CN105152618A - Anti-corrosion composite and preparation method thereof - Google Patents
Anti-corrosion composite and preparation method thereof Download PDFInfo
- Publication number
- CN105152618A CN105152618A CN201510602577.4A CN201510602577A CN105152618A CN 105152618 A CN105152618 A CN 105152618A CN 201510602577 A CN201510602577 A CN 201510602577A CN 105152618 A CN105152618 A CN 105152618A
- Authority
- CN
- China
- Prior art keywords
- parts
- composite material
- sanitas
- preparation
- oxidation inhibitor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anti-corrosion composite and a preparation method thereof, and belongs to the technical field of building materials. The anti-corrosion composite is prepared from, by weight, 10-20 parts of gypsum powder, 15-25 parts of talcum powder, 4-8 parts of carbon fibers, 4-8 parts of wood fiber, 3-9 parts of mica powder, 2-4 parts of dispersing agents, 1.2-2 parts of antioxidants, 1-2 parts of preservatives and 10-30 parts of water. According to the anti-corrosion composite, the anti-corrosion and waterproof effects are good, the adhesion property is excellent, the dangerous hidden dangers of buildings are reduced, the service life of the buildings is prolonged, and the preparation method is simple and suitable for scale production.
Description
Technical field
The present invention relates to a kind of antisepsis composite material and preparation method thereof, belong to building material technical field.
Background technology
Protective system, is generally divided into conventional protective system and heavy-duty coating, is requisite a kind of coating in paint.Conventional protective system is under general condition, plays etch-proof effect to metal etc., the life-span that protection non-ferrous metal uses; Heavy-duty coating refers to relatively conventional protective system, can apply in relatively harsh corrosive environment, and has a class protective system that can reach the protection period longer than conventional protective system.In some specific architectural environments, impregnating material is absolutely necessary coat, it play architecture protection thing not corrode by severe environment, improve work-ing life, avoid buildings corrosion and the dangerous hidden danger come.
Summary of the invention
The object of the invention is to make up the deficiencies in the prior art, a kind of antisepsis composite material and preparation method thereof is provided.Antisepsis composite material of the present invention, anticorrosion, good water-proof effect, adhesion property is excellent, reduces the dangerous hidden danger of building, improves the work-ing life of buildings, and preparation method is simple, is applicable to large-scale production.
The technical scheme that the present invention solves the problems of the technologies described above is as follows: a kind of antisepsis composite material, comprises the raw material of following parts by weight: terra alba 10 ~ 20 parts, talcum powder 15 ~ 25 parts, 4 ~ 8 parts, carbon fiber, wood fibre 4 ~ 8 parts, mica powder 3 ~ 9 parts, dispersion agent 2 ~ 4 parts, 1.2 ~ 2 parts, oxidation inhibitor, sanitas 1 ~ 2 part and 10 ~ 30 parts, water.
On the basis of technique scheme, the present invention can also do following improvement.
Further, the raw material of following parts by weight is comprised: terra alba 15 parts, talcum powder 20 parts, 6 parts, carbon fiber, wood fibre 6 parts, mica powder 6 parts, dispersion agent 3 parts, 1.6 parts, oxidation inhibitor, sanitas 1.5 parts and 20 parts, water.
Further, described dispersion agent is fatty acid polyglycol ester.
Further, described oxidation inhibitor is oxidation inhibitor 16.
Further, described sanitas is isothiazoline-3-ketone sanitas.
A kind of preparation method of antisepsis composite material, comprise the steps: the raw material getting following parts by weight: terra alba 10 ~ 20 parts, talcum powder 15 ~ 25 parts, 4 ~ 8 parts, carbon fiber, wood fibre 4 ~ 8 parts, mica powder 3 ~ 9 parts, dispersion agent 2 ~ 4 parts, 1.2 ~ 2 parts, oxidation inhibitor, sanitas 1 ~ 2 part and 10 ~ 30 parts, water, after mixing, obtain described antisepsis composite material.
On the basis of technique scheme, the present invention can also do following improvement.
Further, the parts by weight of described raw material are: terra alba 15 parts, talcum powder 20 parts, 6 parts, carbon fiber, wood fibre 6 parts, mica powder 6 parts, dispersion agent 3 parts, 1.6 parts, oxidation inhibitor, sanitas 1.5 parts and 20 parts, water.
Further, described dispersion agent is fatty acid polyglycol ester.
Further, described oxidation inhibitor is oxidation inhibitor 16.
Further, described sanitas is isothiazoline-3-ketone sanitas.
The invention has the beneficial effects as follows:
(1) antisepsis composite material of the present invention, anticorrosion, good water-proof effect, adhesion property is excellent, reduces the dangerous hidden danger of building, improves the work-ing life of buildings,
(2) preparation method of the present invention is simple, with low cost, wide market, is applicable to large-scale production.
Embodiment
Be described principle of the present invention and feature below in conjunction with specific embodiment, example, only for explaining the present invention, is not intended to limit scope of the present invention.
