CN104073041A - Steel surface treatment paint - Google Patents
Steel surface treatment paint Download PDFInfo
- Publication number
- CN104073041A CN104073041A CN201410352625.4A CN201410352625A CN104073041A CN 104073041 A CN104073041 A CN 104073041A CN 201410352625 A CN201410352625 A CN 201410352625A CN 104073041 A CN104073041 A CN 104073041A
- Authority
- CN
- China
- Prior art keywords
- parts
- paint
- resin
- steel surface
- acrylic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a steel surface treatment paint which comprises the following raw material ingredients in parts: 3-5 parts of phenyl hydroxide, 20-22 parts of epoxy resin, 18-20 parts of polyester resin, 12-15 parts of rosin resin, 10-12 parts of terpene resin, 8-10 parts of alkyd resin, 10-12 parts of amino resin, 15-18 parts of acrylic resin, 5-6 parts of a lacquer thinner, 8-10 parts of organosilicon oil, 5-8 parts of glycerine, 3-5 parts of ethyl acetate, 5-6 parts of activated zinc oxide, 5-6 parts of fast-dissolving sodium silicate, 3-6 parts of dimethyl malonate, 3-5 parts of glycidyl methacrylate, 5-8 parts of ferric hydroxide, 2-3 parts of polyvinyl alcohol, 20-25 parts of vinyl acetate-acrylic emulsion and 20-30 parts of acrylic emulsion. The steel surface treatment paint mainly plays a wetting and permeating effect on loose rust to separate and wrap the rust to prevent further development of rusting; meanwhile, after forming a film, the paint interacts with the rust by virtue of slow hydrolysis to form an acid complex to achieve the purpose of rust removal; the paint has stable properties, and increases the density of the paint film to prevent permeation of water and oxygen in air.
Description
Technical field
The present invention relates to a kind of steel surface and process the technical field of paint, relate in particular to one can directly eliminate rust, antirust, the steel surface that can make again priming paint or be configured to finish paint is processed paint.
Background technology
Traditional rust-inhibiting paint, comprise new japanning, maintenance repaints and necessarily requires fabulous surface treatment, removes the corrosion thing of steel surface by ways such as artificial, machinery or pickling, surface-treated cost generally accounts for 45% left and right of coating project total price, need to consume a large amount of labor forces and economic cost.For some heavy constructions, as bridge, boats and ships etc., long construction period, has given the steel of priming paint immediately, and paint film is also often damaged, and lays equal stress on and newly gets rusty, and huge like this engineering is carried out to overall on-the-spot surface treatment very difficult.
Summary of the invention
The object of the invention is the shortcoming in order to overcome above-mentioned prior art, provide a kind of steel surface to process paint, this steel surface is processed main moistening, the osmosis of utilizing loose iron rust of paint, iron rust is cut apart and is enclosed among paint vehicle, stop further developing of corrosion, simultaneously after film forming, by being hydrolyzed slowly interaction, form what thing of sour network hard to tolerate with iron rust, reach rust cleaning object; Stable in properties, the density of raising paint film, prevents the infiltration of moisture in air and oxygen.
The technical solution adopted for the present invention to solve the technical problems is: a kind of steel surface is processed paint, composition of raw materials component by following umber forms: 3-5 part phenol, 20-22 part epoxy resin, 18-20 part vibrin, 12-15 part Gum Rosin, 10-12 part terpine resin, 8-10 part Synolac, 10-12 part aminoresin, 15-18 part acrylic resin, 5-6 part lacquer thinner, 8-10 organic silicone oil, 5-8 part glycerol, 3-5 part ethyl acetate, 5-6 part active zinc flower, 5-6 part quick dissolved sodium silicate, 3-6 part dimethyl malonate, 3-5 part glycidyl methacrylate, 5-8 part ironic hydroxide, 2-3 part polyvinyl alcohol, 20-25 part acrylate and vinyl acetate emulsion, 20-30 part ACRYLIC EMULSION.
Further, each composition of raw materials component is: 3 parts of phenol, 20 parts of epoxy resin, 18 parts of vibrin, 12 parts of Gum Rosins, 10 parts of terpine resins, 8 parts of Synolac, 10 parts of aminoresin, 15 parts of acrylic resins, 5 parts of lacquer thinner, 8 organic silicone oils, 5 parts of glycerol, 3 parts of ethyl acetate, 5 parts of active zinc flowers, 5 parts of quick dissolved sodium silicates, 3 parts of dimethyl malonates, 3 parts of glycidyl methacrylate, 5 parts of ironic hydroxides, 2 parts of polyvinyl alcohol, 20 parts of acrylate and vinyl acetate emulsions, 20 parts of ACRYLIC EMULSION.
Or each composition of raw materials component is: 5 parts of phenol, 22 parts of epoxy resin, 20 parts of vibrin, 15 parts of Gum Rosins, 12 parts of terpine resins, 10 parts of Synolac, 12 parts of aminoresin, 18 parts of acrylic resins, 6 parts of lacquer thinner, 10 organic silicone oils, 8 parts of glycerol, 5 parts of ethyl acetate, 6 parts of active zinc flowers, 6 parts of quick dissolved sodium silicates, 6 parts of dimethyl malonates, 5 parts of glycidyl methacrylate, 8 parts of ironic hydroxides, 3 parts of polyvinyl alcohol, 25 parts of acrylate and vinyl acetate emulsions, 30 parts of ACRYLIC EMULSION.
