibenzoic acid
4 parts of ester, 7 parts of titanium carbide, 12 parts of borax, 10 parts of aluminium powder, 7 parts of butyl stearate, 2 parts of pentaerythrite, sorbitol anhydride monostearate
7 parts of ester, 12 parts of Ludox, 8 parts of 4- morpholines phenyl boric acid, 18 parts of flame retardant and acrylic resin are modified 5 parts of casein filming agent.
In the present embodiment, other parts not described are identical with the content of above-described embodiment, therefore do not repeat.
It is described above, be only presently preferred embodiments of the present invention, any formal limitation not done to the present invention, it is every according to
Any simply modification, the equivalent variations made according to the technical spirit of the present invention to above example, each fall within the protection of the present invention
Within the scope of.
Claims (5)
- A kind of 1. formula of fire-retardant paint, it is characterised in that：Including 19 ~ 27 parts of titanium dioxide, Boratex 9 ~ 16 by weight Part, 5 ~ 7 parts of titanium carbide, 8 ~ 12 parts of borax, 5 ~ 11 parts of aluminium powder, 3 ~ 6 parts of methyl methacrylate, trimethylolpropane tris acrylic acid 5 ~ 7 parts of ester, 2 ~ 4 parts of dipropylene glycol dibenzoate, 3 ~ 7 parts of butyl stearate, 5 ~ 7 parts of pentaerythrite, sorbitol anhydride list are stearic 5 ~ 7 parts of acid esters, 10 ~ 12 parts of Ludox, 6 ~ 8 parts of 4- morpholines phenyl boric acid, 11 ~ 19 parts of flame retardant and acrylic resin are modified junket egg White 3 ~ 5 parts of film forming agent.
- A kind of 2. formula of fire-retardant paint according to claim 1, it is characterised in that：Described 20 parts of titanium dioxide, boric acid 10 parts of sodium, 3 parts of methyl methacrylate, 5 parts of trimethylolpropane trimethacrylate, 2 parts of dipropylene glycol dibenzoate, carbonization 5 parts of titanium, 8 parts of borax, 6 parts of aluminium powder, 3 parts of butyl stearate, 5 parts of pentaerythrite, 5 parts of sorbitan monostearate, Ludox 10 parts, 6 parts of 4- morpholines phenyl boric acid, 12 parts of flame retardant and acrylic resin are modified 3 parts of casein filming agent.
- A kind of 3. formula of fire-retardant paint according to claim 1, it is characterised in that：Described 22 parts of titanium dioxide, boric acid 12 parts of sodium, 3 parts of methyl methacrylate, 6 parts of trimethylolpropane trimethacrylate, 2 parts of dipropylene glycol dibenzoate, carbonization 5 parts of titanium, 9 parts of borax, 7 parts of aluminium powder, 4 parts of butyl stearate, 6 parts of pentaerythrite, 6 parts of sorbitan monostearate, Ludox 11 parts, 6 parts of 4- morpholines phenyl boric acid, 14 parts of flame retardant and acrylic resin are modified 3 parts of casein filming agent.
- A kind of 4. formula of fire-retardant paint according to claim 1, it is characterised in that：Described 24 parts of titanium dioxide, boric acid 14 parts of sodium, 5 parts of methyl methacrylate, 6 parts of trimethylolpropane trimethacrylate, 2 parts of dipropylene glycol dibenzoate, carbonization 5 parts of titanium, 10 parts of borax, 8 parts of aluminium powder, 4 parts of butyl stearate, 7 parts of pentaerythrite, 6 parts of sorbitan monostearate, Ludox 10 parts, 7 parts of 4- morpholines phenyl boric acid, 16 parts of flame retardant and acrylic resin are modified 3 parts of casein filming agent.
- A kind of 5. formula of fire-retardant paint according to claim 1, it is characterised in that：Described 26 parts of titanium dioxide, boric acid 15 parts of sodium, 6 parts of methyl methacrylate, 7 parts of trimethylolpropane trimethacrylate, 4 parts of dipropylene glycol dibenzoate, carbonization 7 parts of titanium, 12 parts of borax, 10 parts of aluminium powder, 7 parts of butyl stearate, 8 parts of pentaerythrite, 7 parts of sorbitan monostearate, silicon are molten 12 parts of glue, 8 parts of 4- morpholines phenyl boric acid, 18 parts of flame retardant and acrylic resin are modified 5 parts of casein filming agent.