CN104387923A - Anticorrosive paint - Google Patents
Anticorrosive paint Download PDFInfo
- Publication number
- CN104387923A CN104387923A CN201410741594.1A CN201410741594A CN104387923A CN 104387923 A CN104387923 A CN 104387923A CN 201410741594 A CN201410741594 A CN 201410741594A CN 104387923 A CN104387923 A CN 104387923A
- Authority
- CN
- China
- Prior art keywords
- parts
- protective system
- anticorrosive paint
- resistance
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anticorrosive paint which comprises 4-9 parts of zinc-rich epoxy powder, 5-8 parts of sodium hexametaphosphate, 22-26 parts of water-based acrylic acid modified epoxy resin, 12-16 parts of alkyd resin, 20-30 parts of aluminum tripolyphosphate, 6-9 parts of hydroxyethyl cellulose, 18-24 parts of talcum powder and 4-8 parts of thickener. The anticorrosive paint has the advantages of high brine resistance, favorable weather resistance, favorable corrosion resistance, high adhesive force, high wear resistance and the like.
Description
Technical field
The present invention relates to building coating field, particularly a kind of protective system.
Background technology
protective system, is generally divided into conventional protective system and heavy-duty coating, is requisite a kind of coating in paint.Conventional protective system is under general condition, plays etch-proof effect to metal etc., the life-span that protection non-ferrous metal uses; Heavy-duty coating refers to relatively conventional protective system, can apply in relatively harsh corrosive environment, and has a class protective system that can reach the protection period longer than conventional protective system.The anti-corrosion capability of existing coating is general, is difficult to meet the demand of user to anticorrosion with coat erosion ability.
Summary of the invention
The technical problem that the present invention mainly solves is to provide a kind of protective system, solves that protective system preservative effect is poor, problem not environmentally.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: provide a kind of protective system, its composition of raw materials is made up of the material of following masses percentage composition:
4 ~ 9 parts, zinc-riched epoxy powder;
Six 5 ~ 8 parts, phosphorus meta-acid sodium;
Aqueous acrylic modified epoxy resin 22 ~ 26 parts;
Synolac 12 ~ 16 parts;
Aluminium triphosphate 20 ~ 30 parts;
Natvosol 6 ~ 9 parts;
Talcum powder 18 ~ 24 parts;
Thickening material 4 ~ 8 parts.
The invention has the beneficial effects as follows: a kind of protective system is provided that there is the advantages such as resistance to salt water is strong, good weatherability, antiseptic property are good, stronger sticking power and wear resisting property.
Embodiment
Below preferred embodiment of the present invention is described in detail, can be easier to make advantages and features of the invention be readily appreciated by one skilled in the art, thus more explicit defining is made to protection scope of the present invention.
The embodiment of the present invention 1 comprises: a kind of protective system, and its composition of raw materials is made up of the material of following masses percentage composition:
4 parts, zinc-riched epoxy powder;
Six 5 parts, phosphorus meta-acid sodium;
Aqueous acrylic modified epoxy resin 22 parts;
Synolac 12 parts;
Aluminium triphosphate 20 parts;
Natvosol 6 parts;
Talcum powder 18 parts;
Thickening material 4 parts.
The embodiment of the present invention 2 comprises: a kind of protective system, and its composition of raw materials is made up of the material of following masses percentage composition:
6 parts, zinc-riched epoxy powder;
Six 7 parts, phosphorus meta-acid sodium;
Aqueous acrylic modified epoxy resin 24 parts;
Synolac 14 parts;
Aluminium triphosphate 26 parts;
Natvosol 8 parts;
Talcum powder 22 parts;
Thickening material 6 parts.
The embodiment of the present invention 3 comprises: a kind of protective system, and its composition of raw materials is made up of the material of following masses percentage composition:
9 parts, zinc-riched epoxy powder;
Six 8 parts, phosphorus meta-acid sodium;
Aqueous acrylic modified epoxy resin 26 parts;
Synolac 16 parts;
Aluminium triphosphate 30 parts;
Natvosol 9 parts;
Talcum powder 24 parts;
Thickening material 8 parts.
Above-described embodiment is only for illustrating technical conceive of the present invention and feature; its object is to person skilled in the art can be understood content of the present invention and be implemented; can not limit the scope of the invention with this; all equivalences done according to spirit of the present invention change or modify, and all should be encompassed in protection scope of the present invention.
Claims (1)
1. a protective system, is characterized in that: its composition of raw materials is made up of the material of following masses percentage composition:
4 ~ 9 parts, zinc-riched epoxy powder;
Six 5 ~ 8 parts, phosphorus meta-acid sodium;
Aqueous acrylic modified epoxy resin 22 ~ 26 parts;
Synolac 12 ~ 16 parts;
Aluminium triphosphate 20 ~ 30 parts;
Natvosol 6 ~ 9 parts;
Talcum powder 18 ~ 24 parts;
Thickening material 4 ~ 8 parts.