Embodiment 1:
A kind of antisepsis composite material, comprises the raw material of following parts by weight: terra alba 10 parts, talcum powder 25 parts, 4 parts, carbon fiber, wood fibre 8 parts, mica powder 3 parts, fatty acid polyglycol ester 4 parts, 161.2 parts, oxidation inhibitor, isothiazoline-3-ketone sanitas 2 parts and 10 parts, water.
A kind of preparation method of antisepsis composite material, comprise the steps: the raw material getting following parts by weight: terra alba 10 parts, talcum powder 25 parts, 4 parts, carbon fiber, wood fibre 8 parts, mica powder 3 parts, fatty acid polyglycol ester 4 parts, 161.2 parts, oxidation inhibitor, isothiazoline-3-ketone sanitas 2 parts and 10 parts, water, after mixing, obtain described antisepsis composite material.
Embodiment 2:
A kind of antisepsis composite material, comprises the raw material of following parts by weight: terra alba 15 parts, talcum powder 20 parts, 6 parts, carbon fiber, wood fibre 6 parts, mica powder 6 parts, fatty acid polyglycol ester 3 parts, 161.6 parts, oxidation inhibitor, isothiazoline-3-ketone sanitas 1.5 parts and 20 parts, water.
A kind of preparation method of antisepsis composite material, comprise the steps: the raw material getting following parts by weight: terra alba 15 parts, talcum powder 20 parts, 6 parts, carbon fiber, wood fibre 6 parts, mica powder 6 parts, fatty acid polyglycol ester 3 parts, 161.6 parts, oxidation inhibitor, isothiazoline-3-ketone sanitas 1.5 parts and 20 parts, water, after mixing, obtain described antisepsis composite material.
Embodiment 3:
A kind of antisepsis composite material, comprises the raw material of following parts by weight: terra alba 20 parts, talcum powder 15 parts, 8 parts, carbon fiber, wood fibre 4 parts, mica powder 9 parts, fatty acid polyglycol ester 2 parts, 162 parts, oxidation inhibitor, isothiazoline-3-ketone sanitas 1 part and 30 parts, water.
A kind of preparation method of antisepsis composite material, comprise the steps: the raw material getting following parts by weight: terra alba 20 parts, talcum powder 15 parts, 8 parts, carbon fiber, wood fibre 4 parts, mica powder 9 parts, fatty acid polyglycol ester 2 parts, 162 parts, oxidation inhibitor, isothiazoline-3-ketone sanitas 1 part and 30 parts, water, after mixing, obtain described antisepsis composite material.
The foregoing is only preferred embodiment of the present invention, not in order to limit the present invention, within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (10)
1. an antisepsis composite material, it is characterized in that, comprise the raw material of following parts by weight: terra alba 10 ~ 20 parts, talcum powder 15 ~ 25 parts, 4 ~ 8 parts, carbon fiber, wood fibre 4 ~ 8 parts, mica powder 3 ~ 9 parts, dispersion agent 2 ~ 4 parts, 1.2 ~ 2 parts, oxidation inhibitor, sanitas 1 ~ 2 part and 10 ~ 30 parts, water.
2. a kind of antisepsis composite material according to claim 1, it is characterized in that, comprise the raw material of following parts by weight: terra alba 15 parts, talcum powder 20 parts, 6 parts, carbon fiber, wood fibre 6 parts, mica powder 6 parts, dispersion agent 3 parts, 1.6 parts, oxidation inhibitor, sanitas 1.5 parts and 20 parts, water.
3. a kind of antisepsis composite material according to claim 1 and 2, is characterized in that, described dispersion agent is fatty acid polyglycol ester.
4. a kind of antisepsis composite material according to claim 1 and 2, is characterized in that, described oxidation inhibitor is oxidation inhibitor 16.
5. a kind of antisepsis composite material according to claim 1 and 2, is characterized in that, described sanitas is isothiazoline-3-ketone sanitas.
6. the preparation method of an antisepsis composite material, it is characterized in that, comprise the steps: the raw material getting following parts by weight: terra alba 10 ~ 20 parts, talcum powder 15 ~ 25 parts, 4 ~ 8 parts, carbon fiber, wood fibre 4 ~ 8 parts, mica powder 3 ~ 9 parts, dispersion agent 2 ~ 4 parts, 1.2 ~ 2 parts, oxidation inhibitor, sanitas 1 ~ 2 part and 10 ~ 30 parts, water, after mixing, obtain described antisepsis composite material.
7. the preparation method of a kind of antisepsis composite material according to claim 6, it is characterized in that, the parts by weight of described raw material are: terra alba 15 parts, talcum powder 20 parts, 6 parts, carbon fiber, wood fibre 6 parts, mica powder 6 parts, dispersion agent 3 parts, 1.6 parts, oxidation inhibitor, sanitas 1.5 parts and 20 parts, water.
8. the preparation method of a kind of antisepsis composite material according to claim 6 or 7, is characterized in that, described dispersion agent is fatty acid polyglycol ester.
9. the preparation method of a kind of antisepsis composite material according to claim 6 or 7, is characterized in that, described oxidation inhibitor is oxidation inhibitor 16.
10. the preparation method of a kind of antisepsis composite material according to claim 6 or 7, is characterized in that, described sanitas is isothiazoline-3-ketone sanitas.