In sum, the invention has the beneficial effects as follows: steel surface of the present invention is processed main moistening, the osmosis of utilizing loose iron rust of paint, iron rust is cut apart and is enclosed among paint vehicle, stop further developing of corrosion, simultaneously after film forming, by being hydrolyzed slowly interaction, form what thing of sour network hard to tolerate with iron rust, reach rust cleaning object; Stable in properties, the density of raising paint film, prevents the infiltration of moisture in air and oxygen.
Embodiment
Embodiment 1
The described a kind of steel surface of the present embodiment 1 is processed paint, is made up of the composition of raw materials component of following umber: 3 parts of phenol, 20 parts of epoxy resin, 18 parts of vibrin, 12 parts of Gum Rosins, 10 parts of terpine resins, 8 parts of Synolac, 10 parts of aminoresin, 15 parts of acrylic resins, 5 parts of lacquer thinner, 8 organic silicone oils, 5 parts of glycerol, 3 parts of ethyl acetate, 5 parts of active zinc flowers, 5 parts of quick dissolved sodium silicates, 3 parts of dimethyl malonates, 3 parts of glycidyl methacrylate, 5 parts of ironic hydroxides, 2 parts of polyvinyl alcohol, 20 parts of acrylate and vinyl acetate emulsions, 20 parts of ACRYLIC EMULSION.
Embodiment 2
The described a kind of steel surface of the present embodiment 2 is processed paint, composition of raw materials component by following umber forms: 5 parts of phenol, 22 parts of epoxy resin, 20 parts of vibrin, 15 parts of Gum Rosins, 12 parts of terpine resins, 10 parts of Synolac, 12 parts of aminoresin, 18 parts of acrylic resins, 6 parts of lacquer thinner, 10 organic silicone oils, 8 parts of glycerol, 5 parts of ethyl acetate, 6 parts of active zinc flowers, 6 parts of quick dissolved sodium silicates, 6 parts of dimethyl malonates, 5 parts of glycidyl methacrylate, 8 parts of ironic hydroxides, 3 parts of polyvinyl alcohol, 25 parts of acrylate and vinyl acetate emulsions, 30 parts of ACRYLIC EMULSION.
The above, be only preferred embodiment of the present invention, not principle of the present invention done to any pro forma restriction.Any simple modification, equivalent variations and modification that every foundation technical spirit of the present invention is done above embodiment, all still belong in the scope of technical scheme of the present invention.
Claims (3)
1. a steel surface is processed paint, it is characterized in that, composition of raw materials component by following umber forms: 3-5 part phenol, 20-22 part epoxy resin, 18-20 part vibrin, 12-15 part Gum Rosin, 10-12 part terpine resin, 8-10 part Synolac, 10-12 part aminoresin, 15-18 part acrylic resin, 5-6 part lacquer thinner, 8-10 organic silicone oil, 5-8 part glycerol, 3-5 part ethyl acetate, 5-6 part active zinc flower, 5-6 part quick dissolved sodium silicate, 3-6 part dimethyl malonate, 3-5 part glycidyl methacrylate, 5-8 part ironic hydroxide, 2-3 part polyvinyl alcohol, 20-25 part acrylate and vinyl acetate emulsion, 20-30 part ACRYLIC EMULSION.
2. a kind of steel surface according to claim 1 is processed paint, it is characterized in that, each composition of raw materials component is: 3 parts of phenol, 20 parts of epoxy resin, 18 parts of vibrin, 12 parts of Gum Rosins, 10 parts of terpine resins, 8 parts of Synolac, 10 parts of aminoresin, 15 parts of acrylic resins, 5 parts of lacquer thinner, 8 organic silicone oils, 5 parts of glycerol, 3 parts of ethyl acetate, 5 parts of active zinc flowers, 5 parts of quick dissolved sodium silicates, 3 parts of dimethyl malonates, 3 parts of glycidyl methacrylate, 5 parts of ironic hydroxides, 2 parts of polyvinyl alcohol, 20 parts of acrylate and vinyl acetate emulsions, 20 parts of ACRYLIC EMULSION.
3. a kind of steel surface according to claim 1 is processed paint, it is characterized in that, each composition of raw materials component is: 5 parts of phenol, 22 parts of epoxy resin, 20 parts of vibrin, 15 parts of Gum Rosins, 12 parts of terpine resins, 10 parts of Synolac, 12 parts of aminoresin, 18 parts of acrylic resins, 6 parts of lacquer thinner, 10 organic silicone oils, 8 parts of glycerol, 5 parts of ethyl acetate, 6 parts of active zinc flowers, 6 parts of quick dissolved sodium silicates, 6 parts of dimethyl malonates, 5 parts of glycidyl methacrylate, 8 parts of ironic hydroxides, 3 parts of polyvinyl alcohol, 25 parts of acrylate and vinyl acetate emulsions, 30 parts of ACRYLIC EMULSION.